RESUMO
This study assessed the bond strength of a resin cement when Immediate Sealed Dentin (ISD) was contaminated by different temporary cements applying a microshear test. Forty-eight fragments of third molar crowns were mounted in acrylic resin and worn until the dentin was exposed. The substrates were sealed with a 3-step conventional adhesive system and divided into four groups (n=12): Control (without temporary cement) and three groups that used different temporary cements - Provy, RelyX Temp NE, and Provitemp. The temporary cements were removed after 7 days of storage. Resin cement RelyX ARC was applied to the contaminated substrates. Microshear bond strength was evaluated using a universal testing machine (0.5 mm/min). Data was analyzed with ANOVA and a Dunnett post-hoc test (p<0.05). Additionally, three samples from each group were prepared for scanning electron microscope analysis. Means and standard deviations of microshear bond strength (MPa) were 17.96±1.65, 16.70±1.43, 20.43±1.30 and 33.75±4.72 for Control, Provy, RelyX Temp, and Provitemp, respectively. Statistically significant difference was observed between the Control and Provitemp samples (p=0.0002). Adhesive failures were dominant (50%), followed by cohesive failures with cement (26%), and cohesive failures with dentin (24%). Residues of Provy and Provitemp were observed on the sealed dentin. Provitemp temporary cement sealing increased the microshear bond strength of the resin cement on dentin treated with IDS.
Este estudo investigou a influência de cimentos temporários na resistência de união de um cimento resinoso em dentina selada imediatamente. Quarenta e oito fragmentos obtidos das coroas de terceiros molares foram incluídos em tubos de PVC com resina acrílica e desgastados até exposição da dentina. Os substratos foram tratados com adesivo convencional de três passos e divididos em quatro grupos: Controle (sem cimento temporário) e três grupos usando diferentes cimentos temporários Provy, RelyX Temp NE e Provitemp. Após sete dias, os cimentos foram removidos e o cimento RelyX ARC aplicado sobre o substrato contaminado. A resistência de união foi avaliada em uma máquina de ensaio universal (0,5 mm/min). Os dados foram analisados pelos testes estatísticos ANOVA e Dunnet (p<0,05). Três amostras de cada grupo foram preparadas para análise em micróscopio eletrônico de varredura. Os valores médios e desvio padrão da resistência de união foram 17,96 ±1,65, 16,70 ±1,43, 20,43±1,30 e 33,75 ±4,72 para Controle, Provy, RelyX Temp e Provitemp, respectivamente. Diferença significativa foi observada entre os grupos Controle e Provitemp (p=0,0002). Com relação ao padrão de fratura, a maioria das falhas foram adesivas (50%), seguida por coesiva em cimento (26%) e coesiva em dentina (24%). Resíduos dos cimentos Provy e Provitemp foram observados na dentina selada. Cimento temporário Provitemp aumentou a resistência de união por microcisalhamento do cimento resinoso a dentina com IDS.
Assuntos
Cimentos Dentários , Resistência ao Cisalhamento , Restauração Dentária Temporária , DentinaRESUMO
Background: The study of the phenomenon of fatigue is essential because implant failures usually are caused by this process. Purpose: The objective of this study was to examine the fatigue resistance of straight and anatomical abutments joints that were submitted to cyclic loads. Material and method: We used 37 Morse taper implants and 37 abutments, divided into two groups (n= 16: straight abutment, n= 21 anatomical abutment). The sets were submitted to cyclic loading (5 million) using servo-hydraulic equipment. Three sets from each group were subjected to bending tests to determine the maximum load resistance, which served as the parameter for comparison of the cyclic tests. We evaluated number of cycles, load and bending moment. Result: Of the 31 abutments cyclically tested, 17 (54.8%) fractured in fewer than 5 million cycles; 8 (25.8%) of these were straight abutments, and 9 (29%) were anatomical. A total of 14 samples (45.2%) resisted the cyclic loading. According to Fisher's exact test, there was no difference between groups as the fracture. Conclusion: Despite of the straight abutments have higher average load and bending moment on the anatomical, both types of abutments showed similar performance as the fracture strength in vitro.
