Influence of Sealer and Light-Curing Units on Push-Out Bond Strength Of Composite Resin to Weakened Roots

Abstract The aim of this study was to assess the influence of sealer and light-curing unit on regional bond strength of resin composite to the weakened roots. Ninety roots of incisors were experimentally weakened, subjected to biomechanical preparation and filled with either Endofill, AH Plus or MTA Fillapex The roots were desobturated e reinforced with resin composite and fiber post light-activated with one of the light sources: halogen at 600 mW/ cm2 (QTH-600), LED at 800 mW/ cm2 (LED-800) and LED at 1500 mW/ cm2 (LED-1500). The roots were sectioned in slices from cervical, middle and apical root-reinforcement regions and analyzed by push out test, scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). Bond strength data were analyzed using three-way ANOVA and Tukey´s test (α=0.05). Specimens filled with AH Plus had higher bond strength, followed by MTA Fillapex and Endofill (p<0.05). For light-curing unit, LED-1500 presented superior bond strength than LED-800, which was higher than QTH-600 (p<0.05). The cervical region had the greatest mean values (p<0.05) while apical part showed the lowest bond strength (p<0.05). CLMS revealed remaining filling material in the dentinal tubules for all groups. The eugenol-containing sealer (Endofill) compromised the push-out bond strength of composite resin to the root dentin. Bond strength was favored in the cervical region, and when LED-1500 was used.

Resumo O objetivo neste estudo foi avaliar a influência do cimento endodôntico e da fonte de luz fotoativadora na resistência de união (RU) regional da resina composta às raízes fragilizadas. Noventa raízes de incisivos foram experimentalmente fragilizados, submetidos ao preparo biomecânico e obturadas com Endofill, AH Plus ou MTA Fillapex. Os canais foram desobturados e reforçados com pinos de fibra de vidro e resina composta fotoativada com uma das fontes de luz: halógena a 600 mW/cm2 (QTH-600), diodo emissor de luz a 800 mW/cm2 (LED-800) e LED a 1500 mW/cm2 (LED-1500). As raízes foram seccionadas em slices provenientes dos terços cervical, médio e apical das regiões da raiz reforçada e analisadas por meio do teste de push out, microscopia eletrônica de varredura (MEV) e microscopia confocal de varredura a laser (MCVL). Os dados de resistência de união foram analisados por ANOVA a três critérios e teste de Tukey (α=0,05). Os espécimes obturados com AH Plus apresentaram maior resistência de união, seguido do MTA Fillapex e do Endofill (p<0,05). Para fonte de luz fotoativadora, LED-1500 apresentou resistência de união superior ao LED-800 que foi maior que QTH-600 (p<0,05). A região cervical obteve as maiores médias (p<0,05), enquanto que a região apical apresentou a menor resistência de união (p<0,05). MCVL revelou remanescente de material endodôntico nos túbulos dentinários para todos os grupos. O cimento contendo eugenol (Endofill) comprometeu a resistência de união da resina composta à dentina radicular. A resistência de união foi favorecida na região cervical, e quando o LED-1500 foi empregado.

Effect of Light Sources on the Bond Strength of Resin Material to Thin-walled Roots

The aim of this study was to evaluate the bond strength to the dentin of an adhesive material used for root reinforcement light activated with different sources. Roots were divided into 4 groups (n=15) according to the light source used to activate the resin reinforcement: GI, non-weakened roots (control); GII, halogen light (H) 600 mW/cm2; GIII, LED 800 mW/cm2 and GIV, LED 1500 mW/cm2. The reinforcement was done with adhesive, composite resin and fiberglass posts. After 24 h, the specimens were sectioned and the first slice of each post region was used in the push out test in a universal testing machine with a crosshead speed of 0.5 mm/min. Failure modes of the debonded specimens were examined. Data (MPa) were analyzed by ANOVA and Holm-Sidak test (=0.05). The second slice from each region was analyzed by scanning electron microscopy (SEM). LED-1500 (4.69 ± 1.74) provided bond strength similar to the control group (5.05 ± 2.63) and statistically different from H-600 (1.96 ± 0.94) and LED-800 (2.75 ± 1.90), which were similar to each other (p<0.05). Cervical (4.16 ± 2.32) and middle (4.43 ± 2.32) regions showed higher bond strength than the apical (2.25 ± 1.50) (p<0.05). There was a prevalence of adhesive failures in H-600 and LED-800 and cohesive failures in LED-1500. SEM showed the formation of long, numerous and fine tags. It was concluded that LED-1500 provided higher bond strength of resin reinforcement to the dentin.

