Résumé
ABSTRACT This study evaluated the influence of the mode and time of solvent evaporation on the tensile strength (TS), flexural strength (FS) and elastic modulus (EM) of two adhesive systems: Scotchbond Multipurpose (SBMP) and Clearfil SE (CSEB). For this purpose, rectangular samples (2x1x7 mm) were prepared with 10 μL of primer and the solvents were evaporated with air spray at (23±1) ºC, (40±1) ºC and negative control (without spray). For each temperature, the times of 5, 20, 30, and 60 seconds were investigated. The statistical results showed that evaporation at 40±1ºC resulted in better EM for the two adhesives tested and all the evaporation times evaluated. However, there were no significant differences between the times and modes of evaporation for TS. The results of this study indicate that evaporation at a temperature of (40±1) °C could improve the elastic modulus of both adhesives tested, regardless of the evaporating time.
RESUMO Este estudo avaliou a influência do modo e do tempo de evaporação do solvente na resistência à tração (RT), resistência à flexão (RF) e módulo de elasticidade (MR) de dois sistemas adesivos: Scotchbond Multipurpose (SBMP) e Clearfil SE (CSEB). Para isso, amostras retangulares (2x1x7 mm) foram preparadas com 10 μL de primer e os solventes foram evaporados com aerossol a (23±1) ºC, (40±1) ºC e controle negativo (sem aerossol). Para cada temperatura, foram avaliados os tempos de 5, 20, 30 e 60 segundos. Os resultados estatísticos mostraram que a evaporação a (40±1) ºC resultou em melhor MR para os dois adesivos testados e todos os tempos de evaporação avaliados. No entanto, não houve diferenças significativas entre os tempos e modos de evaporação na RT. Os resultados deste estudo indicam que a evaporação a uma temperatura de (40±1) °C poderia melhorar o módulo de elasticidade de ambos os adesivos testados, independentemente do tempo de evaporação.