Clinical application of lithium disilicate glass ceramic cantilever resin-bonded fixed partial denture in the restoration of single anterior tooth loss / 口腔疾病防治

Objective@#To investigate the clinical effect of lithium disilicate glass ceramic cantilever resin-bonded fixed partial dentures (CRBFPDs) on single anterior tooth loss to provide a reference for the selection of restoration methods for single anterior tooth loss.@*Methods@#This study was reviewed and approved by the Ethics Committee, and informed consent was obtained from the patients. Forty-two patients with less than two anterior teeth with monomaxillary loss were included in this study. After 6 months, 1 year, 2 years, and 3 years, the aesthetic and functional effects of the restorations and the periodontal health status were evaluated, and the visual analog scale (VAS) was used to assess patient satisfaction.@*Results@#During the observation period, the connector fractured in one case within 3 months. One case had debonded within 2 years. The aesthetic restoration effect of all lithium disilicate glass ceramic CRBFPDs was categorized as Class A. The periodontal health was good, there was no clinical absorption in the soft and hard tissues of the abutment or subbridge, periodontal status according to the evaluation indices was classified as class A, and the total satisfaction rate of the patient was 100%.@*Conclusion@#For single anterior tooth loss patients, lithium disilicate glass ceramic cantilever resin-bonded fixed partial denture can achieve the restoration effect of less invasion, better adhesion, aesthetics, comfort and good biocompatibility. With high patient satisfaction, it can be considered an ideal restoration method for replacing a single anterior tooth.

Relined fiberglass posts: influence of resin opacity on the bond strength to intraradicular dentin

Abstract This study aimed to evaluate the bond strength between relined fiberglass posts with different composite resin opacities in different thirds of the intraradicular dentin. Thirty single-rooted premolars were endodontically treated and divided into three groups (n=10): fiberglass posts relined with translucent composite resin, fiberglass posts relined with opaque composite resin, and fiberglass posts without relining. After cementation of the posts, the specimens were cut perpendicular to the long axis of the tooth in slices of approximately 1.3 mm of each third to be analyzed (cervical, middle, and apical) and then subjected to the push-out test. The bond strength (MPa) data were subjected to Shapiro-Wilk normality tests and two-way repeated measures analysis of variance, considering the experimental groups and different regions as study factors. Tukey's post-hoc test (p<.05) was applied for comparisons between the groups. In the cervical third, higher values of bond strength were found for the group relined with translucent resin, with a statistically significant difference for the other groups. In the other regions, both opaque and translucent resins showed similar results, but both showed higher values of bond strength compared to fiberglass posts without relining. The bond strength of fiberglass posts to different thirds of intraradicular dentin is influenced by composite resin relining as well as the opacity of the resin. The use of translucent composite resin is a more effective alternative for fiberglass posts relining.

Resumo Este estudo teve como objetivo avaliar a resistência de união entre pinos de fibra de vidro anatomizados com resinas compostas de diferentes opacidades em diferentes terços da dentina intrarradicular. Trinta pré-molares uniradiculares foram tratados endodonticamente e divididos em três grupos (n=10): pinos de fibra de vidro anatomizados com resina composta translúcida, pinos de fibra de vidro anatomizados com resina composta opaca e pinos de fibra de vidro sem anatomização. Após a cimentação dos pinos, os corpos de prova foram cortados perpendicularmente ao longo eixo do dente em fatias de aproximadamente 1,3 mm de cada terço a ser analisado (cervical, médio e apical) e posteriormente submetidos ao teste de push-out. Os dados de resistência de união (MPa) foram submetidos a testes de normalidade de Shapiro-Wilk e ANOVA dois fatores para análises repetidas, considerando os grupos experimentais e diferentes regiões como fatores de estudo. O teste post-hoc de Tukey (p=0,05) foi aplicado para comparações entre os grupos. No terço cervical foram encontrados maiores valores de resistência de união no grupo com anatomização com resina translúcida, com diferença estatisticamente significativa para os demais grupos. Nas demais regiões, tanto as resinas opacas quanto as translúcidas apresentaram resultados semelhantes, mas ambas apresentaram valores de resistência de união superiores aos pinos de fibra de vidro sem anatomização. A resistência de união dos pinos de fibra de vidro aos diferentes terços da dentina intrarradicular é influenciada pela anatomização da resina composta, bem como pela opacidade da resina. A utilização de resina composta translúcida é uma alternativa mais eficaz para a anatomização de pinos de fibra de vidro.

Effect of photopolymerization time on the microhardness of resin cement beneath feldspathic ceramic / Efecto del tiempo de fotopolimerización en la dureza de cementos de resina debajo de una cerámica feldespática

ABSTRACT During ceramic veneer luting, resin cement polymerization is performed with interposition of the dental ceramic. Aim: To evaluate how and how much the photoactivation time affects the Vickers hardness of resin-based cements with interposed ceramic. Materials and Method: A total 24 specimens H mm in diameter and 1 mm thick were made from Paracore White Coltene (PC), Densell Resin Duo Cement (DC), 3MRelyX Veneer (RX) and Coltene Fill Up! (FU), interposing VitablockMarkII (Vita Zahnfabrik) feldspathic ceramic 0.6 mm thick during photoactivation. The materials were polymerized using 100% and 25% of the times indicated by the manufacturers with a Coltolux LED ((Coltene) light with intensity 1200 mW/cm2. Each polymerization time group consisted of three specimens of each material, which were stored dry in darkness at 37 °C for 7 days. Three Vickers microhardness measurements were made on the top and bottom surfaces of each specimen using a Vickers Future Tech FM300 microhardness tester (300 g, 5 s). The values were averaged, and the bottom/top ratios calculated. Results were analyzed by ANOVA. (p<0.05) complemented with multiple comparisons using Tukey's test (p<0.05). Results: Different photoactivation times were found to have a significant effect on hardness values of the cements evaluated, with significant differences between some of the cements. No statistically significant difference was found for the effect of photoactivation time on bottom/top microhardness ratio in those materials. Conclusions: Under the experimental conditions employed, it can be concluded that photopolymerization for shorter times and the interposition of restorative material significantly affectpolymerization quality as evaluated by microhardness, but the bottom/top ratio was unaffected by differences in polymerization time.

