Influence of pH, bleaching agents, and acid etching on surface wear of bovine enamel

ABSTRACT Development of new materials for tooth bleaching justifies the need for studies to evaluate the changes in the enamel surface caused by different bleaching protocols. Objective The aim of this study was to evaluate the bovine dental enamel wear in function of different bleaching gel protocols, acid etching and pH variation. Material and Methods Sixty fragments of bovine teeth were cut, obtaining a control and test areas. In the test area, one half received etching followed by a bleaching gel application, and the other half, only the bleaching gel. The fragments were randomly divided into six groups (n=10), each one received one bleaching session with five hydrogen peroxide gel applications of 8 min, activated with hybrid light, diode laser/blue LED (HL) or diode laser/violet LED (VHL) (experimental): Control (C); 35% Total Blanc Office (TBO35HL); 35% Lase Peroxide Sensy (LPS35HL); 25% Lase Peroxide Sensy II (LPS25HL); 15% Lase Peroxide Lite (LPL15HL); and 10% hydrogen peroxide (experimental) (EXP10VHL). pH values were determined by a pHmeter at the initial and final time periods. Specimens were stored, subjected to simulated brushing cycles, and the superficial wear was determined (μm). ANOVA and Tukey´s tests were applied (α=0.05). Results The pH showed a slight decrease, except for Group LPL15HL. Group LPS25HL showed the highest degree of wear, with and without etching. Conclusion There was a decrease from the initial to the final pH. Different bleaching gels were able to increase the surface wear values after simulated brushing. Acid etching before bleaching increased surface wear values in all groups.

Choice of toothpaste for the elderly: an in vitro study

Hyposalivation and dental root exposure in the elderly are problems that require special oral care. In this context, the characteristics of certain toothpastes are of particular importance. Thus, the aim of this study was to evaluate the cytotoxicity and dentin wear caused by seven different toothpastes. For dentin wear analysis, 40 root dentin specimens were submitted to 20,000 brushing cycles with the different toothpastes and distilled water (control group-CG), using a brushing machine. Dentin surface loss (SL) was measured by contact profilometer. The cytotoxicity of each toothpaste was tested using cultured fibroblasts submitted to a cell-culture-conditioned medium. Fresh medium served as the control. Cell viability was assessed by MTT assay after 24 h of contact with the conditioned media. The data were analyzed statistically by ANOVA, followed by Tukey’s test (p < 0.05). The SL of the CG was minimal and significantly lower than that of the Oral B Pro Health (OBPH) group (p < 0.05). All other groups presented SL in between that of the CG and the Oral B Pro Health OBPH group, except for the Sensodyne (SEN) group, which presented SL similar to that of CG (p = 0.05). The SEN group presented a percentage of viable cells similar to that of CG: between 60-89%. All the other toothpastes showed high cytotoxicity, with cell viability less than 50% of the CG. Considering study limitations, we concluded that only one of the seven tested toothpastes exhibited the most desirable toothpaste characteristics for the worldwide growing elderly population (e.g. low cytotoxicity and low-abrasive potential).

Minimal alterations on the enamel surface by micro-abrasion: in vitro roughness and wear assessments

ABSTRACT Objective: To evaluate the in vitro changes on the enamel surface after a micro-abrasion treatment promoted by different products. Material and Methods: Fifty (50) fragments of bovine enamel (15 mm × 5 mm) were randomly assigned to five groups (n=10) according to the product utilized: G1 (control)= silicone polisher (TDV), G2= 37% phosphoric acid (3M/ESPE) + pumice stone (SS White), G3= Micropol (DMC Equipment), G4= Opalustre (Ultradent) and G5= Whiteness RM (FGM Dental Products). Roughness and wear were the responsible variables used to analyze these surfaces in four stages: baseline, 60 s and 120 s after the micro-abrasion and after polishing, using a Hommel Tester T1000 device. After the tests, a normal distribution of data was verified, with repeated ANOVA analyses (p≤0.05) which were used to compare each product in different stages. One-way ANOVA and Tukey tests were applied for individual comparisons between the products in each stage (p≤0.05). Results: Means and standard deviations of roughness and wear (µm) after all the promoted stages were: G1=7.26(1.81)/13.16(2.67), G2=2.02(0.62)/37.44(3.33), G3=1.81(0.91)/34.93(6.92), G4=1.92(0.29)/38.42(0.65) and G5=1.98(0.53)/33.45(2.66). At 60 seconds, all products tended to produce less surface roughness with a variable gradual decrease over time. After polishing, there were no statistically significant differences between the groups, except for G1. Independent of the product utilized, the enamel wear occurred after the micro-abrasion. Conclusions: In this in vitro study, enamel micro-abrasion presented itself as a conservative approach, regardless of the type of the paste compound utilized. These products promoted minor roughness alterations and minimal wear. The use of phosphoric acid and pumice stone showed similar results to commercial products for the micro-abrasion with regard to the surface roughness and wear. .