Enamel Surface Roughness Evaluation after Bracket Debonding: Comparison between Light Cure and Self Cure Adhesive Resin 3-Dimensional Profilometric Study

Introduction: After fixed orthodontic treatment, following bracket removal, the debonding procedure should lead to restitutio ad integrum of the enamel or, at least, restore the enamel surface as closely as possible to its pretreatment condition. Adhesion of brackets in orthodontics is that they should be strong enough to prevent failure during all treatment but also low enough, so that enamel damage would be minimal during bracket removal after treatment. Material and Methods: A total of 60 premolars were collected and stored in distilled water. The extracted teeth were divided into two groups of 30 each, group A was to be bonded with self?cure adhesive while group B light cure adhesive was to be used. A standardised protocol was followed for adhering the brackets to the tooth surfaces. All the teeth were bonded with metal brackets (3M Unitek, Gemini Twin Brackets 0.022 slot). In group A, bonding adhesive (3M Unitek self cure adhesive primer) was applied. In group B, the bonding adhesive (3M Unitek light cure adhesive primer) was photopolymerized for 10 seconds after application. Results: Surface roughness of enamel as assessed by profilometry shows that light cure adhesive creates more roughness as compared to self cure adhesive. To conclude, self cure adhesive is clinically better than light cure adhesive. Discussion: In the present study enamel surface roughness were compared after debonding. Enamel surface roughness after bracket debonding depends o

Avaliação do esmalte dentário após recolagens de bráquetes metálicos e cerâmicos / Evaluation of dental enamel after rebonding of metal and ceramic brackets

Na descolagem de bráquetes ortodônticos pode ocorrer a perda de esmalte na interface adesivo-esmalte. O objetivo deste estudo foi avaliar os possíveis danos à superfície do esmalte com recolagens de bráquetes metálicos e cerâmicos novos por meio da resistência adesiva ao cisalhamento (RAC), da análise do índice de adesivo remanescente (IAR), da avaliação da rugosidade de superfície (RA) e pela análise de microscopia eletrônica (MEV). Foram usados 120 pré-molares, divididos aleatoriamente em 4 grupos de 30 dentes: CS (Controle Saliva); CA (Condicionamento Ácido); M (Metálico) e C (Cerâmico). Foram colados 120 bráquetes metálicos e 120 cerâmicos, para os grupos M e C, em quatro tempos. Os ensaios mecânicos foram realizados em máquina SHIMADZU, na velocidade 0,5 mm/min. Na avaliação da RAC, o ANOVA a dois critérios demonstrou não haver diferenças (p= 0,052) entre os grupos. Na avaliação do IAR, o teste U de Mann-Whitney demonstrou diferença entre os grupos (p< 0,001), onde o grupo cerâmico exibiu escores mais altos que o metálico. Para a rugosidade, o ANOVA a um critério demonstrou que o grupo M apresentou maior RA (p< 0,001). O teste de Tukey demonstrou que os grupos M e C, após o polimento com discos Sof-Lex, exibiram valores de rugosidade inferiores aos demais grupos. Conclui-se que na remoção de bráquetes metálicos ou cerâmicos e da resina remanescente existe maior risco de danos ao esmalte nas recolagens sucessivas. O polimento com discos Sof-Lex promoveu superfície com maior lisura do esmalte.

Debonding of orthodontic brackets may cause enamel surface loss primarily at the adhesive-enamel interface. The purpose of the present study was to evaluate by means of shear bond strength (SBS), adhesive remnant index (ARI), assessment of surface roughness and electron microscope analysis, the possible damages at enamel surface with repeated rebonding of new metallic and ceramic brackets. One hundred and twenty human premolars were randomly divided into 4 groups of 30 premolars each: CS (Saliva Control); CA (Acid Etching); M (Metal); C (Ceramic). For CA group, 4 repeated acid conditionings were performed. One hundred and twenty metallic and ceramic brackets, for groups M and C, were bonded and rebonded respectively at 4 stages. Mechanical trials were obtained with a SHIMADZU testing machine at 0.5 mm/min cross-speed. The SBS results were statistically tested with ANOVA, and no statistically significant differences (p=0.052) were observed. The ARI was evaluated by Mann-Whitney test, which demonstrated that there was a statistically significant difference between metallic and ceramic brackets (p<0.001). The ceramic group exhibited higher statistically significant scores for ARI than the metallic group. The roughness assessment was made with one-way ANOVA, that showed statistically significant differences between groups (p<0.001). Tukey´s test has demonstrated that the M and C groups that were polished with SofLex discs had statistically significant lower roughness values as compared to other groups. Polishing with Sof-lex discs, lead to increased smoothness of enamel surfaces.