O objetivo deste estudo foi avaliar a resistência de união à dentina de uma resina utilizada para reforço de raiz, ativada com diferentes fontes de luz. De acordo com a fonte de luz utilizada as raízes foram divididas em 4 grupos (n = 15): GI, raízes não fragilizadas (controle); GII, luz halógena (H) 600 mW/cm2; GIII, LED 800 mW/cm2 e GIV, LED 1500 mW/cm2. O reforço foi feito com adesivo, resina composta e pino de fibra de vidro. Após 24 h, os espécimes foram seccionados e o primeiro slice de cada região utilizado para o teste de união push out, na máquina de ensaios universais com 0,5 mm/min, e o tipo da falha avaliada. Os dados obtidos (MPa) foram analisados utilizando os testes de ANOVA e Holm-Sidak (=0.05). O segundo slice de cada região foi analisado por microscopia eletrônica de varredura (MEV). O LED-1500 (4.69 ± 1.74) proporcionou resistência a união similar ao controle (5.05 ± 2.63) e estatisticamente diferente do H-600 (1.96 ± 0.94) e LED-800 (2.75 ± 1.90), que são similares entre si (p<0.05). As regiões cervical (4.16 ± 2.32) e média (4.43 ± 2.32) apresentaram alta resistência à união quando comparadas à região apical (2.25 ± 1.50) (p<0.05). Houve uma predominância de falhas adesivas com as fontes de luzes H-600 e LED-800 e coesivas com o LED-1500. A análise em MEV demonstrou a formação de longos tags resinosos. Desta forma, pode-se concluir que o LED-1500 proporcionou maior resistência à resina utilizada para o reforço da dentina radicular.

The finite element methods on oral rehabilitation: new for endodontically treated teeth / O método dos elementos finitos na reabilitação oral: novas perspectivas para dentes tratados endodonticamente

Objective: The aim of this study is to present the applicability of Finite Element Analysis (FEA) in oral rehabilitation, especially in endodontically treated teeth, based on its indication, methods, advantages and limitations through a literature review. Material and Methods: The search was conducted on National Library of Medicine’s Pub Med, Google search and Science Direct databases including the keywords “finite element analysis”, “oral rehabilitation” and “endodontics”. Results: A total of 412 articles were found, 42 were carefully selected by two subject matter experts for discussion including 21 articles focusing on the applicability of FEA to endodontically treated teeth. Conclusion: The FEA is a versatile, low-cost and efficient approach for reliable evaluation of complex structures, as oral rehabilitation treatments.

Objetivo: O objetivo deste estudo é apresentar a aplicabilidade do Método dos Elementos Finitos (MEF) na reabilitação oral, especialmente em dentes tratados endodonticamente, destacando sua indicação, métodos, vantagens e limitações por meio de uma revisão de literatura. Material e Métodos: A busca foi realizada na Biblioteca Nacional de Medicina do PubMed, pesquisa Google e Science Direct, incluindo as palavras-chave: “análise de elementos finitos”, “reabilitação oral” e “endodontia”. Resultados: Um total de 412 artigos foram encontrados, sendo que 42 foram cuidadosamente selecionados por dois especialistas no assunto para a discussão e incluídos 21 artigos com foco na aplicabilidade do MEF para dentes tratados endodonticamente. Conclusão: O MEF é uma abordagem versátil, de baixo custo e eficaz para avaliação de estruturas complexas, como tratamentos de reabilitação oral.

Resistência à flexão em porcelana feldspática: efeito da ciclagem mecânica e limite de fadiga pelo método escada / Flexural strength of feldspathic porcelain: effect of mechanical cycling and fatigue limit by the staircase method

Este estudo avaliou o limite de fadiga (LF), determinado pelo método escada, e o efeito da ciclagem mecânica sobre a resistência à flexão (RF) da porcelana feldspática Duceragold. Corpos de prova (25 x 5 x 2 mm) foram confeccionados de acordo com as instruções do fabricante e submetidos ao ensaio de RF (n = 10), em três pontos. Para determinação do LF (n = 30), foram utilizados carregamento inicial de 60% da RF, tensão incremental de 3% da RF, 10.000 ciclos e 2 Hz. Os dados foram submetidos à Anova e teste de Tukey (p < 0,05). Embora os ciclos propostos não tenham reduzido estatisticamente a RF, análises fractográficas evidenciaram estrias, sinais característicos de fadiga mecânica.

