RESUMO
ABSTRACT: Bioactive materials have shown positive results in reducing the deleterious effects of tooth whitening. However, their effects on whitening efficacy is still uncertain. Therefore, the aim of this study was to evaluate the effects of F- 18 bioactive glass incorporation into a bleaching gel on color and microhardness of enamel after tooth whitening. Thirty bovine enamel-stained specimens were randomly divided into three groups (n=10) according to the whitening protocol: control group (unbleached), HP35 % (35 % hydrogen peroxide) and F-18 (F-18 bioactive glass incorporated into HP35 %). pH, color change and microhardness analyzes were performed at baseline, 24 hours and 7 days after tooth whitening. Color evaluation showed that experimental groups were different than control group for all coordinates (p 0.05). No differences in enamel microhardness were found among the groups within the same evaluation time (p > 0.118). Regarding the intragroup comparisons, no differences were observed for control and F-18 groups (p > 0.129). It was concluded that F-18 bioactive glass incorporation did not affect the whitening efficacy and the enamel microhardness.
RESUMEN: Los materiales bioactivos han mostrado resultados positivos en la reducción de efectos nocivos del aclaramiento dental. Sin embargo, sus efectos sobre la eficacia del aclaramiento aún son inciertos. Por lo tanto, el objetivo de este estudio fue evaluar los efectos de la incorporación de vidrio bioactivo F-18 en un gel aclarador sobre el color y la microdureza del esmalte después del aclariamiento dental. Treinta especímenes bovinos teñidos con esmalte se dividieron aleatoriamente en tres grupos (n=10) de acuerdo con el protocolo de aclaramiento: grupo control (sin aclaramiento), HP35 % (peróxido de hidrógeno al 35 %) y F-18 (vidrio bioactivo F-18 incorporado en HP35 %). Se realizaron análisis de pH, cambio de color y microdureza al inicio del estudio, 24 horas y 7 días después del aclaramiento dental. La evaluación del color mostró que los grupos experimentales eran diferentes al grupo de control en todas las coordenadas (p 0,05). No se encontraron diferencias en la microdureza del esmalte entre los grupos dentro del mismo periodo de evaluación (p > 0,118). En cuanto a las comparaciones intragrupos, no se observaron diferencias para los grupos control y F-18 (p > 0,129). Se concluyó que la incorporación de vidrio bioactivo F-18 no afectó la eficacia de aclaramiento ni la microdureza del esmalte.
RESUMO
ABSTRACT: This clinical case described the aesthetic treatment of a patient complaining about the aspect of their upper teeth. After anamnesis and clinical examination, the association of tooth whitening photoactivated by violet LED and resin composite restorations was indicated. Prior to restorative treatment, three bleaching sessions were performed with low concentration hydrogen peroxide (6 %; Nano white flex) for 30 minutes. During this period, violet LED irradiation was intercalating performed every 1 minute, totalizing 15 minutes. Ten days after the final bleaching session, old restorations in the upper lateral incisors were removed for better color selection of resin composites. Then, all upper anterior teeth were directly restored with nanofilled resin composite (Filtek Z350XT), reestablishing anatomy, form, and function. At the end of the treatment, the association of techniques proved to be cost-effective, restoring the esthetics satisfactorily and promoting the patient's well-being by a minimally invasive approach.
RESUMEN: En este reporte de caso se describió el tratamiento para una paciente que se quejaba del aspecto de sus dientes superiores. Tras anamnesis y exploración clínica, se indicó la asociación de blanqueamiento dental fotoactivado por LED violeta y restauraciones de resina compuesta. Antes del tratamiento restaurador, se realizaron tres sesiones de blanqueamiento con peróxido de hidrógeno de baja concentración (6 %; Nano white flex) durante 30 minutos. Durante este período, la irradiación con LED violeta se intercalaba cada 1 minuto, totalizando 15 minutos. Diez días después de la última sesión de blanqueamiento, se retiraron las restauraciones antiguas de los incisivos laterales superiores para una mejor selección del color de la resina compuesta. Luego, todos los dientes anteriores superiores fueron restaurados de manera directa con resina de nanorrelleno (Filtek Z350XT), restableciendo la anatomía, forma y función. Al final del tratamiento, la asociación de las técnicas resultó beneficioso, restaurando la estética de forma satisfactoria y promoviendo el bienestar de la paciente mediante un abordaje mínimamente invasivo.