RESUMEN Durante la fijación de una carilla cerámica, la polimerización del cemento a base de resinas se realiza con la interposición de la cerámica dental. Objetivo: evaluar en qué forma y magnitud afecta el tiempo de fotoactivación en la dureza Vickers de los cementos a base de resinas con la cerámica interpuesta. Materiales y Método: se confeccionaron 24 probetas de 11 mm de diámetro y 1 mm de espesor con: Paracore White Coltene (PC), Resin Duo Cement de Densell (DC), RelyX Veneer de 3M (RX) y Fill Up! De Coltene (FU) interponiendo 0,6 mm de espesor de cerámica feldespática Vitablock Mark II (Vita Zahnfabrik) durante la fotoactivación. Se polimerizó utilizando el 100% y el 25% del tiempo indicado por el fabricante con lámpara Coltolux LED ((Coltene) con 1200 mW/cm2 de intensidad. Cada grupo quedó conformado con tres probetas de cada material que se almacenaron a oscuras y en seco a 37 °C durante 7 días. Se registraron tres mediciones de microdureza Vickers de las superficies top y bottom de cada probeta con un microdurómetro Vickers Future Tech FM300 (300 g, 5 s) y se calculó su promedio, así como la relación entre los valores registrados en cada una de sus caras. Los resultados fueron analizados por medio de la prueba de ANOVA. (p<0.05). complementada con comparaciones múltiples por medio de la prueba de Tukey (p<0.05). Resultados: se encontró un efecto significativo de la modificación del tiempo de fotoactivación en los valores de dureza de los cementos evaluados con diferencias significativas entre algunos de ellos. Simultáneamente no se encontró significación estadística en el efecto de ese factor sobre la relación microdureza bottom/top registrada en esos materiales. Conclusiones: en las condiciones experimentales empleadas puede concluirse que la fotopolimerización en menor tiempo e interposición de material restaurador afecta significativamente la calidad de polimerización evaluada mediante los valores de microdureza, pero la proporción bottom/ top no fue afectada en la variación en el tiempo de polimerización.

Effect of aging and cementation systems on the bond strength to root dentin after fiber post cementation

Abstract This study evaluated the effect of aging and cementation of fiber posts using glass ionomer and resin cements on push-out bond strength, failure mode, and resin tag formation. One hundred and twenty bovine incisors were used. After post-space preparation, the specimens were randomly allocated into 12 groups (n = 10) according to the cementation system used: GC - GC Gold Label Luting & Lining); RL - RelyX Luting 2; MC - MaxCem Elite; RU - RelyX U200 and the aging periods (24 hours, 6 months, and 12 months). Slices from the cervical, middle, and apical thirds were obtained and analyzed by push-out bond strength test and confocal laser scanning microscopy. One-way ANOVA and Tukey's post-hoc test was used at a significance level of 5%. For the push-out bond strength test, no differences among GC, RU, and MC in the cervical and middle thirds were observed, regardless of the period of storage (P > 0.05). In the apical third, GC and RU showed similar bond strength but higher than other groups (P > 0.05). After 12 months, GC showed the highest bond strength (P < 0.05). Bond strength to post-space dentin decreased over time, regardless of the cementation system used. Cohesive failure was the most frequent, regardless of the period of storage, cementation system, and post-space third. Tag formation was similar among all groups. After 12 months, GC showed the highest bond strength values.

Resumo Avaliar o efeito do envelhecimento e sistemas de cimentação usando ionômero de vidro e cimentos resinosos na resistência de união à dentina após a cimentação do pino de fibra. Cento e vinte incisivos bovinos foram utilizados. Após o preparo do pós-espaço, os corpos de prova foram distribuídos aleatoriamente em 12 grupos (n = 10) de acordo com o período de envelhecimento (24 horas, 6 meses e 12 meses) e o sistema de cimentação utilizado: GC - cimento de ionômero de vidro (GC Gold Label Cimentação e Revestimento); RL - RelyX Luting 2; MC - MaxCem Elite; RU - RelyX U200. Cortes dos terços cervical, médio e apical foram obtidos e analisados por teste de resistência de união push-out e microscopia confocal de varredura a laser. ANOVA one-way e teste de Tukey foi usado a um nível de significância de 5%. Para o teste de resistência de união, não foram observadas diferenças entre GC, RU e MC nos terços cervical e médio, independentemente do período de armazenamento (P > 0,05). No terço apical, GC e RU apresentaram resistência de união semelhante, porém superior aos demais grupos (P > 0,05). Após 12 meses, o GC apresentou a maior resistência de união (P < 0,05). A resistência de união à dentina no espaço para pino diminuiu ao longo do tempo, independentemente do sistema de cimentação utilizado. A formação de tags foi semelhante entre todos os grupos. Após 12 meses, o GC apresentou os maiores valores de resistência de união.

Effect of dentin moisture on the adhesive properties of luting fiber posts using adhesive strategies

Abstract The purpose of this study was to evaluate the effect of dentin moisture (moist and dry) on the bonding of fiber posts to root dentin with different adhesive strategies (etch-and-rinse, self-etch, and self-adhesive). Seventy-two extracted single-rooted human teeth were endodontically treated and divided into six groups (n = 12) according to the moisture of dentin surface and adhesive systems as follows: a) etch-and-rinse/moist, b) etch-and-rinse/dry, c) self-etch/moist, d) self-etch/dry, e) self-adhesive/moist, and 6) self-adhesive/dry. The specimens were sectioned into six slices for push-out bond strength (BS), nanoleakage (NL) by SEM, and Vickers microhardness (VHN) of the resin cement. A universal testing machine (AG-I, Shimadzu Autograph) was used at a crosshead speed of 0.5 mm/min until post extrusion, with a load cell of 50 kg for evaluation of the push-out strength. Data on BS, NL, and VHN were evaluated by two-way ANOVA and Tukey's test (α = 0.05). Dentin moisture as the main factor was not significantly different for the push-out test. However, higher BS values can be observed for the etch-and-rinse group. A lower percentage of NL was found in the dry dentin groups. The moisture pattern was not significant in the hardness values for the pre-etching groups. Additional moisture did not increase the evaluated properties.

