Résumé
Aim: The purpose of this study was to investigate the biofilm effect on the hybrid ceramic-resin cement bond strength (BS) by comparing two methods. Methods: Teeth were distributed into groups (n=5), according to the resin cement (Maxcem Elite-(MC) or NX3 Nexus-(NX)) and degradation method (24h or 7 days in distilled water; 7 or 30 days incubated with biofilm and 30 days in sterile media). Treated surfaces of Vita Enamic blocks (5x6x7mm) were luted to treated or no treated dentin surfaces and light-cured. After 24h, beams were obtained (1x1x10mm) and stored accordingly. The flexural bond strength (FBS) was assessed by four-point bending test. Additional beams were obtained from new teeth (n=5), stored for 24h or 7 days in distilled water, and submitted to a microtensile bond strength (µTBS) assay. Failure modes were determined by scanning electron microscopy (100X). The flexure strength of the cements (n=10) was assessed by a four-point bending test. Data were analyzed by 1 and 2-ways ANOVA, and Tukey's test (α=0.05). Results: There was no significant difference between the degradation methods for the FBS groups. For the µTBS, the significant difference was as follows: NX 7days > NX 24h > MC 7days = MC 24h. Failure mode was mainly adhesive and mixed, but with an increase of cohesive within cement and pre-failures for the MC groups assessed by µTBS. NX had better performance than MC, regardless of the method. Conclusions: The biofilm had no effect on the materials BS and FBS test was a useful method to evaluate BS of materials with poor performance
Sujets)
Résistance à la traction , Microscopie électronique à balayage , Collage dentaire , Biofilms , Céments résineRésumé
Aim: To evaluate the influence of cobalt-chromium (Co-Cr) coping fabrication methods and ceramic application on the marginal and internal fit of metal-ceramic crowns. Methods: Co-Cr copings for metal-ceramic crowns were prepared by lost wax casting or CAD-CAM machining of sintered blocks. The fit was analyzed using the silicone replica technique at four assessment points: marginal gap (MG), axial wall (AW), axio-occlusal (AO) angle, and central occlusal (CO) wall. After the initial analysis, the copings were ceramic-veneered with the layering technique, and the fit was again determined. Data were statistically analyzed by paired and unpaired Student's-t test (α=0.05). Results: Marginal and internal fit before ceramic application according to the coping manufacturing method showed significant differences only at CO (p < 0.001), with milled copings (137.98±16.71 µm) showing higher gap values than cast copings (112.86±8.57 µm). For cast copings, there were significant differences at MG (before 109.13±8.79 µm; after 102.78±7.18 µm) and CO (before 112.86±8.57 µm; after 104.07±10.63 µm) when comparing the fit before and after ceramic firing. For milled copings, there was significant difference only at AO (before 116.39±9.64 µm; after 108.54±9.26 µm). Conclusion: This study demonstrated that the coping fabrication method influenced the internal fit. Ceramic firing maintained or improved the fit of the metal-ceramic crowns. The marginal discrepancy of all restorations, before and after ceramic firing, can be considered clinically acceptable
Sujets)
Céramiques , Alliages métal céramique , Adaptation marginale (odontologie) , CouronnesRésumé
Objetivo: Avaliar o efeito de um protetor de superfície na sorção e solubilidade de cimentos de ionômero de vidro. Materiais e Métodos: Quatro materiais foram selecionados: ionômero modificado por resina encapsulado (Riva Light Cure); modificado por resina pó/líquido (Vitremer); convencional encapsulado (Equia Forte) e convencional pó/líquido (Fuji IX). Foram confeccionados 20 espécimes de cada, sendo metade com proteção superficial do Equia Forte Coat. As amostras foram mantidas em estufa a 37°C em repouso por 5 dias. Em seguida, esses foram pesados em intervalos de 24 horas. A espessura e o diâmetro foram medidos com um paquímetro digital para o cálculo do volume. Novas pesagens foram realizadas para a obtenção da massa intermediária. Em seguida, as amostras foram mantidas em repouso por 5 dias a 37°C e realizada nova pesagem. Resultados: Os dados obtidos de sorção e solubilidade foram submetidos à análise de variância (ANOVA dois fatores, material e protetor de superfície) e teste Tukey ( =0,05). Para sorção, houve diferença significativa apenas para o fator material (p<0,05), Vitremer > Equia Forte > Riva Light Cure > Fuji IX. O ionômero Fuji IX apresentou os menores valores de sorção, diferindo significativamente dos demais materiais, independentemente do uso do protetor superficial. Não houve diferença significativa para o fator proteção de superfície (p>0,05). Para solubilidade não houve diferença significativa no fator material, protetor de superfície ou interação material*protetor. Conclusão: O uso do protetor superficial não influenciou nos valores de sorção e solubilidade dos ionômeros avaliados e o ionômero convencional Fuji IX apresentou menores taxas de sorção.
Objective: evaluate the effect of a surface coating agents on the sorption and glass ionomer cements solubility. Materials and Methods: Four materials were selected: Encapsulated resin-modified ionomer (Riva Light Cure); Powder/liquid Encapsulated resin-modified (Vitremer); Encapsulated conventional (Equia Forte) and powder/ liquid conventional (Fuji IX). Twenty samples of each were made, half with surface protection of Equia Forte Coat. The samples were kept in an oven for 5 days. These were then weighed at 24-hour intervals. The thickness and diameter were measured using a digital caliper to calculate their volume. New weightings were performed to obtain the intermediate mass. Then, the samples were kept at rest for 5 days and weighed again. Results: The sorption and solubility data obtained were subjected to analysis of variance (two-way ANOVA, material and surface coating agents) and Tukey test ( =0.05). For sorption, there was a significant difference only for the material factor (p<0.05), Vitremer > Equia Forte > Riva Light Cure > Fuji IX. The Fuji IX ionomer showed the lowest sorption values, differing significantly from the other materials, regardless of the use of surface coating agents. There was no significant difference for the surface protection factor (p>0.05). For solubility there was no significant difference for the material factor, surface coating agents or material*surface coating agent interaction. Conclusion: The use of surface coating agents did not influence the sorption and solubility values of the evaluated ionomers and the conventional Fuji IX ionomer showed lower sorption rates.