This study evaluated the fatigue limit (FL) by the staircase method and the effect of mechanical cycling on the flexural strength (FS) of Duceragold feldspathic porcelain. Specimens (25 x 5 x 2 mm) were made according to manufacturer’s directions and submitted to t hree-point fl exural s trength t est (n = 10). To d etermine FL (n = 30; 10,000 cycles; 2 Hz), an initial loading of 60% of the FS and an incremental loading (step) of 3% of the FS were used. Data were analyzed by Anova and Tukey´s test (p < 0.05). Although the proposed cycles have not reduced FS significantly, fractography analysis showed striation, characteristic signs of mechanical fatigue.

Effect of thermal cycling on denture base and autopolymerizing reline resins

Objective This study evaluated the fracture toughness (FT) of denture base and autopolymerizing reline resins, with and without thermocycling (T). Material and Methods Specimens of each material (denture base acrylic resin - Lucitone 550 – L; autopolymerizing reline resins - Ufi Gel Hard–UH, Tokuyama Rebase II-TR, New Truliner–NT and Kooliner-K), were produced, notched and divided into two groups (n=10): CG (control group of autopolymerizing reline resins and L): FT tests were performed after polymerization; TG (thermocycled group): FT tests were performed after T (5°C and 55°C for 5,000 cycles). Results: Results (MPa.m1/2) were analyzed by two-way ANOVA and Tukey's test (p=0.05). L exhibited the highest FT mean values in both groups (CG - 2.33; TG - 2.17). For the CG groups, NT showed the highest FT (1.64) among the autopolymerizing reline resins, and K the lowest (1.04). After T, when the autopolymerizing reline resins were compared, a statistically significant difference in FT was found only between the NT (1.46) and TR (1.00). Conclusions Thermocycling increased the FT of K and did not influence the FT of L, UH, TR and NT. .

Avaliação in vitro da biocompatibilidade de resinas acrílicas para base de próteses e materiais reembasadores resilientes / In vitro biocompatilibility of denture base acrylic resins and soft reline materials

O objetivo deste estudo foi avaliar a citotoxicidade de 3 resinas acrílicas (RA) para bases de prótese sendo duas polimerizadas por energia de microondas (Vipi Wave-VW e Nature Cryl-NC) e uma fotoativada (Eclipse-E); e a biocompatibilidade de materiais reembasadores resilientes (MRR), sendo 2 à base de silicone (Ufi Gel P e Sofreliner S), 2 à base de resina acrílica (Durabase Soft e Trusoft) e 2 condicionadores de tecidos (Softone e Coe Comfort) por meio de análises do metabolismo celular, da morfologia celular, do padrão de morte celular, da proliferação celular e da expressão do fator de crescimento TGFß 1, da integrina α5ß1 e de citocinas. A análise das RA foi realizada com células L929; para os MRR, as análises foram realizadas utilizando-se células L929, e/ou HaCaT e/ou RAW 264,7. Os resultados obtidos foram submetidos à análise estatística, realizada ao nível de significância de 5%. Todos os materiais quando testados com eluatos não apresentaram efeitos citotóxicos, e quando testados em contato direto (MTT e azul de alamar) alteraram significativamente a viabilidade celular, tendo sido os menores valores observados para o material NC quando comparado ao E. Para os materiais reembasadores o T, S e C. Maior taxa de necrose e apoptose foram observadas para os eluatos de todos os materiais quando avaliados no período de 24 horas; além disso, foi demonstrado que os materiais avaliados podem desencadear a expressão do TGFß 1, da integrina α5ß1 e de proteínas inflamatórias (fator de necrose tumoral - TNF-α, da citocina IL-1ß e de 5 quimiocinas: CCL2, CCL3, CCL5, CXCL2 e CXCL4). Sendo assim, de acordo com as limitações do presente estudo, pode-se concluir que a resina Nature Cryl resultou em menor viabilidade celular que a resina Eclipse e que os materiais Ufi Gel P e Sofreliner S apresentaram, em geral, melhor bicompatibilidade dentre os materiais reembasadores resilientes avaliados