Final irrigation protocols can be used to promote stable long-term bond strength of AH Plus to dentin

Abstract Irrigation solutions might affect dentin surface characteristics and, consequently, endodontic sealers adhesion. Objective This study analyzed the effect of different final irrigation protocols on push-out bond strength (BS) of AH Plus to dentin seven days and 20 months after obturation. Scanning electron micrographs were obtained from the dentin surface of one sample/group after final irrigation. Methodology Canals of bovine incisors were instrumented and received final irrigation with (n=21): G1 - 2.5% sodium hypochlorite (NaOCl) + distilled water; G2 - 2.5% NaOCl + 17% EDTA; G3 - 2.5% NaOCl + 17% EDTA + 2.5% NaOCl; G4 - 2.5% NaOCl + 17% EDTA + 2% chlorhexidine (CHX); G5 - mixture 5% NaOCl + 18% etidronate (HEDP); and G6 - mixture 5% NaOCl + 10% tetrasodium EDTA (Na4EDTA). After irrigation, one root/group was split and images were obtained by scanning electron microscopy (SEM). The other 20 roots/group were filled with only AH Plus sealer. Three slices/root were used for push-out assessment seven days and 20 months after obturation. One-way analysis of variance and Tukey (α<0.05) were used to compare the results among experimental groups, and unpaired t-test (α<0.05) was used to compare the results of the same group over time. Results The photomicrographs showed that, excepting G1, all groups completely removed the smear layer from the samples. In G2 and G4, the opening of the dentin tubules enlarged. In G3, erosion was observed in the peritubular and intertubular dentin. Values of the BS in the seven days were G2=G3=G4=G5>G6=G1 and in the 20 months were G3=G5>G6=G4>G1=G2. G3, G5, and G6 presented values of BS in 20 months similar to the values of seven days (P>0.05). Conclusions The final irrigation protocols tested produced dentin surfaces with different characteristics. Only G3 and G5 presented high BS values that were stable over time.

Influence of medium-translucency monolithic zirconia thicknesses and light-curing time on the polymerization of dual-cure resin cements

Aim: To investigate and compare the effects of different thicknesses of medium-translucency monolithic zirconia and light curing times on the polymerization of two types of dual-cured resin cement. Methods: A total of 200 cement specimens were prepared from TheraCem and RelyX U200 cement. The specimens were divided into 5 groups: Group I, without interposing zirconia; Group II, 0.50 mm thickness; Group III, 1.00 mm; Group IV, 1.50 mm; and Group V, 2.00 mm thickness. Each group was subdivided into (1) RelyX U200 and (2) TheraCem. Each subgroup was subdivided according to the light-curing time into (a) 20 s and (b) 40 s (n =5). The polymerization was tested using Fourier-transform infrared (FTIR) spectroscopy and a Vickers microhardness tester. The data were statistically analyzed using ANOVA, an independent sample t-test, and Tukey's test at a significance level of 0.05. Results: The control group had the highest values of DC and VMH, followed by 0.50, 1.00, and 1.50 mm, respectively, while the 2.00 mm group showed the lowest values. The specimens irradiated for 40 s had greater DC and VMH than those irradiated for 20 s. RelyX U200 revealed higher values for both parameters compared to TheraCem cement. Conclusion: The polymerization of selfadhesive cement depends on the thickness of the monolithic zirconia, the light curing time, and the composition of the cement. The cement should be irradiated for a longer period than recommended to overcome the light attenuation of zirconia. TEGDMA-based self-adhesive cement showed a higher DC and VMH than BISGMA-based cement

Interplay between resin cements and surface-treated Poly-Ether-Ether-Ketone (PEEK): effect of aging

Aim: This study assessed the effect of thermal aging on the interfacial strength of resin cements to surface-treated PEEK. Methods: Ninety-six PEEK blocks were allocated into 4 groups (n=24), according to following surface treatments: SB - sandblasting with aluminum oxide; SA - acid etched with 98% sulfuric acid; CA ­ coupling agent (Visio.link, Bredent) and CO - control group (untreated). Surface roughness (Ra) was measured and one cylinder (1-mm diameter and height) of Rely-X Ultimate - ULT (3M/ESPE) and another one of Panavia V5 - PAN (Kuraray) were constructed on the treated or untreated PEEK surfaces. Half of the samples of each group were thermal aged (1,000 cycles). Samples were tested at a crosshead speed of 1 mm/min in shear mode (µSBS). Ra and µSBS data were compared using one- and three-way ANOVA, respectively, and Tukey's tests. Results: SA and SB samples had the roughest surfaces, while CA the smoother (p<0.001). Thermal aging reduced µSBS regardless the surface treatment and resin cement used. There was interaction between surface treatment and resin cement (p <0.001), with ULT showing higher µSBS values than PAN. SA provided higher µSBS than SB for both resin cements, while for CA µSBS was higher (PAN) or lower than SB (ULT). Conclusion: Aging inadvertently reduces interfacial strength between PEEK and the resin cements. If ULT is the resin cement of choice, reliable interfacial strength is reached after any PEEK surface treatment. However, if PAN is going to be used only SA and CA are recommended as PEEK treatment

Effect of S. mutans biofilm on the hybrid ceramic-resin cement bond strength assessed by different methods

Aim: The purpose of this study was to investigate the biofilm effect on the hybrid ceramic-resin cement bond strength (BS) by comparing two methods. Methods: Teeth were distributed into groups (n=5), according to the resin cement (Maxcem Elite-(MC) or NX3 Nexus-(NX)) and degradation method (24h or 7 days in distilled water; 7 or 30 days incubated with biofilm and 30 days in sterile media). Treated surfaces of Vita Enamic blocks (5x6x7mm) were luted to treated or no treated dentin surfaces and light-cured. After 24h, beams were obtained (1x1x10mm) and stored accordingly. The flexural bond strength (FBS) was assessed by four-point bending test. Additional beams were obtained from new teeth (n=5), stored for 24h or 7 days in distilled water, and submitted to a microtensile bond strength (µTBS) assay. Failure modes were determined by scanning electron microscopy (100X). The flexure strength of the cements (n=10) was assessed by a four-point bending test. Data were analyzed by 1 and 2-ways ANOVA, and Tukey's test (α=0.05). Results: There was no significant difference between the degradation methods for the FBS groups. For the µTBS, the significant difference was as follows: NX 7days > NX 24h > MC 7days = MC 24h. Failure mode was mainly adhesive and mixed, but with an increase of cohesive within cement and pre-failures for the MC groups assessed by µTBS. NX had better performance than MC, regardless of the method. Conclusions: The biofilm had no effect on the materials BS and FBS test was a useful method to evaluate BS of materials with poor performance

Accelerated artificial aging and color stability in resin-based cements / Envejecimiento artificial acelerado y estabilidad de color de medios de fijación a base de resinas

