Resultados 1 - 4 de 4
Filtrar
Añadir filtros








Intervalo de año
2.
ROBRAC ; 20(53)jul. 2011. graf, tab
Artículo en Portugués | LILACS | ID: lil-639286

RESUMEN

Objetivo: Este estudo teve como objetivo principal, analisar a interferência do clareamento dentário com peróxido de carbamida (PC) a 10% sobre a resistência de união à dentina de restaurações de resina composta. Material e Método: Vinte cavidades foram preparadas na face vestibular de dentes bovinos. Após condicionamento ácido e aplicação de agente adesivo nas paredes de dentina e esmalte, as cavidades foram restauradas com resina composta. Os espécimes foram divididos em grupos de acordo com tratamento na superfície de esmalte/restauração: G1 ? controle (sem tratamento) e G2 (aplicação do gel de PC por 8h/dia, durante 14 dias). Após esse período, foram obtidos os corpos-de-prova em forma de palito com secção transversal de aproximadamente 0,81 mm2, os quais foram submetidos ao ensaio de microtração. As fraturas foram analisadas em lupa estereoscópica e classificadas em: coesiva da resina ou dentina, adesiva ou mista. Resultados: A análise estatística (ANOVA/ ?2) revelou que o fator tratamento interferiu na resistência adesiva, sendo que a resistência de união foi significantemente superior para os espécimes do grupo G2 (p<0,05). Fraturas adesivas predominaram em todos os grupos com valores que variaram de 48,3% a 75%. Fraturas mistas foram às segundas mais observadas em G1 e falhas coesivas da resina para G2. Conclusões: Conclui-se que o clareamento caseiro utilizando gel com 10% de PC aumentou a resistência de união de restaurações adesivas à dentina.


Objective: The present study aimed to analyze the effects of tooth bleaching with 10% carbamide peroxide (CP) gel on the bond strength of resin composite restorations to dentin. Material and Methods: Twenty cavities were prepared on the buccal surface of bovine teeth. After acid etching and application of bonding agent on dentin and enamel, the cavities were restored with composite resin. The specimens were divided into groups according to treatment on the surface of enamel / restoration: G1 - control (no treatment) and G2 (10% PC gel application for 8h/day during 14 days). After this period, the teeth were cut to produce beams with 0.81 mm2 cross-sectional area, which were subjected to microtensile test. The fractures were examined with a stereomicroscope and classified as cohesive in resin or dentin, adhesive, or mixed. Results: The statistical analysis (ANOVA / ?2) revealed that the factor treatment interfered with the bond strength, which was significantly higher for specimens of G2 (p <0.05). Adhesive fractures occurred in most of specimens of both groups with values ranging from 48.3% to 75%. Mixed fractures were the second more frequent in G1 and cohesive resin failure in G2. Conclusion: It was concluded that tooth bleaching with 10% of PC increased the bond strength of adhesive restorations to dentin.

3.
ROBRAC ; 20(52)abr. 2011. tab, ilus
Artículo en Portugués | LILACS | ID: lil-609176

RESUMEN

Objetivo: Avaliar as alterações de rugosidade e morfologia superficial do esmalte e da resina composta após diferentes técnicas de clareamento dental. Material e método: incisivos bovinos íntegros foram selecionados, sendo que cavidades padronizadas foram confeccionadas na face vestibular, as quais foram restauradas com resina composta. Os dentes foram distribuídos em grupos, de acordo com o tratamento proposto: G1- clareamento com peróxido de carbamida (PC) 10%; G2 - clareamento com peróxido de hidrogênio (PH) a 38%; G3- clareamento com PH a 38% associado à foto-ativação com LED. Para G1, o agente clareador foi aplicado por 8 horas diárias durante 21 dias. Para G2 e G3, foram realizadas 3 sessões de clareamento, caracterizadas por 3 aplicações do gel clareador por 15 minutos, com intervalos de 7 dias entre as sessões, sendo que em G3 o gel clareador foi ativado com LED (470nm) por 6 minutos. As superfícies do esmalte e da resina composta foram avaliadas antes e após o procedimento clareador através de um rugosímetro e de um microscópio de força atômica. Resultados: Os resultados demonstraram diferença significante da rugosidade do esmalte antes e após o clareamento apenas para G1, em relação ao controle (Wilcoxon, p<0,05). Para a resina composta, nenhum dos grupos apresentou diferença estatística em relação ao controle (Mann-Whitney, p>0,05). Conclusão: O aumento da rugosidade do esmalte aconteceu apenas quando o clareamento foi realizado através da aplicação de um gel com 10% de PC. Nenhum dos procedimentos clareadores avaliados nesta pesquisa interferiram na rugosidade e morfologia da resina composta.


