Résumé
STATEMENT OF PROBLEM: The adjustable dental impression trays were made for being adjusted their width automatically along the width of dental arch. PURPOSE: The purpose of this study was to investigate the best retentive form of adjustable dental impression tray, and so to make it a more satisfactory product. MATERIALS AND METHODS: The eight pairs of adjustable trays were made of ABS(acrylonitrile butadiene styrene) with different distribution of holes and with or without the rim on the border area of them. The experiment was done with the horse-shoe shaped metal plate to pull out the set impression body from the tray, and the tray jig which was made for holding the tray on a lower part of Universal Testing achine(UTM, Zwick Z020, Zwick Co., Germany). After the impression in the tray was allowed to set four minutes, a tensile force was applied at right angles to the tray which had been previously seated on the jig. The force was applied to measure a maximum retentive force by use of a UTM at a constant strain rate of 100mm per minute. A 2-factor analysis of variance (p.05) 4. The rimless trays were more retentive generally, than the rimmed trays except 2 case: upper tray group-all area / 2 mm. intervals and lower tray group-margin only / 2 mm. intervals.(p<.05) 5. Most of the adjustable trays were showed higher retentive force than perforated metal tray except the lower group that perforated on the all area at intervals of 2 mm.
Sujets)
Arcade dentaireRésumé
PURPOSE: The purpose of this study was to compare the fracture strength of the IPS Empress ceramic crown according to the incisal reduction (2.0mm, 2.5mm, 3.0mm) and axial inclination (4degrees., 8.degrees, 12degrees.) of the upper canine. MATERIALS AND METHODS: After 10 metal dies were made for each group, the IPS Empress ceramic crowns were fabricated and each crown was cemented on each metal die with resin cement. The cemented crowns mounted on the testing jig were inclined 30 degrees and the universal testing machine was used to measure the fracture strength. RESULTS: 1. The fracture strength of the ceramic crown with 3.0mm depth and 12degrees inclination was the highest (839N). Crowns of 2.0mm depth and 12degrees inclination had the lowest strength (559N). 2. There was no significant difference in the fracture strength by axial inclination in the same incisal reduction group. 3. The fracture mode of the crowns was similar. Most of fracture lines began at the loading area and extended through proximal surface perpendicular to the margin irrespective of incisal reduction.
Sujets)
Céramiques , Couronnes , Céments résineRésumé
The purpose of this study was to evaluate the amount and interrelationship of the soft and hard tissue change after mandibular setback surgery in skeletal Class III malocclusion. The sample consisted of 25 adult patient (12 male and 13 female) who had severe anteropostrior skeletal discepancy. These patient had received presurgical orthodontic treatment and surgical treatment which is bilateral sagittal split ramus osteotomy. The presurgical and postsurgical lateral cephalograms were evaluated. The computerized statistical analysis was carried out with SPSS/PC program. The result were as follows: 1. After mandibular bilateral sagittal split ramus osteotomy, lower facial soft tissue horizontal posterior changes were high significance value. but vertical soft tissue changes were low significance value. 2. After mandibular bilateral sagittal split ramus osteotomy, relative upper lip protrusion increased(p<0.01) and relative lower lip protrusion decreased(p<0.01) and lower facial soft tissue thickness increased(p<0.01).