ABSTRACT The aim of this study was to determine color change after accelerated artificial ageing (AAA) of different composite cements that are used with veneers. Five cylindrical test specimens, 15 mm in diameter and 2 mm thick, were made from a single layer of each of the following: RelyX Veneer 3M ESPE (RX), Paracore White Coltene (PC), Solocem White Opaque Coltene (SO), Resin Duo Cement Densell (DC), Panavia V5 Paste Kuraray Noritake (PA) and Panavia F2.0 Kuraray Noritake (PF) (30 specimens altogether). The specimens were light cured following manufacturers' instructions using a Coltolux LED (Coltene) unit. Initial color was determined using an Easyshade - Vita Zahnfabrik Spectrophotometer. Then, the specimens were subjected to AAA for two weeks (336 hours) with cycles of 4 hours of UV light at 60 °C and 4 hours of vapor condensation at 50 °C, successively, after which color was recorded again. Color change was determined for each specimen according to the difference in shade on the Vita scale before and after AAA. Results were analyzed using Kruskal Wallis test. Mean and standard deviation for each group were: RX 8.40 (1.52); PC 8.60 (3.13); SO 6.40 (3.51); DC 10.00 (0.00); PA 7.60 (3.29); PF 2.00 (0.00). The Kruskal Wallis test showed significant difference for material (p<0.05), and comparison of means showed difference between Panavia F2.0 and the other materials. A table providing equivalence between the Vita Classic and CIELAB scales was used to transfer the recorded colors to the CIELAB scale, and the color difference ΔE was calculated for each group, where ΔL, Δa and Δb are the differences in the L, a and b values before and after the AAA. The mean and standard deviation were analyzed statistically by the ANOVA test and Tukey's test. Mean and standard deviation for each group were: RX 14.94 (2.02); PC 14.51 (4.02); SO 12.08 (4.53); DC 16.31 (0.00); PA 10.9 (3.38); PF 7.24 (0.00). The ANOVA test showed significant difference for material (p<0.05). Tukey's test showed two groups (PF-DC, RX, PA). Under the experimental conditions of this study, it can be concluded that accelerated ageing significantly affects the color stability of the resin based cements tested.

RESUMEN El objetivo de este trabajo fue determinar el cambio de coloración de distintos medios de fijación a base de resinas con indicación para carillas estéticas luego de someterse al envejecimiento artificial acelerado (AAA). Se confeccionaron 30 probetas cilíndricas de 15 mm de diámetro y 2 mm de espesor con RelyX Veneer 3M ESPE (RX), Paracore White Coltene (PC), Solocem White Opaque Coltene (SO), Resin Duo Cement Densell (DC), Panavia V5 Paste Kuraray Noritake (PA) y Panavia F2.0 Kuraray Noritake (PF) de una sola capa de material. Se polimerizaron según las indicaciones del fabricante con unidad de curado Coltolux LED (Coltene). Cada grupo quedó conformado con 5 probetas de cada material. Se tomó el color con el espectrofotómetro Easyshade de Vita Zahnfabrik. A continuación, se sometieron a AAA por dos semanas (336 horas) con ciclos de 4 horas de radiaciones ultravioletas a 60°C Y 4 horas de condensación de vapor de agua a 50°C sucesivamente. Una vez terminado este proceso se volvió a registrar el color. El cambio de color se evaluó dentro de la escala de color, ordenada en función del valor. El dato registrado fue la diferencia en la posición inicial y final en esta escala. Los resultados obtenidos para cada grupo fueron analizados por medio de la prueba de Kruskal Wallis. Los valores de media y desvío estándar de cada grupo fueron: RX 8,40 (1,52); PC 8,60 (3,13); SO 6,40 (3,51); DC 10,00 (0,00); PA 7,60 (3,29); PF 2,00 (0,00). El análisis con la prueba de Kruskal Wallis mostró diferencia significativa para el factor material (p<0.05) y la comparación de medias mostró diferencia entre PF y el resto de los materiales. Por otra parte, con una tabla de equivalencia entre los colores en escala de Vita Classic y CIE Lab, se hicieron el pasaje de los valores registrados a la escala de CIE Lab y se calculó la diferencia de color ΔE de cada grupo antes y después del AAA. La media y el desvío estándar fueron analizados estadísticamente por el test de ANOVA y prueba de Tukey. Los valores de media y desvío estándar de cada grupo fueron: RX 14,94 (2,02); PC 14,51 (4,02); SO 12,08 (4,53); DC 16,31 (0,00); PA 10,9 (3,38); PF 7,24 (0,00). En la evaluación de los resultados con ANOVA se encontró diferencia significativa entre los materiales evaluados (p<0,05). La comparación de medias con prueba de Tukey mostró la presencia de dos grupos (PF-DC, RX, PA). En las condiciones experimentales de este trabajo puede concluirse que el envejecimiento acelerado afecta significativamente la estabilidad de color de los cementos utilizados en este trabajo.

Novo sistema de retentor pré-fabricado perfurado e de iluminador em fibra óptica: estudo da resistência mecânica frente a variação dos cimentos resinosos / New system of hollow prefabricated post and optical fiber illuminator: study of the mechanical strength by varying resin cements

O presente estudo teve por objetivo avaliar a resistência à flexão de um pino experimental de fibra de vidro vazado, e a resistência adesiva entre este pino experimental à dentina radicular, associando a utilização de um dispositivo iluminador em fibra óptica, sob o processo de envelhecimento, além de determinar a distribuição de tensão pela Análise de Elementos Finitos (FEA). O pino experimental e o dispositivo iluminador de fibra óptica têm por finalidade aumentar a efetividade de fotoativação dos cimentos resinosos nos terços médios e apicais dos canais radiculares. Para o teste de flexão de 3 pontos, estritamente do pino de fibra de vidro, as amostras foram divididas em 4 grupos (n=10): pino convencional (pc), pino experimental sem preenchimento (pp), com preenchimento de cimento resinoso (ppc) e com preenchimento de fibra óptica (ppf). Para o teste de resistência adesiva Pull-out, 100 raízes de dentes bovinos foram restauradas com retentores intrarradiculares e coroas de resina composta, distribuídos em 10 grupos (n=10), tendo como variáveis: o tipo de pino de fibra de vidro [convencional (C) ou perfurado (P)], o sistema de fotoativação [com ou sem o iluminador de fibra óptica (O)], o tipo de cimento resinoso [fotoativado (F) ou polimerização dual (D)] e o envelhecimento das amostras [com e sem ciclagem mecânica (C)]. O processo de envelhecimento foi realizado através da ciclagem mecânica e as amostras foram submetidas ao teste de resistência adesiva Pull-out. A análise do modo de falha foi realizada em Estereomicroscópio. A Análise em Elementos Finitos avaliou a distribuição de tensão pela análise de von Mises, deformação total e tensão máxima principal no Software Ansys 19.3. A análise estatística foi constituída pelo teste de normalidade Shapiro-Wilk, análise de variância (ANOVA) 1, 2 e 3 fatores e teste Tukey 5%. As médias e desvios padrão de resistência à flexão foram (MPa): pc = 677 ± 81,1; ppc = 419 ± 23,2; ppf = 200 ± 32,5 e pp = 177 ± 32,8. As médias e desvios padrão de resistência adesiva foram (MPa): CD = 12,2 ± 1,21; PD = 11,1 ± 1,32; PF = 10,9 ± 1,29; POD = 13,7 ± 1,16; POF = 11,9 ± 1,48; CDC = 10,1 ± 1,33; PDC = 9,25 ± 1,11; PFC = 8,37 ± 1,25; PODC = 10,8 ± 0,95 e POFC = 9,82 ± 1,02. Os resultados do modo de falha foram: adesiva entre pino e cimento (56%), mista predominantemente adesiva entre cimento e dentina (22%), adesiva entre cimento e dentina (14%) e a mista predominantemente adesiva entre pino e cimento (8%). Concluiu-se que entre os pinos experimentais, o grupo do pino perfurado preenchido com cimento resinoso obteve o maior valor de resistência à flexão, a utilização do dispositivo iluminador aumentou os resultados de resistência adesiva nos grupos dos pinos perfurados e não houve diferença na distribuição de tensões entre os grupos. (AU)

