RESUMEN
ABSTRACT With the aim of introducing permanent prostheses with main properties equivalent to cortical human bone, Ti-diamond composites were processed through powder metallurgy. Grade 1 titanium and mixtures of Ti powder with 2%, 5% and 10 wt% diamond were compacted at 100MPa, and then sintered at 1250°C/2hr/10-6mbar. Sintered samples were studied in the point of view of their microstructures, structures, yield strength and elastic modulus. The results showed that the best addition of diamonds was 2 wt%, which led to a uniform porosity, yield strength of 370MPa and elastic modulus of 13.9 GPa. Samples of Ti and Ti-2% diamond were subjected to in vitro cytotoxicity test, using cultures of VERO cells, and it resulted in a biocompatible and nontoxic composite material.
Asunto(s)
Humanos , Animales , Titanio/análisis , Materiales Biocompatibles/análisis , Ensayo de Materiales/métodos , Diamante/análisis , Propiedades de Superficie , Resistencia a la Tracción , Células Vero , Chlorocebus aethiops , PorosidadRESUMEN
Foi utilizado um método inédito para a avaliaçäo do desempenho (tempo de vida útil) de pontas diamantadas, especialmente confeccionadas com 8 tipos de gräos (naturais e sintéticos), cortando-se substrato constituído por vidro, o qual era movimentado contra a ponta em açäo. Estabelecida uma série de necessárias condiçöes operatórias, os valores de tensäo e corrente elétrica no motor da caneta (a qual prendia a ponta em ensaio) eram basicamente transferidos para um microcomputador, onde em tempo real era calculado o valor da respectiva força tangencial de corte, através de um programa de computaçäo especialmente desenvolvido, o qual efetuava uma série de cálculos matemáticos, criando gráficos e mantendo o registro de todos os valores verificados. Nas condiçöes estabelecidas, em ordem decrescente de magnitude da vida útil, os gräos de diamante avaliados assim se comportaram: PDA 433, DMB-T, DMB-G, PDA 555, PDA 665, PDA 768, TED-II e PDA 878