Sujets)
Solutions/composition chimique , Matériaux dentaires , Ciment ionomère au verre/composition chimique , Solubilité , Test de matériaux , Eau , AbsorptionRésumé
Objetivo: O objetivo foi avaliar a resistência de união de seis adesivos experimentais contendo sistemas fotoiniciadores binários ou ternários, associados a três diferentes concentrações de MDP (0-12% em peso) após 12 meses de armazenamento em água destilada. Material e Métodos: Adesivos experimentais foram preparados com: bis-GMA, UDMA, bis-EMA, TEGDMA, HEMA, BHT e etanol, contendo sistemas fotoiniciadores binários (CQ/amina) ou ternários (CQ/amina/DPIHFP 0,5% em peso). Foi adicionado a esta composição 0%, 6% ou 12% em peso de MDP. Os sistemas adesivos foram aplicados seguindo o protocolo com condicionamento ácido. Moldes cilíndricos transparentes foram colocados sobre a dentina hibridizada, preenchidos com resina composta e fotopolimerizados. Os corpos-de-prova foram armazenados em água destilada a 37oC por 24h ou 12 meses e submetidos ao ensaio de microcisalhamento (n=6). Os dados foram analisados por ANOVA de três fatores e teste de Tukey (α=5%). Resultados: Para o sistema binário, após 12 meses de armazenamento, todos os valores de resistência de união foram semelhantes. Em relação à degradação da resistência de adesão ao longo do tempo, as formulações de MDP de 6% e 12% mostraram resistência de união mais estável do que 0% de MDP. Para o sistema ternário, todas as formulações (0%, 6% e 12% em massa de MDP) mostraram resistência de união estável em função do tempo. Conclusão: Para o sistema binário, as concentrações de 6 e 12% em massa de MDP foram capazes de manter a resistência de união em função do tempo, enquanto que para o sistema ternário, a estabilidade de união foi obtida independentemente da concentração de MDP. Pode-se concluir que, para a formulação dos adesivos utilizados neste estudo, independente do sistema fotoiniciador, a concentração de 12% MDP apresentou valores de resistência de união mais estáveis após 12 meses de armazenamento em água (AU)
Objective: The aim was to evaluate the bond strength of six experimental adhesives containing binary or ternary photoinitiator systems, associated with three different MDP concentrations (0-12wt%) after 12 months of storage in distilled water. Material and Methods: Experimental adhesives were prepared with: bis-GMA, UDMA, bis-EMA, TEGDMA, HEMA, BHT, and ethanol, containing binary (CQ/amine) or ternary (CQ/amine/DPIHFP (diphenyliodonium hexafluorophosphate) 0.5wt%) photoinitiator systems. It was added to this composition 0wt%, 6wt%, or 12wt% of MDP. The adhesive systems were applied following the etch-and-rinse protocol. Transparent cylindrical molds were placed on the hybridized dentin, filled with composite resin and light-cured. The specimens were stored in distilled water at 37oC for 24h or 12 months and submitted to a microshear bond strength test (n=6). Data were analyzed by three-way ANOVA and Tukey's test (α=5%). Results: For the binary system, after 12 months of storage, all bond strength values were similar. Regarding bond strength degradation over time, 6wt% and 12wt% MDP formulations showed more stable bond strength than 0wt% MDP. For the ternary system, all formulations (0wt%, 6wt% and 12wt%) showed stable bond strength over time. Conclusion: For the binary photoinitiator system, the 6wt% and 12wt% MDP concentrations were able to keep bond strength stable over time, while for the ternary system, bond strength stability was achieved regardless the MDP concentration. (AU)
Sujets)
Ciments dentaires , Photo-initiateurs dentairesRésumé
Resumo Diferentes práticas agrícolas estão associadas a diferentes riscos para a saúde de camponeses. Objetivou-se analisar a associação entre ideação suicida e exposição a agrotóxicos, comparando camponeses vivendo sob exposição ambiental a agrotóxicos em relação a camponeses envolvidos com práticas agroecológicas, sem o uso de agrotóxicos, no semiárido norte mineiro. As famílias avaliadas foram amostradas, por conveniência, a partir da prática agrícola a qual estavam vinculadas, e os dados coletados por meio de entrevistas com instrumento previamente validado. Foram realizadas análises bivariadas seguidas de regressão logística. Foram entrevistados 547 camponeses, de ambos os sexos, sendo 311 sob exposição a agrotóxicos. Os camponeses expostos a agrotóxicos, em relação a camponeses envolvidos com práticas agroecológicas, tiveram maiores chances para ideação suicida (OR=2,30; IC95% 1,16-4,56), consumo problemático de álcool (OR=2,30; IC95% 1,18-4,48) e episódios prévios de intoxicação aguda por agrotóxicos (OR=8,58; IC95% 2,98-24,72).Conclui-se que as práticas agrícolas que implicam em exposição crônica a agrotóxicos se associam a maiores chances de ideação suicida, independentemente de episódios prévios de intoxicação aguda por agrotóxicos ou do uso problemático do álcool.
Abstract Health risks faced by peasant farmers may vary depending on the type of agriculture they practice. This study examined the association between suicide ideation and exposure to pesticides by comparing two groups of peasant farmers of both sexes living in the semi-arid region of the north of Minas Gerais, Brazil: exposed to pesticides and adopting agroecological practices without the use of pesticides. Group participants were selected using convenience sampling and data was collected using a previously validated questionnaire administered through face-to-face interviews. Bivariate analysis was performed, followed by logistic regression. A total of 547 peasant farmers were interviewed (311 in the group exposed to pesticides and 236 in the group adopting agroecological practices). Respondents from the group exposed to pesticides were more likely to report suicidal ideation (OR=2.30; 95%CI 1.16-4.56), harmful alcohol consumption (OR=2.30; 95%CI 1.18-4.48), and lifetime acute pesticide poisoning (OR=8.58; 95%CI 2.98-24.72). The findings suggest that agricultural practices that lead to chronic pesticide exposure are associated with a greater likelihood of suicide ideation, regardless of previous episodes of acute pesticide poisoning or harmful alcohol consumption.
