Effect of silver-coated silica nanoparticles on the thermal conductivity of thermally activated acrylic resin / Efeito das nanopartículas de sílica revestidas por prata na condutividade térmica da resina acrílica ativada termicamente

Objective: Thermally activated acrylic resins (RAATs) are widely used in dentures as a base material due to their good dimensional stability and biocompatibility. However, their low thermal conductivity is a disadvantage, as it affects acceptance when using dental prostheses. Thus, the objective of this work was to measure the conduction heat in RAATs with and without incorporation of silica and silver nanoparticles (NP) and rigid reline (RR). Material and Methods: For this, samples were made and divided into 10 groups (n = 6). The first five groups were 2-mm-thick samples: G1 (RAAT control), G2 (RAAT + RR control), G3 (RAAT and NP + RR), G4 (RAAT + RR and NP), and G5 (RAAT and RR modified by NP). In the other five groups, 8-mm-thick samples were made: G6 (RAAT control), G7 (RAAT + RR control), G8 (RAAT and NP + RR), G9 (RAAT + RR and NP), and G10 (RAAT and RR modified by NP). The heat that cross the surface of the specimens was quantified using a wireless device. The data were submitted to two-factor ANOVA statistical analysis and Tukey ́s test with a 5% significance level. Results: After measuring the temperature variation as a function of time, it can be observed that there was a statistically significant difference for thermal conduction between the control groups and those modified with NP. Conclusion: Thus, it was possible to conclude that the NP improved the heat conduction in RAAT and in the RR because the nanoparticles have a higher thermal conductivity. (AU)

Objetivo: As resinas acrílicas termicamente ativadas (RAATs) são amplamente utilizada em próteses dentárias como material de base, pois possuem uma boa estabilidade dimensional e biocompatibilidade. Porém, como desvantagem, possuem baixa condutividade térmica, o que prejudica a aceitação do uso de próteses dentárias. Assim, o objetivo deste trabalho foi medir a condução de calor em RAAT com e sem incorporação de nanopartículas de sílica e prata (NP) e reembasador rígido (RR). Material e Métodos: Para isso, foram confeccionadas amostras que foram divididas em 10 grupos (n=6). Os primeiros cinco grupos eram amostras de 2 mm de espessura: G1 (RAAT controle), G2 (RAAT + RR controle), G3 (RAAT e NP + RR), G4 (RAAT + RR e NP) e G5 (RAAT e RR modificados por NP). E nos outros cinco grupos foram feitas amostras com espessura de 8 mm: G6 (RAAT controle), G7 (RAAT + RR controle), G8 (RAAT e NP + RR), G9 (RAAT + RR e NP) e G10 (RAAT e RR modificados por NP). O calor percorrido pela superfície dos corpos ­ de prova foi quantificado por meio de um dispositivo sem fio. Os dados foram submetidos à análise estatística ANOVA dois fatores e teste de Tukey com 5% de significância. Resultados: Após medir a variação da temperatura em função do tempo, pode-se observar que houve diferença estatisticamente significante para a condução térmica entre os grupos controle e os modificados com NP. Conclusão: Assim, foi possível concluir que a NP melhorou a condução de calor na RAAT e no RR, pois as nanopartículas apresentam maior condutividade térmica. (AU)

Thermophysical properties of the pequi pulp in different concentrations / Propriedades termofísicas da polpa de pequi em diferentes concentrações

The pequi fruit (Caryocar coriaceum Wittm) has a great economic interest, regarding the use of its fruits in cooking as a source of vitamins and extraction of oils for the manufacture of cosmetics. However, are unknown studies on the thermophysical properties (specific heat, thermal diffusivity and thermal conductivity), in which properties are very important to the pulp being favored in an industrial level. The work in question was aimed at studying the physical properties of the pequi pulp with levels of total soluble solids of 6, 8, 10 and 12 °Brix. The physical properties were studied: specific heat, thermal diffusivity and thermal conductivity. The specific heat of the pulps was determined using the method of mixtures, the thermal diffusivity was determined using the method proposed by Dickerson and the thermal conductivity KD-2 equipment. Therefore, it was found that the specific heat tended to increase with the increase of temperature and total soluble solids content of the pulp. The thermal diffusivity of the pequi pulp decreased with the increase in total soluble solids; the thermal conductivity of the pulp did not show a definite increase in temperature trend in the pulps investigated.

O fruto do pequi (Caryocar coriaceum Wittm) possui um grande interesse econômico, no que se refere ao uso de seus frutos na culinária como fonte de vitaminas e na extração de óleos para a fabricação de cosméticos. Todavia, são desconhecidos estudos voltados para as propriedades termofísicas (calor específico, difusividade térmica e condutividade térmica), nas quais são propriedades de suma importância para que a polpa seja beneficiada a nível industrial. O trabalho em questão teve como objetivo estudar as propriedades físicas da polpa de pequi com teores de sólidos solúveis totais de 6, 8, 10 e 12 oBrix. As propriedades físicas estudadas foram: calor específico, difusividade térmica e condutividade térmica. O calor específico das polpas foi realizado por meio do calorímetro de mistura, a difusividade térmica utilizando-se o método do cilindro de Dickerson e a condutividade térmica no equipamento KD-2. Portanto, constatou-se que o calor específico apresentou tendência de aumento com o aumento da temperatura e do teor de sólidos solúveis totais das polpas. A difusividade térmica da polpa de pequi diminui com o aumento dos sólidos solúveis totais, a condutividade térmica das polpas não apresentou uma tendência definida com o aumento da temperatura nas polpas estudadas.