Levan was used as agent in the synthesis of new colon-specific polymeric matrix together with Eudragit® FS 30 D. Eudragit® FS 30 D films incorporated with levan were made by casting process and characterized to: water vapour transmission, sweeling index, differential scanning calorimetry and thermogravimetric. The levan increased the films permeability (p < 0.001) however did not influenced in the sweeling index of the formulations (p > 0.05). The thermal analyses of the films indicated a glass transition temperature approximate at 47°C and thermal decomposition at 400°C. The results indicated that there is potential for using such site-specificity blend as pharmaceutical coating material.
Levana foi utilizada na síntese de novo material polimérico cólon-específico conjuntamente com o Eudragit® FS 30 D. Filmes de Eudragit® FS 30 D aditivados de levana foram feitos pelo método de "casting process" e caracterizados quanto à transmissão de vapor de água, índice de intumescimento, calorimetria diferencial de varredura e termogravimetria. A levana aumentou a permeabilidade dos filmes (p < 0,001), entretanto não influenciou no índice de intumescimento das formulações (p > 0,05). As análises térmicas dos filmes indicaram uma temperatura de transição vítrea aproximada de 47°C e temperatura de decomposição de 400°C. Os resultados indicaram que há potencial de uso desta nova blenda sítio-específica como material de revestimento farmacêutico.