Sujets)
Humains , Mâle , Femelle , Pesticides , Exposition professionnelle , Brésil/épidémiologie , Idéation suicidaire , AgriculteursRésumé
Objetivo: O objetivo do presente estudo foi avaliar clinicamente a descoloração da coroa dentária após obturação do canal radicular com diferentes cimentos endodônticos. Métodos: Trinta e dois dentes foram tratados endodonticamente e obturados com AH Plus (AHP), Endofill (END), MTA Fillapex (MTA) ou Sealer 26 (SEA), divididos em oito pacientes por grupo. O registro das cores foi realizado com um espectrofotômetro antes da intervenção (T0 ), aos 30 (T1 ) e aos 90 dias após a intervenção (T2 ). As avaliações foram feitas no centro da coroa dentária e a variação de cor (ΔE) foi calculada por meio da Commission International de l'Eclai- rage (CIE) L*a*b. Um operador, especialista em Endodontia, realizou os procedimentos clínicos. Os dados foram submetidos a medidas repetidas ANOVA e teste de Tukey (Δ=5%). Resultados: Não houve diferença estatisticamente significativa na variação de cores entre os cimentos (AHP ΔE=4,11; END ΔE = 6,34; SEA ΔE = 8,77 e MTA ΔE = 12,15), p>0,05. Porém, houve diferença entre os períodos analisados (T1ΔE= 5,65; T2 ΔE = 10,02). Conclusões: Dentro das limitações deste estudo, todos os cimentos endodônticos causaram alterações cromáticas clinicamente perceptíveis na coroa dentária. No entanto, o AH Plus promoveu menos alterações cromáticas na coroa dentária (AU).
Introduction: The aim of this study was to evaluate the crown discoloration after root canal filling with different endodontic cements clinically. Methods: Thirty-two teeth were endodontically treated and filled with AH Plus (AHP), Endofill (END), MTA Fillapex (MTA), or Sealer 26 (SEA), divided into eight patients per group. Color recording was performed with a spectrophotometer before the intervention (T0 ) and at 30 (T1 ) and 90 days post-intervention (T2 ). The evaluations were done in the center of the dental crown and color variation (ΔE) was calculated by means of the Commission International de IEclairage (CIE) L*a*b. The data were subjected to repeated measures ANOVA and Tukeys test (alpha=5%). Results: There was no statistically significant difference in color variation between the cements (AHP ΔE=4.11; END ΔE=6.34; SEA ΔE=8.77, and MTA ΔE=12.15), p>0.05. However, there was a difference between the periods tested (T1 ΔE=5.65; T2 ΔE=10.02). Conclusions: All tested endodontic cements altered the color of dental crowns (AU).
Sujets)
Humains , Obturation de canal radiculaire , Dyschromie dentaire , Couronne dentaire , Spectrophotométrie , Analyse de varianceRésumé
Introduction: This study evaluated the influence of sonic vibration and thermocycling on the bond strength of fiberglass posts using conventional dual-cured and self-adhesive resin cements. Material and Methods: Ninety-six single-rooted endodontically treated teeth were divided randomly into eight groups according to the cement used (dual-cured or self-adhesive resin cement), use of sonic vibration during post accommodation, and aging conditions (24h in distilled water or 5,000 thermal cycles). The fiberglass posts (White Post DC1, FGM) were cleaned with alcohol, treated with silane and cemented with dual-cured (Allcem Core, FGM) or with self-adhesive resin cement (seT, SDI). For groups in which sonic vibration was used, the posts were accommodated, and sonic vibration was applied for 10 s using a special tip placed on top of the post (Sonic Smart Device, FGM). Pull-out tests were performed after storage in distilled water for 24h at 37°C or after thermocycling (5000 cycles, at 5°C and 55°C). The results were evaluated using three-way ANOVA and Tukey's test (α=0.05). Results: Significant differences were not observed between the bond strengths of dual-cured (87.93±41.81 N) and self-adhesive cement (82.53±41.43 N). Bond strength for the sonic vibration groups (100.36±42.35 N) was significantly higher than for groups without sonic vibration (70.13±34.90 N). There were significant differences between specimens subjected to thermocycling (98.33±39.42 N) and those stored for 24h in distilled water (72.16±39.67 N). Conclusion: It can be concluded that both sonic vibration and thermocycling significantly improved bond strength of fiberglass posts with the two evaluated resin cements.
Introducción: Este estudio evaluó la influencia de la vibración sónica y el termociclado en la fuerza de unión de los postes de fibra de vidrio utilizando cementos de resina autoadhesivos y de curado dual convencionales Material y Métodos: Se dividieron aleatoriamente noventa y seis dientes tratados endodónticamente de raíz única en ocho grupos según el cemento utilizado (cemento de resina de curado dual o autoadhesivo), el uso de vibración sónica durante la acomodación posterior y las condiciones de envejecimiento (24 horas agua destilada o 5.000 ciclos térmicos). Los postes de fibra de vidrio (White Post DC1, FGM) se limpiaron con alcohol, se trataron con silano y se cementaron con cemento de curado dual (Allcem Core, FGM) o con cemento de resina autoadhesivo (seT, SDI). Para los grupos en los que se utilizó vibración sónica, se acomodaron los postes y se aplicó la vibración sónica durante 10 s utilizando una punta especial colocada en la parte superior del poste (Sonic Smart Device, FGM). Las pruebas de extracción se realizaron después del almacenamiento en agua destilada durante 24 horas a 37ºC o después del termociclado (5000 ciclos, a 5ºC y 55ºC). Los resultados se evaluaron mediante ANOVA de tres vías y la prueba de Tukey (α = 0.05). Resultados: No se observaron diferencias significativas entre las resistencias de adhesión del cemento de curado dual (87,93 ± 41,81 N) y el cemento autoadhesivo (82,53 ± 41,43 N). La fuerza de unión para los grupos de vibración sónica (100,36 ± 42,35 N) fue significativamente mayor que para los grupos sin vibración sónica (70,13 ± 34,90 N). Hubo diferencias significativas entre los especímenes sometidos a termociclado (98,33 ± 39,42 N) y los almacenados durante 24 h en agua destilada (72,16 ± 39,67 N). Conclusión: Se puede concluir que tanto la vibración sónica como el termociclado mejoraron significativamente la fuerza de unión de los postes de fibra de vidrio con los dos cementos de resina evaluados.
