Dureza Superficial de Resinas Compostas Nanoparticuladas e Bulk Fill Expostas a Suplementos Nutricionais / Surface Hardness of Composite Resins Nanoparticulate and Bulk Fill Exposed to Nutritional Supplements

Objetivo: Avaliar a microdureza superficial de duas resinas compostas após imersão controlada a dois suplementos nutricionais à base de carboidratos, desenvolvidos para indivíduos que praticam atividade esportiva. Materiais e Métodos: Utilizou-se as resinas compostas Filtek Z350 XT (3M ESPE); Filtek bulk Fill (3M ESPE) ambas na cor A3. Foram confeccionados 60 corpos- -de-prova, 30 para cada material restaurador, os quais foram divididos nos seguintes grupos: Grupo 1 - controle; Grupo 2 ­ imersão em 20 mL de Gatorade (AmBev) durante 5 minutos 3 vezes por dia; Grupo 3 - imersão em 30 g de gel de carboidrato Carbo Gel (Vox Suplementos) durante 5 minutos 3 vezes por dia. Em todos os grupos o período de reposição foi de 15 dias. Durante os intervalos, as resinas ficaram armazenadas em saliva artificial a 37º C. Foi realizado o teste de microdureza Vickers com base na norma ISO 4049 com o auxílio de um Microdurometro Vickers - Buehler - Lake Bluff, Illinois/USA (MMT-3) com a carga de 50 gf por 30 segundos, foram realizadas 5 endentações por corpo-de-prova, uma no centro e quatro nas periferias. A média dos valores de dureza foi comparada usando o teste ANOVA e o pós-teste de Tukey, em nível de significância de 5,0%. Resultados: Todos os corpos de prova que ficaram imersos em Gatorade e Gel de carboidrato apresentaram valores de microdureza estatisticamente menores, quando comparados aos grupos controle. Conclusão: A imersão de resinas compostas em suplementos alimentares Gatorade (Ambev) e Carbo Gel (Vox Suplementos) diminui significativamente sua dureza superficial.

Objective: To evaluate the surface microhardness of two composite resins when exposed to two nutritional supplements based on carbohydrates developed for sports activity. Materials and Methods: Filtek Z350 XT composite resins (3M ESPE) were used; Filtek bulk Fill (3M ESPE) both in color A3. Sixty specimens were prepared, 30 of which were for each restorative material, divided into the following groups: Group 1 (control); Group 2 - immersion in 20 mL of Gatorade (AmBev) for 5 minutes 3 times per day; Group 3 - immersion in 30 g Carbo Gel Carbohydrate Gel (Vox Supplements) for 5 minutes 3 times a day, the process was repeated for 15 days. The Vickers micro hardness test was performed based on ISO 4049 with the aid of a Vickers - Buehler - Lake Bluff, Illinois / USA (MMT - 3) Microduometer with a load of 50 gF for 30 seconds. Performing 5 indentations per body of evidence, one in the center and four in the peripheries. Data were submitted to analysis of statistical variance ANOVA, followed by Tukey test at a level of 5.0% of significance. Results: All specimens that were immersed in Gatorade and Carbohydrate Gel had statistically lower microhardness values when compared to the control group. Conclusions: The use of Gatorade (Ambev) and Carbo Gel supplements (Vox Supplements) decreased the surface hardness of the studied resins.