The aim of this study was to evaluate the cytotoxicity of 3 denture base acrylic resins with different polymerization methods (Eclipse, Vipi Wave and Nature Cryl) and the biocompatibility of soft lining materials, 2 silicone-based (Ufi Gel P and Sofreliner S), 2 acrylic-based (Durabase Soft and Trusoft) and 2 tissue conditioners (Softone and Coe Comfort), by analysing cell metabolism, cell morphology, pattern of cell death, cell proliferation and expression of growth factor TGFß 1, integrin α5ß1 and cytokines. For the acrylic resins, analyses were made with L929 cells, while for the resilient lining materials, analyzes were performed using L929, and/or HaCaT and/or RAW 264.7 cells. Results were statistically analyzed, at a significance level of 5%. The 24 and 48-h eluates from all materials were not cytotoxic to the cells. For the direct contact tests (MTT and Alamar Blue), a significant effect on cell viability was found, with the lowest values observed for materials NC when compared with E and between the reliners Trusoft, Softone and Coe Comfort. For all materials, increased rate of necrosis and apoptosis were observed for the 24 hs eluates. It was also demonstrated that all materials tested can trigger the expression of TGFß 1, α5ß1 integrin and inflammatory proteins (tumor necrosis factor -TNFα, cytokine IL-1ß and 5 chemokines- CCL2, CCL3, CCL5, CXCL2 and CXCL4). Thus, within the limitations of this study, it can be concluded that the denture base acrylic resin Nature Cryl resulted in lower cell viability compared to the Eclipse resin and that the materials Ufi Gel P and Sofreliner S showed better biocompatibility among the soft liner materials evaluated

A quantitative and qualitative evaluation of reports of clinical trials published in six Brazilian dental journals indexed in the Scientific Electronic Library Online (SciELO)

INTRODUCTION: Open access publishing is becoming increasingly popular within the biomedical sciences. SciELO, the Scientific Electronic Library Online, is a digital library covering a selected collection of Brazilian scientific journals many of which provide open access to full-text articles.This library includes a number of dental journals some of which may include reports of clinical trials in English, Portuguese and/or Spanish. Thus, SciELO could play an important role as a source of evidence for dental healthcare interventions especially if it yields a sizeable number of high quality reports. OBJECTIVE: The aim of this study was to identify reports of clinical trials by handsearching of dental journals that are accessible through SciELO, and to assess the overall quality of these reports. MATERIAL AND METHODS: Electronic versions of six Brazilian dental Journals indexed in SciELO were handsearched at www.scielo.br in September 2008. Reports of clinical trials were identified and classified as controlled clinical trials (CCTs - prospective, experimental studies comparing 2 or more healthcare interventions in human beings) or randomized controlled trials (RCTs - a random allocation method is clearly reported), according to Cochrane eligibility criteria. CRITERIA TO ASSESS METHODOLOGICAL QUALITY INCLUDED: method of randomization, concealment of treatment allocation, blinded outcome assessment, handling of withdrawals and losses and whether an intention-to-treat analysis had been carried out. RESULTS: The search retrieved 33 CCTs and 43 RCTs. A majority of the reports provided no description of either the method of randomization (75.3 percent) or concealment of the allocation sequence (84.2 percent). Participants and outcome assessors were reported as blinded in only 31.2 percent of the reports. Withdrawals and losses were only clearly described in 6.5 percent of the reports and none mentioned an intention-to-treat analysis or any similar ...

Resistência à flexão de porcelanas feldspáticas convencionais processadas por injeção / Flexural strength of heat-pressing feldspathic porcelains