Sujets)
Humains , Vibration , Restauration coronoradiculaire/instrumentation , Céments résine/composition chimique , Résistance à la flexion , Verre , Sonication/méthodes , Racine dentaire , Collage dentaire , Agents de collage dentinaire , Dentine/composition chimique , Ondes ultrasonoresRésumé
Abstract The objective of this work was to evaluate the effects of in vitro and in situ biodegradation on the surface characteristics of two resin cements and a hybrid ceramic system. One hundred and eighty specimens (4X1.5mm) of each material (Maxcem Elite, NX3 Nexus and Vita Enamic) were made and randomly distributed in twelve groups (n=15) according to the material and biodegradation method. The specimens were then submitted to the following challenges: storage in distilled water 37 ºC for 24 h or 7 days, storage for 7 days, at 37 ºC, in stimulated saliva or in situ. The in situ stage corresponded to the preparation of 15 intraoral palatal devices, used for 7 days. Each device presented 3 niches, where a sample of each materials was accommodated. Specimens from both saliva and in situ groups suffered a cariogenic challenge, corresponding to the application of a solution of 20% of sucrose, 10 times throughout each day. After each biodegradation method, the surface roughness (Ra), Vickers hardness (VHN) and scanning electron microscopy (SEM) analyzes were performed. The data collected were evaluated by Levene test, two-way ANOVA and Tukey`s test (α=5%). The in situ challenge promoted the greater biodegradation, regardless of the material. Regarding the materials, the Vita Enamic VHN was negatively affected by all biodegradation methods and the Nexus NX3 presented better performance than the self-adhesive cement tested. Therefore, within the conditions of this work, it was concluded that in situ biodegradation can affect negatively the surface characteristics of indirect restorative materials.
Resumo O objetivo deste trabalho foi avaliar os efeitos da biodegradação in vitro e in situ nas características superficiais de dois cimentos resinosos e de um sistema cerâmico híbrido. Cento e oitenta espécimes (4X1,5mm) de cada material (Maxcem Elite, NX3 Nexus e Vita Enamic) foram distribuídos aleatoriamente em doze grupos (n=15) de acordo com o material e o método de biodegradação. Os espécimes foram então submetidos aos seguintes desafios: armazenamento em água destilada 37ºC por 24 horas ou 7 dias, armazenamento por 7 dias, a 37ºC, em saliva estimulada ou in situ. O estágio in situ correspondeu à preparação de 15 dispositivos intra-orais palatinos, utilizados por 7 dias. Cada dispositivo apresentou 3 nichos, onde uma amostra de cada material foi acomodada. As amostras dos grupos saliva e in situ sofreram um desafio cariogênico, correspondendo à aplicação de uma solução de 20% de sacarose, 10 vezes ao longo de cada dia. Após cada método de biodegradação, foram realizadas as análises de rugosidade superficial (Ra), dureza Vickers (VHN) e microscopia eletrônica de varredura (MEV). Os dados coletados foram analisados por meio do teste de Levene, ANOVA two-way e teste de Tukey (α=5%). O desafio in situ promoveu maior degradação, independentemente do material. Em relação aos materiais, a VHN do Vita Enamic foi afetada negativamente por todos os métodos de degradação e o Nexus NX3 apresentou melhor desempenho que o cimento autoadesivo testado. Portanto, dentro das condições deste trabalho, concluiu-se que a biodegradação in situ pode afetar negativamente as características superficiais de materiais restauradores indiretos.
Sujets)
Céments résine , Matériaux dentaires , Propriétés de surface , Test de matériaux , Céramiques , DuretéRésumé
Abstract The aim of this study was to evaluate the effect of acute sepsis in the periodontal ligament, alveolar and furcation bone in absence of periodontitis induction through histological and immunohistochemical analyses. A septic rat model was established by cecal ligation and puncture (CLP). Twelve rats were randomly divided into CLP (n=6) and Sham (n=6) groups. The animals were euthanized at 24 h and hemimandibles were submitted to histomorfometric (bone matrix, collagenous fibers, fibroblasts, osteocytes, inflammatory cells, and blood vessels) and immunohistochemical (BMP-2/4, RANKL and osteocalcin) evaluation in alveolar bone, furcation bone and periodontal ligament. Our results demonstrated that histomorphometric parameters were similar in alveolar bone, furcation bone and periodontal ligament of Sham and CLP rats. Regarding to immunohistochemical analyses, the number of BMP-2/4 and RANKL immunolabeled cells was also similar in both groups. Furthermore, it was detected a reduction in the osteocalcin immunolabeled cells in periodontal ligaments of CLP compared to Sham rats (p=0.0014). In conclusion, the acute sepsis induction resulted in reduced number of osteocalcin labelled cells in periodontal ligament region. Moreover, no significant histological differences were observed in the periodontium of rats under acute sepsis. Considering the role of osteocalcin in bone remodeling, the study contributes to revealing the importance of careful periodontal evaluation in the presence of sepsis.
Resumo O objetivo deste estudo foi avaliar o efeito da sepse aguda no ligamento periodontal, osso alveolar e osso da furca por meio de análise histológica e imunohistoquímica. O modelo de sepse em ratos foi estabelecido pelo procedimento de ligação e perfuração do ceco (CLP). Doze ratos foram divididos de forma randomizada em ratos sépticos (n=6) e controle - grupo Sham (n=6). Os animais foram eutanasiados após 24 horas e suas hemimandíbulas foram submetidas aos procedimentos histotécnicos para análise histomorfométricos (matriz óssea, fibras colágenas, fibroblastos, osteócitos, células inflamatórias e vasos sanguíneos) e imunohistoquímicos (BMP-2/4, RANKL e osteocalcina) no osso alveolar, osso de furca e ligamento periodontal. Nossos resultados demonstraram que os parâmetros histomorfométricos foram similares no osso alveolar, osso de furca e ligamento periodontal dos animais do grupo sepse e do grupo Sham. Em relação à análise por imunohistoquímica, o número de células imunomarcadas para BMP-2/4 e RANKL também foi similar em ambos os grupos. Entretanto, houve redução (p=0.0014) no número de células imunomarcadas para osteocalcina no ligamento periodontal de ratos sépticos em relação ao grupo Sham. Como conclusão, o estabelecimento de sepse aguda resultou em um número reduzido de células imunomarcadas para osteocalcina na região do ligamento periodontal (p=0,0014). Além disso, não foram observadas diferenças histológicas significativas no periodonto de ratos na presença de sepse aguda. Considerando o papel da osteocalcina na remodelação óssea, este estudo contribui para revelar a importância da avaliação periodontal cuidadosa na presença de sepse.