Resistência à flexão de cimentos de ionômero de vidro utilizados em tratamento restaurador atraumático com alteração na proporção pó/líquido / Flexural strength of glass ionomer cements used in atraumatic restorative treatment with change in powder / liquid ratio

Objetivo: Avaliar se a alteração na proporção pó/líquido de cimento de ionômero de vidro nacional indicado para ART (Vitro Molar), proporciona melhorias na resistência à flexão comparando-o ao cimento importado, Fuji IX, considerado atualmente o padrão ouro no mercado. Material e método: Foram confeccionados 30 corpos de prova, divididos igualmente entre três grupos (G1 = Vitro Molar, manipulado conforme orientação do fabricante com proporção pó/líquido (1/1); G2 = Vitro Molar com proporção pó/líquido aumentada em 50 % (1,5/1) e G3 = Fuji IX, manipulado conforme orientação do fabricante. Os corpos de prova foram submetidos ao ensaio mecânico de resistência à flexão de três pontos (ISO 9917-2). Uma força foi aplicada no centro até a ruptura dos corpos-de-prova. Os dados foram submetidos à análise de variância e ao teste de Tukey, com nível de significância de 95%. Resultado: Os resultados médios obtidos para força máxima, em MPa, foram: G1: 3,57; G2: 4,54 e G3: 6,32. Houve diferença estatística entre os grupos G1 e G3. O grupo G2 apresentou semelhança estatística quando comparado aos demais grupos. Conclusão: O Vitro Molar com proporção pó/líquido alterada não apresentou diferença estatisticamente significante quando comparado aos demais grupos. O cimento Fuji IX apresentou valor estatisticamente maior de resistência à flexão que o cimento Vitro Molar manipulado na proporção recomendada pelo fabricante.

Objective: To evaluate whether the change in the proportion powder / liquid of national glass ionomer cement formulated for ART (Vitro Molar) provides improvement in flexural strength, approaching the characteristics of the imported cement (Fuji IX). Materials and Methods: 30 specimens were made, divided between three groups (G1 = Vitro Molar with powder / liquid ratio according to manufacturer's directions (1/1), G2 = with Vitro Molar ratio powder / liquid raised to 50%(1,5/1) and G3 = Fuji IX as manufacturer's guidelines), being subjected to mechanical testing flexural strength of three points (ISO 9917-2). A load was applied at the center until the specimens break. The data were submitted to ANOVA and Tukey's test with 95% significance level. Result: The average results obtained for maximum strength were: G1: 3.57; G2: G3 and 4.54: 6.32. There was statistical difference between G1 and G3. The G2 group had statistically similar results when compared to other groups. Conclusion: Vitro Molar with raised powder / liquid ratio did not present a statistically significant difference when compared to the other groups. The Fuji IX cement presented a statistically higher value of flexural strength than the Vitro Molar cement manipulated in the ratio recommended by the manufacturer.

Avaliação da qualidade de luvas de látex utilizadas em procedimentos odontológicos / Quality evaluation of latex gloves used in dental procedures

Objetivo: O trabalho verificou a qualidade de luvas de látex de procedimento de cinco marcas comerciais utilizadas na prática clínica. Material e Métodos: Foram realizados os testes de Inspeção Visual (IV) e de Integridade (TI) em luvas de procedimento a fim de detectar possíveis defeitos de fabricação. Foram avaliadas 1007 luvas de procedimento (duas caixas tamanho M de cada fabricante). Resultados: Do total, 3,87% apresentaram problemas no teste IV e 1,96% no TI. A marca SATARI® obteve melhor desempenho no teste IV, enquanto a SUPERMAX® o pior. A marca DESCARPACK® obteve o melhor desempenho no TI e a EMBRAMAC® o pior. Conclusão: No quesito hermeticidade, em comparação com o nível de qualidade aceitável, imposto pelo INMETRO, as marcas EMBRAMAC® e LEMGRUBER® foram reprovadas.

Objective: The objective of this study was to verify the quality of latex procedure gloves of 5 trademarks used in clinical practice. Material and Methods: Visual Inspection (VI) and Integrity (IT) tests were performed in procedure gloves in order to detect possible manufacture defects. A number of 1007 procedure gloves (2 packages M size of each manufacturer) were evaluated. Results: In general, 3,87% showed defects in the VI test and 1,98% in the IT. The brand SATARI® had the best performance in the VI test, whereas the brand SUPERMAX® had the worst. Conclusion: The make DESCARPACK® had the best performance in the IT and the brand EMBRAMAC® had the worst. In the hermeticity aspect, in comparison to the acceptable quality level imposed by INMETRO, the brands EMBRAMAC® and LEMGRUBER® were reproved.

