Photoelastic evaluation of the effect of composite formulation on polymerization shrinkage stress

We compared polymerization stress in two commercial composites and three experimental composites made using camphorquinone (CQ) and/or phenylpropanedione (PPD) as photoinitiators. The internal surfaces of photoelastic resin discs with cylindrical cavities were roughened and treated with adhesive. Composites were divided into five groups: two commercial composites (Filtek Silorane and Filtek Z250) and three experimental composites with CQ/amine, CQ/PPD/amine, and PPD/amine. Composites were photopolymerized inside cavities, and subjected to photoelastic analysis immediately and at 24 hours and 7 days later using a plane polariscope. Stress created by Silorane (3.08 ± 0.09 MPa) was similar to that of Z250 (3.19 ± 0.13 MPa) immediately after photopolymerization (p > 0.05). After 24 hours and 7 days, Z250 (3.53 ± 0.15 and 3.69 ± 0.10 MPa, respectively) showed higher stress than Silorane (3.19 ± 0.10 and 3.16 ± 0.10 MPa, respectively). Qualitative analysis immediately after photopolymerization showed composite/CQ promoted higher stress than PPD, but stress levels at other evaluated times were statistically similar, varying between 3.45 ± 0.11 MPa and 3.92 ± 0.13 MPa. At 24 hours and 7 days, Silorane created the lowest stress. All photoinitiators created comparable tensions during polymerization.

Influence of sterilization method on the bond strength of caries-affected dentin

This study evaluated the effect of sterilization method on the bond strength of caries-affected dentin before artificial caries development and after restoration. Twelve bovine incisors were sectioned perpendicularly to their long axes at 7 mm from the amelodentinal junction. They were painted with acid-resistant nail varnish, except on an exposed coronal dentin area. Four groups were formed (n = 3) in accordance with the sterilization method used, before artificial caries development and after complete restoration: NE - no sterilization (control group); G - gamma-rays before and after; A - steam autoclave before and after; AG - steam autoclave before and gamma-rays after. For artificial caries development, dentin sections were immersed in BHI broth with S. mutans. After the soft carious tissue was removed, dentin was restored with Scotchbond Multi-Purpose and Filtek Z250. Next, the samples were sterilized in accordance with the methods described above and microtensile testing was performed. The data were analyzed by the Mann-Whitney test (p < 0.05). The G (22.7 MPa) and AG groups (16.3 MPa) were not statistically different from the NE group (17.5 MPa). Nevertheless, there were statistical differences between groups A (6.3 MPa) and NE, A and G, A and AG, G and AG. The bond strength of caries-affected dentin was not influenced by gamma-ray sterilization irrespective of whether the sterilization was performed before or after restoration.