Evaluation of effect of recasting of nickel‑chromium alloy on its castability using different investment materials: An in vitro study.

Context: Castability has been found to be affected by many aspects of the entire casting system. Very few references in dental literature are available regarding recasting of the base metal alloys. Aims: To evaluate and compare the castability of fresh and reused nickel‑chromium alloy and to evaluate the effect of two brands of investment materials on castability of nickel‑chromium alloy. Subjects and Methods: For the experimental purpose of evaluation of the effect of recasting of nickel‑chromium alloy on its castability, different percentages of new and casted alloy (Nickel‑chromium alloy‑(Wirolloy NB, Type 4 (Ni‑67%; Cr‑25%; Mo‑5%; Si‑1.5%; Mn, Nb, B, C each <1%) and two commercial brands of investment materials namely, Deguvest Impact (Degudent; Dentsply Germany) and Bellavest SH (Degudent; Dentsply Germany) was used to obtain 30 samples. Castability value was obtained using Whitlock’s formula. Student t-test and one way ANOVA using SPSS 20.0 software was done. Results: The results of this study confirm earlier works that demonstrate that there is no significant difference in castability values of new and recast alloys. In addition, it also demonstrated, there was no difference in castability using Deguvest Impact and Bellavest SH investment materials. Conclusions: Within the limitations of the study, it was concluded that there was no significant difference found in castability of different percentage combinations of new and once casted alloy using two investment materials. The addition of new alloy during recasting to maintain the castability of nickel‑chromium alloy may therefore not be required.

Physico-mechanical properties and prosthodontic applications of Co-Cr dental alloys: a review of the literature

Cobalt-Chromium (Co-Cr) alloys are classified as predominantly base-metal alloys and are widely known for their biomedical applications in the orthopedic and dental fields. In dentistry, Co-Cr alloys are commonly used for the fabrication of metallic frameworks of removable partial dentures and recently have been used as metallic substructures for the fabrication of porcelain-fused-to-metal restorations and implant frameworks. The increased worldwide interest in utilizing Co-Cr alloys for dental applications is related to their low cost and adequate physico-mechanical properties. Additionally, among base-metal alloys, Co-Cr alloys are used more frequently in many countries to replace Nickel-Chromium (Ni-Cr) alloys. This is mainly due to the increased concern regarding the toxic effects of Ni on the human body when alloys containing Ni are exposed to the oral cavity. This review article describes dental applications, metallurgical characterization, and physico-mechanical properties of Co-Cr alloys and also addresses their clinical and laboratory behavior in relation to those properties.

Microstructure, mechanical performance and corrosion properties of base metal solder joints.

Context: Alloys have been considered to be of paramount importance in the field of prosthodontics. Long span prosthesis may often require joining of one or more individual castings to obtain better fit, occlusal harmony and esthetics in comparison to one-piece casting. Aim: This study was undertaken to evaluate the mechanical properties of base metal alloys joined by two different techniques, namely, gas oxygen torch soldering and laser fusion, compared to a one-piece casting. Mechanical properties evaluated were tensile strength, percentage of elongation and hardness of the solder joint. In addition, corrosion properties and scanning electron microscopic appearance of the joints were also evaluated. Materials and Methods: The samples were prepared according to American Society for Testing Materials specifications (ASTM, E8). Specimens were made with self-cure acrylic and then invested in phosphate-bonded investment material. Casting was done in induction casting machine. Thirty specimens were thus prepared for each group and compared with 30 specimens of the one-piece casting group. Statistical Analysis Used: SPSS software (version 10.0, Chicago, IL, USA) was used for statistical analysis. ANOVA and Benferroni post hoc tests were done for multiple comparisons between the groups and within the groups for mean difference and standard error. Results: Results showed that tensile strength of the one-piece casting was higher than laser fused and gas oxygen torch soldered joints. Laser fused joints exhibited higher hardness values compared to that of gas oxygen torch soldered joints. Scanning electron microscopic examination revealed greater porosity in the gas oxygen torch soldered joints. This contributed to the reduction in the strength of the joint. Gas oxygen torch soldered joints showed less corrosion resistance when compared to laser fused joints and one-piece casting. Conclusion: Laser fusion, which is a recent introduction to the field of prosthodontics, produces joints which have properties between those of one-piece casting and the gas oxygen torch soldering.