Effect of surface treatment and storage on the bond strength of different ceramic systems

Aim: The aim of this study was to evaluate the micro shear bond strength of different ceramic systems – IPS Empress 2, Cergogold, In-Ceram Alumina and Cercon - and a dual luting agent. Methods: Twelve specimens of each ceramic were fabricated and divided according different surface treatments: Group 1: No additional treatment was applied to the ceramic surface; Group 2: Ceramics were etched with 9.5% hydrofluoric acid; Group 3: specimens treated with airborne particle abrasion for each ceramic system in accordance with manufacturer’s instructions (n=20). The tests were performed after 24 h or after water storage for 6 months. Data were then assessed statistically using the 3-way ANOVA and the Tukey’s test (P<0.05). Results: For Cergogold and IPS Empress 2 systems, the treatments performed with airborne particle abrasion and hydrofluoric acid showed no significant differences from each other, and both were superior to the groups without treatment. For Cercon and In-Ceram ceramics, no differences were found among the groups (P<0.05). When the surface was treated with hydrofluoric acid, the highest bond strength was found to IPS Empress 2 in the 6-month storage period (P<0.05). Conclusion: Lower bond strength values were only observed with IPS Empress 2 ceramic for the control group in the 6-month storage (P<0.05).

O condicionamento ácido prévio ainda é indispensável para a odontologia adesiva? / Is previous total etching still indispensable for the adhesive dentistry?

O objetivo deste trabalho foi avaliar as características dos sistemas adesivos disponíveis atualmente considerando a aplicação ou não do condicionamento prévio com ácido fosfórico. O conhecimento das estruturas e o tratamento adequado do substrato dental são fundamentais para utilização dos adesivos convencionais. Os sistemas adesivos autocondicionantes possuem técnica simplificada dispensando o condicionamento ácido prévio. O profissional deverá ter conhecimento dos mecanismos de adesão ao substrato dental, experiência clínica e domínio da técnica de aplicação do adesivo escolhido. O condicionamento ácido prévio não deve ser considerado indispensável na Odontologia adesiva atual.

Comparação de técnicas de mensuração da infiltração marginal em restaurações de resina composta / Comparison of measurement techniques of marginal leakage in composite restorations

O objetivo deste trabalho foi aplicar dois métodos de mensuração da infiltração marginal da resina composta com intuito de verificar qual delas permite maior confiabilidade dos resultados. Foram confeccionadas cavidades de classe V, com margem cervical em dentina, restauradas com o sistema restaurador Single Bond/Z250. As medidas de infiltração dos grupos foram realizadas por meio de dois métodos: análise por escores e análise por programa de computador específico (Image Tool), através do qual foram realizadas medidas para obtenção de valores em milímetros. A análise estatística demonstrou que não houve compatibilidade dos resultados obtidos através das duas técnicas.

Técnicas alternativas para amenizar os efeitos gerados durante a contração da resina composta / Alternative technique to minimize the effects caused by the shrinkage of the composite resin

O objetivo deste trabalho foi aplicar técnicas alternativas de inserção e fotoativação de resina com o intuito de amenizar os efeitos da contração de polimerização, avaliando a infiltração marginal. Foram confeccionadas cavidades de classe V, com margem cervical em dentina, restauradas com o sistema restaurador Single Bond/Z250. Os dentes foram divididos em quatro grupos, de acordo com a técnica de inserção da resina (incremental ou em incremento único) e formas de fotoativação (máxima intensidade ou gradual). As técnicas de inserção incremental e fotoativação gradual, quando associadas, diminuíram os efeitos gerados durante a contração de polimerização da resina

Avaliação da infiltração marginal em restaurações com resina composta variando-se os métodos de fotoativação / Evaluation of the marginal leakage in restorations with composite, varying the light cure methods

O presente estudo se propôs a avaliar a infiltração marginal em restaurações realizadas pelas técnicas de fotoativação gradual e com máxima intensidade. Foram confeccionadas 32 cavidades de classe V, com margens em esmalte, dimensões ocluso-cervical de 2,0mm, mésio-distal de 2,0mm e profundidade de 1,5mm. As cavidades foram restauradas com o sistema restaurador Single Bond/Z-250 (3M do Brasil). Os dentes foram divididos em dois grupos. Os grupos diferiam entre si de acordo com a técnica de fotoativação da resina. Os resultados, mostraram que a técnica de fotoativação gradual apresentou índice de infiltração estatisticamente menor em relação à técnica de fotoativação com máxima intensidade

Infiltraçäo marginal em restauraçöes utilizando diferentes métodos de inserçäo da resina / Marginal leakage in restorations according to different composite insertion methods

O presente estudo se propôs a avaliar a infiltraçäo marginal em restauraçöes realizadas pelas técnicas de incremento único e incremental. Foram confeccionadas 32 cavidades de classe V, com margens em esmalte, dimensöes ocluso-cervicais de 2,0mm, mésio-distais de 2,0mm e profundidade de 1,5mm. As cavidades foram restauradas com o sistema restaurador Single Bond/Z250 (3M do Brasil). Os dentes foram divididos em dois grupos. Os grupos diferiam entre si de acordo com a técnica de inserçäo da resina na cavidade. Os resultados mostraram que a técnica incremental apresentou índice de infiltraçäo estatisticamente menor em relaçäo à técnica de incremento único