Sujets)
Animaux , Rats , Desmodonte , Ostéocalcine , Sepsie , Modèles animaux de maladie humaine , LigatureRésumé
Abstract The aim of this research was to evaluate the influence of MDP (10-methacryloyloxydecyl dihydrogen phosphate) concentration and application mode of experimental adhesives on microshear bond strength (μSBS) to dentin after storage in distilled water at 37°C for 24h and 6 months. Five experimental adhesives were prepared with: CQ, DABE, BHT, ethanol, HEMA, TEGDMA, Bis-EMA, UDMA, and Bis-GMA. Concentrations of 0 wt%, 3 wt%, 9 wt%, 12 wt% or 15 wt% of MDP were added to their composition. The adhesives were applied to flat dentin surfaces in etch-and-rinse or self-etching modes. Cylindrical molds filled with light-cured composite resin were placed above the dentin. The specimens were stored in distilled water at 37oC for 24h or 6 months and submitted to μSBS testing. The adhesives were also submitted to pH analysis. The data were analyzed by one-way ANOVA, three-way ANOVA and Tukey's test (α = 5%). All the adhesives used in the etch-and-rinse mode showed significantly higher bond strength than the adhesives applied in the self-etching approach. The 9 wt% adhesive showed the highest bond strength values, and 3 wt% was most stable after storage. A strong negative correlation between MDP concentration and pH was observed. It was concluded that the formulations with low concentrations of MDP (up to 9 wt%) showed better results for bond strength and bond strength degradation over time.
Sujets)
Collage dentaire , Résistance à la traction , Test de matériaux , Adhésivité , Agents de collage dentinaire , Résines composites , Céments résine , Ciments dentaires , DentineRésumé
Context: The aims of this study were (i) to evaluate the color stability of two orthodontic adhesives and (ii) to evaluate the color stability of enamel and ceramic brackets bonded with orthodontic adhesives after exposure to different staining agents. Materials and Methods: Disks were prepared with two orthodontic adhesives (Transbond and Enlight). Color stability evaluation was performed with a spectrophotometer using CIELab parameters. The specimens were divided into four groups and immersed in the following staining agents (n = 5): distilled water (control), coffee, red wine, and cola soft drink, for 1 h/day for 120 days. Twenty molar crowns were also used. The baseline color of enamel was obtained and ceramic brackets were bonded with the orthodontic adhesives. The enamel specimens were divided into four groups and immersed in the same staining agents. After 120 days, another color reading with the brackets in position was taken. The brackets were then removed and the enamel color was again evaluated. Color difference (ΔE) in different time periods was determined and the data were analyzed by ANOVA and Tukey's test (α = 5%). Results: Transbond showed lower ΔE than Enlight. Water, cola, and coffee had the lowest ΔE values. Immersion in wine showed the highest ΔE values. For time, the lower ΔE values were found for 24 h and 7 days. Storage times of 60, 90, and 120 days showed the highest ΔE values. ΔE for enamel showed significant differences only for time. Conclusion: Adhesive, staining agents, and storage time influenced the color stability of orthodontic adhesives.
Résumé
Abstract The objective was to evaluate the color stability of thin ceramic veneers as a function of the curing mode (with and without pre-cure) of different adhesive systems applied to the internal surface of ceramics. Five adhesive systems (Scotchbond Multi-Purpose, Single Bond Universal, Gluma 2 Bond, Ambar, and Ambar APS) and photo-cured resin cement (Allcem Veneer) were used for cementing 0.6 mm-thick feldspathic veneers (Mark II) on composite resin substrates (Charisma Diamond). The groups, according to adhesive system, were divided into two subgroups (n=10): i) adhesive and resin cement were polymerized separately (pre-cure of the adhesive), ii) adhesive and resin cement were polymerized simultaneously. The CIELab color parameters were determined with a spectrophotometer at 24h (baseline), 7 days, 30 days and 12 months. Data were analyzed by two-way ANOVA and Tukey's test (α=0.05). The results indicated statistically significant differences for adhesive systems and time. The mode of curing of the adhesive system was not statistically significant: pre-cured adhesives (2.6±1.3) and not pre-cured adhesives (2.8±1.4). For the adhesives, ΔE values varied in the following order: Ambar-APS (1.6±0.5) < Scotchbond Multi-Purpose (2.6±1.2) = Gluma 2 Bond (2.7±1.2) = Ambar (2.9±1.2) < Single Bond Universal (3.5±1.5). For time, ΔE values were: 7 days (1.7±0.7), 30 days (3.5±1.2) and 12 months (2.9±1.3). It can be concluded that the different adhesive systems used for cementing thin ceramic veneers influenced the final color of the indirect restorations. The adhesives curing mode did not present a significant effect in the color stability of thin ceramic veneers.
