RESUMO
ABSTRACT Objective: To investigate the effect of ZnO nanocoating on mechanical properties of NiTi orthodontic wires and antibacterial activity. Methods: 0.016 x 0.022-in NiTi orthodontic wires were coated with ZnO nanoparticles using an electrochemical deposition method with three electrodes system in 0.1M Zn(NO3)2. Mechanical properties and frictional resistance of the coated wires were investigated using an universal testing machine. Antibacterial effect of ZnO coating was also investigated. Results: A stable adhered ZnO nanocoating on NiTi wires was obtained. The coated wires have a significant antibacterial activity against S. aureus, S. pyogens and E. coli, and a reduction of frictional forces by 34%. Conclusion: ZnO nanocoating may improve the antibacterial effects of NiTi wires and reduce the frictional resistance. Coating may be implanted in orthodontic practice for faster and safer treatment.
RESUMO Objetivos: Avaliar o efeito do nanorrevestimento de óxido de zinco (ZnO) sobre as propriedades mecânicas e propriedades antibacterianas de fios ortodônticos de NiTi. Métodos: Fios 0,016" x 0,022" de NiTi foram revestidos com nanopartículas de ZnO por meio de um método de deposição eletroquímica com um sistema de três eletrodos a 0,1M Zn(NO3)2. Uma máquina universal de testes foi utilizada para avaliar as propriedades mecânicas e a resistência friccional dos fios revestidos. Além disso, também foram analisadas as propriedades antibacterianas do revestimento de ZnO. Resultados: Obteve-se uma aderência estável das nanopartículas de ZnO sobre os fios NiTi. Os fios revestidos apresentaram atividade antibacteriana significativa contra S. aureus, S. pyogens e E. coli, e apresentaram uma redução de 34% na força de atrito. Conclusão: O revestimento com nanopartículas de óxido de zinco pode melhorar as propriedades antibacterianas e reduzir a resistência friccional dos fios de NiTi. Assim, o revestimento dos fios pode ser utilizado na Ortodontia visando tratamentos mais rápidos e seguros.
Assuntos
Óxido de Zinco/farmacologia , Fios Ortodônticos , Staphylococcus aureus , Propriedades de Superfície , Titânio/farmacologia , Zinco , Teste de Materiais , Ligas Dentárias , Escherichia coli , Antibacterianos/farmacologia , NíquelRESUMO
ABSTRACT Objective: To qualitatively and quantitatively assess the color changes effect and the color stability of the resin infiltrant on white spot lesions (WSLs), in comparison with nano-hydroxyapatite (nano-HA) toothpaste and microabrasion. Methods: WSLs were artificially created on sixty human premolars enamel surfaces and randomly assigned to equal four groups (n = 15 each): nano-HA toothpaste, microabrasion (Opalusture), resin infiltrant (Icon) treatment, or artificial saliva (control group). The color change (ΔE) of each specimen was measured by dental spectrophotometer (Vita Easyshade) at different time points: baseline, after WSLs' creation, after application of treatments, one month, three and six months after treatments application. Results: The ΔE value did not differ significantly for the four groups at baseline measurement before treatment (p> 0.05). Icon resin infiltrant improved the color of WSLs significantly immediately after its application, giving the lowest ΔE value (3.00 ± 0.59), when compared to other treatments (p< 0.001). There were no significant changes in ΔE (p> 0.05) for all groups during the follow up intervals (one month, three and six months after treatments application). Conclusion: Resin infiltrant can improve the color of WSLs and restore the natural appearance of enamel better than nano-HA toothpaste and microabrasion.
RESUMO Objetivo: avaliar qualitativamente e quantitativamente os efeitos nas mudanças e estabilidade da cor de lesões de mancha branca (LMBs), após tratamento com infiltração de resina, em comparação aos tratamentos com pasta de dentes com nanopartículas de hidroxiapatita (Nano-HA) e com microabrasão. Métodos: As LMBs foram criadas artificialmente em 60 superfícies de esmalte dentário de pré-molares humanos e aleatoriamente divididas em quatro grupos (n=15, cada): pasta de dentes Nano-HA, microabrasão (Opalusture), tratamento com infiltração de resina (Icon) e saliva artificial (grupo controle). A mudança de cor (ΔE) de cada espécime foi aferida com um espectrofotômetro odontológico (Vita Easyshade) em diferentes tempos: início do estudo, após a criação das LMBs, após a aplicação dos tratamentos, um mês, três meses e seis meses após a aplicação dos tratamentos. Resultados: Os valores de ΔE não diferiram significativamente entre os quatro grupos ao início do estudo (p > 0,05). A infiltração com resina Icon melhorou significativamente a coloração das LMBs imediatamente após a sua aplicação, com o menor valor de ΔE (3,00 ± 0,59), quando comparada às outras modalidades de tratamento (p < 0,001). Não houve mudanças significativas nos valores de ΔE (p > 0,05) em qualquer um dos grupos durante os intervalos de acompanhamento (um mês, três meses e seis meses após a aplicação do tratamento). Conclusão: A infiltração de resina é capaz de melhorar a coloração das LMBs e restaurar a aparência natural do esmalte de forma superior à pasta de dentes com Nano-HA e à microabrasão.
