Physical and chemical properties of orthodontic brackets after 12 and 24 months: in situ study

Objective: The aim of this article was to assess how intraoral biodegradation influenced the surface characteristics and friction levels of metallic brackets used during 12 and 24 months of orthodontic treatment and also to compare the static friction generated in these brackets with four different methods of the ligation of orthodontic wires. Material and Methods: Seventy premolar brackets as received from the manufacturer and 224 brackets that were used in previous orthodontic treatments were evaluated in this experiment. The surface morphology and the composition of the deposits found in the brackets were evaluated with rugosimetry, scanning electron microscopy, and energy dispersive X-ray spectroscopy. Friction was analyzed by applying tensile tests simulating sliding mechanics with a 0.019x0.025" steel wire. The static friction levels produced by the following ligation methods were evaluated: loosely attached steel ligature around all four bracket wings, steel ligature attached to only two wings, conventional elastomeric ligation around all 4 bracket wings, and non-conventional Slide® elastomeric ligature. Results: The results demonstrated the presence of biodegradation effects such as corrosion pits, plastic deformation, cracks, and material deposits. The main chemical elements found on these deposits were Carbon and Oxygen. The maximum friction produced by each ligation method changed according to the time of intraoral use. The steel ligature loosely attached to all four bracket wings produced the lowest friction levels in the new brackets. The conventional elastic ligatures generated the highest friction levels. The metallic brackets underwent significant degradation during orthodontic treatment, showing an increase in surface roughness and the deposit of chemical elements on the surface. Conclusion: The levels of static friction decreased with use. The non-conventional elastic ligatures were the best alternative to ...

Influência de diferentes cremes dentais na rugosidade e atrito dos braquetes ortodônticos / Influence of different toothpastes in roughness and friction of orthodontic brackets

Introdução: avaliar, in vitro, a rugosidade, a morfologia e os níveis de atrito oferecidos pelos braquetes antes e após a escovação com diferentes cremes dentais. Métodos: cento e dez braquetes metálicos foram aleatoriamente distribuídos em 11 grupos: 1 grupo controle (saliva artificial) e 10 grupos experimentais (n = 10). Após colagem dos braquetes em dispositivo específico, esses foram submetidos a três escovações diárias com diferentes tipos de cremes dentais durante um período de 28 dias. Os cremes dentais avaliados foram: Close Up Ação Profunda, Close Up Triple, Colgate Luminous White, Colgate Tripla Ação, Oral B Pró Saúde, Oral B Pró-Saúde Whiteness, Sensodine Fresh, Sensodine Original, Sorriso Fresh Plus e Sorriso Original. Entre as escovações, os braquetes foram lavados em água corrente e acondicionados em recipiente contendo saliva artificial e mantidos em estufa à temperatura de 37ºC. Para a avaliação da rugosidade foi utilizada microscopia eletrônica de varredura. As imagens obtidas foram avaliadas quantitativamente por meio de análise de imagem em histogramas. Os níveis de atrito foram medidos por uma máquina de dobramento. Os dados foram comparados estatisticamente por meio da ANOVA, utilizando o teste t de Student. Resultados: observou-se presença de ranhuras, sobretudo no grupo Colgate Luminous White. Houve diferenças estatísticas nos níveis de atrito entre os grupos Close Up Ação Profunda, Close Up Triple e Colgate Luminous White. Conclusão: o creme dental Colgate Luminous White apresentou maior rugosidade de superfície e maior nível de atrito; a menor rugosidade foi observada nos grupos Close Up Ação Profunda e Sorriso Fresh Plus.