Contexto: O estudo do fenômeno de fadiga é essencial porque as falhas de implantes geralmente são causadas por este processo. Objetivo: O objetivo deste estudo foi analisar a resistência à fadiga de conjuntos de pilares retos e anatômicos que foram submetidos a cargas cíclicas. Material e método: Foram utilizados 37 implantes cone Morse e 37 pilares, divididos em dois grupos (n = 16: pilares retos, n = 21: pilares anatômicos). Os conjuntos foram submetidos à carga cíclica (5.000.000) usando o equipamento servo-hidráulico. Três conjuntos de cada grupo foram submetidos a testes de flexão para determinar a resistência de carga máxima, o que serviu de parâmetro para comparação dos testes cíclicos. Foram avaliados número de ciclos, carga e momento de flexão. Resultado: Dos 31 pilares ciclicamente testados, 17 (54,8%) fraturaram em menos de 5 milhões de ciclos; 8 (25,8%) destes eram pilares retos, e 9 (29%) eram anatômicos. Um total de 14 amostras (45,2%) resistiu à carga cíclica. De acordo com o teste exato de Fisher, não houve diferença entre os grupos quanto à fratura. Conclusão: Apesar dos pilares retos terem maior carga média e momento de flexão que os anatômicos, os dois tipos de pilares apresentaram desempenho semelhante quanto a resistência à fratura in vitro.
Assuntos
Técnicas In Vitro , Implantes Dentários , Fenômenos Mecânicos , Resistência à FlexãoRESUMO
This study investigated removal of a force-closed stem, done in order to improve acetabular exposure during revision, with reinsertion afterwards. It is unknown how much this procedure modifies the stem/cement interface. METHODS: Three tapered stem models were implanted into composite femurs. Strain gauges were embedded in the medial aspect of the cement mantle and in several positions on the outer surface of the femurs. The deformation was measured during static loading, which was applied at two different times: after implantation and after one million loading cycles, followed by stem removal and reinsertion. The t test was performed. The differences in deformation were compared (at p ≤ 0.05) between the two static loading times and among the three stem designs. RESULTS: No significant differences in deformation were found after the two loading times for the three models. No significant differences in the initial deformations of the three models were found for most of the gauges attached to the femurs. CONCLUSIONS: Reinsertion of the force-closed stem does not alter the load transmission from the stem to the cement and to the surface of the femur, even after one million loading cycles.
Estudo da remoção de haste do tipo force-closed e a sua reinserção posterior para aumentar a exposição do acetábulo durante a revisão. Não é conhecido o quanto esse procedimento modifica a interface haste/cimento. MÉTODOS: Três modelos de hastes afiladas foram implantadas em fêmures compósitos. Extensômetros de deformação foram embebidos no aspecto medial do manto de cimento e em diversas posições sobre a superfície externa dos fêmures. As deformações foram medidas durante cargas estáticas, as quais foram aplicadas em dois diferentes momentos: após a implantação e após um milhão de ciclos de carga, seguido pela remoção e reinserção. O teste t foi feito. As diferenças entre as deformações foram confrontadas com p ≤ 0,05 entre os dois momentos de carga estática e entre os três projetos de hastes. RESULTADOS: Não foram encontradas diferenças significativas nas deformações após os dois momentos de carga para os três modelos. Não foram encontradas diferenças significativas nas deformações iniciais dos três modelos para a maioria dos extensômetros aderidos aos fêmures. CONCLUSÕES: A reinserção de haste do tipo force-closed não altera a transmissão de carga da haste para o cimento e para a superfície do fêmur, mesmo após um milhão de ciclos.