The effect of air abrasion on the retention of metallic brackets bonded to fluorosed enamel surface.

Background: Bonding brackets to fluorosed enamel remains a clinical challenge and bracket failure at the compromised enamel interface is common. Objective: To check the effect of air abrasion on the retention of metallic brackets bonded to fluorosed enamel surface. Materials and Methods: Sixty freshly extracted human premolar teeth having moderate to severe dental fluorosis as per Dean's criteria were collected and divided into three groups of 20 each. The groups were treated as follows: In group I, acid etching was followed by bonding with Transbond XT® ; in group II, sandblasting and acid etching was followed by bonding with Transbond XT® ; and in group III, sandblasting and acid etching was followed by bonding with Enlight LC® . An Instron™ universal testing machine was used for determining the debonding force, and from this the shear bond strength was computed. The sample with highest shear bond strength from each group was selected for the scanning electron microscopy (SEM) study. The prepared specimens were examined under a JSM-840A scanning electron microscope (JEOL Ltd, Tokyo, Japan) operated at 20 kV. Photographs were taken at progressively higher magnifications of ×50, ×100, ×500, and ×1000 to view the enamel surface and the adhesive remaining on the enamel surface after debonding. The shear bond strengths of the groups were compared using the one-way ANOVA (analysis of variance) and Tukey post hoc test. The distribution of adhesive remnant index (ARI) score was compared using the Chi-square test. Results: The mean shear bond strength in group I was 10.36 MPa, with a standard deviation of 0.225. The corresponding values in group II and group III were 11.41±0.237 MPa and 11.39±0.201 Mpa, respectively. There was a statistically significant difference between the three groups in the mean shear bond strength values. Conclusion: Sandblasting followed by acid etching provides significantly higher bond strength values compared to acid etching alone, irrespective of the bonding material employed.

The Effect of Beverages On The Release of Calcium From The Eanmel Surface

In this study, the effect of beverages (Coke TM, Sprite™, Ribena™, Chrysanthemum tea and mineral water) on the demineralisation of the enamel surface was investigated. Demineralisation was determined by the rate of calcium released from the enamel surface on exposure to the beverages. Calcium was determined using the EDTA titration method. The pH of these beverages was measured using a pH meter and found to be in the acidic range (2.43 to 5.79) while mineral water which served as a control has a pH of 7.00. Ii was found that the rate of calcium released from Coke™(0.76 J..lg/min) showed a significant mean difference from Sprite™ (0.38 J..lg/min), Chrysanthemum tea (0.10 J..lg/min) and mineral water (0.00 J..lg/min)at p< .05, but was however not significantly different from Ribena™. Likewise, Chrysanthemum tea and mineral water also showed statistically no significant mean difference in the released of calcium during the study period. The results obtained in this study indicated that beverages with low pH may pose detrimental effect on the enamel surface which could have clinical implication, especially in people with salivary gland dysfunction or low salivary flow.

Effects of acid etching times on enamel surface morphology and shear bond strength of orthodontic attachment to enamel / 대한치과교정학회지

The porpuse of this in vito study was to evaluate the effects of different acid etching times on the enamel srface morphology, shear bond strength and debinding failure mode of orthodontic attachment. Ninety six extracted human mandibular premolars were divided into eight groups of twelve teeth. The buccal surfaces were etched with 37% phosphoric acid 5, 10, 15, 30, 45, 60, 90 and 120 seconds, respectively. Two teeth from each group were used for scanning electron mocroscope examination. On the etched buccal aurfaces of remaining teeth, orthodontic attachments(lingual buttons) were bonded with light cured orthodontic adhesive. Twenty four hours after bonding, a Instron universal testing machine was used to determine shear bond strength of orhtodontic attachment to enamel. After debonding, bases of orthodontic attachments and enamel surfaces were examined under stereoscopic microscope to determine failure mode. Statistical analysis of the data was carried out with one way ANOVA and Duncan';s multiple range test. The results were as follows : 1. There was no statistically significant difference in shear bond strengths between the various etching times(p<0.05). 2. The failure modes of orthodontic attachments had some differences. In 5, 10 and 15 seconds etching groups, the percentage of adhesive/ enamel interface failure was higher than that of adhesive/attachment interface failure. On the contrary, 30, 45, 60, 90 and 120 seconds etching groups, the recults were reersed. 3. The etching parerns of enmel surfaces had a great variation. So, we could not find any correlation between etching pattern and bond strength. 4. The findings in this study indicate that in vito reduction of the etching time to 5 seconds maintains clinically acceptable bond strength. However, further study is required to determine the cause of failure mode in 5, 10 and 15 seconds groups.