The Medical Journal of Malaysia ; : 25-26, 2004.
Artigo em Malaiala | WPRIM | ID: wpr-629920

RESUMO

The aim of this study was to evaluate the effect of powder-to-liquid ratio on the glass transition temperature (Tg) and the tensile properties of denture base material prepared from poly (methyl methacrylate) (PMMA) and hydroxyapatite (HA) previously treated with 3-trimethoxysilylpropyl methacrylate (gamma-MPS). Specimens for mechanical testing were prepared by adding composites powder (PMMA, BPO and HA) to the monomer (MMA and EGDMA) followed by hand mixing as in dental laboratory description usage. The glass transition temperature was studied by using differential scanning calorimetry (DSC). It was observed that the tensile properties and the Tg were affected by the powder-to-liquid ratio. The mechanical characterization of the materials were performed by using single edge notch-tension (SEN-T) specimens; the fracture toughness was slightly higher in formulation which contained HA filler compared to commercial denture base material.


Assuntos
Fenômenos Biomecânicos , Varredura Diferencial de Calorimetria , Bases de Dentadura/normas , Durapatita , Teste de Materiais , Microscopia Eletrônica de Varredura , Polimetil Metacrilato , Resistência à Tração
2.
The Medical Journal of Malaysia ; : 75-6, 2004.
Artigo em Malaiala | WPRIM | ID: wpr-629763

RESUMO

Hydroxyapatite (HA) has been earmarked as suitable for implantation within the human of its chemical makeup to human bone. In this paper, HA powders were synthesized via the precipitation method where phosphoric acid (H3PO4) was titrated into calcium hydroxide solution [Ca(OH)2]. Two parameters such as temperature and stirring rate were identified as factors that influenced the amount and purity of HA powder. Phase identification of the synthesized powder was done using X-Ray Diffraction (XRD). The results show that HA phase can be synthesized from this titration process of Ca(OH)2 and H3PO4 with yield amount of HA powder around 45 - 61 grams but with less than hundred percent purity. In order to study the effect of heat treatment to HA crystals structure, HA powder was calcined at 850 degrees C for 2 hours. It's found that the degree of crystallinity increases after calcination because of lattice expansion when the materials were heated at higher temperature


Assuntos
Pós , Durapatita , Precipitação Química