Study of the re-osseointegration of implant fixture after mechanical unscrewing / 대한치과보철학회지

PURPOSE: The purpose of this study was to investigate whether the re-osseointegration of the implants that had mechanical unscrewing possibly occurred or not. Furthermore, if it happened, the degree of re-osseointegration was evaluated by comparing with previous osseointegration. MATERIALS AND METHODS: The smooth implant (commercial pure titanium 99%) specimens, whose diameter and length was 3.75 mm, 4 mm, respectively were produced. Two implants were inserted into each tibia of 7 New Zealand female white rabbits weighing at least 3.0 kg. The torque removal force for each implant after 6 weeks of implants placement was measured and included in group I . The torque removal forces were assessed after the fixtures were re-screwed to original position and the subjects were allowed to have 4 more weeks for healing and included in group II. One rabbit was sacrificed after first measurement and produced 4 slide specimens in group I, and two rabbits were sacrificed after 2nd measurement, 7 slide specimens, in group II for histomorphologic investigations. All slide specimens were assessed based on the proportion of BIC (bone-implant contact) as well as CBa (Bone area in the cortical passage) value produced by counting the screw threads embedded in the compact bones under the optical microscopic analysis (x20). Statistical analysis was conducted to evaluate the torque removal force, BIC and CBa between group I and II. RESULTS: As for the torque removal force, the result was 10.8 +/- 3.6 Ncm for group I and 20.2 +/- 9.7 Ncm for group II. Furthermore, the torque removal force of group II increased by 98.1% in average compared to group I (P .05), and RT/BIC and RT/CBa between group I and group II were statistically significant (P < .05). CONCLUSION: It is possible to obtain more substantial re-osseointegration within shorter periods than the period needed for the initial osseointegration in case of iatrogenically unscrewed implants.

Effects of electrical stimulation on healing of endo-osseous titanium implants in circumferential defect / 대한치주과학회지

Several experimental studies showed that the application of small amounts of electric current to bone stimulated osteogenesis at the site of the cathode and suggested that electrical currents promote osseointegration around dental implants. The purpose of this study was to determine the effect of direct microcurrent to endosseous titanium implants placed in bone defects. The right and left 2nd, 3rd and 4th mandibular premolars in ten mongrel dogs (15Kg of weight) were extracted. One monthe later, Ti-machined screw type implants(3.8 mm diameter x 8.5 mm length, AVANA(R), Ostem) were placed in surgically created circumferential defect area(width 5mm, depth 4mm). The implants were divided into three groups according to the treatment modalities: Control group- implants without electrical stimulation; Experimental group I- implants with allogenic demineralized freeze dried bone grafting; and Experimental group IIimplants allogenic demineralized freeze dried bone grafting and electric stimulation. The animals were sacrificed in the 4th and 8th week after implant placement and un-decalcified specimens were prepared for histological and histometrical evaluation of bone-implant contact ratio (BIC) and bone formation area ratio (BFA) in defect area. Some specimens at 8 weeks after implantation were used for removal torque testing. Histologically, there was connective tissue infiltration in the coronal part of defect area in control and the experimental group I, whereas direct bone contact was found in the experimental group II without connective tissue invasion. Average BIC ratios at 4 weeks of healing were 60.1% in the experimental group II, 47.4% in the experimental group I and 42.7% in the control. Average BIC ratios at 8 weeks after implantation were 67.6% in the experimental group II, 55.9% in the experimental group I and 54.6% in the control. The average BFA ratio was 84.0% in the experimental group II, 71.8% in the experimental group I and 58.8% in the control at 4 weeks, and the BFA ratios were 89.6% in the experimental group II, 81.4% in the experimental group I and 70.5% in the control at 8 weeks after implantation. The experimental group II showed also significantly greater BIC and BFA ratios compared to the control and the experimental group I (p<0.05). The removal torque values at 8 weeks after implantation were 56 Ncm in the experimental group II, 49 Ncm in the experimental group I and 43 Ncm in the control. There was a statistically significant difference among 3 groups (p<0.05). These results suggest that electrical stimulation improve and accelerate bone healing around endosseous titanium implants in bone defect.