RESUMEN
[Objective]To design a method of in vitro preparation and seperation for metallic wear particles around joint prosthesis and evaluate its feasibility in medical experiments.[Method]Ti-6Al-4V and Co-Gr-Mo alloys were used to make two friction jars respectirely. National inventive patent applied number 03142073.7.Lots of quadrate blocks made of the same materials are put into the jars respectively,which were then.lubri cated by man-made body fluid and vibrated on a bottle shaker.After 21 days the fluid was harvested and centrifuged to get the produced wear particles.The collected particles were studied by using element trace analysis,laser countersizer and scanning electron microscopy.The J774.A1 macrophages cultured together with these particles for 24 hours were observed under inverted phase contrast microscopy and transmission electron microscopy.[Result]A got great amounts of metallic particles with 1?m diameter coned beproduce using this method.The aver age diameter of titanium alloys(Dv90) is 1.011 and that of Co-Gr-Mo is 1.010.Particle size distribution had good consistency in different materials.Under scanning electron microscopy ,the particles had irregular shapes just like those got from revision operations.The particles taken into the J774.A1 macrophages could be seen under inverted p hase contrast microscopy and transmission electron microscopy.[Conclusion]This method is good enough to producl lots of metallic wear particles mosth like those around total joint prosthesis and can be used in further in vivo and in vitro studies about joint prosthesis loosening.