Résumé
Aqueous dispersion and stability of Fe3O4 nanoparticles remain an issue unresolved since aggregation of naked iron nanoparticles in water. In this study, we successfully synthesized different Fe3O4 super-paramagnetic nanoparticles which were modified by three kinds of materials [DSPE-MPEG2000, TiO2 and poly acrylic acid (PAA)] and further detected their characteristics. Transmission electron microscopy (TEM) clearly showed sizes and morphology of the four kinds of nanoparticles. X-ray diffraction (XRD) proved successfully coating of the three kinds of nanoparticles and their structures were maintained. Vibrating sample magnetometer (VSM) verified that their magnetic properties fitted for the super-paramagnetic function. More importantly, the particle size analysis indicated that Fe3O4@PAA had a better size distribution, biocompatibility, stability and dispersion than the other two kinds of nanoparticles. In addition, using CNE2 cells as a model, we found that all nanoparticles were nontoxic. Taken together, our data suggest that Fe3O4@PAA nanoaparticles are superior in the application of biomedical field among the four kinds of Fe3O4 nanoparticles in the future.
Résumé
Aqueous dispersion and stability of Fe3O4 nanoparticles remain an issue unresolved since aggregation of naked iron nanoparticles in water. In this study, we successfully synthesized different Fe3O4 super-paramagnetic nanoparticles which were modified by three kinds of materials [DSPE-MPEG2000, TiO2 and poly acrylic acid (PAA)] and further detected their characteristics. Transmission electron microscopy (TEM) clearly showed sizes and morphology of the four kinds of nanoparticles. X-ray diffraction (XRD) proved successfully coating of the three kinds of nanoparticles and their structures were maintained. Vibrating sample magnetometer (VSM) verified that their magnetic properties fitted for the super-paramagnetic function. More importantly, the particle size analysis indicated that Fe3O4@PAA had a better size distribution, biocompatibility, stability and dispersion than the other two kinds of nanoparticles. In addition, using CNE2 cells as a model, we found that all nanoparticles were nontoxic. Taken together, our data suggest that Fe3O4@PAA nanoaparticles are superior in the application of biomedical field among the four kinds of Fe3O4 nanoparticles in the future.
Sujets)
Composés du fer III , Chimie , Nanoparticules de magnétite , Chimie , Microscopie électronique à transmission , Spectroscopie infrarouge à transformée de Fourier , Propriétés de surface , Eau , Chimie , Diffraction des rayons XRésumé
The purpose of this study was to develop docetaxel-poly (lactide-co-glycolide) (PLGA) loaded nanoparticles by using nanoprecipitation method and optimize the relative parameters to obtain nanoparticles with higher encapsulation efficiency and smaller size. The physicochemical characteristics of nanoparticles were studied. The optimized parameters were as follows: the oil phase was mixture of acetone and ethanol, concentration of tocopheryl polyethylene glycol succinate (TPGS) was 0.2%, the ratio of oil phase to water phase was 1:5, and the theoretical drug concentration was 5%. The optimized nanoparticles were spherical with size between 130 and 150 nm. The encapsulation efficiency was (40.83±2.1)%. The in vitro release exhibited biphasic pattern. The results indicate that docetaxel-PLGA nanoparticles were successfully fabricated and may be used as the novel vehicles for docetaxel, which would replace Taxotere® and play great roles in future.
Résumé
The purpose of this study was to develop docetaxel-poly (lactide-co-glycolide) (PLGA) loaded nanoparticles by using nanoprecipitation method and optimize the relative parameters to obtain nanoparticles with higher encapsulation efficiency and smaller size. The physicochemical characteristics of nanoparticles were studied. The optimized parameters were as follows: the oil phase was mixture of acetone and ethanol, concentration of tocopheryl polyethylene glycol succinate (TPGS) was 0.2%, the ratio of oil phase to water phase was 1:5, and the theoretical drug concentration was 5%. The optimized nanoparticles were spherical with size between 130 and 150 nm. The encapsulation efficiency was (40.83±2.1)%. The in vitro release exhibited biphasic pattern. The results indicate that docetaxel-PLGA nanoparticles were successfully fabricated and may be used as the novel vehicles for docetaxel, which would replace Taxotere® and play great roles in future.