O objetivo deste estudo foi investigar o efeito do processamento por injeção (método da cera perdida) na resistência à flexão, em três pontos, de porcelanas feldspáticas convencionalmente obtidas por sinterização. Foram avaliadas as porcelanas Ceramco-2, Duceragold, Duceram-Plus, Excelsior, Omega-900, Symbio, Vitadur-Alpha e VMK-95. Como controle, foi também utilizada a porcelana Cergogold, fornecida na forma de pastilhas pré-sinterizadas e processada exclusivamente por injeção. Corpos de prova em forma de barra (n = 10), com dimensões de 25 × 5 × 2 mm (ISO-6872), foram confeccionados em matrizes metálicas e processados, por sinterização ou injeção, nas temperaturas de cocção indicadas pelos fabricantes. Os ensaios foram realizados em equipamento MTS-810 (Material Test System, EUA), com célula de carga de 10 kN e velocidade de 0,5 mm.min-1. Os resultados, submetidos à análise de variância (p menor ou igual a 0,05), mostraram que o processamento por injeção foi capaz de proporcionar maior resistência à fexão para as porcelanas Duceram-Plus, Excelsior, Omega-900, Symbio e VMK-95 (p < 0,001). Nessa mesma condição experimental, a porcelana Cergogold mostrou-se estatisticamente superior apenas à porcelana Vitadur-Alpha, sendo inferior à porcelana Omega-900 e semelhante às demais (p < 0,001). A resistência à fexão das porcelanas Ceramco-2, Duceragold e Vitadur-Alpha não foi influenciada pelo processo de obtenção (p < 0,001).

The aim of this study was to evaluate the effect of injection process, on the three-point flexural strength on feldspathic ceramic, fabricated by sintering technique. The ceramics evaluated were Duceragold, Duceram Plus, Excelsior, Omega 900, Symbio,Vitadur Alpha, VMK 95 and Ceramco 2. Cergogold, that the processing technique is based on a conventional injection moulding, was used for control. The bar-shaped specimens (n = 10) with the size of 25 × 5 × 2 mm (ISO-6872) were fabricated in a metal mould and processed by injection or sinterized, according to manufacturing specifcations. The fexural test was performed in a MTS 810 testing machine (Material Test System, USA), with a 10 kN load cell and a crosshead speed of 0.05 mm.min-1. The data (MPa) were subjected to analysis of variance (p less than or equal to 0.05), and showed that the injection processed enhance the flexural strength of Duceram-Plus, Excelsior, Omega-900, Symbio and VMK-95 (p < 0.001). In this experimental condition, the ceramic Cergogold showed high value than Vitadur-Alpha, was inferior to the ceramic Omega-900, but there were no signifcant difference with the others (p < 0.001). The flexural strength was not influenced by the processing method for the ceramics Ceramco-2, Duceragold and Vitadur-Alpha.

Bond strength durability of self-etching adhesives and resin cements to dentin

OBJECTIVES: To evaluate the microtensile bond strength (µTBS) of one- (Xeno III, Dentsply) and two-step (Tyrian-One Step Plus, Bisco) self-etching adhesive systems bonded to dentin and cemented to chemically cured (C&B Metabond) or light-cured paste of a dual-cure resin cement (Variolink II, Ivoclar) within a short (24 h) and long period of evaluation (90 days). MATERIAL AND METHODS: Forty recently extracted human molars had their roots removed and their occlusal dentin exposed and ground wet with 600-grit SiC paper. After application of one of the adhesives, the resin cement was applied to the bonded surface and a composite resin block was incrementally built up to a height of 5 mm (n=10). The restored teeth were stored in distilled water at 37ºC for 7 days. The teeth were then cut along two axes (x and y), producing beam-shaped specimens with 0.8 mm² cross-sectional area, which were subjected to µTBS testing at a crosshead speed of 0.05 mm/min and stressed to failure after 24 h or 90 days of storage in water. The µTBS data in MPa were subjected to three-way analysis of variance and Tukey's test (α= 0.05). RESULTS: The interaction effect for all three factors was statistically significant (three-way ANOVA, p<0.001). All eight experimental means (MPa) were compared by the Tukey's test (p<0.05) and the following results were obtained: Tyrian-One Step Plus /C&B/24 h (22.4±7.3); Tyrian-One Step Plus /Variolink II/24 h (39.4±11.6); Xeno III/C&B/24 h (40.3±12.9); Xeno III/Variolink II/24 h (25.8±10.5); Tyrian-One Step Plus /C&B/90 d (22.1±12.8) Tyrian-One Step Plus/VariolinkII/90 d (24.2±14.2); Xeno III/C&B/90 d (27.0±13.5); Xeno III/Variolink II/90 d (33.0±8.9). CONCLUSIONS: Xeno III/Variolink II was the luting agent/adhesive combination that provided the most promising bond strength after 90 days of storage in water.

