Influence of the incorporation of triclosan methacrylate on the physical properties and antibacterial activity of resin composite

Abstract The incorporation of antimicrobials in the composites as an attempt to reduce bacterial adhesion without jeopardizing mechanical properties is a challenge for Dentistry. Objective: To evaluate the bacterial adhesion and physical properties of a composite containing the methacrylate triclosan- derivative monomer (TM). Methodology: TM was synthesized and added to an experimental composite. Samples were divided into two groups: Control and TM (13.4 wt%). Antibacterial Activity: Three specimens of each material were prepared and placed on bacterial suspensions of Streptococcus mutans for 1, 5 and 10 days. After these periods the counting of the colonies (log10) was performed. Assays was performed in triplicate. Physical Properties: Three-body Abrasion (TBA): Ten specimens of each material were prepared and stored at 37°C/24 h. The surface roughness (Ra) and hardness (KHN) were analyzed. Next, the specimens were submitted to abrasive wear (30,000 cycles) and re-evaluated for Ra and KHN; Sorption/solubility (SS): cylindrical specimens (n=10) were prepared and weighted. The specimens were immersed in deionized water for 7 days at 37°C and then their weight was verified again. SS were calculated using accepted formulas; Diametral tensile strength (DTS): specimens (n=10) underwent test performed in an Instron universal testing machine at a crosshead speed of 1 mm/min. Data were submitted to appropriate statistical tests according to data distribution and assay (p<0.05). Results: Bacterial Adhesion: TM showed a significant reduction on biofilm accumulation in the evaluated periods: 1 day (1.537±0.146); 5 days (2.183±0.138) and 10 days (4.469±0.155) when compared with Control: 1 day (4.954±0.249); 5 days (5.498±0.257) and 10 days (6.306±0.287). Physical Properties: For TBA, SS and DTS no significant difference was found between groups Control and TM. The incorporation of methacrylate triclosan-based monomer in the experimental composite reduce bacterial adhesion of S. mutans and did not affect important polymer properties.

In-vitro comparative study of the use of 2 % chlorhexidine on microtensile bond strength of different dentin adhesives: a 6 months evaluation / Estudio comparativo in vitro del uso de clorhexidina al 2 % sobre la resistencia de unión microtensil de diferentes adhesivos dentinarios: una evaluación de 6 meses

The aim of this study was to evaluate the effect of chlorhexidine (CHX) dentin treatment on microtensile bond strength (µTBS) of adhesive systems in different storage times. Occlusal enamel was removed from ninety third-molars and flat surfaces of middle dentin were exposed. Teeth were randomly divided in 6 groups according to adhesive system (etch-and-rinse : Adper Scotchbond 1XT - ASB ; self-etch: Adper Prompt L-Pop ­ APP; and universal: Single Bond Universal - SBU) and chlorhexidine (CHX) dentin treatment (2 % CHX application for 20 s prior Primer). After resin composite build up, teeth were sectioned to obtain beam specimens and divided in 3 subgroups (n=5): 72h, 3 and 6 months storage times. After the storage times, teeth were tested in tension until failure (0.5 mm/min). SEM was performed to observe hybrid layer of adhesive systems. Data were analyzed using one-way ANOVA and Tukey tests. At 72 h, all equivalent groups (same adhesive system, different dentin treatments) maintained their µTBS when compared CHX-treatment. At 3 and 6 months, non-treated CHX groups showed less µTBS than CHX-treated ones. Six months storage time did not significantly decrease µTBS, except for G2-ASB. The effect of CHX on dentin µTBS depends on storage times and adhesive systems. While immediate µTBS was not affected by CHX treatment, CHX improved dentin µTBS after 3 and 6 months.

