Crystallographic and topographic analysis of Ultra-Translucent zirconia after various surface treatments / Análisis cristalográfico y topográfico de la zirconia ultra-translúcida después de diversos tratamientos de superficie

Abstract The aim of the present study was to analyze the effects of 4 different surface treatments, on the crystallographic characteristics of Ultra-Translucent Zirconia. Fully sintered zirconia specimens of highly translucent yttria partially stabilized zirconia (Y-PSZ) (KATANA UTML) were divided into four experimental groups and a control group (n=10). Each group received one of the following surface treatments: sandblasting with 50µm alumina particles sandblasting with 110µm alumina particles, and grinding with a rotary high-speed turbine with and without water irrigation. For each sample, x-ray diffraction was carried out to analyze peak intensity, calculate the crystallite size, and detect the presence of compressive and tensile stress. Surface roughness was measured on all specimens using a standard scanning profilometer. Additionally, scanning electron microscopy (SEM) was performed to qualitatively analyze the surfaces of the specimens. Statistical analysis included repeated measures analysis of variance and post hoc Tukey test (p≤0.05). The control group exhibited the highest crystallite size (323nm). All surface treatments led to a reduction in the crystallite size, with the most significant reduction observed in the groups subjected to sandblasting with 110µm alumina particles and high- speed grinding with irrigation. Sandblasting with 50µm alumina particles resulted in less transformation of the crystallite size. A general tendency of the diffraction peaks to shift to a lower angle can be observed in the experimental groups, indicating the presence of compressive stress on the samples. Profilometry revealed higher roughness in the ground samples (6,14µm and 6,57µm) compared to the sandblasted groups (2,93µm and 2,02µm). The crystal domain size showed a tendency to decrease after the surface treatments. Sandblasted samples, as well as ground samples without irrigation, exhibited compressive stress. Sandblasted samples had lower surface roughness compared to the ground samples. Sandblasting with 50µm alumina particles caused the least decrease in crystallite size.

Resumen El objetivo del presente estudio fue analizar los efectos de 4 tratamientos de superficie en las características cristalográficas de la zirconia ultratranslúcida. Especímenes de zirconia totalmente sinterizados, altamente translúcidos de zirconia parcialmente estabilizada con itrio (Y-PSZ) (KATANA UTML) se dividieron en cuatro grupos experimentales y un grupo de control (n=10). Cada grupo recibió uno de los siguientes tratamientos de superficie: arenado con partículas de alúmina de 50µm (Al2O3), arenado con partículas de alúmina de 110µm y desgaste con una turbina rotativa de alta velocidad con y sin irrigación. Para cada muestra, se llevó a cabo una difracción de rayos X para analizar la intensidad del pico, calcular el tamaño del cristalito y detectar la presencia de tensiones compresivas y tensiles. La rugosidad superficial se midió en todos los especímenes utilizando un perfilómetro estándar. Además, se realizó microscopía electrónica de barrido (SEM) para analizar cualitativamente las superficies de los especímenes. El análisis estadístico incluyó un análisis de varianza de medidas repetidas y una prueba de Tukey post hoc (p≤0,05). El grupo de control mostró el tamaño de cristalito más alto (323nm). Todos los tratamientos de superficie llevaron a una reducción en el tamaño del cristalito, con la reducción más significativa observada en los grupos sometidos a arenado con partículas de alúmina de 110µm y desgaste de alta velocidad con irrigación. El arenado con partículas de alúmina de 50µm resultó en una menor transformación del tamaño del cristalito. Se puede observar una tendencia general de los picos de difracción a desplazarse a un ángulo más bajo en los grupos experimentales, lo que indica la presencia de estrés compresivo en las muestras. La perfilometría reveló una mayor rugosidad en las muestras con desgaste con instrumento rotatorio (en comparación con los grupos arenados. El tamaño del cristalito mostró una tendencia a disminuir después de los tratamientos de superficie. Las muestras arenadas, así como las muestras desgastadas sin irrigación, mostraron estrés compresivo. Las muestras arenadas tuvieron una menor rugosidad superficial en comparación con las muestras desgastadas con rotatorio. El arenado con partículas de alúmina de 50µm provocó la menor disminución en el tamaño del cristalito.

Marginal gap of zirconia and lithium disilicate frameworks produced by the CAD-CAM technique through a comparator microscope ­ in vitro analysis / Fenda marginal de estruturas de zircônia e dissilicato de lítio produzidas pela técnica CAD-CAM através de um microscópio comparador ­ análise in vitro

Objective: The aim of this study was to evaluate the marginal gap of frameworks produced using the CAD-CAM system, from zirconia and lithium disilicate blocks, adapted to a tooth preparation and a gypsum die. Material and Methods: For this study, a human first molar tooth was used as a master model with a full crown preparation. It was molded 20 times to obtain the gypsum die and randomly divided into 2 groups (n=10) for the fabrication of zirconia and lithium disilicate frameworks. The frameworks were made using pre-sintered zirconia blocks and lithium disilicate blocks, both CAD-CAM systems. The marginal gap was measured in µm at four points (buccal, palatal, mesial, and distal) using a comparator microscope with 30x magnification, with the framework seated on the master model (tooth), and on the gypsum die. Marginal gap data (µm) were evaluated using two-way analysis of variance and Tukey's test with a significance level of 5%. Results: The results showed that there was no statistically significant interaction between the factors studied (p=0.223) or isolated factors (ceramic factor p=0.886 and die factor p=0.786). Conclusion: Both ceramics produced using the CAD-CAM technique did not exhibit statistical differences in marginal adaptation on the two types of substrates, both on tooth preparation and on the gypsum die (AU)

Objetivo: O objetivo deste estudo foi avaliar o espaço marginal de estruturas produzidas usando o sistema CAD-CAM, a partir de blocos de zircônia e dissilicato de lítio, adaptadas a um preparo sobre dente e a um troquel de gesso. Material e Métodos: Para este estudo, um dente molar humano foi utilizado como modelo mestre com preparo para coroa total. Este foi moldado 20 vezes para obter o troquel de gesso e dividido aleatoriamente em 2 grupos (n=10) para a fabricação de estruturas de zircônia e dissilicato de lítio. As estruturas foram feitas usando blocos de zircônia pré-sinterizados e blocos de dissilicato de lítio, ambos sistemas para CAD-CAM. O espaço marginal foi medido em µm, em quatro pontos (bucal, palatal, mesial e distal), utilizando um microscópio comparador com ×30 de ampliação e com a estrutura assentada no modelo mestre (dente) e no troquel de gesso. Os dados de espaço marginal (µm) foram avaliados usando análise de variância bidirecional e teste de Tukey com um nível de significância de 5%. Resultados: Os resultados mostraram que não houve interação estatisticamente significativa entre os fatores estudados (p=0,223) ou isoladamente (fator cerâmica p=0,886 e fator troquel p=0,786). Conclusão: Ambas as cerâmicas produzidas usando a técnica CAD-CAM não apresentaram diferenças estatísticas em relação à adaptação marginal nos dois tipos de substratos, tanto na preparação dentária quanto no troquel de gesso(AU)

