RESUMO
ABSTRACT Tooth bleaching is one of the most conservative aesthetic techniques. At-home and in-office bleaching may be performed, as well as the combination of both techniques. As this combination may be done in different manners, distinct orders of combinations were proposed in this report. A 24 years-old man, whose upper central incisor and canine shades were A2 and A3 respectively, was initially treated by chair-side with 40-min application of 40% hydrogen peroxide (HP) for two sessions. Afterwards, an two-week overnight at-home bleaching was performed with 10% carbamide peroxide (CP). The shade of upper central incisors changed to 1M1 and canine was B1. Conversely, a 30 years-old woman was firstly conducted with at-home bleaching (overnight 4-weeks 10% CP) and, subsequently, with a single appointment of in-office bleaching for 45 minutes (35% HP). The shade of her upper central incisor changed from A1 to 0.5M1 and the upper canine from A3 to B1. The VITA classical (A1-D4) shade guide and VITA Bleached guide 3D-MASTER were used to determine the tooth color during the treatments. In both bleaching treatments, patients reported no significant tooth sensitivity and the final outcomes met their expectation.
RESUMO O clareamento dental é uma das técnicas estéticas mais conservadoras no âmbito odontológico. Técnicas de clareamento caseira ou de consultório, ou a combinação de ambas, podem ser realizadas para alcançar o prognóstico desejado. Esta combinação das técnicas pode ser realizada por meio de diferentes abordagens, como apresentado neste relato de casos. Um paciente do gênero masculino, 24 anos de idade, cujos incisivo central superior e caninos apresentaram cor A2 e A3, respectivamente, foi inicialmente submetido à técnica de clareamento de consultório de duração por sessão de 40 mim com gel de peróxido de hidrogênio (PH) 40%, em duas sessões. Posteriormente, a técnica de clareamento caseira foi realizada durante duas semanas com gel de peróxido de carbamida (PC) a uma concentração de 10%.A cor final dos incisivos centrais superiores foi alterada para 1M1, enquanto a dos caninos para B1. Por outro lado, uma paciente do gênero feminino, 30 anos de idade, foi inicialmente submetida ao clareamento caseiro (durante a noite, por 4 semanas- PC 10%), e subsequentemente, com aplicação pontual de agente clareador (PH 35%) em consultório, em sessão de 45 min. A cor do incisivo central superior da paciente, mudou de A1 para 0,5M1 e do canino superior de A3 para B1. As escalas de cor VITA Classic (A1-D4), e VITA Bleachedguided 3D-MASTER foram utilizadas nesta série de casos para determinar a coloração dos dentes durante os tratamentos. Em ambos os tratamentos, os pacientes não reportaram sensibilidade dental significante, e suas expectativas finais foram atendidas.
RESUMO
Objective: to evaluate the effect of aluminum oxide sandblasting (AOS), argon plasma application (APL) and their combination (AOS+APL) on the shear bond strength (SBS) of dual-cure resin cement (Panavia F 2.0, Kuraray Noritake) to two zirconia-based ceramics (Lava, 3M ESPE and Katana, Kuraray Noritake). Material and Methods: One hundred twenty zirconia plates (13 mm in length X 5 mm in width X 1 mm in thickness) were prepared and treated according to the following treatments: 1- AOS, 2- APL,3- AOS+APL and 4- no treatment (control). After treatments, resin cement cylinders (1.4 mm in diameter x 1 mm in height) bonded to zirconia surface were obtained by filling up the silicon matrix. The shear bond test was performed following storage of the samples for 24 hours and one year. Bond strength values were recorded in MPa and the data were analyzed by three-way ANOVA and Tukey post-hoc test (preset alpha of 0.05). Results: In general, AOS and AOS +APL showed the higher SBS. After one-year storage, SBS of the resin cement to the Katana zirconia did not reduce, regardless of the zirconia surface treatment. Conclusion: AOS alone was able to increase the SBS of the resin cement to both zirconia ceramics compared to control and SBS remained stable after one year depending on type of zirconia ceramic. (AU)
Objetivo: avaliar o efeito do jateamento de óxido de alumínio (AOS), aplicação de plasma de argônio (APL) e sua combinação (AOS + APL) na resistência ao cisalhamento (SBS) do cimento resinoso dual (Panavia F 2.0, Kuraray Noritake) a duas cerâmicas à base de zircônia (Lava, 3M ESPE e Katana, Kuraray Noritake). Material e Métodos: Cento e vinte placas de zircônia (13 mm de comprimento X 5 mm de largura X 1 mm de espessura) foram preparadas e tratadas de acordo com os seguintes tratamentos: 1- AOS, 2- APL, 3- AOS + APL e 4 - sem tratamento (controle). Após realizados os tratamentos, com a utilização de uma matriz de silicone (1,4 mm de diâmetro x 1 mm de altura) foram confeccionados cílindros de cimento resinoso na superfície da zircônia. O teste de cisalhamento foi realizado após o armazenamento das amostras por 24 horas e um ano. Os valores de resistência de união foram registrados em MPa e os dados foram analisados por ANOVA de três fatores e teste post-hoc de Tukey (alfa de 0,05). Resultados: Em geral, AOS e AOS + APL apresentaram a maior SBS. Após um ano de armazenamento, o SBS do cimento resinoso para a zircônia Katana não reduziu, independentemente do tratamento da superfície da zircônia. Conclusão: AOS isoladamente foi capaz de aumentar a SBS do cimento resinoso para ambas as zircônias em comparação com o controle e a SBS permaneceu estável após um ano, dependendo do tipo de zircônia. (AU)