Resumo O objetivo deste estudo foi avaliar a estabilidade de cor de laminados cerâmicos de espessura fina em função do momento de ativação de diferentes sistemas adesivos na superfície interna das cerâmicas. Foram utilizados 5 sistemas adesivos (Scotchbond Multiuso, Single Bond Universal, Gluma 2 Bond, Ambar and Ambar APS) e o cimento resinoso fotoativado (Allcem Veneer) para cimentação de lâminas de cerâmica feldspática (Mark II) com 0,6 mm de espessura, sobre substratos de resina composta (Charisma Diamond). Os grupos, de acordo com o sistema adesivo utilizado, foram divididos em dois subgrupos (n=10): i) adesivo e cimento resinoso foram polimerizados separadamente (polimerização isolada do adesivo), ii) adesivo e cimento resinoso foram polimerizados ao mesmo tempo (polimerização simultânea). Os parâmetros de cor do sistema CIELab foram determinados com um espectrofotômetro nos tempos de 24 h (baseline), 7 dias, 30 dias e 12 meses. Os dados foram analisados por ANOVA a dois fatores e teste de Tukey (α=0,05). Os resultados indicaram diferenças estatísticas significantes para os sistemas adesivos e tempo. O momento da fotoativação do sistema adesivo não foi estatisticamente significante: polimerização prévia (2,6±1,3) e polimerização simultânea (2,8±1,4). Para o sistema adesivo, os valores médios de ΔE variaram na seguinte ordem: Ambar APS (1,6±0,5)<Scotchbond Multi-Purpose (2,6±1,2)=Gluma 2 Bond (2,7±1,2)=Ambar (2,9±1,2)<Single Bond Universal (3,5±1,5). Para o fator tempo o ΔE foi: 7 dias (1,7±0,7), 30 dias (3,5±1,2) e 12 meses (2,9±1,3). Pode-se concluir que os diferentes sistemas adesivos utilizados na cimentação de laminados cerâmicos de espessura fina influenciaram na cor final das restaurações. O momento da fotoativação, isolada ou simultânea ao cimento resinoso, não apresentou efeito significativo na estabilidade de cor dos laminados cerâmicos de espessura fina.
Sujets)
Ciments dentaires , Facettes dentaires , Test de matériaux , Céramiques , Couleur , Céments résine , Photopolymérisation d'adhésifs dentairesRésumé
Aim: To evaluate the physicomechanical properties of different hybrid composites (Charisma Diamond - CD, Aura - AU, NT Premium - NT, Opallis - OP, Filtek Z250 Z250) after 6 months of aging in distilled water. Methods: Discs were fabricated and color measurements were performed after 24 hours and at 7, 30, and 180 days. Flexural strength was determined using the three-point bending test. For the microhardness test, the specimens were flattened to obtain polished and flat surfaces and indentations. The results for ∆E and microhardness were analyzed by two-way repeated-measures ANOVA and Tukey's HSD test. The flexural strength results were analyzed by two-way ANOVA and Tukey's test (α=0.05). Results: The ∆E values for composite resins varied in the following order: CD (3.54)a < Z250 (4.70)ab < AU (4.95)ab < OP (5.20)ab < NT (6.23)b. ∆E values were lower for 24 h (3.84)a < 7 days (4.43)ab < 30 days (4.93)b. The highest values were observed after 180 days (ΔE = 6.54)c. The flexural strength of composite resins varied in the following order: CD (89.17 MPa)a < Z250 (73.06 MPa)b < OP (60.30 MPa)c < NT (51.28 MPa)c < AU (23.77 MPa)d. Flexural strength values were significantly higher for 24 h (68.62 MPa)a < 180 days (51.40 MPa)b. The microhardness of composite resins varied in the following order: Z250 (112.05)a < CD (102.15)ab < OP (92.04)bc < NT (87.77)d < AU (87.68)d. Microhardness was significantly higher for 180 days (113.44)a < 24 h (78.21)b. Conclusion: The microhybrid (Z250) and one of the nanohybrid composites (CD) performed better. The color stability and flexural strength of all tested composites decreased with storage time
Sujets)
Couleur , Phénomènes mécaniques , DuretéRésumé
Aim: The aim of this study was to evaluate knowledge and attitudes regarding potentially malignant oral lesions and oral cancer among undergraduate dental students with or without training in the oral medicine. Methods: A cross-sectional study was undertaken to assess all undergraduate dental student (1st to 5th year) in two private universities in the state of Paraná, Brazil. A structured questionnaire about knowledge regarding potentially malignant oral lesions, continuing education, and different approaches to diagnosis was administered to dental students with or without training in the oral medicine discipline between May and July 2015. Descriptive statistics were obtained, and the data were analyzed using a chi-square test to compare knowledge in dental students. Results: A total of 662 undergraduate dental students were invited to participate, and the response rate was 97.6% (n = 646). Of the responders, 472 were female (73.1%), 168 were male (26.0%), and 6 did not declare what sex they were (0.9%). Undergraduate dental students who had previously studied oral medicine tended to report that they always perform complete intraoral examination (76.3%) and identified alcohol (87%) and tobacco consumption (97%) and sun exposure (80%) as major risk factors for developing oral cancer. While students who had not yet studied oral medicine poorly identified these factors. Students who had previously studied the discipline did not identify cheilitis actinica (26%) and erythroplakia (32%) as potentially malignant lesions. Only, 32.6% of dental students participate in continuing education during the past year. Conclusions: Dental students trained in the oral medicine discipline exhibited satisfactory knowledge necessary for the prevention and early identification of potentially malignant oral lesions and oral cancer. Continuing education during undergraduate and after academic training is very important
Sujets)
Humains , Mâle , Femelle , Adulte , Étudiant dentisterie , Tumeurs de la bouche , Stomatologie , Savoir , Formation dentaire continueRésumé
Aim: This study evaluated the surface topography and bacterial adhesion of a hybrid ceramic and a nano ceramic resin composite after different surface finishes. Methods: Hybrid ceramic (Vita Enamic, VITA - EN) and nano ceramic resin composite (Lava Ultimate, 3M/ESPE - LV) blocks of 12 x 14 x 18 mm were cut into 1 mm slices. Each slice was divided into four specimens (6 x 7 mm) that were randomly allocated into 4 groups (n=8) according to the surface finishing: CTL - without surface finish (control); DB - wear with a diamond bur; VT - polishing system for hybrid ceramic (VITA); and DD - polishing system for ceramics (Dedeco). The specimens were analyzed regarding surface roughness parameters (Ra, Rz, Rq), sterilized and subjected to bacterial adhesion. Representative specimens from each group were observed by SEM and Confocal Laser Scanning Microscopy. Data were submitted to two-way ANOVA and Tukey's test (α=0.05). Results: EN had lower surface roughness and bacterial adhesion than LV (p<0.05), regardless of the surface finish. The highest values for all roughness parameters was observed in LVDB group, differing from the other groups, which were not significantly different. Smaller bacterial adhesion values (CFU/mL) were observed for ENDD and ENVT, which differed significantly from the other groups, except ENCTL. For LV groups there was no significant difference between the different surface finishes (p>0.05). The type of material and surface finish system significantly interfered with surface roughness parameters and bacterial adhesion. The hybrid ceramic performed better after polishing than the nano-ceramic resin. Conclusion: An adequate finishing/polishing technique should always be performed after any kind of adjustment to indirect restorations made with these materials tested