Effect of photopolymerization time on the microhardness of resin cement beneath feldspathic ceramic / Efecto del tiempo de fotopolimerización en la dureza de cementos de resina debajo de una cerámica feldespática

ABSTRACT During ceramic veneer luting, resin cement polymerization is performed with interposition of the dental ceramic. Aim: To evaluate how and how much the photoactivation time affects the Vickers hardness of resin-based cements with interposed ceramic. Materials and Method: A total 24 specimens H mm in diameter and 1 mm thick were made from Paracore White Coltene (PC), Densell Resin Duo Cement (DC), 3MRelyX Veneer (RX) and Coltene Fill Up! (FU), interposing VitablockMarkII (Vita Zahnfabrik) feldspathic ceramic 0.6 mm thick during photoactivation. The materials were polymerized using 100% and 25% of the times indicated by the manufacturers with a Coltolux LED ((Coltene) light with intensity 1200 mW/cm2. Each polymerization time group consisted of three specimens of each material, which were stored dry in darkness at 37 °C for 7 days. Three Vickers microhardness measurements were made on the top and bottom surfaces of each specimen using a Vickers Future Tech FM300 microhardness tester (300 g, 5 s). The values were averaged, and the bottom/top ratios calculated. Results were analyzed by ANOVA. (p<0.05) complemented with multiple comparisons using Tukey's test (p<0.05). Results: Different photoactivation times were found to have a significant effect on hardness values of the cements evaluated, with significant differences between some of the cements. No statistically significant difference was found for the effect of photoactivation time on bottom/top microhardness ratio in those materials. Conclusions: Under the experimental conditions employed, it can be concluded that photopolymerization for shorter times and the interposition of restorative material significantly affectpolymerization quality as evaluated by microhardness, but the bottom/top ratio was unaffected by differences in polymerization time.

RESUMEN Durante la fijación de una carilla cerámica, la polimerización del cemento a base de resinas se realiza con la interposición de la cerámica dental. Objetivo: evaluar en qué forma y magnitud afecta el tiempo de fotoactivación en la dureza Vickers de los cementos a base de resinas con la cerámica interpuesta. Materiales y Método: se confeccionaron 24 probetas de 11 mm de diámetro y 1 mm de espesor con: Paracore White Coltene (PC), Resin Duo Cement de Densell (DC), RelyX Veneer de 3M (RX) y Fill Up! De Coltene (FU) interponiendo 0,6 mm de espesor de cerámica feldespática Vitablock Mark II (Vita Zahnfabrik) durante la fotoactivación. Se polimerizó utilizando el 100% y el 25% del tiempo indicado por el fabricante con lámpara Coltolux LED ((Coltene) con 1200 mW/cm2 de intensidad. Cada grupo quedó conformado con tres probetas de cada material que se almacenaron a oscuras y en seco a 37 °C durante 7 días. Se registraron tres mediciones de microdureza Vickers de las superficies top y bottom de cada probeta con un microdurómetro Vickers Future Tech FM300 (300 g, 5 s) y se calculó su promedio, así como la relación entre los valores registrados en cada una de sus caras. Los resultados fueron analizados por medio de la prueba de ANOVA. (p<0.05). complementada con comparaciones múltiples por medio de la prueba de Tukey (p<0.05). Resultados: se encontró un efecto significativo de la modificación del tiempo de fotoactivación en los valores de dureza de los cementos evaluados con diferencias significativas entre algunos de ellos. Simultáneamente no se encontró significación estadística en el efecto de ese factor sobre la relación microdureza bottom/top registrada en esos materiales. Conclusiones: en las condiciones experimentales empleadas puede concluirse que la fotopolimerización en menor tiempo e interposición de material restaurador afecta significativamente la calidad de polimerización evaluada mediante los valores de microdureza, pero la proporción bottom/ top no fue afectada en la variación en el tiempo de polimerización.

An engineering perspective of ceramics applied in dental reconstructions

Abstract The demands for dental materials continue to grow, driven by the desire to reach a better performance than currently achieved by the available materials. In the dental restorative ceramic field, the structures evolved from the metal-ceramic systems to highly translucent multilayered zirconia, aiming not only for tailored mechanical properties but also for the aesthetics to mimic natural teeth. Ceramics are widely used in prosthetic dentistry due to their attractive clinical properties, including high strength, biocompatibility, chemical stability, and a good combination of optical properties. Metal-ceramics type has always been the golden standard of dental reconstruction. However, this system lacks aesthetic aspects. For this reason, efforts are made to develop materials that met both the mechanical features necessary for the safe performance of the restoration as well as the aesthetic aspects, aiming for a beautiful smile. In this field, glass and high-strength core ceramics have been highly investigated for applications in dental restoration due to their excellent combination of mechanical properties and translucency. However, since these are recent materials when compared with the metal-ceramic system, many studies are still required to guarantee the quality and longevity of these systems. Therefore, a background on available dental materials properties is a starting point to provoke a discussion on the development of potential alternatives to rehabilitate lost hard and soft tissue structures with ceramic-based tooth and implant-supported reconstructions. This review aims to bring the most recent materials research of the two major categories of ceramic restorations: ceramic-metal system and all-ceramic restorations. The practical aspects are herein presented regarding the evolution and development of materials, technologies applications, strength, color, and aesthetics. A trend was observed to use high-strength core ceramics type due to their ability to be manufactured by CAD/CAM technology. In addition, the impacts of COVID-19 on the market of dental restorative ceramics are presented.

Tratamentos de superfície prévios à camada de caracterização: efeitos na resistência adesiva e comportamento mecânico de cerâmicas de óxido de zircônio / Surface treatments prior to the characterization layer: effects on bond strength and mechanical behavior of zirconium oxide ceramics

