Characterization of Mechanical Properties, Fluoride Release and Colour Stability of Dental Sealants

Objective: To compare the mechanical properties, fluoride release, colour stability and spreading characteristics of glass ionomer cement (GIC), compomer (CO), chemical (CR) and light-cured resin based (LR) fissure sealants. Material and Methods: Cylinders were prepared to determine mechanical properties by diametral tensile strength tests (stored for 24h in distilled water at 37°C) and fluoride release (24 hours, 3, 7 and 15 days; deionised water). Disk shaped specimens were prepared to determine colour stability (1 week in pigmenting solution; 37°C; CIE L*a*b*; ΔE). A simplified method of a spreading test was proposed to predict viscosity characteristics of the tested materials. Data were analysed using one-way ANOVA followed by T-test (p<0.05). Results: Results showed differences between materials regarding all tested properties. CO was statistically more resistant than the other materials (p<0.05), but no difference was observed between CR and LR. The fluoride release of GICs was significantly higher than the other materials (p<0.05). CO showed lower ΔE than the other materials in the following order: CO

Correção do zênite gengival no manejo estético pré-restaurador por gengivectomia dupla combinada / Combined double-gingivectomy procedure for gingival zenith position correction in restorative esthetic management

As intervenções odontológicas atuais visam, além do restabelecimento funcional, alternativas terapêuticas para contemplar as necessidades estéticas de nossos pacientes. A crescente exigência por altos padrões estéticos alavanca uma integração entre as diversas especialidades, propondo um tratamento global que objetive a previsibilidade e resolução dos casos clínicos. Nesse contexto, as abordagens periodontais assumem um importante papel, sobretudo em casos em que alterações no complexo dentogengival estão presentes. Além das recessões gengivais, as assimetrias no contorno gengival e exposição excessiva de tecido gengival podem interferir diretamente na composição estética de um sorriso. Diante do exposto, o objetivo do presente trabalho foi relatar um caso clínico em que um procedimento de aumento de coroa clínica foi realizado para promover a harmonia do sorriso no planejamento estético integrado da exposição excessiva de tecido gengival, e hiperplasia gengival dos dentes anteriores inferiores. Foram realizados procedimentos cirúrgicos periodontais para definir o posicionamento da nova margem gengival, proporcionar uma arquitetura gengival fisiológica e obter ambiente mais favorável para que o recondicionamento dentário com resina composta pudesse ser realizado nos dentes superiores.

Incisivos centrais unitários: o grande desafio: descrição da técnica passo a passo / Incisal central unit por: single incisal central

A procura por restaurações estéticas vem aumentando ao longo dos anos, pois cada vez mais pacientes apresentam alta exigência em busca de restaurações que possam mimetizar os dentes naturais. Por isso, a restauração de um incisivo central superior pode ser considerada um grande desafio. O presente caso descreve as etapas de um tratamento estético em um incisivo central superior, 21, com severa alteração de cor. Após o exame radiográfico foi detectada displasia pulpar distrófica e reabsorção radicular externa. Para este tratamento foi tomada a decisão de uma conduta conservadora, com base na idade do paciente e em sua preocupação em preservar o elemento dental...

The demand for aesthetic restorations has been increasing over the years, as more patients are looking for restorations that can simulate natural teeth. Therefore, the restoration of a maxillary central incisor can be considered a challenge. The present case describes the steps of the aesthetic treatment in a maxillary central incisor (#21) with severe discoloration. After radiographic examination, pulp calcification and external root resorption have been detected. For this treatment, a conservative approach was chosen based on patient’s age and his concern for tooth preservation...

Tratamento da agenesia dentária com implantes osseointegrados e correção do plano incisal após Ortodontia na zona estética / Treatment of tooth agenesis with osseointegrated implants and correction of the incisal plane after orthodontic treatment in the esthetic zone

Pacientes com agenesia de incisivos laterais superiores necessitam de um tratamento adequado para o sucesso estético e funcional do sistema estomatognático. Vários estudos têm sido realizados em busca de uma solução para esses pacientes nas áreas da Ortodontia, Dentística e Implantodontia. O objetivo deste trabalho foi demonstrar, através de um caso clínico, a solução protética encontrada para o caso de um paciente com agenesia de incisivos laterais superiores. Após correção ortodôntica dos dentes e abertura para inserção dos implantes, implantes osseointegráveis foram fixados na maxila na região dos dentes 12 e 22; posteriormente, o tratamento estético com próteses livres de metal e resinas anteriores nos elementos 11 e 21 foi executado para alinhar a simetria do sorriso da paciente, provendo um resultado satisfatório

Patients with agenesis of upper lateral incisors need a proper treatment for the aesthetic and functional success of the stomatognathic system. Several studies have been made to find a solution for these patients including orthodontic, implantodontic, and prosthetic proposals. The objective of this paper is to demonstrate through a case study, the prosthetic solution found for the case of a patient with agenesis of maxillary lateral incisors. After orthodontic correction and space making for implant placement, dental implants were positioned at 12 and 22 regions, followed by metal-free prostheses and resin composite restorations at 11 and 21 to align smile simmetry providing a satisfactory result.

