A new approach for Y-TZP surface treatment: evaluations of roughness and bond strength to resin cemen

Abstract Objective This study aims to evaluate the effect of sonochemical treatment on the surface of yttria-stabilized tetragonal zirconia (Y-TZP) before and after the final sintering. Material and Methods Twenty-eight Y-TZP discs were divided into four groups (n=7), according to surface treatment: PRE: pre-sintering sonication with 30% nominal power for 15 min; POS: post-sintering sonication with 30% nominal power for 15 min; JAT: air abrasion with 50-μm alumina particles; and CON: control group with no treatment. The POS and JAT groups were sintered before sonication and the PRE group after sonication. Surface roughness was analyzed using confocal microscopy, after which resin cement cylinders were placed on the surface of the Y-TZP discs and subjected to mechanical microshear bond strength test until fracture. Surface roughness and microshear bond strength values underwent ANOVA and the Tukey tests. Results The surface roughness values for the PRE group (299.91 nm) and the POS group (291.23 nm) were not significantly different (p≥0.05), statistically, and the surface roughness value of the JAT group (925.21 nm) was higher than those of PRE and POS (p=0.007) groups. The mechanical microshear bond strength test showed that there was no statistically significant difference between the groups (p=0.08). Conclusions Therefore, the results showed that sonochemical treatment modifies the Y-TZP surface and is similar to the well-established sandblasting surface treatment regarding the strength of the bond with the resin cement.

Understanding the interaction of resin composite with light for predictable aesthetic results in anterior teeth: A case report / Compreensão da interação das resinas compostas com a luz para resultados estéticos previsíveis em dentes anteriores: Relato de caso

This case report illustrates a conservative technique for reintervention on anterior composite restorations in a young patient with composite veneers. The treatment incorporated the use of photos and digital planning to establish a harmonious smile design. In order to conserve the dental tissues, existing resin composites restorations in maxillary anterior teeth were carefully removed to minimize enamel reduction, followed by a study of color and shade of teeth considering factors such as hue, chroma, luminosity, opacity, translucency and light effects. Eight direct veneers were built up with resin composite taking the optical properties of the material into account and their influence on the thickness of the layers that create specific light effects when superimposed on each other. To obtain excellent results with a predictable working protocol, nanohybrid composite systems facilitate good aesthetics, avoiding more invasive treatment in an economic manner.(AU)

O presente relato de caso ilustra uma técnica conservadora para a re-intervenção em restaurações diretas de resina composta em pacientes jovens. O tratamento consistiu em fotos e planejamento digital para obtenção de um desenho digital do sorriso individual e harmonioso. De acordo com os princípios de máxima conservação da estrutura dentária, as restaurações existentes nos dentes superiores anteriores foram criteriosamente removidas para minimizar a redução do esmalte, seguido do estudo de cor e sombra dos dentes considerando fatores como matiz, croma, valor, opacidade, translucidez e efeitos de luz. Oito facetas diretas foram realizadas em resina composta considerando as propriedades ópticas do material e a influência destas na espessura das camadas de resina para criar efeitos de luz singulares quando sobrepostas. Para a execução de uma odontologia estética e consciente, em associação a um protocolo de trabalho previsível, os sistemas de resinas compostas nanohibridas possibilitam resultados estéticos satisfatórios, evitando tratamentos mais invasivos de maneira economicamente viável.(AU)