Este estudo avaliou o efeito do jateamento com óxido de alumínio prévio à camada de caracterização no comportamento adesivo e mecânico de zircônias de segunda e terceira gerações. Na parte A, foi realizado um estudo de resistência flexural. Para isso, discos de cada zircônia (3Y-TZP, 4Y-PSZ ou 5YPSZ) foram confeccionados. Após polimento e sinterização, os discos foram divididos de acordo com os tratamentos de superfície: Polimento, Jateamento com Al2O3 50 µm e Jateamento com Al2O3 110 µm (n = 30). A superfície tratada de todos os discos recebeu uma fina camada de pigmentação e uma fina camada de glaze. O ensaio de flexão biaxial foi realizado na configuração pistonon-three-balls e as superfícies fraturadas foram observadas em Microscopia Eletrônica de Varredura (MEV). Os dados foram submetidos à Análise de Weibull. Na parte B, avaliou-se o efeito dos diferentes tratamentos de superfície prévio à camada de caracterização no comportamento à fadiga das diferentes zircônias. Discos de 3Y-TZP, 4Y-PSZ e 5Y-PSZ foram confeccionados e distribuídos entre os tratamentos de superfície: Polimento ou Jateamento Al2O3 50 µm (n = 15), que foram realizados conforme a parte A deste estudo. Os discos foram cimentados adesivamente a um análogo de dentina (NEMA G10). Os testes de fadiga foram realizados pelo método stepwise, com aplicação de carga axial por um pistão hemisférico (carga inicial: 400 N, step: 100 N, ciclos/step: 10.000, frequência: 20 Hz). Na parte C, avaliou-se a resistência de união entre as diferentes zircônias e a camada de caracterização. Foram preparados os mesmos grupos descritos na "parte A" (n = 15). Cilindros de stain seguido por glaze foram construídos nas superfícies das zircônias. A resistência de união foi avaliada pelo teste de cisalhamento. Os tipos de falha (adesiva, predominantemente adesiva ou coesiva) foram analisados em estereomicroscópio e MEV. Análises complementares em perfilômetro e goniômetro foram realizadas. Para a parte A, o jateamento com Al2O3 110 µm aos menores valores de resistência à flexão, seguido do jateamento com as partículas de Al2O3 50 µm. Os maiores valores foram observados no grupo que não recebeu jateamento prévio à camada de caracterização. Esses resultados foram observados em todos os materiais. Na parte B, o jateamento com Al2O3 reduziu significativamente a carga e o número de ciclos para falha em fadiga de todos os materiais. Na parte C, os melhores valores de resistência de união foram atribuídos para o tratamento de superfície com Al2O3 110 µm, seguido de jateamento com Al2O3 50 µm e polimento. Dessa forma, o jateamento prévio à camada de caracterização reduz a resistência mecânica de zircônias de segunda geração e melhora a resistência de união entre os dois materiais (AU)

This study evaluated the effect of aluminum oxide sandblasting prior to the characterization layer on the adhesive and mechanical behavior of second- and third-generation zirconia. Part A consisted of a flexural strength study. Discs of each zirconia (3Y-TZP, 4Y-PSZ, or 5Y-PSZ) were prepared. After polishing and sintering, the discs were divided according to the surface treatments: Polishing, Sandblasting with Al2O3 50 µm and Sandblasting with Al2O3 110 µm (n = 30). The treated surface of all discs received a thin layer of stain and a thin layer of glaze. The biaxial bending test was performed in a piston-on-three-balls set-up. The fractured surfaces were observed by Scanning Electron Microscopy (SEM). Data were subjected to Weibull Analysis. In part B, the effect of different surface treatments prior to the characterization layer on the fatigue behavior of different zirconia was evaluated. Discs of 3Y-TZP, 4Y-PSZ and 5Y-PSZ were prepared and divided among the surface treatments: Polishing or Sandblasting Al2O3 50 µm (n = 15), which were performed according to part A of this study. The discs were adhesively cemented to a dentin-analogue (NEMA G10). Fatigue tests were performed using the stepwise method, with an axial load application by a hemispherical piston (initial load: 400 N, step: 100 N, cycles/step: 10,000, frequency: 20 Hz). Part C evaluated the bond strength between the different zirconia and the characterization layer. The same groups described in part A (n = 15) were prepared. Stain cylinders followed by glaze were built on the zirconia surfaces. The bond strength was evaluated by the shear test. The types of failure (adhesive, predominantly adhesive or cohesive) were analyzed using a stereomicroscope and SEM. Complementary analyzes in profilometer and goniometer were carried out. In part A, sandblasting with Al2O3 110 µm led to the lowest flexural strength results, followed by sandblasting with Al2O3 50 µm. Polishing group achieved the highest values. These results were observed in all tested ceramics. In part B, sandblasting with Al2O3 50 µm significantly reduced the fatigue failure load and the number of cycles for fatigue failure. In part C, the highest bond strength results were reached by sandblasting with Al2O3 110 µm, followed by sandblasting with Al2O3 50 µm, and polishing. Therefore, aluminum oxide particles sandblasting diminishes the mechanical behavior of second- and third-generation zirconias and improves the bond strength between the two materials. (AU)

Influence of testing environment on static fatigue behavior of a glass and a polycrystalline ceramic

Abstract It aims on evaluate the effect of the test environment on static fatigue behavior of lithium disilicate-based (LD), and yttrium oxide-stabilized zirconia (YSZ) ceramics. Specimens of LD (IPS e.max CAD, Ivoclar Vivadent) and YSZ (IPS e.max ZirCAD MO, 3 mol% Y2O3, Ivoclar Vivadent) were randomly allocated into three groups: tested in air, inert (paraffin oil, Sigma Aldrich) or distilled water. The static fatigue test (n=15) was performed using a piston-on-three ball assembly, adapted from ISO 6872, as follows: starting load 100 N for LD and 300 N for YSZ; loading application time set to 1 hour for each loading step; step size of 50 N for LD and 100 N for YSZ, applied successively until fracture. Data from static fatigue strength (MPa) and time to fracture (hours) were recorded. Fractographic analysis was executed. Survival analysis corroborates absence of influence of environment on static fatigue outcomes (fatigue strength, time to fracture and survival rates) for YSZ. For LD, specimens tested in air presented statistically superior survival rate and static fatigue strength (p= 0.025). In regards of time to fracture, LD tested in air were superior than when tested in distilled water (p=0.019) or inert (p=0.017) environments. No statistical differences for Weibull modulus were observed. Failures started on the tensile stress surface. Thus, the test environment did not affect slow crack growth (SCG) mechanisms during static fatigue test of YSZ ceramics, but it plays a significant role for the static fatigue behavior of lithium disilicate-based glass ceramics, indicating a high susceptibility to SCG.

Resumo O presente estudo objetivou investigar a influência do ambiente de teste no comportamento a fadiga estática (resistência à fratura e tempo para falha) de cerâmicas à base de dissilicato de lítio (LD) e zircônia estabilizada com ítria (YSZ). Espécimes de LD (IPS e.max CAD, Ivoclar Vivadent) e YSZ (IPS e.max ZirCAD MO, 3mol% Y2O3, Ivoclar Vivadent) foram obtidos e alocados aleatoriamente em três grupos: testado em ar, em líquido inerte (óleo de parafina) ou em água destilada. O teste de fadiga estática (n= 15) foi realizado usando o teste pistão sobre três esferas, ISO 6872, da seguinte forma: carga inicial 100 N para LD e 300 N para YSZ; tempo de aplicação de carregamento definido para 1 hora para cada etapa de carregamento; tamanho do passo de 50 N para LD e 100 N para YSZ, aplicados sucessivamente até a fratura. Dados de resistência à fadiga estática (MPa) e tempo até a fratura (horas) foram registrados. A análise fractográfica foi executada. A análise de sobrevivência corrobora a ausência de influência do ambiente de teste nos resultados de fadiga estática (resistência à fadiga, tempo de fratura e taxas de sobrevivência) para a YSZ. Para LD, os corpos de prova testados em ar apresentaram taxa de sobrevivência e resistência à fadiga estática estatisticamente superiores (p= 0,025). Em relação ao tempo de fratura, os espécimes LD testados em ar foram superiores aos testados em água destilada (p= 0,019) ou em ambiente inerte (p= 0,017). Não foram observadas diferenças estatísticas para o módulo de Weibull. Todas as falhas começaram no lado onde se concentra a tensão de tração (lado de baixo) durante o teste. Com base nisso, observa-se que o ambiente de teste não afetou os mecanismos de crescimento lento de trinca durante o teste de fadiga estática da cerâmica YSZ, mas desempenha um papel significativo na resistência à fadiga estática da cerâmica de vidro à base de dissilicato de lítio, indicando alta susceptibilidade ao crescimento lento e subcrítico de trincas.