El objetivo de este estudio fue evaluar el efecto del tratamiento con clorhexidina (CHX) de la dentina sobre la resistencia de la unión microtensil (mTBS) de los sistemas adhesivos en diferentes tiempos de almacenamiento. Se retiró el esmalte oclusal de noventa terceros molares y se expusieron superficies planas de la dentina media. Los dientes se dividieron al azar en 6 grupos de acuerdo con el sistema adhesivo (con grabado ácido: Adper Scotchbond 1XT-ASB, auto-grabado: Adper Prompt L-Pop-APP y universal: Single Bond Universal- SBU) y el tratamiento de la dentina con clorhexidina (CHX) (aplicación de CHX al 2 % 20 s antes del Primer). Después de la aplicación de la resina compuesta, los dientes fueron seccionados para obtener muestras en forma de barras y divididos en 3 subgrupos (n = 5) con tiempos de almacenamiento de 72 h, 3 y 6 meses. Después de los tiempos de almacenamiento, los dientes se sometieron a tensión hasta la fractura (0,5 mm / min). SEM se realizó para observar la capa híbrida de sistemas adhesivos. Los datos se analizaron mediante ANOVA unidireccional y pruebas de Tukey. A las 72 h, todos los grupos equivalentes (el mismo sistema adhesivo, diferentes tratamientos de dentina) mantuvieron su mTBS cuando se comparó el tratamiento CHX. A los 3 y 6 meses, los grupos CHX no tratados mostraron menos mTBS que los tratados con CHX. Seis meses de tiempo de almacenamiento no disminuyó significativamente el mTBS, excepto para el G2-ASB. El efecto de CHX sobre la dentina mTBS depende del tiempo de almacenamiento y de los sistemas adhesivos. Mientras que el mTBS inmediato no se vio afectado por el tratamiento con CHX, CHX mejoró la mTBS a dentina después de 3 y 6 meses.

Effect of 2 % chlorhexidine on dentin shear bond strength of different adhesive systems: a 6 months evaluation / Efecto de la clorhexidina al 2 % sobre la resistencia al cizallamiento de diferentes sistemas adhesivos: una evaluación de 6 meses

This study evaluated the effect of chlorhexidine dentin treatment on shear bond strength (SBS) of adhesive systems after different storages. The work included 144 third molars that had their dentin exposed and were divided in 6 groups: G1 (ASB+CHX: Adper Scotchbond 1XT + chlorhexidine 2 % prior Primer); G2(ASB); G3 (APP+CHX: Adper Prompt L-Pop + CHX); G4(APP); G5 (SBU+CHX: Single Bond Universal + CHX); and G6(SBU). Resin build-up was performed and teeth were subdivided regarding storage times (n=8): 72 h, 3 and 6 months. Next, SBS test was performed. At 72 hours, all equivalent groups (same adhesive system, different dentin treatment) showed no significant difference in SBS (P.05). Self-etch adhesive groups (with or without CHX) presented lower SBS compared to other systems (P.05). After 3 and 6 months, all CHX-treated groups presented significantly higher SBS compared to equivalent non-treated groups (P.05). For both storage times, Single Bond Universal presented the highest SBS values within the same dentin treatment (P.05), while Adper Scotchbond and Adper Prompt-L-Pop were not significantly different among them, also within the same dentin treatments [3 months (with CHX: P=.966; without: P=.958) and 6 months (with CHX: P =.887; without: P=.990)]. CHX Dentin disinfection is indicated for all classes of adhesives studied.