O sorriso gengival - tratamento basedo na etiologia: uma revisão de literatura / The gummy smile – treatment based on etiology: review

O sorriso gengival é definido pela exposição excessiva de gengiva maxilar durante o sorriso. A etiologia do sorriso gengival é variada e sua correta identificação é fundamental para confecção de um plano de tratamento eficaz. Para podermos diagnosticar precisamente o fator causador preponderante em cada caso, alguns aspectos clínicos devem ser avaliados. São esses: saúde periodontal, exposição dentária durante repouso, análise dimensional e funcional do lábio superior, mensuração da coroa clínica dos incisivos e caninos e harmonia entre os planos oclusais anteriores e posteriores. Este artigo tem como objetivo revisar literatura atual acerca dos fatores etiológicos do sorriso gengival (Hiperplasia gengival, Extrusão Dento-Alveolar anterior, Excesso Vertical de Maxila (VME), e Lábios superiores curtos ou hiperativos durante o sorriso, erupção passiva alterada) assim como da semiotécnica relacionada, visando auxiliar o cirurgião dentista na tomada de decisão e no estabelecimento do plano de tratamento adequado para cada uma essas etiologias.

The gummy smile is an excessive maxillary gingival display during the smile. The etiology of the gummy smile is varies and its correct definition is principal for making an effective treatment plan. In order to accurately diagnose the main causer factor in each case, some of clinical aspect must be evaluated. Are these: periodontal health, dental exposure at rest, dimensional review and upper lip functional, measurement of the clinical crown of the incisor and canine and harmonious occlusal planes. The goal of this article is to review the actual etiological factors of the gummy smile (Gingival hyperplasia, anterior incisor overeruption, vertical maxillary excess (VME), and short upper lip or hyperactive mobile upper lip during the smile and altered passive eruption), as the semi- technical related, to assist dentist to make decisions and to establish the appropriate treatment plan for each of these etiologies.

Tratamento estético restaurador com o uso de resina composta em dentes anteriores associado a clareamento dentário prévio: relato de caso / Esthetic restorative treatment using resin composite in anterior teeth associated toprevious dental bleaching: clinical case report

O tratamento estético utilizando o clareamento dentário e restaurações com resina composta é uma excelente alternativa para a obtenção de um belo sorriso. A procura da estética pelos pacientes tem sido cada vez mais frequente, em busca de dentes claros e de um sorriso harmonioso. O clareamento dentário proporciona uma estética mais favorável, porém já é bastante elucidado que os agentes clareadores atuam somente na estrutura dentária, e não nos materiais restauradores, no que diz respeito à descoloração. Por isso, muitas vezes há a necessidade de substituir restaurações de resina composta após o tratamento clareador. O presente artigo apresenta o relato de um caso clínico em que foi realizado o clareamento dentário em consultório com peróxido de hidrogênio a 20 por cento com posterior substituição das restaurações de resina composta pela técnica estratificada, utilizando um compósito mecrohíbrido. O resultado clínico foi adequado e satisfatório, oferecendo um belo sorriso ao paciente, o que demonstra a possibilidade de se realizar os dois procedimentos, visando melhorar a estética, através de um sorriso harmonioso.

The esthetic treatment using dental bleaching and resin composite restorations is an excellent alternative to obtain a beautiful smile. Patients' demands for cosmetic have been much more often in search of bleached teeth and a bright harmonic smile. Dental bleaching provides a beautiful smile, but it is quite known that bleaching agents act only in the tooth structure and do not in restorative materials. Therefore, there is often the need to replace resin composite restorations after bleaching. This article presents a case report in which was performed a dental office bleaching with hydrogen peroxide at 20%, with subsequent replacement of resin composite restorations through the stratified technique using a micro-hybrid resin composite. Clinical outcome was adequate and satisfactory offering a beautiful smile to the patient. This demonstrates the possibility of performing both procedures, and therefore improve esthetics as the proportion of a harmonious smile.

Overdenture mandibular com carga imediata em implantes de corpo único / Mandible overdenture with immediate loading in one-piece dental implants

Um dos problemas odontológicos mais evidentes no tratamento reabilitador com prótese total em pacientes edêntulos é a falta de retenção e estabilidade. O presente trabalho tem como objetivo apresentar uma alternativa na reabilitação para pacientes edêntulos com uma overdenture mandibular em implantes de corpo único.