Surface Hardness of Glass Ionomer Cements used in Atraumatic Restorative Treatment

Objective: To evaluate the surface hardness of a national glass ionomer cement with increased powder / liquid ratio, suitable for the atraumatic restorative treatment technique. Material and Methods: This is a study of the quantitative experimental type, in which 30 specimens were made and divided equally into 03 experimental groups (glass ionomer cement restorative Vitro Molar -DFL in the proportion specified by the manufacturer; glass ionomer cement restorative Vitro molar ratio -DFL modified with incorporation of 50% powder; and Gold Label 9 - GC Corporation in the proportion specified by the manufacturer). After handling, the materials were placed in a Teflon mold for manufacturing the cylindrical samples (5mm x 2 mm), with the aid of a Centrix syringe (Centrix, Shelton, CT, USA). Specimens were stored in liquid petroleum jelly at a temperature 37 ° ± 1 for up to 7 days. The specimens were evaluated by Vickers hardness test at time intervals of 24 hours and 7 days after manufacture. The data were subjected to the Independent Student's-t tests and analysis of variance (ANOVA), and subsequently by Tukey's test at 95% level of significance. Results: The setting time positively influenced the hardness of the two glass ionomer cements (p<0,001). Cement Gold Label 9 showed higher hardness values than cement Vitro Molar (p<0,001), irrespective of the evaluation time interval. The latter in turn, showed improved values when manipulated with the modified powder / liquid ratio (3: 2) (p<0,001). Conclusion: Vitro Molar glass ionomer cement showed higher hardness values when manipulated with the modified powder/liquid ratio.

Influence of two methods of additional activation on composite resins surface hardness

Aim: To evaluate the influence of two methods of additional activation on the surface hardness of composite resins. Methods: Two types of composites were tested: Filtek P60 and Filtek P350. For each material, 48 specimens were prepared and divided into four groups: Group 1 (control) - conventional activation, using a halogen light for 40 s; Group 2 - conventional activation and additional activation with a halogen lamp for 60 s; Group 3 - conventional activation and additional activation with an autoclave at 127°C for 6 min at 1.7 kg/cm3 pressure; and Group 4 - conventional activation and additional activation with an autoclave at 134 °C for 15 min at 2.1 kg /cm3 pressure. The use of autoclave has been suggested for being a standard equipment at dental offices, and thus, even at locations far from dental laboratories, it would be possible to have simple techniques that allow access to indirect restorations at lower costs. Data obtained in the study were analyzed statistically by analysis of variance followed by Tukey’s test at a 5% level of significance. Results: For Z350, there was a significant increase in hardness for all groups of additional activation (Groups 2, 3 and 4), compared with the control group. For P60, a significant increase in surface hardness was found compared with the control group for the groups that used additional activation with an autoclave (Groups 3 and 4). Conclusions: Additional activation with an autoclave increased the surface hardness of the tested resins to a greater degree than additional activation with a halogen light.

Avaliação de três métodos de ativação complementar sobre a dureza superficial de resinas compostas diretas / Evaluation of three post-cure methods at hardness of direct composite resins