Este estudio evaluó el efecto del tratamiento de la dentina con clorhexidina sobre la resistencia al cizallamiento (SBS) de sistemas adhesivos después de diferentes almacenamientos. Se removió el esmalte oclusal a 144 terceros molares y se dejó su dentina media expuesta, posteriormente se dividieron al azar en 6 grupos: G1 (ASB + CHX: Adper Scotchbond 1XT + clorhexidina 2 % antes del Primer); G2 (ASB); G3 (APP + CHX: L-Pop + CHX de Adper); G4 (APP); G5 (SBU + CHX: Single Bond Universal + CHX); y G6 (SBU). Se realizó la aplicación de la resina compuesta y se subdividieron los grupos con respecto a los tiempos de almacenamiento (n = 8): 72h, 3 y 6 meses. A continuación, se realizó la prueba SBS. A las 72 horas, todos los grupos equivalentes (el mismo sistema adhesivo, diferentes tratamientos de dentina) no mostraron diferencias significativas en los valores de SBS (P.05). Los grupos de adhesivo de auto-grabado (con o sin CHX) presentaron valores de SBS más bajos en comparación con otros sistemas (P.05). Después de 3 y 6 meses, todos los grupos tratados con CHX presentaron valores de SBS significativamente mayores en comparación con los grupos no tratados equivalentes (P.05). Para ambos tiempos de almacenamiento, Single Bond Universal presentó los valores de SBS más altos dentro del mismo tratamiento dentinario (P.05), mientras que el Adper Scotchbond y el Adper Prompt-L-Pop no fueron significativamente diferentes entre ellos, también dentro de los mismos tratamientos dentinarios 3 meses (con CHX: P = .966, sin: P = .958) y 6 meses (con CHX: P = .887; sin: P = .990). La desinfección de la dentina con CHX está indicada para todas las clases de adhesivos estudiados.

Streptococcus Mutans Biofilm Influences on the Antimicrobial Properties of Glass Ionomer Cements

Abstract The aim of this study was to evaluate the in vitro antibacterial and biofilm inhibition properties of glass ionomer restorative cements. Ketac Nano, Vitremer, Ketac Molar Easymix and Fuji IX were analyzed using the following tests: a) agar plate diffusion test to evaluate the inhibitory activity of cements against S. mutans (n=8); b) S. mutans adherence test by counting colony-forming units after 2 h of material/bacteria exposure (n=10); c) biofilm wet weight after seven days of bacterial accumulation on material disks, with growth medium renewed every 48 h (n=10); d) pH and fluoride measurements from the medium aspired at 48 h intervals during the 7-day biofilm development (n=10). Data from the a, b and c tests were submitted to Kruskal-Wallis and Mann-Whitney tests and the fluoride-release and pH data were submitted to two-way ANOVA and Tukey tests (a=5%). Vitremer followed by Ketac Nano showed the greatest inhibitory zone against S. mutans than the conventional ionomers. Vitremer also showed higher pH values than Ketac Nano and Fuji IX in the first 48 h and released higher fluoride amount than Ketac Nano e Ketac Molar Easymix throughout the experimental period. The chemical composition of restorative glass ionomer materials influenced the antibacterial properties. The resin modified glass ionomer (Vitremer) was more effective for inhibition of S. mutans and allowed greater neutralization of the pH in the first 48 h. However, the type of glass ionomer (resin modified or conventional) did not influence the weight and adherence of the biofilm and fluoride release.

Resumo O objetivo neste estudo foi avaliar in vitro as propriedades antibacterianas e a inibição do biofilme de cimentos de ionômero de vidro restauradores. Ketac Nano, Vitremer, Ketac Molar Easymix and Fuji IX foram avaliados através dos seguintes testes: a) teste de difusão em ágar para avaliar a inibição de S. mutans nos cimentos (n=8); b) adesão de S. mutans pela contagem de unidades formadoras de colônia após 2h de exposição material/bactéria (n=10); c) peso do biofilme úmido após sete dias de acúmulo bacteriano nos discos do material, com meio de cultura renovado após 48 h (n=10); d) mensuração do pH e liberação de flúor do meio aspirado nos intervalos de 48 h durante 7 dias de crescimento do biofilme (n=10). Os dados dos testes a, b e c foram submetidos aos testes Kruskal-Wallis e Mann-Whitney e os dados de liberação de flúor e pH a ANOVA dois fatores e Tukey (a = 5%). Vitremer seguido pelo Ketac Nano mostrou maior zona de inibição contra S. mutans quando comparados aos ionômeros convencionais. Vitremer também apresentou valores de pH mais elevados do que Ketac Nano e Fuji IX nas primeiras 48 h e liberou maior quantidade de flúor do que Ketac Nano e Ketac Molar Easymix durante todo o período experimental. A composição química dos ionômeros de vidro restauradores influenciou nas propriedades antibacterianas. O ionômero de vidro modificado por resina (Vitremer) foi mais eficaz na inibição de S. mutans e permitiu maior neutralização do pH nas primeiras 48 h. No entanto, o tipo de ionômero de vidro (modificado por resina ou convencional) não influenciou no peso e adesão do biofilme e na liberação de flúor.