One of the most common problems in the rehabilitation of totally edentulous patients is the difficulty in obtaining retention and stability. The aim of this present work is to present a treatment possibility with a mandibular overdenture in implants of with one-piece dental implants.

Resistência à fratura de próteses parciais fixas provisórias / Fracture strength of provisional partial prosthetic bridge

O objetivo deste trabalho foi comparar a resistência à fratura de próteses parciais fixas provisórias (PPFP) confeccionadas com diferentes materiais. Foram confeccionadas PPFP com os materiais: Dencor, Duralay, Luxatemp, Snap, seguindo as instruções do fabricante (n = 10). Os valores de resistência à fratura foram submetidos à análise de variância e teste de Tuckey (p < 0,05). As médias de resistência à fratura foram (MPa): Dencor 59,16 > Duralay 44,48 > Luxatemp 31,52 = Snap 29,69. As restaurações provisórias confeccionadas com as resinas Dencor e Duralay mostraram-se superiores aos materiais Luxatemp e Snap.

Uso de sistema de fibras de reforço em prótese adesiva posterior: relato de caso clínico / Reinforcerd fibers system use in posterior adhesive prothesis: clinical case report

A utilização de resinas associadas a fibras de reforço é uma excelente alternativa para casos de prótese adesiva. Este trabalho apresenta um caso clínico em que foi confeccionada uma prótese fixa reforçada do sistema de pônticos e fibras de vidro Fibrex-Lab (Angelus, Brasil) associada à resina composta Natural Look (DFL, Brasil). O resultado clínico foi altamente satisfatório, oferecendo função e estética ao paciente, o que demonstra a possibilidade da utilização das fibras de vidro como alternativa às ligas metálicas e cerâmicas reforçadas para subestruturas em situações clínicas bem indicadas de próteses parciais fixas. Dessa forma, o trabalho executado foi muito útil para que o emprego desses materiais permita aos dentistas clínicos a escolha de novas alternativas seguras para reabilitar sorrisos.

Sistema de attachment resiliente utilizado em overdenture implantorretida: relato de caso / Resilient attachment system for implant-retained overdenture: a case report

Um dos problemas odontológicos mais evidentes no tratamento reabilitador em pacientes desdentados totais é a falta de retenção e estabilidade desejadas, o que torna certos casos clínicos difíceis e desafiadores. Para a resolução adequada desses casos, a utilização de sistemas de encaixe associados com implantes osseointegrados parece ser uma estratégia viável. Este artigo descreve um caso clínico de paciente edentado total, em que se utiliza o sistema resiliente de attachment ERA® em overdenture implantorretida.

Caracterização de sistemas cerâmicos aluminizados infiltrados por vidro, por meio de microscopia eletrônica de varredura e resistência à flexão / Characterization of glass-infused alumina-based ceramic systems by means of scanning electron microscopy and flexural strength

Objetivo: O objetivo do trabalho foi caracterizar e comparar sistemas cerâmicos aluminizados infiltrados por vidro, por meio de difração por RX, microscopia eletrônica de varredura e resistência à flexão uniaxial em três pontos. Os sistemas cerâmicos utilizados foram: (IC)- In-Ceram Alumina (VITA), (VC)- Vitro-Ceram (Angelus) e (AG)- Alglass (Celmat). A fase cristalina de cada material foi identificada por meio de difração por RX. Dez espécimes em forma de barra (25X4X1,2±0,1) de cada material foram produzidos seguindo as instruções do fabricante de acordo com a ISO 6872. Os espécimes foram levados em uma máquina de ensaio universal para avaliação da resistência à flexão em três pontos, com carga de 500Kgf, velocidade de 0,5mm/min e distância entre os apoios de 15mm. Os dados foram submetidos a análise estatística ANOVA (p<0,01). Os espécimes fraturados foram observados no MEV em diversas condições: superfície jateada, superfície polida, superfície fraturada e alumina sem infiltração. Resultados: Foi identificada uma segunda fase cristalina de zircônia dopada com Ítrio no VC. Os valores médios de resistência à flexão foram (MPa): VC (483±38,3)= IC (456,6±29,4) > AG(263,8±37,8) (nível de 1% de significância). A micromorfologia dos sistemas apresentou características bem distintas, com diferenças em relação ao tamanho e distribuição das partículas de alumina e capacidade de molhamento do vidro de infiltração. A análise da fratura demonstrou comportamento semelhante contornando a maioria dos grãos de alumina e atravessando outros...