The present study aimed to evaluate the flexural strength of an experimental hollow glass fiber post, and the bond strength between this experimental post and root dentin, associating the use of an optical fiber illuminating device, under the aging process, in addition to determine the stress distribution by Finite Element Analysis (FEA). The experimental post and optical fiber illuminating device are intended to increase the polymerization effectiveness of resin cements in the middle and apical regions of root canals. For the 3-point bending test, strictly of the fiber post, the samples were divided into 4 groups (n=10): conventional post (pc), experimental post without filling (pp), with resin cement filling (ppc) and with optical fiber filling (ppf). For the Pull-out test, 100 roots of bovine teeth were restored with intraradicular retainers and composite resin crowns, distributed into 10 groups (n=10), with the following variables: glass fiber post type [conventional (C) or hollow (P)], the photocuring system [with or without the optical fiber illuminating device (O)], the type of resin cement [light cured (F) or dual cured (D)] and aging of the samples [with and without mechanical cycling (C)]. The aging process was performed by mechanical cycling and the samples were submitted to the Pull-out bond strength test. Failure mode analysis was performed using a stereomicroscope. Finite Element Analysis evaluated the stress distribution by von Mises analysis, total strain and maximum principal stress in Ansys Software 19.3. Statistical analysis consisted of the Shapiro-Wilk normality test, 1-, 2- and 3-way analysis of variance (ANOVA) and Tukey test 5%. The means and standard deviations of flexural strength were (MPa): pc = 677 ± 81.1; ppc = 419 ± 23.2; ppf = 200 ± 32.5 and pp = 177 ± 32.8. The means and standard deviations of bond strength were (MPa): CD = 12.2 ± 1.21; PD = 11.1 ± 1.32; PF = 10.9 ± 1.29; POD = 13.7 ± 1.16; POF = 11.9 ± 1.48; CDC = 10.1 ± 1.33; PDC = 9.25 ± 1.11; PFC = 8.37 ± 1.25; PODC = 10.8 ± 0.95 and POFC = 9.82 ± 1.02. The failure mode results were: adhesive between post and cement (56%), mixed predominantly adhesive between cement and dentin (22%), adhesive between cement and dentin (14%) and mixed predominantly adhesive between post and cement (8 %). It was concluded that among the experimental posts, the hollow post group filled with resin cement obtained the highest flexural strength value, the use of the illuminating device increased the results of bond strength in the hollow post groups and there was no difference in the stress distribution among the groups (AU)

Análise da interface adesiva entre pinos de fibra de vidro e dentina intrarradicular submetida à técnica alcoólica simplificada / Analysis of the adhesive interface glass fiber posts and intrarradicular dentil submitted to the simplified alcoholic technique

A cimentação de pinos de fibra de vidro à dentina intrarradicular, principalmente no terço apical, continua sendo um desafio na odontologia. O objetivo desse estudo foi avaliar a influência do controle de umidade com etanol na resistência de união de pinos de fibra de vidro em diferentes terços de dentina intrarradicular, 24 horas e 6 meses após o processo de cimentação adesiva. Sessenta e quatro incisivos bovinos extraídos foram submetidos ao tratamento endodôntico e divididos em dois grupos, de acordo com o tipo de controle de umidade (técnica convencional e alcoólica). Cada grupo foi dividido em 4 subgrupos (n=8) de acordo com a cimentação: RXU: Single bond Universal + RelyX Ultimate; PNV: primer de dentes Panavia V5 + Panavia V5; U200: RelyX U200; SET: Set PP. A resistência de união do pushout foi medida em diferentes áreas da interface entre o pino e a superfície radicular, 24 horas e 6 meses após o procedimento de união. Os dados foram submetidos ao teste de Bonferroni (α = 0,05). Os menores valores de resistência de união foram encontrados para o grupo SET, com diferença estatisticamente significante entre os demais grupos para os terços cervical e médio. Os maiores valores de resistência de união foram encontrados para o grupo PNV com diferença estatisticamente significante para os demais grupos nos terços médio e apical em 24 horas. Avaliando os diferentes terços, em geral, os maiores valores de resistência de união foram encontrados para o terço cervical. O grupo PNV apresentou maiores valores de resistência de união para os terços cervical e médio, sem diferença estatisticamente significante entre eles. Quanto ao tipo de controle de umidade, pode-se observar que não há diferença estatisticamente significativa para o grupo PNV às 24 horas, U200 e SET aos 6 meses. Na comparação entre os tempos (24 horas e 6 meses), em geral, os valores de resistência de união diminuíram após o armazenamento. Diferenças significativas com menores valores foram observadas após o tempo de seis meses nos valores de envelhecimento para a resistência de união. Por meio de um microscópio óptico e um aparelho de microscopia eletrônica de varredura o padrão de fratura na interface adesiva foi caracterizado.

Cementation of fiberglass posts to intraradical dentin, especially in the apical third, remains a challenge in dentistry. The study was to evaluate the influence of moisture control with ethanol on the bond strength of fiberglass posts in different thirds of intraradicular dentin, 24 hours and 6 months after the adhesive cementation process. Sixty-four extracted bovine incisors were endodontically protected and divided into two groups, according to the type of moisture control (conventional and alcoholic technique). Each group was divided into 4 subgroups (n=8) according to cementation: RXU: Single bond Universal + RelyX Ultimate; PNV: Panavia V5 tooth primer + Panavia V5; U200: RelyX U200; SET: Set PP. The pushout bond strength was measured in different areas of the interface between the post and the root surface, 24 hours and 6 months after the bonding procedure. The data were confirmed by the Bonferroni test (α = 0.05). The lowest bond strength values were found for the SET group, with a statistically significant difference between the other groups for the cervical and middle thirds. The highest bond strength values were found for the PNV group, with a statistically significant difference for the other groups in the middle and apical thirds at 24 hours. Evaluating the different thirds, in general, the highest bond strength values were found for the cervical third. The PNV group showed higher bond strength values for the cervical and middle thirds, with no statistically significant difference between them. As for the type of humidity control, it can be observed that there is no statistically significant difference for the PNV group at 24 hours, U200 and SET at 6 months. In the comparison between times (24 hours and 6 months), in general, the bond strength values decreased after storage. Minor elevation differences with values were observed after the six-month time in the ageing values for bond strength. Using an optical microscope and a scanning electron microscopy device, the fracture pattern at the adhesive interface was characterized.