Sujets)
Adhérence bactérienne , Céramiques , Conception assistée par ordinateur , Résines composites , Polissage dentaireRésumé
Aim: To evaluate crown and root discoloration promoted by different endodontic sealers after root canal filling. Methods: Eighty bovine incisors were prepared and filled with: Endofill, Sealer 26, AH Plus, and MTA Fillapex. Color was recorded using a spectrophotometer before endodontic treatment (T0) and at 24 hours (T1), seven days (T2), 30 days (T3), and 90 days (T4) after treatment. Analyses were performed on the middle and cervical regions of the crown, and on the cervical third of the root, immediately below the cementoenamel junction. The color alterations (ΔE) were calculated using Commission International de I'Eclairage (CIE) L*a*b parameters, and data were analyzed by analysis of variance (ANOVA) and Tukey's test (p<0.05). Results: All sealers induced color alterations. Sealer 26 resulted in the smallest changes in color (ïE = 5.32). The other materials did not present statistical differences (AH Plus ïE = 6.98; MTA Fillapex ïE = 6.88; Endofill ïE = 6.41). Of the three regions analyzed, the largest discoloration was observed at the cervical third of the root (ïE=10.67). In terms of time, the largest ΔE values (ïE=7.72) were observed at T4. Color changes at T1 (ïE=5.88), T2 (ïE=6.10), and T3 (ïE=5.89) were statistically similar. Conclusions: All endodontic sealers promoted discoloration on the tooth crown and root
Sujets)
Animaux , Bovins , Produits d'obturation des canaux radiculaires , Dyschromie dentaire , Couronne dentaire , EndodontieRésumé
Aim: This study aims to evaluate the effect of different surface treatments on the bond strength of glass fiber posts. Methods: Ninety unirradicular premolars had their crowns removed and were endodontically treated. After 24h, post spaces were prepared and the roots (n=15) were divided into six groups according to the post surface treatment: NT no treatment, UA universal adhesive (Single Bond Universal), SUA silane (Prosil), followed by universal adhesive, H H2O2 (Whitness HP Maxx, 35%, gel, 1 min), HUA H2O2, followed by universal adhesive, and HSUA H2O2, followed by silane and universal adhesive. The posts were cemented with dual-cured resin cement (RelyX Ultimate). Bond strength was evaluated with pull-out test (0.5 mm/mim) after 24h-storage in distilled water at 37oC. Data were submitted to ANOVA and Tukey's test (α=5%). Results: HSUA group showed the highest bond strength value (236.5 N) followed by HUA (206.5 N), NT (194 N) and SUA (184 N) groups. UA group showed the lowest bond strength value (60 N). Conclusion: The use of H2O2, the silane application or the combination of these two treatments significantly increased bond strength values in groups in which the universal adhesive was used. A simplified procedure, such as cleaning with alcohol, can be recommended as surface treatment for the cementation of glass fiber posts (AU)
Sujets)
Humains , Agents de collage dentinaire , Endodontie , Peroxyde d'hydrogèneRésumé
Aims: The objective of this study was to evaluate the mechanical properties of two bis-acryl interim resin materials, such as color stability, flexural strength and shear bond strength to flowable composite resin, simulating clinical situations when this material has to be used for repair as add-on. Two shades of two bis-acryl interim resin materials [Structur 2 SC (shades Bleach and A2); Protemp 4 (shades A1 and A2)] were evaluated. Discs (5 x 1 mm) were fabricated and baseline color was determined after 1 h. Ten specimens were immersed at 37oC in solutions of distilled water (control) and cola-based soft drink (Coca-Cola). Color measurements were performed with a spectrophotometer using CIELab parameters. Color readings were again measured after 2 hours, 4 hours, 24 hours and 7 days. Flexural strength was determined using the three-point bending test (10 x 1 x 2 mm) on a universal testing machine (0.5 mm/min) (n = 10). Discs of bis-acryl resin were embedded in acrylic resin, planned and distributed in 2 groups: G1 - Filtek Z350 Flow/Protemp4 and G2 - Grandio SO Flow/Structure 3 (n = 15). Cylinders (3.5 x 2 mm) were made with the flowable composite resins and polymerized for 20 s. The specimens were stored in distilled water at 37oC for 24 h and subjected to shear bond strength test. Data were analyzed using one-way ANOVA and Tukey's test (α = 0.05). ΔE values were higher for Structur Bleach (3.08)a compared with Protemp 4 (shade A1, 2.22)b (shade A2, 2.25)b. There were no significant differences between Structur Bleach and Structur A2 (2.62)ab. Coca-Cola presented higher ΔE values (3.08)a than (2.00)b. Regarding time, ΔE values increased from 1.84a after 2 h to 2.31b after 4 h. The higher values were observed after 24 h and 7 days (2.93c and 3.09d, respectively). No significant differences were observed for the flexural strength of Structur (22.05 MPa)a and Protemp 4 (19.01 MPa)a. The repairs executed with Structur/Grandio flow (9.21 MPa)a were similar to those performed with Protemp 4/Z350XT flow (10.71 MPa)a. It can be concluded that the two bis-acyl resins evaluated showed similar physical and mechanical properties (AU)
Sujets)
Couleur , Résines composites , Résistance au cisaillementRésumé
Abstract Marginal and internal adaptation is critical for the success of indirect restorations. New imaging systems make it possible to evaluate these parameters with precision and non-destructively. This study evaluated the marginal and internal adaptation of zirconia copings fabricated with two different systems using both silicone replica and microcomputed tomography (micro-CT) assessment methods. A metal master model, representing a preparation for an all-ceramic full crown, was digitally scanned and polycrystalline zirconia copings were fabricated with either Ceramill Zi (Amann-Girrbach) or inCoris Zi (Dentslpy-Sirona), n=10. For each coping, marginal and internal gaps were evaluated by silicone replica and micro-CT assessment methods. Four assessment points of each replica cross-section and micro-CT image were evaluated using imaging software: marginal gap (MG), axial wall (AW), axio-occlusal angle (AO) and mid-occlusal wall (MO). Data were statistically analyzed by factorial ANOVA and Tukey test (a=0.05). There was no statistically significant difference between the methods for MG and AW. For AO, there were significant differences between methods for Amann copings, while for Dentsply-Sirona copings similar values were observed. For MO, both methods presented statistically significant differences. A positive correlation was observed determined by the two assessment methods for MG values. In conclusion, the assessment method influenced the evaluation of marginal and internal adaptation of zirconia copings. Micro-CT showed lower marginal and internal gap values when compared to the silicone replica technique, although the difference was not always statistically significant. Marginal gap and axial wall assessment points showed the lower gap values, regardless of ceramic system and assessment method used.
