Shear bond resistance and enamel surface comparison after the bonding and debonding of ceramic and metallic brackets

OBJECTIVE: To evaluate, in vitro, the shear bond strength presented by three brands of polycrystalline ceramic brackets and one brand of metallic bracket; verify the adhesive remnant index (ARI) after the tests, and analyze, through scanning electron microscopy (SEM) the enamel surface topography after debonding, detecting the release of mineral particles. METHODS: Sixty bovine lower incisors were used. Three ceramic brackets (Allure(r), InVu(r), and Clarity(r)) and one metallic bracket (Geneus(r)) were bonded with Transbond XT(r). Kruskal-Wallis's test (significance level set at 5%) was applied to the results of share bond and ARI. Mann Whitney's test was performed to compare the pairs of brackets in relation to their ARI. Brown-Forsythe's test (significance level set at 5%) was applied to the results of enamel chemical composition. Comparisons between groups were made with Games-Howell's and the Post-hoc tests. RESULTS: No statistically significant difference was observed in relation to the shear bond strength loads. Clarity(r) brackets were the most affected in relation to the surface topography and to the release of mineral particles of enamel (calcium ions). CONCLUSION: With regard to the ARI, there was a prevalence of score 4 (40.4%). As for enamel surface topography, the Geneus(r) bracket was the only one which did not show superficial tissue loss. The InVu(r) and Clarity(r) ones showed cohesive fractures in 33.3% and the Allure(r) in 50%, the latter being the one that presented most fractures during removal. .

OBJETIVO: avaliar, in vitro, a resistência ao cisalhamento apresentada por três marcas de braquetes ortodônticos cerâmicos policristalinos e uma marca de braquete metálico, verificando os índices de resina remanescentes (IRA) após os ensaios, e analisar, por meio de microscopia eletrônica de varredura, as topografias superficiais do esmalte após a descolagem, detectando o desprendimento de partículas minerais desse. MÉTODOS: foram utilizados 60 incisivos inferiores bovinos. Os braquetes cerâmicos (Allure, InVu e Clarity) e metálico (Geneus) foram colados utilizando-se o adesivo Transbond XT. Para os resultados referentes ao cisalhamento e ao IRA, foi utilizado o teste de Kruskal-Wallis, com nível de significância de 5%. A prova de Mann-Whtiney foi utilizada para comparar os diferentes tipos de braquetes aos pares, quanto ao IRA. Para a análise dos resultados referentes às composições químicas do esmalte, aplicou-se o teste de Brown-Forsythe, com significância de 5%. As comparações entre os grupos foram realizadas utilizando os testes Post Hoc e de Games-Hoewell. RESULTADOS: não foram observadas diferenças significativas quanto às cargas de cisalhamento. O Clarity foi o mais afetado em relação à topografia e ao desprendimento de partículas minerais do esmalte (íons Ca). CONCLUSÃO: em relação ao IRA, foi confirmada a prevalência do escore 4, com um percentual de 40,4%. Em relação à topografia superficial do esmalte, o Geneus foi o único que não apresentou perda de tecido . O InVu e o Clarity apresentaram fraturas coesivas de 33,3% de suas amostras, e o Allure de 50%, sendo o que mais fraturou durante a remoção. .

Avaliação comparativa in vitro da resistência à força decisalhamento apresentada pelo bráquete cerâmico InVuTM / Comparative in vitro evaluation of the shear bond strength of the ceramic bracket InVuTM

Objetivo: Avaliar in vitro a resistência ao cisalhamento e o IRA (Índice de Adesivo Remanescente no esmalte) em bráquetes ortodônticos cerâmicos. Método: Sessenta pré-molares humanos com os bráquetes devidamente colados em suas superfícies vestibulares, foram fixados em tubos de PVC, constituindo os corpos de prova, aleatoriamente divididos em 4 grupos: bráquetes Clarity (3M Unitek), 20/40 (American Orthodontics), InVuTM (TP Orthodontics) e um grupo controle composto por bráquetes metálicos (3M Unitek). Após a remoção dos bráquetes, as superfícies de esmalte foram analisadas sob estereomicroscópio (Stemi 2000-C; Zeiss, Bernried, Alemanha) com 25X de magnificação para determinação do IRA (índice Remanescente de Adesivo), sistema usado para avaliar a quantidade de adesivo remanescente sobre o dente após a descolagem. Resultados: Não houve diferença estatisticamente significativa entre os grupos, exceto o grupo de bráquetes Clarity que foi estatisticamente significante (p<0,05). Quanto ao Índice de Remanescente de Adesivo na superfície de esmalte (IRA) o grupo de bráquetes InVuTM apresentou maior freqüência de fraturas ocorridas na interface bráquete-adesivo (p= 0,08). Conclusão: O grupo de bráquetes Clarity apresentou maior resistência ao cisalhamento, se comparado aos demais e em relação aos escores do IRA, o grupo de bráquetes InVuTM apresentou melhor resultado, com maior quantidade de fraturas ocorridas na interface bráquete-adesivo.