Objective: the aim of this study was to evaluate and compare the roughness and superficial morphology of enamel and a composite restorative resin after different bleaching techniques application. Material and Methods: Bovine incisors were selected and standardized cavities were prepared on the buccal surface, which were restored with composite resin. The teeth were distributed according to the following treatments: G1- bleaching with 10% carbamide peroxide (CP); G2 - bleaching with 38% hydrogen peroxide (HP); and G3 - bleaching with 38% of HP associated to light irradiation. For G1, the bleaching gel was applied for 8 hours daily during 21 days. For G2 and G3, 3 sessions were performed, consisting of 3 applications of 15 minutes each, with 7 days of intervals between the sessions. For G3, the LED (470nm) light was used to activate the bleaching agent for 6 minutes. The surface of enamel and composite resin were evaluated before and after the bleaching procedures using a roughness tester and an atomic force microscope. Results: The results showed significant differences in surface roughness of enamel after bleaching only for G1 (Wilcoxon, p<0.05). For composite resin, neither group showed a statistical difference compared to control (Mann-Whitney, p>0.05). Conclusion: It was concluded that the increase in the roughness of enamel occurred only after bleaching therapy using a gel with 10% of CP. The bleaching procedures evaluated in this investigation did not increase the roughness or cause changes in the superficial morphology of the composite resin.

4.
ROBRAC ; 19(48)abr. 2010. graf, ilus, tab
Artículo en Portugués | LILACS | ID: lil-558303

RESUMEN

O objetivo deste estudo foi avaliar a citotoxicidade de diferentes técnicas de clareamento dentário, utilizando agentes clareadores com 20% e 38% de peróxido de hidrogênio (H2O2) sobre células odontoblastóides MDPC-23. Sessenta discos de esmalte/dentina foram adaptados em câmaras pulpares artificiais e divididos em seis grupos de acordo com o tratamento realizado sobre a superfície do esmalte: G1- 20% H2O2 (1 aplicação); G2- 20% H2O2 (2 aplicações); G3- 38% H2O2 (1 aplicação); G4- 38% H2O2 (2 aplicações); G5- 38% H2O2 (3 aplicações) e G6- controle. Em cada aplicação, os agentes clareadores com 20% ou 38% de H2O2 permaneceram sobre o esmalte por 45 ou 10 minutos, respectivamente. Após a última aplicação do gel, o meio de cultura em contato com a dentina foi obtido (extrato) e aplicado sobre as células previamente cultivadas (30.000 células/cm2). Foram realizadas avaliações do metabolismo (Teste de MTT) e da morfologia celular (MEV). A redução do metabolismo celular foi de 96,29%; 96,11%; 96,42%; 95,62% e 97,18% para G1, G2, G3, G4 e G5, respectivamente. Houve diferença estatisticamente significante apenas quando se comparou os grupos tratados com o grupo controle (G6) (Mann Whitney, p<0,05). Nestes grupos tratados, as poucas célulasque sobreviveram aos extratos apresentavam notáveis alterações morfológicas. Concluiu-se que ambas as técnicas de clareamento avaliadas resultaram em intenso efeito citotóxico trans-amelodentinário para ascélulas MDPC-23.


The aim of this in vitro study was to evaluate the trans-enamel and transdentinal cytotoxic effects of two in-office tooth bleaching techniques that employ bleaching gels containing 20% and 38% of H2O2 on cultured odontoblast-like cell line (MDPC-23). Sixty enamel/dentin discs were obtained from bovine central incisors and placed individually in artificial pulp chambers. Six groups were formed according to the following enamel treatments: G1- 20% H2O2 (1 application); G2- 20% H2O2 (2 applications); G3- 38% H2O2 (1 application); G4- 38% H2O2 (2 applications); G5- 38% H2O2 (3 applications); and G6- control (no treatment). In G1 and G2, the bleaching gel was left in contact with the enamel surface for 45 min in each application. However, in G3, G4, and G5 the bleaching gel was applied for only 10 min per application. After the last application, the extracts were collected and applied on previously cultured cells (30.000 cells/cm2) for 24 h. Cell metabolism was evaluated by the MTT assay and cell morphology was analysed by scanning electron microscopy. Cell metabolism decreased by 96.29%; 96.11%; 96.42%; 95.62%; and 97.18% in G1, G2, G3, G4, and G5, respectively. All treated groups differed significantly from non-treated control group (G6) (p < 0.05). However, the difference in cell metabolism among treated groups was not significant statistically. In addition, significant morphological cell alterations were observed in all treated groups. Under the tested experimental conditions, the extracts collected after both tooth bleaching techniques evaluated in this study caused severe toxic effects on cultured odontoblast-like cell MDPC-23.