Avaliação da infiltração na margem cervical em dentina de restaurações classe V, variando-se as técnicas de inserção e fotoativação da resina composta / Evaluation of the leakage in the dentin cervical margin of restorations class V being varied the insert and polymerization techniques of the composed resin

O objetivo desse estudo foi avaliar a infiltração na margem cervical em dentina em restaurações realizadas pelas técnicas de incremento único e incremental, associadas ou não à fotoativação gradual. Foram confeccionadas 64 cavidades de classe V, com margens oclusal, mesial e distal em esmalte e margem cervical em dentina, com dimensões ocluso-cervical de 2,00 mm, mésio-distal de 2,0 mm e profundidade de 1,5 mm. As cavidades foram restauradas com o sistema restaurador Single-Bond/Z250 (3M do Brasil). A aplicação do sistema adesivo foi realizada de acordo com as instruções do fabricante. Os dentes foram divididos em quatro grupos. Os grupos diferiam entre si de acordo com a técnica de inserção da resina na cavidade (incremental ou em incremento único) e de acordo com as formas de fotoativação (gradual, variando a intensidade através da distância da fonte de luz em relação à restauração). Os grupos foram assim divididos: Grupo 1 - técnica de incremento único, associada à ativação com máxima intensidade de luz (aproximação máxima); Grupo 2 - técnica incremental e fotoativação com máxima intensidade de luz; Grupo 3 - técnica de incremento único, associada à fotoativação gradual; e Grupo 4 - técnica incremental, associada à fotoativação gradual. Os corpos foram submetidos à ciclagem térmica (500X, 5ºC e 55ºC, com duração de 30 segundos cada ciclo) e imersos em solução de Fucsina básica a 0,5%. Cada dente foi seccionado longitudinalmente no sentido disto-mesial, separando as duas cavidades restauradas, vestibular e lingual. Posteriormente, as metades, já separadas, foram levadas à máquina de corte e as restaurações foram seccionadas ao meio. Os cortes foram realizados no sentido longitudinal da restauração, originando duas fatias, de onde foi escolhido o corte de maior infiltração. Obteve-se a imagem digital de cada corte e em cada um deles, foi medido o índice de infiltração linear do corante, em milímetros, através de um programa de computação para este fim. A análise estatística demonstrou que a técnica incremental apresentou um menor índice de infiltração marginal em relação à técnica de incremento único. O método de fotoativação gradual permitiu melhor selamento marginal, quando comparada à ativação com máxima intensidade de luz. As técnicas de inserção incremental e fotoativação gradual, quando associadas, resultaram em índices de microinfiltração, estatisticamente, menores do que as outras técnicas experimentadas

The objective of this study was to evaluate the dentin margin leakage of Single Bond/Z-250 adhesive system restorations according to different insertion and light activation methods. Class V cavities 2 mm in width and height and 1,5 mm depth were prepared in buccal and lingual surfaces of extracted human third molars. The adhesive agent was applied in accordance to the manufacturer's instructions. These teeth were divided into four groups of sixteen cavities each. The insertion techniques used were: bulk and incremental technique. Two different methods of light activation were used: conventional light activation technique and ramp technique (gradual increase of light intensity). This method was performed approaching the light activator tip from the restoration. According to the results, it was concluded that the marginal leakage of incremental technique restorations was lower compared to bulk filling technique. The ramp technique led to lower marginal leakage penetration compared to conventional light cure technique. The association of incremental and ramp techniques showed the lowest marginal leakage results

Avaliação da infiltração na margem cervical em dentina de restaurações classe V, variando-se as técnicas de inserção e fotoativação da resina composta / Evaluation of the leakage in the dentin cervical margin of restorations class V being varied the insert and polymerization techniques of the composed resin

O objetivo desse estudo foi avaliar a infiltração na margem cervical em dentina em restaurações realizadas pelas técnicas de incremento único e incremental, associadas ou não à fotoativação gradual. Foram confeccionadas 64 cavidades de classe V, com margens oclusal, mesial e distal em esmalte e margem cervical em dentina, com dimensões ocluso-cervical de 2,0 mm, mésio-distal de 2,0mm e profundidade de 1,5mm. As cavidades foram restauradas com o sistema restaurador Single-Bond/Z250 (3M do Brasil). A aplicação do sistema adesivo foi realizada de acordo com as instruções do fabricante. Os dentes foram divididos em quatro grupos. Os grupos diferiam entre si de acordo com a técnica de inserção da resina na cavidade (incremental ou em incremento único) e de acordo com as formas de fotoativação (gradual, variando a intensidade através da distância da fonte de luz em relação à restauração). Os grupos foram assim divididos: Grupo 1 - técnica de incremento único, associada à ativação com máxima intensidade de luz (aproximação máxima); Grupo 2 - técnica incremental e fotoativação com máxima intensidade de luz; Grupo 3 - técnica de incremento único, associada à fotoativação gradual; e Grupo 4 - técnica incremental, associada à fotoativação gradual. Os corpos foram submetidos...