Acta odontol. venez ; 46(1): 15-19, mar. 2008. ilus, tab
Artigo em Espanhol | LILACS | ID: lil-630134

RESUMO

El fracaso en la adhesión de brackets es algo que ocurre frecuentemente y requiere el uso de un aditamento nuevo. Con la introducción del arenado, se pretende reutilizarlos sometiéndolos a un proceso de limpieza mejorando así la adhesión. El objetivo del estudio es comparar el esfuerzo a la tracción de brackets arenados mediante óxido de aluminio nuevo y reciclado con y sin ultrasonido. Se incluyeron 80 primeros y segundos premolares humanos dividido aleatoriamente en 5 grupos de 16 premolares: (C) brackets nuevos, (AN) brackets arenados con óxido de aluminio nuevo, (AN+U) arenado con óxido de aluminio nuevo más ultrasonido, (AR) arenado reciclado y (AR+U) arenado reciclado más ultrasonido. La adhesión se realizó con el mismo tipo de brackets y resina; el esfuerzo a la tracción se realizó mediante máquina Instrom. Se evidenció que los brackets AN aumentaron el esfuerzo a la tracción y esta se incrementó con el baño ultrasónico. Los brackets AR disminuyeron su esfuerzo a la tracción considerablemente, pero con ultrasonido mostraron valores cercanos al grupo C. La prueba t-student demostró que los grupos C vs. AN, AN vs. AN+U, y C vs. AR+U no tuvieron diferencias significativas. En cambio los grupos C vs. AN+U, C vs. AR, AN vs. AR, AN vs. AR+U, AN+U vs. AR+U mostraron diferencias significativas (p<0.05). Bajo las condiciones de este estudio se concluye que la mejor técnica de preparación de la base, es utilizando baño ultrasónico con etanol al 100 por ciento durante 5 minutos después de ser arenados con óxido de aluminio nuevo


Faults in the adhesion of brackets occur frequently and generally the use of a new bracket is required. With the introduction of the sanded technique it has been demonstrated that the brackets can be reused by subjecting them to a cleaning process, thereby improving adhesion. The objective of the study is comparer the tensile strength to the brackets sanded by means of new and recycled aluminum oxide, both with and without ultrasound. The assessment of tensile strength of the new and recycled base of brackets subjected to a sanding process of with new and recycled aluminum oxide in Instrom universal test machine of 80 first and second human premolars, divided in 5 groups of 16-piece: (C) used new brackets,  (AN) used new aluminum oxide  sanded brackets,  (AN+U) new aluminum oxide sanded plus ultrasound, (AR) recycled sanded, and (AR+U) recycled sanded plus ultrasound. The same type of brackets and adhesion system were used in all groups. It was demonstrated that the brackets AN increased the tensile strength and it increases even more when putting the attachments to an ultrasonic bath.  In the case of AR, their tensile strength diminished considerably, but when put under the ultrasonic bath, values were very close to those of the control group.  The t-student test, it was found that groups C vs. AN, AN vs. AN+U, and C vs. AR+U did not have significant statistical differences.  However, in groups C vs. AN+U, C vs. AR, AN vs. AR, AN vs. AR+U, AN+U vs. AR+U statistically significant differences were found. The tensile strength analysis allow concluding that the best preparation of the base technique is to use a bath in an ultrasound device with 100 percent ethylic alcohol for 5 minutes after being sanded with new aluminum oxide


Assuntos
Humanos , Óxido de Alumínio , Aparelhos Ortodônticos , Desenho de Aparelho Ortodôntico/instrumentação , Ortodontia/instrumentação , Ortodontia Corretiva
2.
Acta odontol. venez ; 40(1): 26-30, 2002. ilus, tab
Artigo em Espanhol | LILACS | ID: lil-317839

RESUMO

El propósito de este estudio fue evaluar el grabado del esmalte con ácido fosfórico al 37 por ciento en diferentes tiempos de aplicación en piezas con ápices inmaduro y maduro por medio de microscopía electrónica de barrido (MEB). Se incluyeron 40 premolares humanos de recientes extracción, 20 con ápice inmaduro y 20 con ápice maduro. Los especímenes fueron seccionados, grabados durante 15, 30, 45 y 60 segundos y analizados por medio de MEB. Los datos fueron evaluados con la prueba de J2 (chi cuadrado). Los resultados no revelaron diferencias significativas entre los dientes con ápice inmaduro y maduro al utilizar tiempos de 15, 30 y 45 seugndos, excepto en las piezas con ápice maduro tratados por 60 segundos donde encontramos los peores resultados (p<0.05). Bajo las condiciones de este estudio, concluimos que el grabado del esmalte en piezas con ápice maduro no debe de ser realizado clínicamente por períodos de 60 segundos


Assuntos
Ácidos Fosfóricos/química , Esmalte Dentário , Condicionamento Ácido do Dente/instrumentação , Condicionamento Ácido do Dente/métodos , Ápice Dentário/anatomia & histologia , Dente Pré-Molar , Distribuição de Qui-Quadrado , Estudo de Avaliação , Microscopia Eletrônica de Varredura/métodos , Fotomicrografia , Interpretação Estatística de Dados