The Micromorphometric change of the GBA and RBM implant surface conditioned with tetracycline-HCl / 대한치주과학회지

The present study was performed to evaluate the effect of tetracycline-HCl on the change of implant surface microstructure according to application time. Implant with pure titanium machined surface, GBA surface and RBM surface were utilized. Implant surface was rubbed with 50mg/ml tetracycline-HCl solution for 1/2min. 1min. 1 1/2min. 2min. and 2 1/2min. respectively in the test group. Then, specimens were processed for scanning electron microscopic observation. The results of this study were as follow. 1. Both test and control group showed a few shallow grooves and ridges in pure titanium machined surface implants. There were not significant differences between two group. 2. In GBA surfaces, control group exhibit many porous depression, and each depression were divided by strict border. Experimental group applied with tetracycline-HCl for 2min. were similar with control group. But when applied for 2 1/2min. surface alteration and border breakdown started, resulting enlargement of the porous depression. 3. In RBM surface, control group exhibit rough, uneven surface with crater-like depression can be found. The surface alteration started when tetracycline-HCl was applied for 30sec. resulting breakdown of the crater-like depression. Depression became larger as applying time increased.

Micromorphometric change of implant surface conditioned with tetracycline-HCl: FBR(R) and CellNest surface / 대한치주과학회지

The present study was performed to evaluate the effect of tetracycline-HCL on the change of implant surface microstructure according to application time. Implant with pure titanium machined surface, double coated FBR(R) surface and oxidized CellNest surface were utilized. Implant surface was rubbed with 50mg/ml tetracycline-HCL solution for 1/2, 1, 1 1/2, 2 and 2 1/2min. respectively in the test group. Then, specimens were processed for scanning electron microscopic observation. The results of this study were as follows. 1. Both test and control group showed a few shallow grooves and ridges in pure titanium machined surface implants. There were not significant differences between two groups. 2. The double coated FBR(R) surfaces showed fine crystalline structures. The roughness of surfaces conditioned with tetracycline-HCL was lessened relative to the application time. 3. The oxidized CellNest surfaces showed the porous structures. The surface conditioning with tetracycline-HCl influenced on its micro-morphology. In conclusion, the detoxification of the affected implant surface with 50mg/ml tetracycline-HCL should be applied respectively with different time according to various implant surfaces.

Micromorphometric change of implant surface conditioned with Tetracycline-HCl: HA and Etched surface / 대한치주과학회지

The present study was performed to evaluate the effect of tetracycline-HCl on the change of implant surface microstructure according to application time. Implant with pure titanium machined surface, HA-coated surface and dual acid etched surface were utilized. Implant surface was rubbed with 50mg/ml tetracycline-HCL solution for 1/2min., 1min., 1 1/2min., 2min., and 2 1/2min. respectively in the test group. Then, specimens were processed for scanning electron microscopic observation. The results of this study were as follows. 1. Both test and control group showed a few shallow grooves and ridges in pure titanium machined surface implants. There were not significant differences between two groups. 2. In HA-coated surfaces, round particles were deposited irregularly. The roughness of surfaces conditioned with tetracycline-HCL was lessened and the cracks were increased relative to the application time. 3. The etched surfaces showed the honey comb structures. The surface conditioning with tetracycline-HCl didn't influence on its micro-morphology. In conclusion, the detoxification with 50mg/ml tetracycline-HCl must be applied respectively with different time according to various implant surfaces.

Scanning Electron Microscopic Study of the Effect of Tetracycline-HCl on the Change of Implant Surface Microstructure according to Application Time / 대한치주과학회지

The present study was performed to evaluate the effect of tetracycline - HCl on the change of implant surface microstructure according to application time. Implants with pure titanium machined surface, SLA surface and TiO2blasted surface were used. Implant surface was rubbed with 50mg/ml tetracycline - HCl solution for 1/2 min., 1 min., 1 1/2 min., 2 min., and 3min. respectively in the test group and with no conditioning in the control group. Then, the specimens were processed for scanning electron microscopic observation. The following results were obtained. 1. In the pure titanium machined surfaces, the control specimen showed a more or less rough machined surface composed of alternating positive and negative lines corresponding to grooves and ridges. After treatment, machining line was more pronounced for the control specimens. but in general, test specimens were similar to control. 2. In the SLA surfaces, the control specimen showed that the macro roughness was achieved by large-grit sandblasting. subsequently, the acid-etching process created the micro roughness, which thus was superimposed on the macro roughness. 3. In the SLA surfaces, irrespective of the application time of 50mg/ml tetracycline - HCl solution , in general, test specimens were similar to control. 4. In the TiO2blasted surfaces the control specimen showed the rough surface with small pits. The irregularity of the TiO2blasted surfaces with 50mg/ml tetracycline - HCl solution was lessened and the flattened areas were wider relative to the application time of tetracycline - HCl solution. In conclusion, pure titanium machined surfaces and SLA surfaces weren't changed irrespective of the application time of tetracycline - HCl solution. And the TiO2blasted surfaces conditioned with tetracycline - HCl solution began to be changed from 1 1/2 min. This results are expected to be applied to the regenerative procedures for peri-implantitis treatment.