Assuntos
Humanos , Artroplastia de Quadril , Fenômenos Mecânicos , Desenho de PróteseRESUMO
Subtle differences in stem design can result in different mechanical responses of the total hip arthroplasty. Tests measuring migration of the stem relative to the femur, as well as the strains in the cement mantle and on the femur can detect different mechanical behavior between stems. Methods: In this article, conical, double and triple tapered stems were implanted in composite femurs and subjected to static and cyclic loads. Stems differed mainly on taper angle, calcar radius and proximal stiffness. Stem migration and strains on the femur and in the cement mantle were achieved. Results: Significant differences (p < 0.05) were noted in the permanent rotation between double and triple tapers, in the strains on the proximal medial femur between triple and both conical and double tapers, and in the strains on the lateral proximal femur between double tapers and both conical and triple tapers. Conclusion: The proposed mechanical tests were able to detect significant differences in the behavior of these resembling stems. Stem proximal stiffness and the calcar radius of the stem influence its rotational stability and the strain transmission to the femur.
Diferenças sutis no projeto da haste podem resultar em diferentes respostas mecânicas da artroplastia total do quadril. Testes que meçam a migração da haste em relação ao fêmur, bem como as deformações no cimento e no fêmur, podem salientar as diferenças entre diferentes projetos de hastes. MÉTODOS: Neste artigo foram implantadas hastes cônicas, hastes duplamente afiladas e triplamente afiladas em fêmures compósitos e submetidas a cargas estáticas e cíclicas. As hastes diferenciaram-se principalmente em relação aos afilamentos, ao raio do calcar e à rigidez proximal. A migração das hastes e as deformações tanto no fêmur quanto no cimento foram medidas. RESULTADOS: Foram observadas diferenças significativas (p < 0,05) na rotação permanente entre as hastes duplamente e triplamente afiladas, nas deformações do nível proximal medial do fêmur entre as hastes triplamente afiladas e ambas cônicas e duplamente afiladas e nas deformações do nível proximal lateral do fêmur entre as hastes duplamente afiladas e ambas cônicas e triplamente afiladas. CONCLUSÃO: Os ensaios mecânicos propostos foram capazes de produzir diferenças significativas no comportamento dessas hastes semelhantes. A rigidez proximal da haste e o raio do calcar influenciam a estabilidade rotacional e a transmissão de deformação da haste ao femur.
Assuntos
Artroplastia de Quadril , Fenômenos Biomecânicos , Desenho de PróteseRESUMO
Introdução: O cimento resinoso dual é o principal material para cimentação de cerâmicas. Contudo, fatores, como fonte de luz, podem influenciar no desempenho do cimento. Objetivo: Avaliar a influência de duas fontes de luz de diferentes intensidades sobre a microdureza de um cimento resinoso quando fotoativado sob diferentes cerâmicas. Material e método: Foram fotoativados 40 espécimes de cimento resinoso dual (10 mm × 1,0 mm) por meio de duas fontes de luz LED, com intensidades de 1.000 mW/cm² e 800 mW/cm² durante 40 segundos, sob cerâmicas (15 mm × 2 mm) à base de zircônia, espinélio MgAl2O4 e dissilicato de lítio. No grupo controle, foi utilizada uma placa de vidro de mesma dimensão. As amostras tiveram a superfície regularizada com lixa d`água (600 e 1200). Após armazenagem a seco no escuro (24 h), foram realizadas as medidas de microdureza Vickers (HMV Shimadzu - 50g/10 segundos). Os dados foram submetidos à Anova fatorial e ao teste de Tukey com nível de significância de 5%. Resultado: O cimento polimerizado apresentou valor médio de microdureza e desvio padrão para o grupo controle de 43,9±1,5 e 43,4±1,3, para as intensidades de 1.000 mW/cm2 e 800 mW/cm2, respectivamente. O menor valor de microdureza do cimento foi observado para a cerâmica à base de espinélio MgAl2O4, polimerizado a 800 mW/cm², com valor de 34,3±3,3.