Mechanical properties of composites as functions of the syringe storage temperature and energy dose

Objective: To investigate the mechanical properties of different classifications of composites indicated for posterior application as functions of the storage condition and of the energy dose. Material and Methods: Specimens (8x2x2 mm) were obtained according to the factors: I) Composites (3M ESPE): Filtek P60, Filtek Z350XT, and Filtek Silorane; II) Syringe storage conditions: room temperature, aged, oven, refrigerator, and freezer; and III) Energy dose: 24 J/cm2 and 48 J/cm2. After photoactivation, the specimens were stored at 37ºC for 24 h. After storage, a three-point bending test was carried out in a universal testing machine at 0.5 mm/min. Flexural strength (S) and flexural modulus (E) were calculated. Data were analyzed by three-way ANOVA and Tukey's test (α=0.05). Results: Different storage conditions significantly affected the silorane composite for S; conversely, no effects were noted in terms of E. The accelerated aging protocol significantly increased the S of Filtek P60 and Filtek Silorane, whereas storage in the oven significantly decreased the S for all of the composites tested. Filtek P60 was the only composite not affected by the lower storage temperatures tested for S, whereas for the silorane this parameter was impacted at the same conditions. The factor "dose" was not statistically significant. Conclusions: The syringe storage at different temperature conditions proved to influence mostly the flexural strength, a clinically important characteristic considering the posterior indication of the materials tested. The silorane composite should not be stored at lower temperatures. .

Fracture resistance of teeth restored with different resin-based restorative systems

The aim of the present study was to evaluate the fracture resistance of teeth restored with resin composite. Forty-eight maxillary premolar teeth were chosen and randomly divided to six groups: G1 (control): sound teeth; G2: MOD preparation, unrestored; G3: MOD + Adper Single Bond 2/P60; G4: MOD + Adper Easy One/P60; G5: MOD + P90 restorative system; G6: MOD + Adper Easy One/P90 Bond/P90. Specimens were subjected to compressive axial loading (0.5 mm/min). Flexural strength and the modulus of elasticity were also tested (n = 7). The only statistical equivalence with sound teeth was noted for G3 (p < 0.05). Flexural strength and the modulus of elasticity varied among the composites tested (n = 10). The reestablishment of the resistance to fracture in premolars subjected to Class II MOD preparations is restorative-system-dependent. The silorane restorative system is not able to recover the resistance to fracture.