Cytotoxicity Comparison of a Calcium Silicate-Based Resin Cement versus Conventional Self-Adhesive Resin Cement and a Resin-Modified Glass Ionomer: Cell Viability Analysis

Abstract Objective: To compare the cytotoxicity level of a new calcium silicate-based resin cement (TheraCem) with two commonly used cements, including a conventional self-adhesive resin cement (Panavia SA) and a resinmodified glass ionomer cement (FujiCem2), on the human gingival fibroblast cells after 24 and 48 hours. Material and Methods: Twelve discs of each cement type were fabricated. The extract of cement disks was made by incubating them in the cell medium. Human gingival fibroblast cells were cultured and exposed to cement extracts for 24 h and 48 h. MTT assay was performed on extracts and optical density and cell viability rates were calculated by the spectrophotometer device at 570 nm. Data were analyzed using ANOVA and Tukey HSD tests. Results: The cell viability rates after 24 hours and 48 hours were as follows: TheraCem: 89.24% and 85.46%, Panavia SA: 49.51% and 46.57% and FujiCem2: 50.63% and 47.36%. TheraCem represented the highest cell viability rate. However, no significant difference was noted between Panavia SA and FujiCem2. Time had no significant effect on cell viability. Conclusion: TheraCem exhibited the best results among three tested cements and was considered non-toxic. Panavia SA and FujiCem2 were not significantly different regarding the cell viability rate. Time had no significant effect on the cytotoxicity level of cements (AU).

Effect of ceramic thicknesses and opacities on water sorption and solubility of a light-curing resin cement by different units

Aim: This study evaluated the water sorption and solubility of a light-cured resin cement, under four thicknesses and four opacities of a lithium disilicate ceramic, also considering three light-emitting diode (LED) units. Methods: A total of 288 specimens of a resin cement (AllCem Veneer Trans ­ FGM) were prepared, 96 samples were light-cured by each of the three light curing units (Valo ­ Ultradent / Radii-Cal ­ SDI / Bluephase II ­ Ivoclar Vivadent), divided into 16 experimental conditions, according to the opacities of the ceramic: High Opacity (HO), Medium Opacity (MO), Low Translucency (LT), High Translucency (HT), and thicknesses (0.3, 0.8, 1.5, and 2.0 mm) (n = 6). The specimens were weighed at three different times: Mass M1 (after making the specimens), M2 (after 7 days of storage in water), and M3 (after dissection cycle), for calculating water sorption and solubility. Results: The higher thickness of the ceramic (2.0 mm) significantly increased the values of water sorption (44.0± 4.0) and solubility (7.8±0.6), compared to lower thicknesses. Also, the ceramic of higher opacity (HO) generated the highest values of sorption and solubility when compared to the other opacities, regardless of the thickness tested (ANOVA-3 factors / Tukey's test, α = 0.05). There was no influence of light curing units. Conclusion: Higher thicknesses and opacities of the ceramic increased the water sorption and solubility of the tested light-cured resin cement

Effect of ethanol-conditioned dentine on sealer penetration into dentinal tubules: a confocal microscopy study

Aim: The aim of this study was to evaluate the effect of ethanol-conditioned dentin on endodontic sealer penetration into dentinal tubules by confocal laser scanning microscopy (CLSM). Methods: Forty human maxillary anterior teeth were instrumented and divided into four groups (n = 10) according to the drying methods: 1) wet: vacuum only, 2) paper points: vacuum + absorbent paper points, (3) 70% ethanol: 70% ethanol (1 min) + vacuum + absorbent paper points, and (4) 100% ethanol: 100% ethanol (1 min) + vacuum + absorbent paper points. All root canals were filled with resin-based endodontic sealer. Four sections from each third (cervical, middle, and apical) were examined by CLSM. Root canal wall perimeter infiltrated by sealer, maximum depth of sealer penetration, percentage of penetrated area, and fluorescence intensity of rhodamine B were measured. Statistical analysis was performed by analysis of variance and Tukey's tests (α = 0.05). Results: No statistical difference was found when percentage of root canal wall coverage infiltrated by sealer were compared. The groups in which ethanol solutions were used presented greater depth of sealer penetration, higher percentage of penetrated area, and higher fluorescence intensity of rhodamine B (p< 0.05) when compared with the wet and paper point groups. Overall, 100% ethanol produced better results than 70% ethanol, except for rhodamine B intensity (cervical third). In addition, the absorbent paper points drying method behaved better than did vacuum only group, except for rhodamine B intensity (apical third). Conclusion: Ethanol-conditioned dentin improved the penetration of resin-based sealer into dentinal tubules, especially at the concentration of 100%

Surface treatment and adhesion approaches on polymer-infiltrated ceramic network: influence on the bond strength to resin cement

Aim: To evaluate the effect of different surface treatments and adhesive approaches on the microshear bond strength of resin cement to a polymer-infiltrated ceramic network (PICN). Methods: PICN blocks were randomly assigned into 9 groups (n=10): CTRL: no treatment; HF: 5% hydrofluoric acid etching; HF-S: HF + silane; HF-S-A: HF-S + adhesive (Adper Single Bond 2); HF-UA: HF + universal adhesive (Single Bond Universal); SB: sandblasting with 50 µm Al2O3 particles; SB-S: SB + silane; SB-S-A: SB-S + adhesive; SB-UA: SB + universal adhesive. Resin cement microcylinders (Ø = 0.96 mm; height = 1 mm) (RelyX Ultimate) were built upon the PICN surface after roughness and contact angle measurements. Next, microshear bonding tests (µSBS) were performed (0.5 mm/min) after water storage (37ºC, 90 days) and thermocycling (12,000 cycles; 5ºC-55ºC). Failure modes were observed under stereomicroscope. Bond strength data were analyzed by two-way ANOVA/Tukey's test and t-tests. Kruskal-Wallis/Dunn's tests were conducted for roughness and contact angle data (α = 0.05). Results: A rougher surface and lower contact angles were observed for Sandblasting. HF-S (18.54 ± 2.03 MPa), SB-S (19.00 ± 1.66 MPa) and SB-UA (18.07 ± 2.36 MPa) provided the highest bond strength values, followed by the other treated groups. The CTRL group resulted in lower bond strength (7.18 ± 2.34 MPa). Conclusion: Hydrofluoric acid etching followed by silane application and sandblasting followed by silane or universal adhesive are useful clinical steps to enhance bonding to PICN. Adhesive applications after HF etching have no advantages in bonding to PICN

Is the Er:YAG laser affect the surface characteristics and bond strength of Y-TZP?

