Fluoride release and uptake in enhanced bioactivity glass ionomer cement ("glass carbomer™") compared with conventional and resin-modified glass ionomer cements

Abstract Objectives To study the fluoride uptake and release properties of glass carbomer dental cements and compare them with those of conventional and resin-modified glass ionomers. Materials and Methods Three materials were used, as follows: glass carbomer (Glass Fill), conventional glass ionomer (Chemfil Rock) and resin-modified glass ionomer (Fuji II LC). For all materials, specimens (sets of six) were matured at room temperature for time intervals of 10 minutes, 1 hour and 6 weeks, then exposed to either deionized water or sodium fluoride solution (1000 ppm in fluoride) for 24 hours. Following this, all specimens were placed in deionized water for additional 24 hours and fluoride release was measured. Results Storage in water led to increase in mass in all cases due to water uptake, with uptake varying with maturing time and material type. Storage in aqueous NaF led to variable results. Glass carbomer showed mass losses at all maturing times, whereas the conventional glass ionomer gained mass for some maturing times, and the resin-modified glass ionomer gained mass for all maturing times. All materials released fluoride into deionized water, with glass carbomer showing the highest release. For both types of glass ionomer, uptake of fluoride led to enhanced fluoride release into deionized water. In contrast, uptake by glass carbomer did not lead to increased fluoride release, although it was substantially higher than the uptake by both types of glass ionomer. Conclusions Glass carbomer resembles glass ionomer cements in its fluoride uptake behavior but differs when considering that its fluoride uptake does not lead to increased fluoride release.

Mechanical and optical properties of conventional restorative glass-ionomer cements - a systematic review

Abstract Objectives To perform a systematic review of test methodologies on conventional restorative glass-ionomer cement (GIC) materials for mechanical and optical properties to compare the results between different GICs. Material and Methods Screening of titles and abstracts, data extraction, and quality assessments of full-texts were conducted in search for in vitro studies on conventional GICs that follow the relevant specifications of ISO standards regarding the following mechanical and optical properties: compressive strength, flexural strength, color, opacity and radiopacity. Sources The Latin American and Caribbean Health Sciences (LILACS), Brazilian Bibliography of Dentistry (BBO) databases from Latin-American and Caribbean System on Health Sciences Information (BIREME) and PubMed/Medline (US National Library of Medicine - National Institutes of Health) databases were searched regardless of language. Altogether, 1146 in vitro studies were selected. Two reviewers independently selected and assessed the articles according to pre-established inclusion/exclusion criteria. Among all the properties investigated, only one study was classified as being of fair quality that tested compressive strength and was included. It was observed that many authors had not strictly followed ISO recommendations and that, for some properties (diametral tensile strength and microhardness), there are no guidelines provided. Conclusions It was not possible to compare the results for the mechanical and optical properties of conventional restorative GICs due to the lack of standardization of studies.