RESUMO
INTRODUCTION: This study evaluated changes in the smile characteristics of patients with maxillary constriction submitted to rapid maxillary expansion (RME). METHODS: The sample consisted of 81 extraoral photographs of maximum smile of 27 patients with mean age of 10 years, before expansion and 3 and 6 months after fixation of the expanding screw. The photographs were analyzed on the software Cef X 2001, with achievement of the following measurements: Transverse smile area, buccal corridors, exposure of maxillary incisors, gingival exposure of maxillary incisors, smile height, upper and lower lip thickness, smile symmetry and smile arch. Statistical analysis was performed by analysis of variance (ANOVA), at a significance level of 5%. RESULTS: RME promoted statistically significant increase in the transverse smile dimension and exposure of maxillary central and lateral incisors; maintenance of right and left side smile symmetry and of the lack of parallelism between the curvature of the maxillary incisal edges and lower lip border. CONCLUSIONS: RME was beneficial for the smile esthetics with the increase of the transverse smile dimension and exposure of maxillary central and lateral incisors.
INTRODUÇÃO: esse estudo avaliou as alterações das características do sorriso de pacientes com atresia maxilar submetidos à expansão rápida da maxila (ERM). MÉTODOS: a amostra consistiu de 81 fotografias extrabucais do sorriso máximo de 27 pacientes, com idade média de 10 anos, antes da expansão e aos três e seis meses após a fixação do parafuso expansor. As análises das fotografias foram realizadas por meio do programa Cef X 2001, e as seguintes medidas foram analisadas: dimensão transversal do sorriso, corredores bucais, quantidade de exposição dos incisivos superiores, exposição gengival dos incisivos superiores, altura do sorriso, espessuras dos lábios superior e inferior, simetria e arco do sorriso. As alterações no sorriso durante as diferentes fases foram avaliadas por meio da análise de variância (ANOVA), seguida pelo teste de comparações múltiplas de Bonferroni, com nível de significância de 5%. RESULTADOS: a ERM promoveu aumento estatisticamente significativo da dimensão transversal do sorriso e da quantidade de exposição dos incisivos centrais e laterais superiores; manutenção da simetria entre os lados direito e esquerdo e da falta de paralelismo entre a curvatura das bordas dos incisivos superiores e a do lábio inferior. CONCLUSÃO: a ERM beneficiou a estética do sorriso com o aumento da dimensão transversal do sorriso e da quantidade de exposição dos incisivos centrais e laterais superiores.
RESUMO
Because a greater research effort has been directed to analyzing the adhesive effectiveness of self etch primers to dentin, the aim of this study was to evaluate, by microtensile testing, the bond strength to enamel of a composite resin combined with a conventional adhesive system or with a self-etching primer adhesive, used according to its original prescription or used with previous acid etching. Thirty bovine teeth were divided into 3 groups with 10 teeth each (n= 10). In one of the groups, a self-etching primer (Clearfil SE Bond - Kuraray) was applied in accordance with the manufacturer's instructions and, in the other, it was applied after previous acid etching. In the third group, a conventional adhesive system (Scotchbond Multipurpose Plus - 3M-ESPE) was applied in accordance with the manufacturer's instructions. The results obtained by analysis of variance revealed significant differences between the adhesive systems (F = 22.31). The self-etching primer (Clearfil SE Bond) presented lower enamel bond strength values than the conventional adhesive system (Scotchbond Multipurpose Plus) (m = 39.70 ± 7.07 MPa) both when used according to the original prescription (m = 27.81 ± 2.64 MPa) and with previous acid etching (m = 25.08 ± 4.92 MPa).
Assuntos
Animais , Bovinos , Condicionamento Ácido do Dente/métodos , Resinas Compostas/química , Colagem Dentária/métodos , Esmalte Dentário/química , Adesivos Dentinários/química , Adesividade , Análise de Variância , Lâmpadas de Polimerização Dentária , Teste de Materiais , Cimentos de Resina/química , Resistência à Tração , Fatores de TempoRESUMO
Com a grande busca pelo desenvolvimento das técnicas de polimerização das resinas compostas e dos sistemas adesivos, foram introduzidos no mercado os LEDs. Com base na literatura estudada, neste trabalho é avaliada a força de união da resina composta ao esmalte associado a um sistema adesivo convencional e a um sistema autocondicionante polimerizados por luz halógena e LED, por meio do teste de microtração. Os dentes bovinos foram divididos em 4 grupos com 10 dentes em cada um (n = 10), para aplicação do adesivo Scotchbond Multipurpose Plus (3M-ESPE) e do Clearfil SE Bond (Kuraray) conforme orientação do fabricante, ambos polimerizados por 10 s tanto pela luz halógena (Degulux Soft Start Degussa Hulls) com potência de 550 mW/cm2 como pelo LED (Kerr Demetron) com potência de 600 mW/cm2. A resina composta Filtek Z-250 foi aplicada em 4 incrementos de 1 mm com auxílio de uma matriz de silicona de condensação de formato quadrado com dimensões de 5 mm x 5 mm; sendo polimerizada tanto pela luz halógena como pelo LED por 40 s. O adesivo Scotchbond Multipurpose Plus polimerizado com luz halógena apresentou os maiores valores de adesão (39,69 ± 7,07 MPa) e os outros grupos não apresentaram diferença estatisticamente significante entre si: Scotchbond Multipurpose Plus polimerizado por LED (22,28 ± 2,63 MPa), Clearfil SE Bond polimerizado por luz halógena (27,82 ± 2,65 MPa) e por LED (22,89 ± 5,09 MPa).
Assuntos
Animais , Bovinos , Resinas Compostas/efeitos da radiação , Esmalte Dentário , Colagem Dentária/métodos , Luz , Cimentos de Resina/efeitos da radiação , Adesividade , Análise de Variância , Resinas Compostas/normas , Colagem Dentária/normas , Esmalte Dentário/química , Esmalte Dentário/efeitos da radiação , Halogênios , Polímeros , Cimentos de Resina/normas , Resistência à TraçãoRESUMO
Para isso, 120 dentes bovinos foram submetidos à raspagem coronária, inclusão em resina acrílica e desgaste com lixas de granulação crescente, expondo dentina superficial. O armazenamento foi em água destilada em estufa a 37 graus Celcious. Posteriormente, os corpos de prova foram armazenados por 1 semana em recipiente escuro e tracionados com auxílio da máquina de ensaios universal Mini lnstron 4442. Resultados: Quando os adesivos foram polimerizados com luz halógena, não houve diferença entre os três sistemas, porém quando polimerizados com laser de argônio por 10 segundos, os adesivos Scothbond Multipurpose Plus e Excite promoveram maior adesão que o One Bond. Conclusões: O laser de argônio quando utilizado para polimerização do adesivo promoveu maior adesão desde que a resina tivesse sido polimerizada com a luz halógena.