Avaliação mecânica das cerâmicas IPS-Empress 2 e In-Ceram Zircônia / Mechanical Evaluation of All-Ceramic IPS Empress 2 and In-Ceram Zirconia

O objetivo deste trabalho foi comparar a resistência à flexão em três pontos e a resistência à tração diametral do material de infra-estrutura dos sistemas cerâmicos IPS-Empress 2 (Ivoclar) e In-Ceram Zirconia (Vita). Para a realização do experimento, foram confeccionadas dez amostras de cada material para o ensaio de flexão (25mm x 5mm x 2mm)e 15 amostras para o ensaio de tração diametral (6mm x 3mm). Os testes foram realizados em equipamento MTS810 (Material Test System - EUA), com célula de carga de 10kN e velocidade de 0,5mm/minuto. Os resultados, após testes estatísticos de Mann-Whitney, mostraram que o In-Ceram Zirconia (434,17 MPa) apresentou maior resistência à flexão em relação ao IPS-Empress 2 (230,80 MPa). Entretanto, observou-se maior resistência à tração diametral doIPS-Empress 2 (175,41 MPa) em relação ao In-Ceram Zirconia (151,11 MPa). Pode-se concluir que a relação entre as duas propriedades não é a mesma para os materiais estudados e que a decisão pela indicação de um material não pode ser baseada em apenas uma propriedade mecânica.

Effect of ridge lap surface treatment and thermocycling on microtensile bond strength of acrylic teeth to denture base resins

This study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (µTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artificial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm² were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4ºC and 60ºC). µTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (α=0.05). There was no statisticaly significant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean µTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The µTBS of Biotone artificial teeth to the denture base acrylic resins was not influenced by the polymer type, surface treatment or thermocycling.

Este estudo avaliou o efeito do tipo de resina de base (termo-polimerizada e polimerizada por microondas), tratamento da superfície de união (com e sem aplicação de metil metacrilato) e termociclagem sobre a resistência adesiva à microtração (RAµT) do dente artificial Biotone. A superfície cervical dos dentes foi desgastada para se obter superfícies planas, as quais foram unidas a cada uma das resinas, constituindo os seguintes grupos (n=6): (G1a) Clássico/com MMA; (G1b) Clássico/sem MMA; (G2a) OndaCryl/com MMA; (G2b) OndaCryl/sem MMA. Corpos-de-prova retangulares com área transversal de 1 mm² foram preparados. Metade dos espécimes em cada grupo foi termociclado (5000 ciclos de 4ºC a 60ºC). O teste de resistência adesiva foi realizado numa máquina de ensaios universal (velocidade da carga: 1 mm/min). Os dados foram analisados estatisticamente por meio da ANOVA para 3 fatores (α=0,05). Os valores médios de RAµT e desvios-padrão foram: Termociclagem - G1a: 41,00 (14,00); G1b: 31,00 (17,00); G2a: 50,00 (27,00); G2b: 40,00 (18,00); Sem termociclagem - G1a: 37,00 (14,00); G1b: 43,00 (25,00); G2a: 43,00 (14,00); G2b: 40,00 (27,00). A RAµT entre os dentes artificiais e as resinas acrílicas para base de prótese não foi influenciada pelos fatores resina acrílica, tratamento de superfície ou termociclagem.

Avaliação in vitro da citotoxicidade de monômeros, plastificante e produtos de degradação liberados a partir de resinas para reembasamento imediato / In vitro cytotoxicity of monomers, plasticizer and degradation by-products released from hard chair side reline resin

O presente estudo teve como objetivo avaliar o efeito citotóxico dos monômeros isobutil metacrilato (IBMA) e 1,6 – Hexanediol dimetacrilato (1,6 – HDMA), do plastificante di-n-butil ftalato (DBP), e dos produtos de degradação ácido metacrílico (AM) e ácido benzóico (AB) sobre células L929. Esses compostos foram testados em faixas de concentrações liberadas, em um período de 30 dias, por materiais reembasadores rígidos, previamente quantificadas em estudos anteriores. O efeito citotóxico foi verificado por meio dos testes de MTT e 3H-timidina, após as células terem sido expostas às substâncias testadas nas concentrações estabelecidas. A classificação da citotoxicidade foi baseada na viabilidade celular em relação ao controle (células expostas ao meio sem as substâncias testadas). A atividade de síntese de DNA foi inibida por todos os compostos. Os resultados do presente estudo demonstraram que o teste de 3H-timidina foi mais sensível que o teste de MTT e que os compostos avaliados mostraram diferentes níveis de citotoxicidade in vitro. A atividade da desidrogenase mitocondrial diminuiu nas células tratadas com os monômeros, o plastificante e o produto de degradação AM; porém, para o AB, a maioria das concentrações testadas não apresentou efeito citotóxico.