Effect of thickness of indirect restoration and distance from the light-curing unit tip on the hardness of a dual-cured resin cement

This study evaluated the Knoop hardness and polymerization depth of a dual-cured resin cement, light-activated at different distances through different thicknesses of composite resin. One bovine incisor was embedded in resin and its buccal surface was flattened. Dentin was covered with PVC film where a mold (0.8-mm-thick and 5 mm diameter) was filled with cement and covered with another PVC film. Light curing (40 s) was carried out through resin discs (2, 3, 4 or 5 mm) with a halogen light positioned 0, 1, 2 or 3 mm from the resin surface. After storage, specimens were sectioned for hardness measurements (top, center, and bottom). Data were subjected to split-plot ANOVA and Tukey's test (a=0.05). The increase in resin disc thickness decreased cement hardness. The increase in the distance of the light-curing tip decreased hardness at the top region. Specimens showed the lowest hardness values at the bottom, and the highest at the center. Resin cement hardness was influenced by the thickness of the indirect restoration and by the distance between the light-curing unit tip and the resin cement surface.

O estudo avaliou a profundidade de polimerização de um cimento resinoso dual, através da dureza Knoop (KHN), ativado em diferentes distâncias e espessuras de compósito resinoso. A dentina bovina foi planificada e embutida em resina, coberta com filme de PVC, onde um molde (0,8 mm x 5 mm) sobreposto foi preenchido com cimento e coberto com outro filme de PVC. A fotoativação (40 s) foi realizada através de discos de compósito (2, 3, 4 ou 5 mm-espessura) com a luz a 0, 1, 2 ou 3 mm de distância da superfície do compósito. Após armazenagem, os espécimes foram seccionados e a KHN medida (superfície, centro e base). Os dados foram submetidos à ANOVA com parcelas subdivididas e teste de Tukey (a=0.05). A espessura do compósito diminuiu a dureza do cimento. O aumento da distância de fotoativação diminuiu a dureza na superfície do cimento. Espécimes mostraram menores valores de dureza na região de base e os maiores valores no centro. A dureza do cimento resinoso foi influenciada pela espessura da restauração indireta e pela distância entre a ponta da unidade fotoativadora e a superfície do cimento resinoso.

Sedative effect of oral diazepam and chloral hydrate in the dental treatment of children.

PURPOSE: The purpose was to evaluate two sedation protocols during dental sessions in anxious children. MATERIALS AND METHODS: It was a randomized and double-blind study, with each individual being his/her own control within each protocol. Furthermore, the two protocols were compared. Twenty children (36 to 84 months old) who exhibited "definitely negative" behavior according to the Frankl scale were assigned to receive oral chloral hydrate (40 mg/kg) (Group I) or Diazepam (5 mg) (Group II). Behavior during local anesthesia, application of rubber dam, cavity preparation, restorative procedures was evaluated, considering the degree of sleep, body movement, crying and overall behavior. Vital signs were assessed at three different times. The Wilcoxon, Mann-Whitney, Exact Fisher's and Spearman correlation tests were used to analyze the data. RESULTS: Group I presented higher scores for sleep during the CH session than placebo session during rubber dam application (P = 0.0431) and restoration (P = 0.0431). In Group II there was no statistically significant difference (p > 0.05). There were no statistically significant differences between sessions and groups in the evaluation of body movement, crying and vital signs. Overall behavior in the placebo session was better than in the CH session during local anesthesia, but there was no difference between the two drug regimens. There was influence of age during anesthesia and cavity preparation in Group I and during rubber dam application in Group II. It was concluded that oral diazepam and chloral hydrate had no influence on the behavior management for dental treatment with the studied sample.