RESUMO
ABSTRACT Color stability is among the most frequent causes of restoration failures, and influences surface properties. Aim: The aim of this study was to investigate the influence of pigment solutions on low-shrinkage and conventional composites regarding changes in the physical properties of composite surfaces. Materials and Method: Specimens of four composites (Filtek Z350 XT, Point 4, N'Durance and Venus Diamond) were randomly distributed into three groups to be submitted to each of three pigment solutions (red wine, tomato sauce and coffee) in fifteen-minute daily cycles, for twenty-eight days. There were 12 groups altogether (n = 10). Color, surface roughness and hardness tests were performed. Statistical analysis includedAnalysis of variance (ANOVA) and Tukey's significance test (a = 0.05). Results: Color changes caused by the solutions did not differ significantly among Filtek Z350 XT, Venus Diamond and N'Durance. Hardness decreased significantly in Filtek Z350 XT and Venus Diamond after chemical challenge with each solution. For the composite independent factor, roughness was highest in Venus Diamond, followed by Filtek Z350 XT, Point 4 and N'Durance. Conclusions: Treatment with different pigment solutions (red wine, tomato sauce or coffee) increased stainability and decreased hardness of both low-shrinkage and conventional composites, while roughness was unaffected.
RESUMO A estabilidade de cor está entre as causas mais frequentes de falhas de restauragoes, que também influenciam suas propriedades superficiais. Objetivo: O objetivo do presente estudo foi investigar a influencia de solugoes de pigmentos em compósitos convencionais e de baixa retragao, bem como alteragoes naspropriedades físicas da superficie dos compósitos. Materiais eMétodo: Amostras de cada compósito (Filtek Z350XT, Point 4, N'Durance e Venus Diamond) foram distribuidas aleatoriamente em grupos submetidos a cada solugao pigmentante (vinho tinto, molho de tomate e café) em ciclos diários de quinze minutos, durante vinte e oito dias. Assim, totalizando 12 grupos (n = 10). Foram realizados testes de cor, rugosidade superficial e dureza. A Análise Estatistica foi realizada usando Análise de variáncia (ANOVA) e o teste de significáncia de Tukey (a = 0.05). Resultados: As alteragoes de cor desencadeadas pelas solugoes investigadas nao mostraram diferenga estatisticamente significativa entre os compósitos Filtek Z350 XT, Venus Diamond e N'Durance. Os valores de dureza registrados para Filtek Z350XT e Venus Diamond diminuiram significativamente após o desafio químico com cada uma das solugoes pigmentantes. Para o fator independente compósito, Venus Diamond registrou a maior rugosidade; foi seguido por Filtek Z350XT, Point 4 e N'Durance. Conclusoes: Os tratamentos das amostras com diferentes solugoes pigmentantes (vinho tinto, molho de tomate e café) aumentaram a manchabilidade dos compósitos convencionais e de baixa retragao e diminuiram sua dureza, embora nao tenham afetado a rugosidade dos compósitos.
RESUMO
This study compared the surface detail reproduction and dimensional accuracy of stone models obtained from molds prepared using different alginate impression materials (Cavex Color Change, Hydrogum 5, or Jeltrate Plus) and with different storage times (1, 3, and 5 days) to models from molds that were filled immediatel y with no storage time. The molds were prepared over a matrix containing 50-μm line, (ISO 1563 standard) under pressure with a perforated metal tray. The molds were removed2 minutes after loss of sticky consistency and either filled immediately or stored in closed jars at 100% relative humidity and 37°C for 1, 3, or 5 days. The molds were filled with dental plaster (Durone IV). Surface detail reproduction and dimensional accuracy were evaluated using optical microscopy on the 50-μmwide line, which was 25 mm in length, according to ISO 1563 standard. The dimensional accuracy results (%) were subjected to analysis of variance. The 50-μm wide line (ISO 1563 standard)was completely reproduced by all alginate impression materials regardless of the storage time. There was no statistically significant difference in the mean dimensional accuracy values of stone models made from molds composed of different alginate impression materials and with different storage times (p = 0.989).In conclusion, storing the mold for five days prior to filling did not change the surface detail reproduction or dimensional accuracy of the alginates examined in this study.
Este estudo comparou a reprodução de detalhes da superfície e estabilidade dimensional de modelos de gesso obtidos a partir de diferentes alginatos (Cavex Color Change, Hydrogum 5, Jeltrate Plus) e com diferentes tempos de armazenagem (1, 3, e 5 dias)para modelos obtidos de moldes que foram preenchidos imediatamente sem tempo de armazenagem. Os moldes foram preparados sobre matriz contendo linha de 50 μm (norma ISO1563) realizado sob pressão com moldeira de metal perfurada.Os moldes foram removidos 2 minutos após a perda de consistência pegajosa e preenchidos imediatamente ou armazenado sem frascos fechados com temperatura (37°C) e umidade relativa(100%) controladas por 1, 3 ou 5 dias. Os moldes foram preenchidos com gesso dental (Durone IV). A reprodução de detalhes da superfície e a estabilidade dimensional foram avaliadas usando microscopia óptica na linha 50 μm com 25 mm de comprimento, de acordo com a norma ISO 1563. Os resultados de estabilidade dimensional (%) foram submetidos á análise de variância. A linha de 50 μm (norma ISO 1563) foi completamente reproduzida por todos os alginatos, independentemente do tempo de armazenagem. Não houve diferença estatisticamente significa -tiva nos valores médios de estabilidade de modelos de gesso obtidos de moldes de diferentes alginatos com diferentes tempos de armazenagem (p = 0.989). Em conclusão, o armazenamento do molde durante cinco dias antes do preenchimento não alterou a reprodução de detalhes da superfície ou estabilidade dimensional dos alginatos examinadas neste estudo.