Alternativas de tratamiento para pacientes jóvenes con pérdida de estructura dentaria. Parte 2: caso clínico / Treatment alternatives for young patients with loss of dental structure. Part 2: a clinical case

El objetivo de este artículo es presentar una alternativa de tratamiento rehabilitador para pacientes jóvenes con gran pérdida de estructura dental, vinculada a lesiones de origen no bacteriano. Se presenta el caso clínico de un paciente de sexo masculino, de 39 años de edad, que acudió a la Cátedra de Odontología Integral Adultos de la Facultad de Odontología de la Universidad de Buenos Aires (FOUBA) relatando síntomas compatibles con hipersensibilidad dentaria y fatiga de los músculos masticadores. Al mismo tiempo, manifestó disconformidad con el aspecto estético de su sonrisa. Teniendo en cuenta la gran pérdida de sustancia en sus piezas dentarias producida por hábitos parafuncionales (bruxismo), se realizó una rehabilitación oral adhesiva con cerámicas utilizando el protocolo de abordaje terapéutico sugerido por la Cátedra. En pacientes que presentan severos desgastes (AU)

Rehabilitación oral adhesiva: diagnóstico y tratamiento. Caso clínico / Adhesive oral rehabilitation: diagnosis and treatment. A clinical case

El objetivo de este reporte de caso clínico es presentar una rehabilitación integral adhesiva resuelta por alumnos de grado de la Facultad de Odontología de la Universidad de Buenos Aires (FOUBA), bajo un protocolo de abordaje terapéutico que simplifica su realización. Esta sistematización hace foco en un abordaje completamente aditivo con la finalidad de devolver la salud, la función y la estética de manera predecible. Un paciente de 55 años concurrió a la consulta por motivos estéticos. En el diagnóstico se evidenciaron desgastes severos producto de la parafunción. Se realizó una rehabilitación oral adhesiva seleccionando a la cerámica vítrea como material restaurador. El diagnóstico y la comprensión de su etiología son fundamentales para realizar un tratamiento conservador con restauraciones adheridas y con alto grado de predictibilidad, que se prolongará en el tiempo, gracias a la utilización de una placa orgánica y a los controles de mantenimiento correspondientes (AU)

Resin Nano-Ceramic Material Surface Roughness, Color Stability, and Bacterial Adhesion Evaluation After Different Scaling Methods / Rugosidade superficial, estabilidade de cor e adesão bacteriana de resina nano-cerâmica após diferentes métodos de raspagem

Objective: TThe study evaluated in vitro the changes in roughness, color stability, and bacterial count of a CAD/CAM Resin Nano-Ceramic material surface treated by various scaling procedures. Material and Methods: 70 disks (5mm diameter, 0.5 mm thickness) of Resin Nano-Ceramic (Lava ™Ultimate, 3M, ESPE) material were cemented in standardized cavities prepared in bovine teeth. A custom-made scaling apparatus of a double pan balance was used for different scaling methods, simulating standard clinical conditions. The specimens were assigned to three main groups: no scaling(C), ultrasonic scaling (U), and manual scaling (M). Each group was then divided into three subgroups according to scaling tip material; stainless steel tip (St), plastic tip (P), and titanium tip (Ti). The surface texture was analyzed quantitatively and qualitatively with a tactile profilometer and atomic force microscopy. A spectrophotometer was used for color measurement. Streptococcus mutans were counted in a colony counter. All the data were tabulated and statistically analyzed. Results: Two-way ANOVA was used to study the effect while One-way ANOVA was performed to compare between study groups. The significance level was set at p ≤ 0.05. The ultrasonic titanium tip(UTi) revealed the significant highest mean value of alterations (p < 0.001). The integrity of the material surface was altered in the form of deep scratches on the ultrasonically scaled surfaces and numerous smaller scratches on the hand-scaled surfaces. Conclusion: The plastic instrument would appear to be the instrument of choice during a routine maintenance procedure for Resin Nano-Ceramic materials (AU).

Objetivo: Este estudo avaliou in vitro as alterações na rugosidade, estabilidade de cor e quantidade de bactérias da superfície de uma resina nano-cerâmica produzida em CAD/CAM tratada por diferentes procedimentos de raspagem. Material e Métodos: 70 discos (5 mm diâmetro, 0,5 espessura) de resina nano-cerâmica (Lava ™Ultimate, 3M, ESPE) foram cimentadas em cavidades padronizadas preparadas em dentes bovinos. Um aparato customizado de raspagem com pratos duplos de balança foram usados para os diferentes métodos de raspagem, simulando uma condição clínica padronizada. Os espécimes foram distribuídos em três principais grupos: Sem raspagem (C), raspagem ultrassônica (U) e raspagem manual (M). Cada grupo foi dividido em três subgrupos de acordo com a ponta do material de raspagem; ponta de aço inoxidável (St), ponta plástica (P), ponta de titânio (Ti). A textura da superfície foi analisada qualitativamente e quantitativamente por um perfilômetro tátil e microscopia de força atômica. Um espectrofotometro foi usado para a mensuração da cor. Estreptococos mutans foram contados em um contador de colônias. Todos os dados foram tabulados e analisados estatisticamente. Resultados: Anova dois fatores foi utilizado para estudar os efeitos, enquanto ANOVA um fator foi utilizado para comparar os grupos experimentais. O nível de significância foi estabelecido em p≤ 0,05. A ponta de ultrassom de titânio (UTi) revelou o valor significante mais alto de alterações (p < 0,001). A integridade da superfície d matérias foi alterada na forma ranhuras profundas, nas superfícies raspada por ultrassom e numerosas ranhuras menores nas superfícies raspadas à mão. Conclusão: O instrumento plástico poderia apresentar-se como um instrumento de escolha durante o pocedimento de manutenção routineira para materiais de resina nano-ceramica. (AU)

Machinability of Zirconia Toughened Mica Glass Ceramics for Dental Restorations / Usinabilidade de cerâmica de vidro de mica temperada com zircônia para restaurações dentárias

