Abrasion resistance of direct and indirect resins as a function of a sealant veneer.

Background: Abrasive wear is one of the most common type of wear that not only affect teeth, as also dental restorations. Thus to investigate one of the etiological factors as tooth brushing procedure is clinical relevant in order to select the best material combination that may prevent damage of resin dental restoration's abrasion. Aims: This study evaluated the influence of tooth brushing on mass loss and surface roughness of direct Venus (Vs) and indirect Signum (Sg) resin composites, with and without a surface sealant, Fortify (F). Materials and Methods: Twenty‑four specimens were prepared with each resin composite, using their proprietary curing units, according to manufacturer’s instructions. All the specimens were polished and ultrasonically cleaned in distilled water for 5 minutes. Half of the specimens of each resin (n = 12) were covered with F (VsF and SgF), except for the control (C) specimens (VsC and SgC), which were not sealed. Mass loss (ML) as well as surface roughness (Ra) was measured for all the specimens. Then, the specimens were subjected to toothbrush–dentifrice abrasion, using a testing machine for 67.000 brushing strokes, in an abrasive slurry. After brushing simulation, the specimens were removed from the holder, rinsed thoroughly and blot dried with soft absorbent paper. The abrasion of the material was quantitatively determined with final measurements of ML and surface roughness, using the method described above. Results: ML data were analyzed by two‑way analysis of variance (ANOVA) and the analysis indicated that resin composites were not statistically different; however, the specimens sealed with F showed higher ML. Ra mean values of the groups VsF and SgF significantly increased. Conclusion: Tooth brushing affects mainly the roughness of the direct and indirect resin composites veneered with a sealant.

Avaliação in vitro da resistência à compressão de condicionadores de tecido submetidos a diferentes tempos de armazenamento / In vitro evaluation of the compressive strength of tissue conditioners submitted to different storage times

Objetivou-se avaliar in vitro a resiliência de dois condicionadores de tecido, UG - Ufigel SC (Voco) e D - Dentusoft (DMG), depois de serem submetidos a diferentes tempos de armazenamento em água destilada a 37ºC (24 horas, 14 dias, 30 dias e 180 dias). Foram confeccionadas 20 cápsulas de resina acrílica termicamente ativada, com 20 mm de diâmetro interno e 3 mm de profundidade. Os condicionadores de tecido, UG e D, foram manipulados de acordo com o fabricante, acomodados no interior das cápsulas (n = 10) e armazenados por 24 horas, 14 dias, 30 dias e 180 dias. Cada grupo foi submetido ao teste de resiliência utilizando uma ponta romba de 3 mm de diâmetro em máquina de ensaio universal (EMIC-DL 1000). Os dados foram submetidos à análise estatística two-way ANOVA e ao teste de Tukey (α = 0,05). Os valores de média para os materiais/tempo de armazenagem foram: UG/24 horas - 3,81A; D/30 dias - 5,54B; UG/14 dias - 5,58B; UG/30 dias - 5,66BC; UG/180 dias - 5,77BC; D/24 horas - 5,79BC; D/180 dias - 6,13C; D/14 dias - 6,54D. Dentusoft armazenado por 14 dias obteve valores de média de resiliência significantemente superiores em relação aos demais. Ufigel armazenado nos períodos de 1 a 14 dias apresentaram valores de resiliência menores do que D, sendo estatisticamente significante nesses períodos. Entretanto, para os períodos de avaliação de 30 e 180 dias, não se observaram diferenças significantes entre os materiais.

Prótese parcial removível associada a implantes osseointegrados / Removable partial denture associated the osseointegrated implants: a clinical report

A prótese parcial removível (PPR) conjugada a implantes osseointegrados é um desafio na Odontologia restauradora, pois a biomecânica que envolve dois sistemas diferentes é um tanto quanto complexa. Este relato de caso expõe a instalação de uma PPR associada a dois implantes osseointegrados com encaixe do tipo ERA, fixados na região distal. Após minuciosos exames clínico, radiográfico e realização de modelos de estudo fez-se os planejamentos cirúrgico e protético. Restabeleceu-se função e estética associadas a um grande conforto e satisfação relatados pelo paciente, mas vale ressaltar que mais estudos clínicos são necessários para se ter um posicionamento mais definido em relação a esta modalidade terapêutica.

Shear bond strenght between metal alloy and a ceramic system, submitted to different thermocycling immersion times

El objetivo de este estudio fue evaluar la resistencia a cizallamiento de aleaciones metálicas de Co-Cr y Ni-Cr; con un mismo tipo de cerámica, sometidos a diferentes tiempos de inmersión en el termociclaje. Sesenta especímenes fueron confeccionados de forma standarden formato cilindrico. Tres condiciones de termociclaje fueron evaluadas: sin termociclaje, 3000 ciclos (5ºC/55ºC±1) con 30s y 3.000 ciclos (5ºC/55ºC±1) con 60s de tiempo de inmersión. El ensayo de cizallamiento fue realizado en una máquina universal usando un dispositivo para concentrar la tensión en la interfase metalocerámica durante el test. La carga fue aplicada hasta que ocurra la fractura de los especimenes. La información fue estadísticamente analizada por ANOVA(two-way) y el test de Tukey (p<0,05). Los resultados no mostraron diferencia estadísticamente significante entre las combinaciones metal-porcelana. Sin embargo, ambas combinaciones metalocerámicas sometidas a 60s de tiempo de inmersión mostraron valores más bajos en comparación con los especimenes del grupo sin termociclaje. Fue concluido que el tiempo de inmersión de termociclaje de 1 minuto afectó los valores de resistencia de cizallamiento en los grupos de Ni-Cr/porcelana y Cr-Co/porcelana.