Surface agents' influence on the flexural strength of bilaminated ceramics

The objective of this study was to evaluate the influence of different surface agents on the flexural strength of a ceramic system. Eighty bar-shaped specimens of zirconia were divided into four groups according to the agent to be used: group Control - to be cleaned with alcohol; group VM9 - application of a fluid layer of porcelain; group Effect Bonder - application of a bonding agent; and group Coloring Liquid - application of coloring liquid. All specimens received the porcelain application by the layering technique and were then subjected to thermocycling. The four-point bending test was performed to calculate the strength values (σ, MPa) and the failure modes were classified. ANOVA did not detect significant differences among the groups. The Weibull modulus were 5 (Control, VM9 and Effect Bonder) and 6 (Coloring Liquid). The cracking of the porcelain ceramic toward the interface was the predominant failure mode. It was concluded that the surface agents tested had no effect on the flexural strength of the bilaminated ceramic specimens.

Comparison of physical and mechanical properties of microwave-polymerized acrylic resin after disinfection in sodium hypochlorite solutions

This study evaluated the color stability, surface roughness and flexural strength of a microwave-polymerized acrylic resin after immersion in sodium hypochlorite (NaOCl), simulating 20 min of disinfection daily during 180 days. Forty disk-shaped (15 x 4 mm) and 40 rectangular (65 x 10 x 3 mm) specimens were prepared with a microwave-polymerized acrylic resin (Onda-Cryl). Specimens were immersed in either 0.5 percent NaOCl, 1 percent NaOCl, Clorox/Calgon and distilled water (control). Color measurements were determined by a portable colorimeter. Three parallel lines, separated by 1.0 mm, were registered on each specimen before and after immersion procedures to analyze the surface roughness. The flexural strength was measured using a 3-point bending test in a universal testing machine with a 50 kgf load cell and a crosshead speed of 1 mm/min. Data were analyzed statistically by ANOVA and Tukey's test (?=0.05). There was no statistically significant differences (p>0.05) among the solutions for color, surface roughness and flexural strength. It may be concluded that immersion in NaOCl solutions simulating short-term daily use during 180 days did not influence the color stability, surface roughness and flexural strength of a microwave-polymerized acrylic resin.

Este estudo avaliou a estabilidade de cor, rugosidade superficial e resistência à flexão de resina acrílica polimerizada por microondas após desinfecção em hipoclorito de sódio, simulando 20 min de desinfecção diária durante 180 dias. Quarenta espécimes circulares (15 x 4 mm) e 40 retangulares (65 x 10 x 3 mm) foram preparados em resina acrílica polimerizada por microondas (Onda-Cryl). As amostras foram imersas em hipoclorito de sódio a 0,5 por cento, hipoclorito de sódio a 1 por cento, Clorox/Calgon e água destilada (controle). Medidas de cor foram determinadas por um espectrocolorímetro portátil. Três linhas paralelas, separadas por 1,0 mm, foram registradas em cada amostra antes e depois dos procedimentos de imersão para analisar a rugosidade superficial. A resistência à flexão foi medida utilizando um teste de flexão por 3 pontos em uma máquina universal de ensaios com uma célula de carga de 50 Kgf e uma velocidade de 1 mm/min. Os dados foram analisados estatisticamente por ANOVA e teste de Tukey (?=0,05). Não houve diferença estatisticamente significante (p>0,05) entre as soluções para cor, rugosidade superficial e resistência à flexão. Pode-se concluir que a imersão em soluções de hipoclorito de sódio, simulando um uso diário de curta duração durante 180 dias, não influenciou a estabilidade de cor, rugosidade superficial e resistência à flexão de resina acrílica polimerizada por microondas.