RESUMEN
Severely worn dentition causes various complications such as loss of tooth structure, discoloration, pulp complications and loss of function and aesthetics. In this case, the patient showed particularly severe attrition in the anterior teeth and lack of space for restoration. The amount of vertical dimension was determined based on the diagnostic wax up, and the patient’s adaptation was evaluated by using a removable occlusal splint for 6 weeks. Thereafter, the coordination of the muscular nervous system, aesthetics, temporomandibular joint were re-evaluated for 3 months by restoring the fixed provisional restoration. Through the above treatment process, the final restoration was completed with full mouth fixed prosthesis using monolithic zirconia, and functionally and aesthetically stable results were obtained.
RESUMEN
PURPOSE: The aim of this study was to compare the film thicknesses of several resin cements as a function of time after mixing and to examine the effect of working time on the film thicknesses. MATERIALS AND METHODS: The film thickness (microm) of 4 resin cements (n=10), 1 composite resin (Panavia F 2.0), 3 self-adhesive resin (Clearfil SA luting, Zirconite, RelyX U200) cements was measured at 20-second intervals after mixing of the cements up to 200 seconds under a load of 50 N. Linear regression was fitted to verify the effect of working time on the film thickness of each cement. Data were compared to the working time recommended by manufacturers using Wilcoxon test (alpha=.05). RESULTS: All of the materials showed a positive linear correlation between the film thickness and working time. There was no statistically significant difference between the working time based on our results and the values recommended by the manufacturers even though there was a discrepancy between those two values. CONCLUSION: The film thickness of resin cements could increase with the increase of working time. Working time to meet the ISO standard of 50-microm maximum film thickness could be different from the manufacturer's recommended value.