RESUMEN
Abstract This in vitro study evaluated the effect of the beam homogeneity of a multiple-peak light-curing unit on the surface microhardness and the effect of toothbrushing wear on the microhardness, surface roughness, roughness profile, volume loss, and gloss retention of incremental and bulk-fill resin-based composites (RBCs). A LED light-curing unit (VALO) with four LEDs at the tip end (405, 445, 465A, and 465B nm emission peak) was used according to each manufacturer-recommended time to obtain disks (n=10) of six RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra, and Filtek Bulk Fill. Microhardness values were obtained according to each LED positioning of the light-curing unit on the top surface of the RBCs and were analyzed before and after toothbrushing regarding microhardness, surface roughness, roughness profile, volume loss, and gloss retention. Microhardness was considered homogeneous on the top surface regardless of the type of RBC or wavelength tested (p>0.05). Overall, toothbrushing did not reduce the microhardness of the RBCs but influenced the gloss values for most RBCs (p<0.001). Charisma Classic presented the greatest surface roughness and roughness profile after toothbrushing (p<0.05). Volume loss did not differ among RBCs (p>0.05). In conclusion, different wavelengths of the LED did not affect the top surface microhardness, regardless of the RBCs tested; and bulk-fill composites presented similar surface changes (microhardness, surface roughness, roughness profile, volume loss, and gloss retention) when compared to conventional composites after toothbrushing.
Resumo Este estudo in vitro avaliou a homogeneidade do feixe de um fotopolimerizador de múltiplos picos na microdureza superficial e o efeito da escovação na microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho de compósitos a base de resina (RBCs) incrementais ou bulk-fill. Um fotopolimerizador LED (VALO) com quatro LEDs na ponteira (405, 445, 465A e 465B nm de pico de emissão) foi usado de acordo com o tempo recomendado por cada fabricante para obtenção de discos (n=10) de seis RBCs: Estelite Sigma Quick, Charisma Classic, Tetric EvoCeram Bulk Fill, Filtek Z250, Filtek Supreme Ultra e Filtek Bulk Fill. Os valores de microdureza foram obtidos seguindo o posicionamento de cada LED na superfície superior das amostras e foram analisados antes e após a escovação quanto a microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e retenção do brilho. A microdureza foi considerada homogênea no topo da superfície, independentemente do tipo de RBCs ou comprimento de onda testados (p>0.05). No geral, a escovação não reduziu a microdureza das RBCs, mas influenciou o brilho para a maioria das RBCs (p<0.001). Charisma Classic apresentou os maiores valores de rugosidade superficial e perfil de rugosidade após a escovação (p<0.05). A perda de volume não diferiu entre as RBCs (p>0.05). Em conclusão, os diferentes comprimentos de onda do LED não alteraram a microdureza do topo da superfície, independentemente das RBCs testadas; e as resinas bulk-fill apresentaram alterações superficiais similares (microdureza, rugosidade superficial, perfil de rugosidade, perda de volume e manutenção do brilho) quando comparadas às resinas convencionais após a escovação.
Asunto(s)
Resinas Compuestas , Materiales Dentales , Propiedades de Superficie , Ensayo de Materiales , PolimerizacionRESUMEN
Abstract This study evaluated the effects of three metal primers and one multi-mode adhesive system on the shear bond strength (SBS) of a flowable composite resin to nickel-chrome metal alloy (Ni-Cr). Ninety plates were cast from Ni-Cr and divided in nine groups (n=10). The surfaces were sandblasted with Al2O3 and primed with three adhesive primers: Alloy Primer (AP), Universal Primer (TP) and RelyX Ceramic Primer (CP), and a multi-mode adhesive (Scotchbond Universal, SU). The Adper Single Bond Plus (SB) and SU adhesives were also combined with adhesive primers. Control group did not have any surface treatment. The groups were: AP, AP+SB, AP+SU, TP+SB, TP+SU, CP+SB, CP+SU and SU. Composite cylinders were built on alloy surface. After 24 h, half the specimens were subjected to SBS and the other half to thermal cycling before testing. Data were analyzed by two-way ANOVA and Tukey’s test (a=0.05). Failure modes were assessed by SEM observation. Higher SBS were obtained with AP and TP combined with adhesives at 24 h and the lowest one for control group. Thermocycling reduced SBS for AP, CP+SU and SU. Combination between TP and SU resulted in the highest SBS after the thermocycling. TP groups showed all types of failures and high incidence of mixed failures. The use of AP and UP metal primers before application of SU and SB adhesive systems increased the SBS of composite to Ni-Cr. These combinations between metal primers and adhesives had the highest SBS after thermocycling.
Resumo Este estudo avaliou os efeitos de três primers para metais e um sistema adesivo multi-mode na resistência da união por cisalhamento (SBS) de um compósito resinoso de baixa viscosidade a uma liga niquel-cromo (Ni-Cr). Noventa placas Ni-Cr foram divididas em 9 grupos (n=10). As superfícies foram jateadas com Al2O3 e condicionadas com três primers adesivos: Alloy Primer (AP), Universal Primer (TP) e Rely X Ceramic Primer (CP) e um adesivo multi-mode (Scotchbond Universal, SU). Os adesivos Adper Single Bond Plus (SB) e SU foram combinados com os primers para metais. O grupo controle não recebeu nenhum tipo de tratamento superficial. Os grupos foram: AP, AP+SB, AP+SU, TP+SB, TP+SU, CP+SB, CP+SU e SU. Cilindros de resina foram construídos na superfície da liga. Após 24 h, metade dos espécimes foi submetido ao SBS, a outra metade foi termociclada previamente. Os dados foram analisados pelos testes ANOVA dois fatores e Tukey (a=0.05). Os tipos de fraturas foram determinados utilizando microscopia eletrônica de varredura (MEV). Os maiores valores de SBS foram obtidos com AP e TP combinados com adesivos após 24 h e o menor valor foi obtido no grupo controle. A ciclagem térmica reduziu a SBS para AP, CP+SU e SU. Combinação entre TP e SU resultou em altos valores de SBS após termociclagem. Os grupos TP apresentaram todos os modos de fratura e alta incidência de fraturas mistas. O uso dos primers AP e UP para metais antes da aplicação dos sistemas adesivos SU e SB aumentou a SBS entre o Ni-Cr e a resina composta. Essa combinação entre primers e adesivos mostrou os maiores valores de SBS após a termociclagem.