Objective: For a dental material to be machinable for CAD/CAM technology, it must offer convenient machining, under a given set of cutting conditions. Quantitative evaluation of machinability has been assessed in literature through various parameters such as tool wear, penetration rates, surface roughness, cutting force and power. A machinable ceramic will typically demonstrate a higher tool penetration rate with signs of reduced diamond tool wear and edge chipping. The purpose of this in vitro study was to evaluate the feasibility of machining an experimental ceramic, 20 wt.% zirconia reinforced mica glass ceramics (G20Z) for indirect dental restorations and compare the tool penetration rates of G20Z to commercially available dental ceramics, Presintered Zirconia (PSZ) and IPS emax CAD. Material and Methods: Precursors of base glass (SiO2 -Al2O3 -K2O -MgO-B2O3 -F) were melted at 15000C for 2 h in a platinum crucible and quenched in deionised water. The glass frit was ball milled with 20 wt. % YSZ (G20Z) and subject to two stage heat treatment in a muffle furnace. Specimens of G20Z (12 X 2 mm) were evaluated for their feasibility of machining under varying spindle speed, depth of cut, and feed rates. Influence of depth of cut, spindle speed and feed rate (vc=8000-16000 rpm, d=0.4-0.8 mm, f=0.1- 0.3 mm/tooth) on cutting forces, material response, surface roughness and tool wear were investigated. Tool penetration rates, tool wear and margin chipping were also evaluated and compared with Pre-sintered Zirconia (PSZ) and e.max CAD in a custom dental milling surveyor at 30,000 rpm with a load of 0.98 N under water lubrication for 6 min. Tool penetration rates were calculated as the ratio of length of cut and milling time with a measuring microscope and scanning electron microscope was used for tool wear and edge chipping. ANOVA and Tukey Kramer tests were used for statistically comparing the means of each group. Results: Spindle speed and feed rate play a significant role in influencing surface roughness, thrust force, cutting forces and tool wear. Penetration rates of G20Z (0.32 ±0.12 mm/min) was significantly greater than PSZ (0.26 ±0.06 mm/min) and IPS e.max CAD (0.21 ±0.05 mm/min). SEM observations reveal tool abrasion and edge chipping regardless of the ceramic type. Conclusion: High spindle speeds delivers low cutting forces with an average surface roughness of 1.61 µm, with abrasive wear of the tool insert and brittle fracture of zirconia mica glass ceramic composites. G20Z with its machinable nature demonstrates greater tool penetration rates than PSZ and IPS e.max CAD. Tool wear and edge chipping is seen in all the investigated ceramics. (AU)

Objetivo: Para que um material odontológico seja usinável para a tecnologia CAD / CAM, ele deve oferecer uma usinagem conveniente, sob um determinado conjunto de condições de corte. A avaliação quantitativa da usinabilidade tem sido avaliada na literatura por meio de vários parâmetros, como desgaste da ferramenta, taxas de penetração, rugosidade da superfície, força de corte e potência. Uma cerâmica usinável normalmente demonstrará uma maior taxa de penetração da ferramenta com sinais de desgaste reduzido da ferramenta de diamante e lascamento da borda. O objetivo deste estudo in vitro foi avaliar a viabilidade da usinagem de uma cerâmica experimental, 20% em peso de cerâmica de vidro de mica reforçada com zircônia (G20Z) para restaurações dentárias indiretas e comparar as taxas de penetração da ferramenta de G20Z com as cerâmicas dentais comercialmente disponíveis, Zircônia Presinterizada (PSZ) e IPS emax CAD. Material e Métodos: Precursores de vidro base (SiO2-Al2O3-K2O -MgO-B2O3 -F) foram fundidos a 15000C por 2 h em um cadinho de platina e temperados em água deionizada. A frita de vidro foi moída com 20% em peso de YSZ (G20Z) e submetida a tratamento térmico em duas fases em mufla. Amostras de G20Z (12 x 2 mm) foram avaliadas quanto à sua viabilidade de usinagem sob variação de velocidade do fuso, profundidade de corte e taxas de avanço. A influência da profundidade de corte, velocidade do fuso e taxa de avanço (vc = 8000-16000 rpm, d = 0,4-0,8 mm, f = 0,1- 0,3 mm / dente) nas forças de corte, resposta do material, rugosidade da superfície e desgaste da ferramenta foram investigadas. As taxas de penetração da ferramenta, o desgaste da ferramenta e o lascamento da margem também foram avaliados e comparados com Zircônia pré-sinterizada (PSZ) e e.max CAD em um topógrafo de fresamento dentário personalizado a 30.000 rpm com uma carga de 0,98 N de lubrificação subaquática por 6 min. As taxas de penetração da ferramenta foram calculadas como a razão entre o comprimento de corte e o tempo de fresamento com um microscópio de medição e um microscópio eletrônico de varredura foi usado para o desgaste da ferramenta e lascamento da borda. Os testes ANOVA e Tukey Kramer foram usados para comparar estatisticamente as médias de cada grupo. Resultados: a velocidade do fuso e a taxa de avanço desempenham um papel significativo em influenciar a rugosidade da superfície, força de impulso, forças de corte e desgaste da ferramenta. As taxas de penetração de G20Z (0,32 ± 0,12 mm / min) foram significativamente maiores do que PSZ (0,26 ± 0,06 mm / min) e IPS e.max CAD (0,21 ± 0,05 mm / min). As observações do SEM revelam a abrasão da ferramenta e o lascamento da borda, independentemente do tipo de cerâmica. Conclusão: As altas velocidades do fuso proporcionam baixas forças de corte com uma rugosidade superficial média de 1,61 µm, com desgaste abrasivo do inserto da ferramenta e fratura frágil de compósitos de cerâmica de vidro de zircônia. G20Z com sua natureza usinável demonstra maiores taxas de penetração da ferramenta do que PSZ e IPS e.max CAD. O desgaste da ferramenta e o lascamento da borda são vistos em todas as cerâmicas investigadas. (AU)

Effect of different surface treatments and multimode adhesive application on the Weibull characteristics, wettability, surface topography and adhesion to CAD/CAM lithium disilicate ceramic

Abstract This paper aims to evaluate the effect of different surface treatments on surface topography, wettability, and shear bond strength of resin cement to glass ceramic. Methodology: For SBS test, 32 blocks (7x7x2 mm) of lithium disilicate were obtained and randomly divided into eight groups (four blocks per group) according to each surface treatment (HF 20 s, 60 s, 120 s + silanization/S or Scotch Bond Universal/ SBU) and the Monobond Etch & Prime - MEP application followed or not by SBU. On each treated surface ceramic block, up to four dual-curing resin cement cylinders were prepared and light-cured for 40s (N=120/n=15). The specimens were thermocycled (10,000 cycles, 5-55°C, 30 s) and the SBS test (50KgF, 0.5 mm/min) was performed. Furthermore, failure analysis, wettability, AFM, and SEM were carried out. SBS data (MPa) were analyzed using Student's t-test, two-way ANOVA, Tukey's test (5%) and Weibull's analysis. Results: For HF experimental groups, two-way ANOVA presented the factors "etching time" and "bonding agent" as significant (p<0.05). After silane application, the HF groups presented similar bond strength. SBU application compromised the SBS, except for 120s etching time (HF120sS: 23.39ᵃ±6.48 MPa; HF120sSBU: 18.76ᵃ±8.81MPa). For MEP groups, SBU application did not significantly affect the results (p=0.41). The MEP group presented the highest Weibull modulus (4.08A) and they were statistically different exclusively from the HF20sSBU (0.58B). Conclusion: The HF 20s, 60s, 120 s followed by silane, promoted similar resin-bond strength to ceramic and the SBU application after HF or MEP did not increase the SBS.

