RESUMO
To try to reduce the deleterious effects of tooth whitening, bioactive materials have been used. Forty enamel/dentin blocks were stained on dark tea and randomly assigned into four groups (n=10): control group (unbleached), HP35 % (35 % hydrogen peroxide), BG45S5 (Bioglass 45S5® incorporated into HP35 %), and BIO (Biosilicate® incorporated into HP35 %). Colorimetric analysis and microhardness evaluation was performed at baseline, 24 hours and 7 days after the final whitening session. Two-way ANOVA for repeated measures and Bonferroni test was used at a significance level of 5 %. All the coordinates (ΔL*, Δa*, Δb*, ΔE00 and WID) showed a difference between the control group and the experimental ones (p0.05), which suggest a color stability over a week. In contrast, after 7 days, the WID showed that control and PH35 % were different than the other groups (p 0.05). The microhardness did not change over time (p>0.05), except for 35 % HP. In conclusion Bioglass 45S5® and Biosilicate® prevented enamel damage without negatively affect the whitening efficacy.
Para intentar reducir los efectos nocivos del aclaramiento dental, se han usado materiales bioactivos. Cuarenta bloques de esmalte/dentina se tiñeron con té oscuro y se asignaron al azar en cuatro grupos (n=10): grupo de control (sin blanquear), HP35% (peróxido de hidrógeno al 35 %), BG45S5 (Bioglass 45S5® incorporado en HP35%) y BIO (Biosilicato® incorporado a HP35%). El análisis colorimétrico y la evaluación de la microdureza se realizaron al inicio del estudio, 24 horas y 7 días después de la última sesión de blanqueamiento. Se utilizó ANOVA de dos vías para medidas repetidas y la prueba de Bonferroni a un nivel de significancia del 5 %. Todas las coordenadas (ΔL*, Δa*, Δb*, ΔE00 y WID) mostraron diferencia entre el grupo control y el experimental (p0.05), lo que sugiere una estabilidad del color durante una semana. En cambio, a los 7 días, el WID mostró que el control y el PH35 % eran diferentes a los demás grupos (p 0.05). La microdureza no cambió con el tiempo (p>0.05), excepto para 35 % HP. En conclusión Bioglass 45S5® y Biosilicate® previnieron el daño del esmalte sin afectar negativamente la eficacia del blanqueamiento.
RESUMO
ABSTRACT: This clinical case described the aesthetic treatment of a patient complaining about the aspect of their upper teeth. After anamnesis and clinical examination, the association of tooth whitening photoactivated by violet LED and resin composite restorations was indicated. Prior to restorative treatment, three bleaching sessions were performed with low concentration hydrogen peroxide (6 %; Nano white flex) for 30 minutes. During this period, violet LED irradiation was intercalating performed every 1 minute, totalizing 15 minutes. Ten days after the final bleaching session, old restorations in the upper lateral incisors were removed for better color selection of resin composites. Then, all upper anterior teeth were directly restored with nanofilled resin composite (Filtek Z350XT), reestablishing anatomy, form, and function. At the end of the treatment, the association of techniques proved to be cost-effective, restoring the esthetics satisfactorily and promoting the patient's well-being by a minimally invasive approach.
RESUMEN: En este reporte de caso se describió el tratamiento para una paciente que se quejaba del aspecto de sus dientes superiores. Tras anamnesis y exploración clínica, se indicó la asociación de blanqueamiento dental fotoactivado por LED violeta y restauraciones de resina compuesta. Antes del tratamiento restaurador, se realizaron tres sesiones de blanqueamiento con peróxido de hidrógeno de baja concentración (6 %; Nano white flex) durante 30 minutos. Durante este período, la irradiación con LED violeta se intercalaba cada 1 minuto, totalizando 15 minutos. Diez días después de la última sesión de blanqueamiento, se retiraron las restauraciones antiguas de los incisivos laterales superiores para una mejor selección del color de la resina compuesta. Luego, todos los dientes anteriores superiores fueron restaurados de manera directa con resina de nanorrelleno (Filtek Z350XT), restableciendo la anatomía, forma y función. Al final del tratamiento, la asociación de las técnicas resultó beneficioso, restaurando la estética de forma satisfactoria y promoviendo el bienestar de la paciente mediante un abordaje mínimamente invasivo.