Evaluation of ceramic veneer adaptation by optical coherence tomography: a clinical report / Avaliação da adaptação de laminado cerâmico por tomografia de coerência óptica: relato de caso

Introduction: Ceramic veneers represent a treatment approach in aesthetic dentistry. They are indicated in cases of alterations in size, contour, form and color of the teeth. The clinical and radiographic examinations may not allow the correct identification of failures in the treatment with ceramic veneers. Objective: To report the use of Optical Coherence Tomography (OCT) for the evaluation and repair of an aesthetic oral rehabilitation involving ceramic veneers. Case report: A 24-year-old female patient complained of unsatisfied color change in the ceramic veneer placed on the right maxillary central incisor. The clinical examination showed color changes between the middle and incisal thirds of mesial surface of the tooth crown. The OCT sagittal images evidenced the presence of bubbles or gaps in the adhesive interface. The treatment consisted of repair of the restoration by infiltration of a composite resin. Conclusion: The OCT was found to be valid tool to evaluate the adaptation of the ceramic veneer placed on the maxillary central incisor (AU)

Introdução: Laminados cerâmicos representam uma abordagem de tratamento em Odontologia. São indicados em casos de alterações no tamanho, contorno, forma e cor dos dentes. O exame clínico e o emprego de radiografias convencionais podem não permitir a correta identificação de falhas no tratamento com laminados cerâmicos. Objetivo:Relatamos o uso da tomografia de coerência óptica (TCO) para avaliação da adaptação e reparo de uma reabilitação oral estética com laminados cerâmicos. Relato de caso:Paciente do sexo feminino, 24 anos, queixou-se de alteração de cor em laminado cerâmica cimentado no incisivo central superior direito. O exame clínico evidenciou alterações de cor entre os terços médio e incisal da superfície mesial do dente. As imagens obtidas por TCO mostraram a presença de bolhas ou gaps na interface adesiva da região. O plano de tratamento consistiu no reparo mediante infiltração de uma resina composta no local indicado pela TCO. Conclusão: A tomografia de coerência óptica se mostrou um método auxiliar eficaz para análise da adaptação do laminado cerâmico no incisivo superior direito. (AU)

Radiopacity of resin cements: in vitro study / Radiopacidade de cimentos resinosos: estudo in vitro

Objective: To evaluate the radiopacity of seven different resin cements, noting whether they are in accordance with the requirements of ANSI/ADA no. 27/1993 and ISO no. 4049/2000, comparing the conventional radiographic system with digital (phosphor plate). Methods: For each material, five samples were prepared that were irradiated and tested in both systems; the optical density of the cement and each step-wedge of the penetrometer were measured. From the resulting values, the equivalent for each mm of aluminum material was obtained.Results: We found the lowest values in AllCem-FGM, Joinville, Brazil (2.06 and 4.63 Eq mmAl), and the highest values in the Fill Magic Dual Cement-Vigodent, Rio de Janeiro, Brazil (4.03 and 9.20 mmAl eq). Through the F-test (ANOVA) with two factors, a significant difference was confirmed between the two system types (p <0.05) and between cements (p <0.05). On the other hand, the interaction between type of system and cement was not significant (p> 0.05). Through the Tukey test, a significant difference was found between the cement Fill Magic Dual Cement (Vigodent, Rio de Janeiro, Brazil) and each of the other cements: AllCem (FGM, Joinville, Brazil), Cement Post (Angelus, Londrina, Brazil), RelyX Unicem (3M ESPE, St. Paul, MN, USA), SET (SDI, Victoria, Australia), regardless of the system. Conclusion: All cements fell within the standards, where the AllCem (FGM, Joinville, Brazil) had the lowest value of radiopacity and Fill Magic Dual Cement (Vigodent, Rio de Janeiro, Brazil) the highest, irrespective of the type of system.

Objetivo: Avaliar a radiopacidade de sete cimentos resinosos diferentes, observando se os mesmos encontram-se de acordo com as normas da ANSI / ADA n. 27/1993 e ISO n. 4049/2000, comparando-se o sistema radiográfico convencional com o digital (placa de fósforo). Métodos: Para cada material confeccionaram-se cinco amostras, que foram irradiadas, e analisadas em ambos os sistemas, mediram-se a densidade óptica dos cimentos e de cada degrau do penetrômetro. A partir dos valores encontrados obteve-se o equivalente em milímetros de alumínio para cada material. Resultados: Constatou-se menores valores no AllCem-FGM, Joinville, Brasil (2,06 e 4,63 Eq mmAl), e maiores no Fill Magic Dual Cement-Vigodent, Rio de Janeiro, Brasil (4,03 e 9,20 Eq mmAl) . Através do teste F (ANOVA) com dois fatores se comprovou diferença significativa entre os dois tipos de sistema (p < 0,05) e entre os cimentos (p < 0,05). Por outro lado, a interação do tipo de sistema e cimento não se mostrou significativa (p > 0,05). Através do teste de Tukey se evidenciou diferença significativa entre o cimento Fill Magic Dual Cement (Vigodent, Rio de Janeiro, Brasil) com cada um dos cimentos: AllCem (FGM, Joinville, Brasil), Cement Post (Angelus, Londrina, Brasil), RelyX Unicem (3M ESPE, Saint Paul, EUA), seT (SDI, Victória, Austrália), independente do tipo de sistema.Conclusão: Todos os cimentos estavam dentro das normas, onde o AllCem (FGM, Joinville, Brasil) apresentou menores valores de radiopacidade e o Fill Magic Dual Cement (Vigodent, Rio de Janeiro, Brasil) os maiores, independente do tipo de sistema.