RESUMEN
Abstract This study aimed to evaluate the effect of an elastomeric urethane monomer (Exothane-24) in different concentrations on physicochemical properties, gap formation, and polymerization shrinkage stress of experimental resin composites. All experimental composites were prepared with 50 wt.% of Bis-GMA and 50 wt.% of TEGDMA, to which 0 wt.% (control), 10 wt.%, 20 wt.%, 30 wt.%, and 40 wt.% of Exothane-24 were added. Filler particles (65 wt.%) were then added to these resin matrixes. Ultimate tensile strength (UTS: n = 10), flexural strength (FS: n = 10), flexural modulus (FM: n = 10), hardness (H: n = 10), hardness reduction (HR: n = 10), degree of conversion (DC: n = 5), gap width (GW: n = 10), and polymerization shrinkage stress in Class I (SS-I: n = 10) and Class II (SS-II: n = 10) simulated configuration. All test data were analyzed using one-way ANOVA and Tukey's test (α = 0.05; β= 0.2). Exothane-24 in all concentrations decreased the H, HR, DC, GW, SS-I, and SS-II (p < 0.05) without affecting the UTS, and FS (p > 0.05). Reduction in FM was observed only in the Exothane 40% and 30% groups compared to the control (p < 0.05). Exothane-24 at concentrations 20% and 30% seems suitable since it reduced GW and polymerization SS without affecting the properties of the composite resins tested, except for H.
Resumo Este estudo teve como objetivo avaliar o efeito de um monômero elastomérico de uretano (Exothane-24) em diferentes concentrações em propriedades físico-químicas, formação de fenda e tensão de contração de polimerização de resinas compostas experimentais. Todos os compósitos experimentais foram preparados com 50% em peso de Bis-GMA e 50% em peso de TEGDMA, nos quais 0% (controle), 10%, 20%, 30% e 40% em peso de Exothane-24 foram adicionados. Partículas de carga (65% em peso) foram então adicionadas as matrizes resinosas. Resistência coesiva (RC: n = 10), resistência à flexão (RF: n = 10), módulo de flexão (MF: n = 10), dureza (D: n = 10), redução de dureza (RD: n = 10), grau de conversão (GC: n = 5), largura de fenda (LF: n = 10) e tensão de contração de polimerização em simulações de cavidades Classe I (TC-I: n = 10) e Classe II (TC-II: n = 10). Todos os dados do teste foram analisados usando one-way ANOVA e teste de Tukey (α = 0,05; β = 0,2). O Exothane-24 em todas as concentrações diminuiu a D, RD, GC, LF, TC-I e TC-II (p < 0,05) sem afetar o RC e RF (p > 0,05). A redução da MF foi observada apenas nos grupos Exothane 40% e 30% em relação ao controle (p < 0,05). O Exothane-24 nas concentrações de 20% e 30% pareceu ser adequado, pois reduziu LF e TC de polimerização sem afetar as propriedades das resinas compostas testadas, exceto para D.
RESUMEN
Purposes: This study aimed to assess the dimensional accuracy of five commercial alginates verified in stone casts. Methods: Each alginate impression (Cavex ColorChange, Cavex Holland BV; Jeltrate Plus, Dentsply; Hydrogum, Zhermack; Kromopan 100, Lascod; Ezact Kromm, Vigodent) was performed on partially edentulous standard stainless steel mandibular arch cast with reference points on teeth 33, 43, 37 and 47. On the stainless steel cast, the anteroposterior (33-37 and 43-47) and transverse (33-43 and 37-47) distances were measured in a stereomicroscope at 30x magnification and 0.5 µm accuracy. The distances between these points were measured three times, obtaining an average, which was analyzed statistically and compared with the distances obtained from the stone casts. For each alginate the casts were poured gypsum (n = 5) immediately and after a period of 1, 2, 3 and 5 days of the impression procedure. Results: The dimensional accuracy values of stone and stainless steel casts were analyzed statistically by two-way ANOVA and Tukey's test (α=0.05). The results showed significant differences between the alginates; however, no differences in dimensional accuracy were found among the different storage times of alginate impression. Conclusions: It can be concluded that the alginate impressions can be stored for up to 5 days (AU)