Abstract This study evaluated the surface characteristics and bond strength of Y-TZP treated with Er:YAG laser at different focal distances. 120 Y-TZP blocks were divided into five groups (n=24), according to the surface treatment: no treatment (C-); sandblasting with silica-coated aluminum oxide particles (C+); and Er:YAG laser application at focal distances of 1mm (Er:YAG-1), 4mm (Er:YAG-4), and 7mm (Er:YAG-7). Surface characteristics were analyzed using Vickers microhardness, confocal laser microscope, scanning electron microscopy (SEM), and X-ray diffractometer (XRD). For the bond strength test, 100 Y-TZP blocks were subdivided into two subgroups (n=10), according to the resin cement used: with (MDP+) or without 10-methacryloyloxydecyl dihydrogen phosphate (MDP-). The Vickers microhardness and surface roughness were analyzed by one-way ANOVA and bond strength by two-way ANOVA and Tukey's test for both (α=0.05). Vickers microhardness differences were not observed between the groups (p>0.05); C+ showed higher surface roughness values. SEM images showed micromorphological differences between the groups. The XRD data detected tetragonal crystals for C- and, for the other groups, tetragonal and monoclinic peaks. For bond strength, no statistically difference significance were observed among the cements with or without MDP (p>0.05) but showed significant difference between the surface treatments (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Suggested that the Er:YAG laser cannot replace conventional treatment with aluminum oxide particles and the presence of MDP in the resin cement had no influence on the bond strength.

Resumo Este estudo avaliou as características de superfície e resistência de união de Y-TZP tratado com laser de Er: YAG em diferentes distâncias focais. Cento e vinte blocos de Y-TZP foram divididos em cinco grupos (n=24), de acordo com a superfície de tratamento: sem tratamento (C-); asperização com partículas de óxido de alumínio revestidas por sílica (C +); e aplicação de laser Er: YAG a distâncias focais de 1 mm (Er: YAG-1), 4 mm (Er: YAG-4) e 7 mm (Er: YAG-7). As características de superfície foram analisadas por meio de microdureza Vickers, microscópio confocal a laser, microscopia eletrônica de varredura (MEV) e difratômetro de raios-X (DRX). Para o ensaio de resistência de união, cem blocos de Y-TZP foram subdivididos em 2 subgrupos (n=10) de acordo com o cimento resinoso utilizado (n=12): com 10-metacriloiloxidecil dihidrogenofosfato (MDP+) ou sem (MDP-). Microdureza Vickers e rugosidade de superfície foram analisadas por ANOVA a 1 fator e a resistência de união por ANOVA a 2 fatores e ambos seguidos de teste complementar de Tukey (α=0,05). Não foram observadas diferenças de microdureza Vickers entre os grupos; C+ apresentou maiores valores de rugosidade superficial. Imagens de MEV mostraram diferenças micromorfológicas entre os grupos. Os dados de DRX detectaram apenas cristais tetragonais para C- e, para os outros grupos, picos de zircônia nas fases tetragonal e monoclínica. Para a resistência de união, não foram observadas diferenças estatisticamente significante entre os cimentos com e sem MDP (p>0.05), mas foram observadas diferenças significativas entre os tratamentos de superfície (C+ > C- = Er:YAG1 > Er:YAG4 = Er:YAG7) (p<0.05). Sugere-se que o laser de Er: YAG não pode substituir o tratamento convencional com partículas de óxido de alumínio e a presença de MDP no cimento resinoso não influenciou na resistência de união.

Microtensile Bond Strength Between Self-Adhesive Resin Cements and Resin Based Ceramic CAD/CAM Block / Resistencia adhesiva microtensil entre cementos de resina autoadhesivos y bloques de cerámica CAD/CAM a base de resina

Abstract: Purpose: The objective of this study is to evaluate and compare the microtensile bond strength (μTBS) of four different self-adhesive resin cements to a resin-based ceramic CAD/CAM block, at the baseline, and after subjecting them to 5,000 thermo-cycles.Materials and Methods: Four self-adhesive dual-cured resin cements; G-CEM LinkAce (GC EUROPE, Leuven, Belgium), RelyX U200 (3M ESPE, Seefeld, Germany), Maxcem Elite (Kerr, CA, USA), TheraCem (Bisco, Schaumburg, USA) were applied to Cerasmart CAD/CAM blocks (GC EUROPE, Leuven, Belgium). CAD/CAM blocks were sectioned into sticks and subjected to µTBS tests at 24 hours, and the other half were subjected to tests after 5000 thermo-cycles. The data were tested by one-way variance analysis (p<0.05). Results: The highest bond strength values were observed in TheraCem, followed by G-CEM LinkAce and RelyX U200, respectively (p<0.05). At the baseline, G-CEM LinkAce, RelyX U200, and Maxcem Elite showed statistically similar results. After 5,000 thermal-cycles, a significant decrease was observed in the bond strength values of G-CEM LinkAce (p<0.05). Conclusion: Between the adhesive cements used in the study, TheraCem showed the highest micro-tensile bond strength values both in the baseline (24h) results, and after the 5,000 thermal- cycle aging procedures.

Resumen: Propósito: Evaluar y comparar la resistencia adhesiva microtensil (μTBS) de cuatro cementos de resina autoadhesivos diferentes con un bloque CAD/CAM de cerámica a base de resina, antes y después de 5.000 ciclos de termociclado. Materiales y métodos: cuatro cementos de resina de doble curado autoadhesivos; G-CEM LinkAce (GC EUROPE, Lovaina, Bélgica), RelyX U200 (3M ESPE, Seefeld, Alemania), Maxcem Elite (Kerr, CA, EE. UU.), TheraCem (Bisco, Schaumburg, EE. UU.) fueron aplicados a bloques Cerasmart CAD/CAM (GC EUROPE, Lovaina, Bélgica). Los bloques CAD/CAM se seccionaron en barras y se sometieron a pruebas µTBS a las 24 horas, y la otra mitad se sometió a pruebas después de 5000 ciclos térmicos. Los datos fueron probados por análisis de varianza unidireccional (p<0.05). Resultados: Los valores más altos de fuerza de unión se observaron en TheraCem, seguido de G-CEM LinkAce y RelyX U200, respectivamente (p<0.05). En la línea de base, G-CEM LinkAce, RelyX U200, Maxcem Elite mostró resultados estadísticamente similares. Después de 5.000 procesos de ciclo térmico, se observó una disminución significativa en los valores de resistencia de la unión de G-CEM LinkAce (p<0.05). Conclusión: entre los cementos adhesivos utilizados en el estudio, TheraCem mostró los valores más altos de resistencia de la unión micro-extensible tanto en la línea de base (24 h) como después de 5,000 procedimientos de envejecimiento térmico.