Resumo A adaptação marginal e interna é fundamental para o sucesso das restaurações indiretas e novos sistemas de imagem permitem avaliar esses parâmetros de maneira não-destrutiva e com precisão. Este estudo avaliou a adaptação marginal e interna de copings de zircônia fabricados com dois sistemas diferentes, utilizando as técnicas da réplica em silicone e micro-CT. Um modelo-mestre de metal, representando um preparo para uma coroa totalmente cerâmica foi digitalizado e copings de zirconia policristalina (Ceramill Zi, Amann Girrbach e inCoris Zi, Dentslpy Sirona, n=10) foram fabricados. Para cada coping, a adaptação marginal e interna foi avaliada pelas técnicas da réplica em silicone e micro-CT. Foram avaliados quatro pontos de cada seção transversal e imagem de micro-CT: adaptação marginal (MG), parede axial (AW), ângulo axial-oclusal (AO) e parede centro-oclusal (MO) utilizando um software de imagem. Os dados foram analisados estatisticamente por ANOVA e teste de Tukey (a=0,05). Não houve diferença estatisticamente significativa entre as duas técnicas para MG e AW. Para AO, houve diferenças significativas entre as técnicas para copings da Amann, enquanto que para copings da Dentsply Sirona foram observados valores semelhantes. Para o MO, ambas as técnicas apresentaram diferenças estatisticamente significativas. Observou-se uma correlação positiva entre os valores de adaptação determinados pelas duas técnicas. O método de avaliação influenciou a avaliação da adaptação marginal e interna de copings de zircônia. Pode-se concluir que a micro-CT mostrou menores valores de adaptação marginal e interna quando comparado com a técnica de réplica em silicone. Os pontos de avaliação da margem e da parede axial mostraram os menores valores de adaptação, independente do sistema cerâmico e da técnica de avaliação utilizados.
Sujets)
Couronnes , Conception de prothèse dentaire , Zirconium , Céramiques , Conception assistée par ordinateur , Microtomographie aux rayons XRésumé
Abstract Sonic vibrations may improve the bond strength and durability of fiberglass posts by improving adhesive penetration into dentin as well as the cement flow. The objective of this study was to evaluate the effect of sonic vibrations on the bond strength between fiberglass posts and root dentin using the pull-out test. Bovine roots were endodontically treated and divided randomly into four groups (n=12): Group C - conventional cementation (control); Group SA - sonic vibration (Smart Sonic Device, FGM) of the adhesive system and conventional post accommodation; SP group - conventional adhesive application and sonic vibration of the post during accommodation; and SASP - sonic vibration of the system adhesive and the post during accommodation. The posts were cleaned, treated with a silane and adhesive system (Ambar, FGM), and cemented with a dual-cured resin cement (Allcem Core, FGM). After 24 h, the specimens were subjected to mechanical tests and failure analyses. Representative specimens were analyzed by a scanning electron microscope to observe the cementation line. The results were analyzed using ANOVA and Tukey's test (a=5%). The bond strengths were as follows: SASP (90.9±27.1 N), C (121.4±60.6 N), SA (127.6±31.8 N) and SP (156.4±41.3 N). The use of sonic vibrations during the application of adhesive or post cementation separately did not affect the bond strength but had a negative effect when used for both procedures.
Resumo Vibrações sônicas podem melhorar a resistência e a durabilidade da união de pinos de fibra de vidro, melhorando a penetração do sistema adesivo à dentina, bem como o escoamento do cimento. O objetivo deste estudo foi avaliar o efeito da vibração sônica na resistência de união de pinos de fibra de vidro à dentina radicular, através de ensaio pull out. Raízes bovinas tratadas endodonticamente foram preparadas e divididas aleatoriamente em quatro grupos (n=12): Grupo C - cimentação convencional, (controle); Group SA - vibração sônica (Smart Sonic Device(r), FGM) do sistema adesivo e assentamento convencional do pino; grupo SP - aplicação convencional do sistema adesivo e vibração sônica no assentamento do pino; e SASP - vibração sônica do sistema adesivo e no assentamento do pino. Os retentores foram limpos, tratados com silano e sistema adesivo (Ambar, FGM) e cimentados com cimento resinoso dual (Allcem Core, FGM). Após 24 h as amostras foram submetidas ao teste mecânico e análise de falha. Amostras representativas foram avaliadas sob microscópio eletrônico de varredura, para avaliação da linha de cimentação. Os resultados foram analisados por meio de análise de variância e teste de Tukey (a=5%). Os resultados obtidos foram: SASP (90,9±27,1 N, C (121,4±60,6 N), SA (127,6±31,8 N) e SP (156,4±41,3 N). A vibração sônica para aplicação apenas do sistema adesivo ou pino não afetou a resistência de união, entretanto interferiu negativamente quando utilizada para ambos procedimentos.