RESUMEN
PURPOSE: The purpose of this study is finding proper bonding agents to be used when adding bis-acryl composite provisional materials. MATERIALS AND METHODS: Three bonding agents with different chemical compositions were included in this study. Forty disk shaped specimens of bis-acryl composite provisional material were prepared and divided into 4 groups according to the bonding agents. Control group didn't have bonding agent. Through the Teflon mould with 4.0 mm diameter hole with 4.0 mm thickness the same bis-acryl composite provisional material was added on the disks after the surface of each specimen was treated with designated bonding agent according to the manufacturer's instructions. Shear bond test was performed and the fractured surfaces were inspected with a microscope. One-way analysis of variance was conducted and the result was further analysed with Turkey post hoc test at the significance level of 0.05. RESULTS: The highest strength was acquired from the specimens bonded with chemical cure system and it was statistically significant (P < 0.05). This group showed 100% cohesive failures. The lowest bonding strength was recorded from the specimens used conventional light cure bonding agent, and this group's result was similar with the control group. The group used a light cure bonding agent claiming improved compatibility revealed significantly higher bond strength to the traditional light cure bonding agent group in a statistically significant way (P = 0.043). CONCLUSION: According to the bonding agent used the shear bond strength was significantly affected. Therefore the choice of proper bonding agent is important when hiring a bonding agent to add bis-acryl composite provisional materials.