Objective: To assess in vitro the shear bond strength and the adhesive remnant index (ARI) in enamel of ceramic orthodontic brackets. Method: Sixty human premolars with brackets bonded to their buccal surfaces were fixed in PVC cylinders and were randomly assigned to 4 groups: Clarity (3M Unitek), 20/40 (American Orthodontics), InVuTM (TP Orthodontics) brackets and a control group consisting of metallic brackets (3M Unitek). After removal of the brackets, the enamel surfaces were analyzed with a stereomicroscope (Stemi 2000-C; Zeiss, Bernried, Germany) at ×25 magnification for determination of the ARI, a system used for evaluating the amount of adhesive remaining on the tooth surface after debonding. Results: There was no statistically significant difference (p>0.05) among the groups except for the Clarity brackets group, which differed significantly (p<0.05) from the other groups. Regarding the ARI, the InVuTM brackets group presented the highest incidence of fractures at the adhesive-bracket interface (p=0.08). Conclusion: The Clarity brackets group presented higher shear bond strength as compared to the other groups. The InVuTM brackets group presented the highest RAI scores, with a larger number of fractures at the adhesive-bracket interface.

Avaliação de erro sistemático e discrepância das medições de modelos odontológicos utilizando-se paquímetro digital / Analysis of systematic error and discrepancy in measurements of dental models using digital caliper

Objetivo: Determinar os índices de erro e de discrepância de medições realizadas em modelos ortodônticos em acrílico com dentes de estoque em oclusão dentária e maloclusão, utilizando paquímetro digital e avaliar a influência do tempo de experiência profissional na exatidão das medições. Método: Duas medições, com um intervalo mínimo de 30 dias, foram realizadas por 30 alunos de graduação em Odontologia da FO da UFJF, 12 alunos do curso de especialização em Ortodontia da FO da UFJF e 6 professores do curso de especialização em Ortodontia da UFJF. Após a realização das medidas, as médias das dimensões utilizadas no estudo foram obtidas por grupo. A análise estatística utilizada lançou mão do teste t de Student, do ANOVA e do teste de Tukey. Resultados: Erros sistemáticos foram observados na oclusão dentária entre os alunos da especialização e na maloclusão entre os professores da especialização e os alunos da graduação. Discrepâncias de medidas foram observadas na oclusão dentária e na maloclusão entre os alunos da especialização e os da graduação. Erros de medidas foram encontrados na oclusão dentária entre os alunos da graduação e os da especialização. Erros de medidas foram encontrados na maloclusão entre os professores da especialização e os alunos da graduação. Conclusão: O tempo de experiência profissional teve influência significativa nas medições, pois se verificou que o número de erros sistemáticos e discrepâncias de medidas foi maior no grupo de menor experiência, isto é, alunos de graduação, e menor no grupo de maior experiência, grupo de professores da especialização.

Alterações esqueléticas craniofaciais em portadores de anemia falciforme na cidade de Juiz de Fora / Craniofacial skeletal alterations in sickle cell anemia patients of Juiz de Fora

Este trabalho avaliou as características esqueléticas craniofaciais de 30 indivíduos negros portadores de anemia falciforme, com idade variando entre 20 e 46 anos, cadastrados na Fundação Centro de Hematologia e Hemoterapia de Minas Gerais - Fundação Hemominas, na cidade de Juiz de Fora/MG. Após a obtenção das radiografias cefalométricas em norma lateral de perfil de todos os pacientes, foram realizados os traçados cefalométricos, utilizando alguns ângulos da análise cefalométrica de Steiner e Downs, os quais foram comparados com os valores encontrados por Fortes. As variáveis avaliadas neste trabalho foram os ângulos SNA, SNB, ANB, SND, GoGn.SN, ângulo facial, ângulo de convexidade e ângulo do eixo Y que, após aferidos, foram divididos em tabelas e comparados aos valores padrão preconizados por estes autores e submetidos ao tratamento estatístico, utilizando o teste t-student. O nível de significância adotado foi de 5%. Para avaliação da confiabilidade, foram utilizados os testes t-student para amostras pareadas e de correlação de Pearson. Neste estudo, as variáveis que apresentaram diferença estatisticamente significante entre a média dos valores medidos e o valor padrão de cada variável (p < 0,05) foram SNA, SNB, SND, GoGn.SN e o ângulo de convexidade. As alterações ósseas craniofaciais observadas nestes pacientes foram protrusão da maxila, retrusão da mandíbula, aumento do plano mandibular e perfil facial convexo, com características do padrão esquelético de classe II, sugerindo que a anemia falciforme tem participação nas alterações esqueléticas craniofaciais observadas.

The present study evaluated craniofacial skeletal characteristics of 30 black patients with sickle cell anemia. Their age ranged from 20 to 46 years-old and all of them were enrolled for treatment at Fundação Centro de Hematologia e Hemoterapia de Minas Gerais - Hemominas, in Juiz de Fora. After obtaining all the cephalometrics radiographs of the patients in lateral profile position, cephalometric tracings were done using specificangles of the analysis of Steiner and Downs, and comparing them with values founded by Fortes. Variables assessed in this study were SNA, SNB, ANB, SND, GoGn.SN angle, facial angle, convexity angle and Y axis angle. Angular measurements were them divided into tables and compared to standard values as described by these authors. Statistical analysis was performed using Student's t-test. Significance level was set at 5%. For reliability evaluation, Student's t-test with paired samples and Pearson correlation test were performed. In this study, variables that showed statistically significant difference between the mean of the values obtained and the standard value of each variable (p<0.05) were SNA, SNB, SND, GoGn.SN angle and convexity angle. Craniofacial skeletal alterations founded in these patients were: maxillary protrusion, mandibular retrusion, increase of mandibular plane and convex facial profile. These are characteristics of a Class II skeletal malocclusion, suggesting that sickle cell anemia is involved in the onset of these skeletal alterations.