Feldspathic and Lithium Disilicate Onlays with a 2-Year Follow-Up: Split-Mouth Randomized Clinical Trial

Abstract The present study was a prospective, controlled, randomized, clinical short-term trial aiming to evaluate the clinical performance of adhesively luted, lithium disilicate and feldspathic glass-ceramics onlays over a period up to 2 years. A total of 11 patients (7 female, 4 male; age range: 18-60 years, mean age: 39 years) were selected for this study. Each patient received a maximum of two restorations per group in a split-mouth-design. LD: Eleven onlays, performed with lithium disilicate-based ceramic (IPS e.max CAD, Ivoclar Vivadent, Schaan, Liechtenstein), and FP: Eleven onlays, performed with feldspathic ceramic (Vita Mark II, Vita Zanhfabrik, Bad Säckingen). Recalls were performed at 2 weeks (baseline = R1), 1 year (R2) and 2 years (R3) after the cementation by three calibrated blinded independent investigators using mirrors, magnifying eyeglasses, probes and bitewing radiographs. The postoperative sensitivity, secondary caries, marginal integrity, marginal discoloration, color match, surface roughness, tooth integrity, and restoration integrity were evaluated. The Friedman test was used to determine if there was a statistically significant difference in time-to-time comparison of the parameters in the ceramics restorations. A total of 95.4% of the restorations were clinically acceptable at the 2-year recall, without a difference for any evaluation parameter for both ceramic materials. Based on the 2-year data, the CAD-CAM onlays manufactured with feldspathic and lithium-disilicate based ceramics showed similar clinical performance.

Resumo O presente estudo é um estudo clínico prospectivo, controlado, randomizado e de longo curto prazo, com o objetivo de avaliar o desempenho clínico de restauraç ões adesivas cerâmica vítrea reforçada com dissilicato de lítio e cerâmica feldspática por um período de até 2 anos. Um total de 11 pacientes (7 mulheres, 4 homens; faixa etária: 18-60 anos, idade média: 39 anos) foram inseridas para este estudo. Cada paciente recebeu duas restaurações por grupo em um delineamento de boca dividida. LD: Onze onlays, realizados com cerâmica à base de dissilicato de lítio (IPS e.max CAD, Ivoclar Vivadent, Schaan, Liechtenstein); e FP: Onze onlays, realizados com cerâmica feldspática (Vita Mark II, Vita Zanhfabrik, Bad Säckingen). Os retornos foram realizados em 2 semanas (linha de base = R1), 1 ano (R2) e 2 anos (R3) após a cimentação, por três investigadores independentes, cegos e calibrados, usando espelhos, óculos de aumento, sondas e radiografias interproximais. Foram avaliadas a sensibilidade pós-operatória, cárie secundária, integridade marginal, descoloração marginal, correspondência de cores, rugosidade da superfície, integridade dentária e integridade da restauração. O teste de Friedman (95%) foi utilizado para determinar se havia uma diferença estatisticamente significante na comparação periódica dos parâmetros nas restaurações cerâmicas. Um total de 95,4% das restaurações estava clinicamente aceitável no retorno de 2 anos, sem diferença para qualquer parâmetro de avaliação para ambos os materiais cerâmicos. Com base nos dados de 2 anos, as restaurações CAD-CAM fabricados com cerâmica feldspática e à base de dissilicato de lítio apresentaram desempenho clínico semelhante.

Use of Self-Adhesive Resin Cements in Dentistry: a Literature Review / Uso de Cimentos Resinosos Autoadesivos em Odontologia: uma Revisão da Literatura

Self-adhesive resin cements (SARCs) are cementing agents and have the objective of simplifying adhesive cementation, with a simplified use protocol. The aim of this article was to review the literature on SARCs with a focus on the advantages of their use, highlighting their adhesion and biocompatibility mechanism. Thus, the Health Sciences Descriptors "Self-Adhesive Resin Cement", "Dental Cements", "Adhesion" and "Dental Prosthesis" were used, as well as their Portuguese counterparts in the online databases SciELO, PubMed and Bireme in the period of time between the years 2000 to 2020. According to the studies, SARCs have excellent physical and mechanical properties, which include low solubility in the oral environment, adhesion to the dental substrate and the prosthetic part, color mimicry, biocompatibility and fluoride release, in addition to being applied in a single step, optimizing the operator's working time. In addition, self-adhesive cements seem to offer a promising new approach in indirect restorative procedures, which may present a performance similar to conventional ones, however more studies are needed to support their long-term applicability. (AU)

Os cimentos resinosos autoadesivos (CRAAs) são agentes de cimentação e possuem o objetivo de simplificar a cimentação adesiva, com um protocolo simplificado de utilização. Assim, o objetivo deste trabalho foi revisar na literatura acerca dos CRAAs com enfoque nas vantagens de sua adequada utilização, evidenciando seu mecanismo de adesão e biocompatibilidade. Dessa forma, foram utilizados os descritores em Ciências da Saúde (DeCS) "Cimento Resinoso Autoadesivo", "Cimentos Dentários", "Adesão" e "Prótese Dentária", assim como seus correspondentes na língua inglesa nas bases de dados online SciELO, PubMed e Bireme no período de tempo entre os anos 2000 a 2020. De acordo com os estudos, os CRAAs apresentam excelentes propriedades físicas e mecânicas, que incluem baixa solubilidade no meio bucal, adesão ao substrato dental e a peça protética, mimetização de cores, biocompatibilidade e liberação de fluoretos, além de serem aplicados em uma única etapa clínica, otimizando o tempo de trabalho do operador. Além disso, os cimentos autoadesivos oferecem uma nova abordagem promissora em procedimentos restauradores indiretos, podendo apresentar um desempenho semelhante aos convencionais, porém são necessários mais estudos que sustentem sua aplicabilidade a longo prazo. (AU)