Biaxial flexural strength of different types of monolithic zirconia / Resistência Flexural Biaxial de diferentes tipos de zircônia monolítica

Objective: This study was designed to evaluate the biaxial flexural strength (BFS) of different types of unshaded and shaded monolithic zirconia. Material and Methods: 120 monolithic zirconia ceramic discs were fabricated. They were divided into twelve groups (n=10), Group 1; Bruxzir unshaded, Group 2; Bruxzir shaded A2, Group 3; Bruxzir anterior white, Group 4; Bruxzir anterior shade A2, Group 5; Prettau unshaded, Group 6; Prettau shaded with A2 coloring liquid, Group 7; Prettau anterior white, Group 8; Prettau anterior shaded with A2 coloring liquid, Group 9; Katana HT white, Group 10; Katana HT shade A2, Group 11; Katana ST white, Group 12; Katana ST shade A2. All discs were milled using a dental milling machine, and had final dimensions after sintering of 15 mm diameter and 1 mm thickness. BFS was tested using piston on three ball technique. Results: One-way ANOVA revealed significant differences among the 12 groups. Tukey post-hoc tests revealed no significant differences between the groups 3, 4, ,7 ,8 11, and 12. However, they all had BFS values that are significantly lower than all other groups. Group 2 showed statistically significant higher BFS values when compared to group 3,4, 7, 8, 11, and 12 while it showed statistically significant lower values when compared to groups 1, 5, 6, 9, and 10. Conclusion: Increase in the yttria content in zirconia led to a decrease in its BFS. Shading of zirconia did not have a significant effect on the final strength of zirconia. (AU)

Objetivo: Este estudo foi desenhado para avaliar a resistência à flexão biaxial (RFB) de diferentes tipos de zircônia monolítica maquiada e não-maquiadas. Material e Métodos: 120 discos cerâmicos de zircônia monolítica foram fabricados. Eles foram divididos em doze grupos (n = 10), Grupo 1; Bruxzir Não-maquiado, Grupo 2; Bruxzir maquiado A2, Grupo 3; Branco anterior de Bruxzir, Grupo 4; Maquiagem anterior de Bruxzir A2, Grupo 5; Prettau não maquiado, Grupo 6; Prettau maquiado com corante A2, Grupo 7; Prettau anterior branco, Grupo 8; Prettau anterior maquiado com corante A2, Grupo 9; Katana HT branco, Grupo 10; Katana HT maquiagem A2, Grupo 11; Katana ST White, Grupo 12; Katana ST maquiagem A2. Todos os discos foram fresados em uma fresadora dentária e tiveram suas dimensões finais após sinterização de 15 mm de diâmetro e 1 mm de espessura. A RFB foi testado usando pistão na técnica de três bolas. Resultados: One-way ANOVA revelou diferenças significativas entre os 12 grupos. Os testes post-hoc de Tukey não revelaram diferenças significativas entre os grupos 3, 4, 7, 8 11 e 12. No entanto, todos eles exibiram valores de RFB significativamente menores do que todos os outros grupos. O Grupo 2 apresentou valores estatisticamente significantes de ICS mais elevados quando comparado aos grupos 3,4, 7, 8, 11 e 12, enquanto apresentou valores estatisticamente significantes menores quando comparados aos grupos 1, 5, 6, 9 e 10. Conclusão: o aumento do conteúdo de ítria na zircônia levou a uma diminuição em sua RFB. A maquiagem da zircônia não teve um efeito significativo sobre a resistência final da zircônia. (AU)

Polishing of ground y-tzp ceramic is mandatory for improving the mechanical behavior

Abstract It evaluated the effect of aging by Low Temperature Degradation (LTD), executed after post- processing surface treatments (polishing, heat treatment and glazing), on the surface characteristics (micromorphology and roughness) and on the structural stability (phase transformation and mechanical behavior-flexural strength and structural reliability) of a ground yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramic. Discs of Y-TZP (VITA In-Ceram YZ) were manufactured (ISO:6872-2015; 15 mm in diameter and 1.2 ± 0.2 mm in thickness) and randomly assigned into 10 groups according two factors: "aging" in 2 levels (with or without) and "surface treatment" in 5 levels (Ctrl: as-sintered; Gr: grinding with coarse diamond bur; Gr + HT: grinding plus heat treatment; Gr + Pol: grinding plus polishing; Gr + Gl: grinding plus glazing). Roughness (n=30), biaxial flexural test (n=30), phase transformation (n=2), and surface topography (n=2) analyses were performed. Aging led to an intense increase in monoclinic (m) phase content for all the tested conditions, being the as-sintered samples (Ctrl= 65.6%) more susceptible to the t-m phase transformation. Despite of increasing the m-phase content, aging was not detrimental for characteristic strength (except to the grinding condition). There was no significant reduction in the Weibull modulus after surface treatments. Additionally, heat treatment and glazing after grinding led to a decrease in characteristic strength, while polishing presented the highest characteristic strength values. Thus, polishing is mandatory after grinding the Y-TZP ceramic, while performing glazing or heat-treatment alone after grinding lead to the worst mechanical performance.

Resumo Este estudo avaliou o efeito do envelhecimento através da degradação a baixas temperaturas (low temperaturare degradation - LTD) após a realização de tratamentos de superfície pós- sinterização (polimento, tratamento térmico e glaze) nas características superficiais (micromorfologia e rugosidade), e na estabilidade estrutural (transformação de fase e comportamento mecânico - resistência flexural e confiabilidade estrutural) de uma cerâmica de zircônia tetragonal policristalina estabilizada por ítria (Y-TZP) desgastada. Discos de cerâmica Y-TZP (VITA In-Ceram YZ) foram confeccionados (ISO:6872-2015; 15mm de diâmetro e 1,2 ± 0,2mm de espessura) e randomicamente divididos em 10 grupos de acordo com dois fatores: "envelhecimento" (com e sem) e "tratamento de superfície" (Ctrl - sem tratamento; Gr - desgaste com ponta diamantada grossa; Gr + HT - desgaste mais tratamento térmico; Gr + Pol - desgaste mais polimento; Gr + Gl - desgaste mais glazeamento). Foram realizadas as análises de rugosidade (n=30), flexão biaxial (n=30), transformação de fase (n=2) e topografia de superfície (n=2). O envelhecimento levou a um aumento intenso no conteúdo de fase monoclínica (m) em todas as condições testadas, sendo observada uma maior susceptibilidade de transformação de fase t-m nas amostras do grupo controle (Ctrl= 65.6%). Apesar de provocar elevada transformação de fase, o envelhecimento não apresentou efeitos negativos nos desfechos avaliados. Não houve redução significativa do módulo de Weibull após os tratamentos. Além disso, o tratamento térmico e o glaze após desgaste levaram a uma redução da resistência característica, enquanto que o grupo polimento apresentou o mais alto valor de resistência característica. O glaze e o tratamento térmico geraram o pior desempenho mecânico, portanto a realização do polimento após desgaste de uma cerâmica Y-TZP é obrigatória.

