Do pediatric medicines induce topographic changes in dental enamel?

Abstract The purpose of the present study was to evaluate the effect of common pediatric liquid medicines on surface roughness and tooth structure loss and to evaluate the pH values of these medicines at room and cold temperatures in vitro. Eighty-four bovine enamel blocks were divided into seven groups (n = 12): G1-Alivium®, G2-Novalgina®, G3-Betamox®, G4-Clavulin®, G5-Claritin®, G6-Polaramine® and G7-Milli-Q water (negative control). The pH was determined and the samples were immersed in each treatment 3x/day for 5 min. 3D non-contact profilometry was used to determine surface roughness (linear Ra, volumetric Sa) and the Gap formed between treated and control areas in each block. Scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) were also performed. The majority of liquid medicines had pH ≤ 5.50. G1, G4, and G5 showed alterations in Ra when compared with G7 (p < 0.05). According to Sa and Gap results, only G5 was different from G7 (p < 0.05). Alteration in surface was more evident in G5 SEM images. EDS revealed high concentrations of carbon, oxygen, phosphorus, and calcium in all tested groups. Despite the low pH values of all evaluated medicines, only Alivium®, Clavulin®, and Claritin® increased linear surface roughness, and only Claritin® demonstrated the in vitro capacity to produce significant tooth structure loss.

Surface degradation of composite resins by acidic medicines and ph-cycling

This study evaluated the effects of acidic medicines (Dimetapp® and Claritin®), under pH-cycling conditions, on the surface degradation of four composite resins (microhybrid: TPH, Concept, Opallis and Nanofilled: Supreme). Thirty disc-shaped specimens (Ø = 5.0 mm / thickness = 2.0 mm) of each composite were randomly assigned to 3 groups (n = 10): a control and two experimental groups, according to the acidic medicines evaluated. The specimens were finished and polished with aluminum oxide discs, and the surface roughness was measured by using a profilometer. After the specimens were submitted to a pH-cycling regimen and immersion in acidic medicines for 12 days, the surface roughness was measured again. Two specimens for each material and group were analyzed by scanning electron microscopy (SEM) before and after pH-cycling. Data were analyzed by the Student's-t test, ANOVA, Duncan's multiple range test and paired t-test (α=0.05). Significant increase in roughness was found only for TPH in the control group and TPH and Supreme immersed in Claritin® (p<0.05). SEM analyses showed that the 4 composite resins underwent erosion and surface degradation after being subjected to the experimental conditions. In conclusion, although the roughness was slightly affected, the pH-cycling and acidic medicines caused surface degradation of the composite resins evaluated. Titratable acidity seemed to play a more crucial role on surface degradation of composite resins than pH.