O objetivo do presente trabalho foi avaliar o efeito da ativação complementar utilizando estufa e energia de microondas sobre a dureza Vickers de dois tipos de resinas compostas. Para obtenção das amostras, uma matriz metálica foi posicionada sobre uma placa de vidro e o seu espaço interior foi preenchido com uma das resinas compostas estudadas (Filtek P60 e Filtek Z350) em incremento único. Foram confeccionados 10 corpos-de-prova para cada grupo a seguir: Grupo I - fotoativação convencional com fotopolimerizador (controle); Grupo II - após a fotoativação convencional, os corpos-de-prova foram levados a uma estufa a 125°C por 10 min; Grupo III - após a fotoativação convencional os corpos-de-prova foram levados individualmente ao microondas e irradiados por 5 min a uma potencia de 480W ; Grupo IV - após a fotoativação convencional os corpos-de-prova foram colocados individualmente no microondas imersos em 200ml de água destilada e irradiados por 5 min a uma potencia de 480W. Os dados obtidos a partir das médias foram submetidos à análise de variância estatística (ANOVA), seguida pelo teste de Tukey (5%). Observou-se que para a resina Filtek P60, os diferentes métodos de polimerização adicional obtiveram resultados significativamente maiores em relação ao grupo controle, sendo o grupo IV o que se obteve o melhor resultado. Para a resina Filtek Z350 não houve diferença entre os grupos. Levando em consideração a propriedade de microdureza, a ativação complementar por meios como microondas e estufa podem trazer benefícios às propriedades mecânicas de determinadas resinas, como os encontrados para a resina Filtek P60.

The purpose of this study was to evaluate Vickers hardness of two composite resins after post-cure at stove or with energy of microwaves. For obtaining of the samples, a metallic matrix was positioned on a glass plate and its interior space was filled with one of the studied composed resins (Filtek P60 and Filtek Z350) in only one increment. They were made 10 samples for each group to proceed: Group I - conventional light cure (control); Group II - after the conventional light cure, the samples were taken to a stove for 10 min at 125°C; Group III - after the conventional light cure, the samples were individually irradiated in microwaves for 5 min at 480W; Group IV - after the conventional light cure, the samples were placed individually in microwaves immerged in 200 ml of distilled water and irradiated for 5 min at 480W. The obtained data were submitted to analysis of variance (ANOVA) and the Tukey's test (5%). It was found that for the Filtek P60 resin, the different methods of post-cure resulted in higher hardness in comparison of control's group. The group IV obtained the best result. For the Filtek Z350 resin there was not difference among the groups. For hardness property, the post-cure activation using microwaves and stove can bring benefits in mechanical properties of specific resins, as found them for the Filtek P60 resin.

Efeito da desinfecção química e por microondas na alteração dimensional e resistência de união de resinas para reembasamento imediato e resina termopolimerizável / Effect of chemical and microwave disinfection on the linear dimensional change and the shear bond strength between denture base and reline acrylic resins

Este estudo avaliou o efeito da desinfecção química e por irradiação com microondas sobre a estabilidade dimensional e a resistência ao cisalhamento entre uma resina termopolimerizável para base de prótese (Luciton 550-L) e quatro resinas autopolimerizáveis para reembasamento (Kooliner-K, New Truliner-NT, Tokuso Rebase-TR, Ufi Gel Hard-UGH). Foi avaliada também a resistência ao cisalhamento de corpos-de-prova reembasados com a resina L. Para cada material, 48 corpos-de-prova (50 mm diâmetro x 0.5 mm espessura) foram preparados, seguindo-se as recomendações dos fabricantes, utilizando-se uma matriz metálica circular com pontos de referência (A,B,C e D). Um projetor de perfil Nikon foi utilizado para mensurar a distância entre os pontos de referências (AB e CD) na matriz metálica e nos corpos-de-prova. Os corpos-de-prova foram divididos em 6 grupos (n=8) e as mensurações foram realizadas após as seguintes condições experimentais: G1 - 2 ciclos de desinfecção química (corpos-de-prova imersos em solução de perborato de sódio a 3,8 percento aquecida a 50ºC por 10 minutos); G2 - 2 ciclos de desinfecção com microondas (corpos-de-prova imersos em 200 mL de água e irradiados com 650 W por 6 minutos); G3 - 7 ciclos de desinfecção química; G4 - 7 ciclos de desinfecção com microondas...