The surface treatment of dental ceramics: an overview

This review proposes to present some aspects of dental ceramics surface treatments, which involve the related physical and mechanical properties, as well as new technologies. The correct cementation of prosthetic restoration is essential for clinical success. However, the adhesive technique is a very recent procedure and clinicians should have a more detailed knowledge about the technique and related materials so that they can use them in their day-to-day clinical practice. Information about the the principles, indications and contraindications of adhesive cementation technique were obtained from the literature. The studies indicate that the adhesive system seems to be a valid option for fixed prosthesis cementation, since it has several advantages over conventional cementation method, especially in all-ceramic restorations. In clinical practice, the clinician should always keep in mind the characteristics of the material they are working with, so that they can select the best technique and the best cement for each clinical situation. Although more research is required in this field, there are no scientific reasons to contraindicate in routine practice.

Cerámica libre de metal terminada y caracterizada por pulido manual / Metal free ceramic finished and characterized by manual polishing

RESUMEN: La rehabilitación oral mediante prótesis libres de metal ha dado solución funcional y estética a diversas situaciones clínicas, sin embargo, coronas unitarias anteriores aún son consideradas un gran desafío estético. En ellas, al igual que en estructuras métalo-cerámicas, brillo y lisura superficial se obtienen comúnmente mediante glaseado. Esta técnica puede presentar algunas limitaciones para replicar características de superficie, especialmente en dientes con gran riqueza microanatómica. Caso: El objetivo es presentar la rehabilitación anterior unitaria mediante corona IPS E.max® terminada mediante pulido manual, logrando así ajustes clínicos, personalización microanatómica y una superficie suave y brillante, culminando con un resultado estético muy satisfactorio. Conclusiones: El acabado manual es un procedimiento ampliamente documentado, de fácil ejecución y bajo costo. Podría disminuir envíos repetidos al laboratorio protésico y así los efectos asociados a la sobrecocción cerámica, sin embargo, requiere conocimiento del tipo de cerámica a pulir y una aplicación sistemática.

ABSTRACT: Oral rehabilitation through metal free prosthetics has given functional and aesthetic solutions to various clinical conditions; nevertheless, single-tooth rehabilitation in the anterior region is still considered a major challenge. In these crowns as well as in metallo-ceramic structures, the finishing is obtained by the glazing technique. This technique could show some limitations to replicate the surface characteristics, especially in teeth with a rich micro-anatomy. Case Report: The aim is to present an anterior single-tooth rehabilitation with IPS E.max® crown, and its finishing by hand polishing technique, achieving clinical adjustments and customized surface anatomy, a smooth surface, excellent brightness and a very satisfactory aesthetic result. Conclusions: Manual finishing technique is well documented, easy to execute and with low cost. Eventually, it could decrease repeated laboratory shipments and so the associated effects of the over-cooking of ceramic; nevertheless it requires knowledge of the type of ceramic to polish and a systematic clinical protocol implementation.

Esthetic rehabilitation with zirconia on tooth and morse taper implant: case report / Reabilitação estética em zircônia sobre dente e implante cone morse: caso clínico

Among the ceramic materials used in dentistry, Zirconia presents the ideal opacity for cases where the clinical challenge is to neutralize the difference in the colors of the substrates. The "ceramic steel", so called by some authors, guarantees to Zirconia resistance and hardness similar to a metal, but with aesthetic advantages superior to the metal-ceramic restorations, which can exhibit exposure of the metal band over time. This article describes a complex rehabilitation treatment involving dental elements with different substrates: 11 - vital tooth with large crown damage; 21 ­ endodontically treated tooth and cast metal core; 22 - Morse taper implant. The selection of a completely zirconia-based ceramic system allowed masking the different conditions of substrates, so achieving the esthetic expectations. Moreover, considering the patient's high smile line, excellent gingival esthetics was obtained with an internal connection Morse taper implant associated with an individualized anatomic abutment.

Dentre os materiais cerâmicos utilizados na Odontologia, a Zircônia apresenta a opacidade ideal para os casos em que o desafio clinico é neutralizar a diferença nas cores dos substratos. O "aço cerâmico", assim chamado por alguns autores, garante à Zircônia resistência e dureza semelhantes a um metal, mas com vantagens estéticas superiores às restaurações metalocerâmicas, as quais podem apresentar exposição da cinta metálica ao longo do tempo. Este artigo descreve um tratamento reabilitador complexo, envolvendo elementos dentários com diferentes substratos: 11 - dente vital com ampla destruição coronária; 21 - dente com tratamento endodôntico e núcleo metálico fundido; 22 ­ ausente, reabilitado com implante do tipo cone morse. A seleção do sistema totalmente cerâmico à base de zircônia, permitiu mascarar as diferentes condições dos substratos atingindo as expectativas estéticas. Além disso, diante do sorriso alto gengivoso presente neste caso, a excelência na estética gengival foi obtida utilizando implante com conexão interna do tipo cone morse associado a um pilar anatômico individualizado.

Bond strength between a polymer-infiltrated ceramic network and a composite for repair: effect of several ceramic surface treatments

Abstract: The effects of several ceramic surface treatments on bond strength of a polymer-infiltrated ceramic network and resin composite as repair material were evaluated. CAD-CAM blocks of a polymer-infiltrated ceramic network (Vita Enamic) were sliced and subjected to aging process, followed by embedding in acrylic resin. The bonding/repair area was treated as follows (n = 30): C- without treatment; UA- universal adhesive application; FM- 10% hydrofluoric acid and silane application; OM-airborne-particle abrasion with aluminum oxide and silane application; RP- tribochemical silica coating; and CA- surface grinding and application of universal adhesive. Composite resin cylinders were made on the treated surface. Specimens from each group were assigned randomly to two subgroups (n = 15) considering storage condition: Baseline (shear tests after 48 hours) or Storage (tests after 6 months under distilled water). The treated surfaces were analyzed by goniometry, roughness, and SEM. Two-way ANOVA and 1-way ANOVA were applied to analyze the bond data and roughness / contact angle data, respectively, followed by Tukey's test (α = 5%). Surface treatments and storage conditions affected bond strengths (p < 0.01). Surface grinding (CA) followed by universal adhesive promoted the highest value of bond strength (14.5 ± 4.8 MPa for baseline, 8.5 ± 3.4 MPa for storage) and the roughest ceramic surface. Grinding with silicon carbide paper (simulating diamond bur) followed by the application of a universal adhesive system is the best option for repairing fractures of the polymer-infiltrated ceramic network.