Assuntos
Humanos , Cárie Dentária , Resinas Sintéticas , Espectrofotometria , Cor , Esmalte DentárioRESUMO
ABSTRACT Objective: To evaluate the effect of silica dioxide (SiO2) nanofillers in different bonding systems on shear bond strength (SBS) and mode of failure of orthodontic brackets at two experimental times. Methods: Ninety-six intact premolars were divided into four groups: A) Conventional acid-etch and primer Transbond XT; B) Transbond Plus self-etch primer; and two self-etch bonding systems reinforced with silica dioxide nanofiller at different concentrations: C) Futurabond DC at 1%; D) Optibond All-in-One at 7%. Each group was allocated into two subgroups (n = 12) according to experimental time (12 and 24 hours). SBS test was performed using a universal testing machine. ARI scores were determined under a stereomicroscope. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to determine the size and distribution of nanofillers. One-way ANOVA was used to compare SBS followed by the post-hoc Tukey test. The chi-square test was used to evaluate ARI scores. Results: Mean SBS of Futurabond DC and Optibond All-in-One were significantly lower than conventional system, and there were no significant differences between means SBS obtained with all self-etch bonding systems used in the study. Lower ARI scores were found for Futurabond DC and Optibond All-in-One. There was no significant difference of SBS and ARI obtained at either time points for all bonding systems. Relative homogeneous distribution of the fillers was observed with the bonding systems. Conclusion: Two nanofilled systems revealed the lowest bond strengths, but still clinically acceptable and less adhesive was left on enamel. It is advisable not to load the brackets immediately to the maximum.
RESUMO Objetivo: avaliar o efeito das nanopartículas de dióxido de silício (SiO2), presentes em diferentes sistemas adesivos, na resistência ao cisalhamento da colagem (RAC) e no modo de fratura de braquetes ortodônticos avaliados em dois momentos. Métodos: noventa e seis pré-molares intactos foram divididos em quatro grupos: A) condicionador ácido convencional e primer Transbond XT; B) primer autocondicionador Transbond Plus; e dois sistemas adesivos autocondicionantes reforçados com nanopartículas de dióxido de silício em diferentes concentrações, C) DC Futurabond a 1%; D) Optibond All-In-One a 7%. Cada grupo foi dividido em dois subgrupos (n = 12), de acordo com o tempo para realização do teste (12 e 24 horas). O teste da RAC foi realizado em uma máquina universal de ensaios. Os resultados do índice de adesivo remanescente foram determinados com um estereomicroscópio. Para determinar o tamanho e a distribuição das nanopartículas, utilizou-se microscopia eletrônica de varredura (MEV) e microscopia eletrônica de transmissão (MET). O ANOVA a um critério foi usado para comparar a RAC, seguido pelo teste post-hoc de Tukey. O teste qui-quadrado foi usado para avaliar os índices de adesivo remanescente. Resultados: a RAC média do Futurabond DC e do Optibond All-In-One foi menor do que a do sistema convencional, de forma estatisticamente significativa; e não houve diferença estatisticamente significativa entre os níveis médios de RAC obtidos nos sistemas adesivos autocondicionantes avaliados nesse estudo. Os menores índices de adesivo remanescente foram observados com o Futurabond DC e o Optibond All-In-One. Não houve, entre os sistemas adesivos, diferença significativa na RAC e nos índices de adesivo remanescente obtidos nos dois tempos de aplicação. Foi observada uma distribuição relativamente homogênea das partículas nos sistemas adesivos. Conclusão: os dois sistemas com nanopartículas demonstraram menor RAC, mas ainda aceitável e com o menor índice de adesivo remanescente no esmalte. É, assim, aconselhável não submeter os braquetes à carga máxima logo após a colagem.