A multiple-stimuli-responsive drug-conjugated cross-linked micelles was prepared by radical copolymerization. The chemical structure, morphology, and size of the cross-linked micelles were characterized, and the drug loading of the micelle was calculated. The experimental results indicated that the hydrodynamic size of the drug-loaded micelles were about 100 nm, and the as prepared micelles could be degraded and swelled in presence of reducing glutathione (GSH). The low critical solution temperature (LCST) of the micelle was around 39.4℃. According to the experimental results, the micelles will shrink at temperature above the LCST. Subsequently, the accumulative drug release rate was up to 91.78% under acidic (pH 5.0), reductive (GSH 10 mmol/L) and high temperature (42.0℃) conditions mimicking the tumor microenvironment, while a relatively low release rate of 1.12% was observed without stimulation. The drug-conjugated cross-linked micelles showed a strong cell uptake behavior. In the cytotoxicity assay, the micelles exhibited effective anti-cancer activity and excellent biocompatibility. In brief, the experimental results show that the as-prepared drug-conjugated cross-linked micelle exhibits multiple stimuli-responsiveness, which holds great promise for anti-cancer drug delivery.
RESUMEN
In order to construct a novel multifunctional targeting nano-carrier based on pH-redox characteristics of tumor microenvironment,ketone bonds and disulfide bonds were bonded to the oligomeric hyaluronic acid (oHA) being sensitive to pH and the reduction environment.The chemical structure of oligomeric hyaluronic acid-8-mercaptomenthone 1,2-glycerolketal (oHMST) was characterized by 1H NMR,IR and ESI-MS.Curcuminloaded micelles were prepared by dialysis.The single factor investigation was carried out on the dosage form.Some properties,including particle size zeta potential,the morphology of micelles,and pH-sensitivity were studied.The materials were synthesized successfully.The micelles were spheric with a diameter of about 100 nm.The Zeta potential of the micelles was-(21.97 ± 1.08) mV.The in vitro test showed that oHMST carriers have good pH-sensitivity and redox-sensitivity.