In vitro analysis of dental ceramics: evaluation of the radiopacity and chemical composition by Raman spectroscopy / Análise in vitro de cerâmicas odontológicas: avaliação da radiopacidade e composição química por espectroscopia Raman

Objective: This study compared the radiopacity of different ceramic systems by means of digital radiographs and evaluate the chemical composition of the samples by Raman spectroscopy. The hypothesis tested was that there was a difference in radiopacity among the tested materials. Material and Methods: Specimens were prepared for each ceramic tested: FLD - VM7 (VITA Zahnfabrik), LD - IPS Empress e.max Press (IPS Empress), AL - In Ceram Alumina (VITA Zahnfabrik), ALYZ - In Ceram Zirconia (VITA Zahnfabrik), YZ - Lava All Ceram (3M/ESPE), and MYZ - Zirconzahn (Talladium Brazil). The specimens were radiographed and submitted to radiographic density readings using a histogram tool. The spectrometer coupled to a petrographic microscope was used for Raman spectroscopy measurements. Analysis of variance (ANOVA) and a Tukey post-hoc test were used to compare radiopacity of the different materials. Results: For all tested materials, the radiopacity showed statistically significant differences, except YZ and MYZ. Lava All Ceram and ZirkonZahn had high radiopacity values and VM7 and IPS Empress e.max Press showed lower radiopacity than human dental structures. Conclusion: It was possible to conclude that radiopacity is closely linked to ceramic chemical composition. (AU)

Objetivo: Este estudo comparou a radiopacidade de diferentes sistemas cerâmicos por meio de radiografias digitais e avaliou a composição química das amostras por espectroscopia Raman. A hipótese testada foi que haveria diferença na radiopacidade entre os materiais testados. Material e Métodos: Os espécimes foram preparados para cada cerâmica testada: FLD - VM7 (VITA Zahnfabrik), LD - Impressora IPS Empress e.max (IPS Empress), AL - Em Ceram Alumina (VITA Zahnfabrik), ALYZ - In Ceram Zirconia (VITA Zahnfabrik), YZ - Lava All Ceram (3M / ESPE) e MYZ - Zirconzahn (Talladium Brasil). Os espécimes foram radiografados e submetidos a leituras de densidade radiográfica utilizando uma ferramenta de histograma. O espectrômetro acoplado a um microscópio petrográfico foi utilizado para medidas de espectroscopia Raman. Análise de variância (ANOVA) e teste post-hoc de Tukey foram usados para comparar a radiopacidade dos diferentes materiais. Resultados: Para todos os materiais testados, a radiopacidade apresentou diferenças estatisticamente significantes, exceto YZ e MYZ. Lava All Ceram e ZirkonZahn apresentaram altos valores de radiopacidade e o VM7 e o IPS Empress e.max Press apresentaram menor radiopacidade do que as estruturas dentais humanas. Conclusão: Foi possível concluir que a radiopacidade está intimamente ligada à composição química da cerâmica. (AU)

Crystal Modification on Lithium Disilicate Glass Ceramics Sintered Using Microwaves / Modificación de Cristales de Cerémicas de Vidrio de Disilicato de Litio Sinterizadas con Microondas

ABSTRACT: Microwaves are an interesting alternative to process dental ceramics. It is well documented that Microwave Hybrid Sintering (MHS) allows important savings in time and energy consumption. However, little is known about its effect on lithium disilicate glass ceramics, a popular material in dentistry today. We analyzed the microstructure of lithium disilicate glass ceramics sintered with MHS compared with conventional sintering. We sintered lithium disilicate glass ceramics using MHS and conventional furnaces, and we analyzed the samples using X-Ray diffraction and SEM. Samples sintered with MHS showed an increased crystalline phase, with an increased number of crystals. These crystals have larger perimeters compared with samples sintered in conventional furnaces. MHS produced a different crystallization pattern and crystal/ matrix ration in lithium disilicate glass ceramics when compared to conventional sintering. This can be associated with the improved mechanical properties of these materials reported previously.

RESUMEN: Las microondas son una interesante alternativa para procesar cerámicas dentales. Está bien documentado que el Sinterizado Híbrido por Microondas (MHS) permite ahorros importantes de tiempo y energía. Sin embargo, poco se ha publicado respecto a sus efectos en cerámicas de disilicato de litio, un material bastante popular en odontología en estos días. En este artículo analizamos la micro estructura de cerámicas de disilicato de litio sinterizada con MHS comparada con el sinterizado convencional. Sinterizamos muestras de cerámicas de disilicato de litio usando MHS y hornos convencionales, y analizamos las muestras usando difracción de rayos X y SEM. Las muestras sintetizadas usando MHS tienen una mayor fase cristalina, con mayor número de cristales. Estos cristales tienen además perímetros mayores, comparados con las muestras sinterizadas en hornos convencionales. MHS produce patrones de cristalización y proporción de cristal/matrix diferentes a las producidos por sinterizado convencional. Esto puede asociarse a las mejoras en propiedades mecánicas reportadas previamente.

Efecto de un tratamiento experimental de una superficie sobre la resistencia flexural en una zirconia Y-TZP / Effect of an experimental surface treatment on Y-TZP zirconia flexural strength

RESUMEN Objetivo: Analizar el efecto del microgranallado superficial como tratamiento experimental de regeneración, en la resistencia flexural y esfuerzos residuales de una Zirconia Y-TZP, una vez ha sido alterada con otros tratamientos mecánicos como microarenado y fresado. Métodos: Un total de 75 probetas de Zirconia Y-TZP fueron divididas en cinco grupos n=15 y sometidas a tratamientos de superficie así: fresado y microarenado (Grupos 2 y 4) microarenado + microgranallado y fresado + microgranallado (Grupos 3 y 5), y comparadas con un grupo control (Grupo 1), mediante Difracción de Rayos X (DRX), Microscopía electrónica de barrido (SEM), Microscopía confocal (CLSM) y sometida a falla en máquina universal de ensayos. Resultados: Los grupos de microgranallado y microarenado presentaron un aumento significativo de la resistencia flexural p=0.0082 con relación al grupo de fresado. Las mediciones mediante DRX no mostraron relación estadística con los cambios en la resistencia flexural. Significancia: Es posible que el microgranallado se considere un tratamiento para regenerar las propiedades mecánicas reducidas por fresado o arenado en la Zirconia Y-TZP.

ABSTRACT Objective: To analyze the effect of surface micro shot peening as an experimental regeneration treatment on the flexural strength and residual stresses of a Y-TZP Zirconia, once it has been altered with other mechanical treatments such as micro sandblasting and milling. Methods: A total of 75 Zirconia Y-TZP specimens were divided into five n = 15 groups and subjected to surface treatments such as: milling and micro sandblasting (Groups 2 and 4) micro sandblasting + micro shot peening; and milling + micro shot peening (Groups 3 and 5), compared to a control group (Group 1), by X-ray diffraction (XRD), scanning electron microscopy (SEM), confocal microscopy (CLSM) and subjected to failure in a universal testing machine. All the results were compared to find a statistical relationship between them using a mixed linear model and Tuckey. Results: The groups of micro shot peening and micro sandblasting presented a significant increase of the flexural strength p = 0.0082 vs the milling group. The XRD technique is not related to flexural strength measurements. Significance: It is possible that the micro shot peening be considered a treatment to regenerate the mechanical properties reduced by milling or sandblasting in Zirconia Y-TZP.