The aim of this study was to evaluate the cytotoxic effect of the monomers 1,6 – hexanediol dimethacrylate (1,6 - HDMA) and isobutyl methacrylate (IBMA), the plasticizer di-n-butyl phthalate (DBP), and the degradation by-products methacrylic acid (MA) and benzoic acid (BA) on L929 cells. These compounds were tested in the range of concentrations released in 30 days from hard chairside reline resins that were quantified in previous investigations. Cytotoxic effects were assessed by using MTT and 3H - thymidine assays after the cells had been exposed to the test compounds at the given concentrations. Cytotoxicity was rated based on cell viability relative to controls (cells exposed to medium without test substances). The results presented in this study demonstrated that the 3H-thymidine assay was more sensitive than the MTT assay, and all compounds tested showed varying degrees of cytotoxic effect in vitro. DNA synthesis activity was inhibited by all compounds. Mitochondrial dehydrogenase activity decreased in cells treated with monomers, plasticizer and MA by-product, whereas no cytotoxic effect was observed on contact with BA at the majority of concentrations tested.

Prótese fixa em porcelana livre de metal: sistema IPS Empress II / Metal-free porcelain fixed prosthesis: IPS Empress II system

Atualmente, há tendência na utilização de próteses livres de metal, em função da busca de um tratamento com excelência estética. Este trabalho propôs abordar essa modalidade terapêutica e relatar a sequência de um caso clínico de prótese fixa posterior de 3 elementos (14, 15 e 16) confeccionada com a cerâmica IPS Empress II. Apresentar-se-á o tratamento de uma paciente, 39 anos, que procurou a clínica de prótese fixa (FOSJC - UNESP). Possui oclusão adequada e ausência de hábitos parafuncionais. Por este tratamento apresentar ausencia de margem metálica, biocompatibilidaee e resistência mecânica, proporciona um trabalho que atende às exigências estéticas e funcionais do paciente

Avaliação "in vitro" de materiais empregados no vedamento do terço cervical da obturação e assoalho da câmara pulpar / Evaluation \"in vitro\" of employed stuff in the vedamento of the cervical portion of the filling and floor of the chamber pulpar

O presente estudo testou “in vitro”, a capacidade vedante de três materiais em forma de película seladora, aplicada sobreo terço cervical das obturações e assoalho da câmara pulpar, imediatamente pós-obturação de canais radiculares, visandoprevenir a microinfiltração coronária, através da interface parede dentinária / material obturador do canal radicular.Utilizou-se de quarenta molares humanos com raízes completamente formadas, os canais radiculares instrumentadospela técnica de Oregon, irrigados com solução de hipoclorito de sódio a 0,5% e obturados pela técnica clássica decondensação lateral. Após a limpeza da câmara pulpar e das superfícies dentais, impermeabilizaram-se coroas e raízescom a utilização do esmalte para unhas incolor. Os dentes foram divididos aleatoriamente em quatro grupos de dezdentes, sendo um grupo controle e três grupos experimentais. Diferentes materiais foram aplicados sobre o assoalhoda câmara pulpar e terço cervical das obturações de cada grupo experimental: G1- Super Bonder; G2- Esmalte paraunhas; G3- Primer & Bonder 2.1; e G4- nenhum material foi aplicado. Logo após aplicação, os elementos dentáriosforam termociclados e imersos na tinta Nankin por um período de cinco dias. Em seguida foram então lavados, secose o esmalte para unhas aplicado superficialmente, removido. Os espécimes foram então descalcificados, desidratadose diafanizados sendo, posteriormente, examinados por três examinadores previamente calibrados. Os resultados, apóstestes estatísticos, segundo técnica descritiva e inferencial (Kruskal-Wallis e Comparação Pareada), determinaram quenão houve diferença estatisticamente significante entre os três materiais. Os produtos, esmalte para unhas e Super Bondermostraram-se estatisticamente superiores ao grupo controle.