Objective: The purpose of this study was to characterize and compare glass-infused alumina-based ceramic systems by using X-Ray diffraction, scanning electron microscopy (SEM) and flexural strength with a three-point bending test. The ceramic systems used were: (IC)- In-Ceram Alumina (VITA), (VC)- Vitro-Ceram (Angelus) and (AG)- Alglass (Celmat). The crystalline phase of each material was identified through X-Ray diffraction. Ten bar specimens (25X4X1,2±0.1) of each material were produced following the manufacturer's instructions according to ISO 6872. The specimens were taken to a universal testing machine to evaluate flexural strength with a three-point bending test, with a constant load of 500Kgf, crosshead speed of 0,5mm/min and a 15mm distance between supports. The data was submitted to ANOVA (p<0.01) statistical analysis. The fractured specimens underwent SEM analysis in different conditions: sandblasted surface, polished surface, fractured surface and alumina without infiltration. Results: a second crystalline phase of yttrium-stabilized zirconia was identified in VC. Mean values of flexural strength were (MPa): VC (483±38.3)= IC (456,6±29.4) > AG(263,8±37.8). The micro morphology presented distinct characteristics for each system, with differences in relation to size and distribution of the alumina particles, and the ability of glass infiltration. Fracture analysis showed similar behavior contouring most alumina particles and though others...

Depth of cure of dental composites submitted to different light-curing modes

OBJECTIVE: This study evaluated the depth of cure of five dental composites submitted to different light-curing modes. MATERIAL AND METHODS: Canal-shaped cavities with 5mm of length were prepared on the buccal surfaces of extracted third molars, and restored using P-60, A-110, Admira, Z-250 and Supreme resin composites. Materials were light-cured from the top, according to three modes (Group 1- Conventional (C): 500 mW/cm² / 40 s; Group 2 - Soft-Start (SS): 250 mW/cm²/ 20 s + 500 mW/cm²/ 20 s + 500 mW/cm²/ 10 s and Group 3 - LED: 250 mW/cm²/ 40 s). After that, cavity longitudinal surfaces were polished and marked with a millimeter scale of 4mm of length. Depth of cure was evaluated by means of Knoop hardness number (KHN), so that five indentations were performed at each millimeter. Original data were submitted to three-way ANOVA and Fisher's LSD test (alpha = 0.01). RESULTS: All materials presented a significant reduction on KHN from first to third millimeter. Regarding depth of cure, the results obtained for Conventional and Soft-Start modes were similar, but statistically superiors to those found for group 3 (LED). CONCLUSION: This performance may be related to the differences among energy densities obtained with different light-curing modes.

OBJETVO: Este estudo avaliou a profundidade de polimerização de cinco compósitos fotopolimerizáveis submetidos a diferentes métodos de fotoativação. MATERIAL E MÉTODO: Cavidades em forma de canaleta com 5 mm de comprimento, preparadas nas faces vestibulares de terceiros molares, foram restauradas com os compósitos P-60, A-110, Admira, Z-250 e Supreme. Os materiais foram fotoativados pelo topo das cavidades com três técnicas (Grupo 1 - Convencional (C): 500 mW / cm² / 40 s; Grupo 2 - Soft-Start (SS): 250 mW / cm² / 20 s + 500 mW / cm² / 20 s + 500 mW / cm² / 10 s e Grupo 3 - LED: 250 mW / cm² / 40 s). Após a fotoativação, as superfícies longitudinais dos materiais foram polidas e marcadas com uma escala milimetrada com 4 mm de comprimento. A profundidade de polimerização foi avaliada através do número de dureza Knoop (NDK), com cinco indentações a cada milímetro. Os dados originais foram submetidos à Análise de Variância de três fatores e teste de Fisher para comparações entre médias (alfa = 0,01). RESULTADOS: Todos os materiais apresentaram diminuição do NDK do primeiro para o terceiro milímetro (p < 0,01). Os resultados obtidos com os Grupos Convencional e Soft-Start foram similares e superiores ao Grupo LED (p < 0,01). CONCLUSÃO: Este desempenho pode ser relacionado às diferenças nas densidades de energia obtidas com os métodos de fotoativação utilizados.

Depth of cure of dental composites submitted to different light-curing modes%Profundidade de polimerização de compósitos restauradores submetidos a diferentes métodos de fotoativação

OBJETVO: Este estudo avaliou a profundidade de polimerização de cinco compósitos fotopolimerizáveis submetidos a diferentes métodos de fotoativação. MATERIAL E MÉTODO: Cavidades em forma de canaleta com 5 mm de comprimento, preparadas nas faces vestibulares de terceiros molares, foram restauradas com os compósitos P-60, A-110, Admira, Z-250 e Supreme. Os materiais foram fotoativados pelo topo das cavidades com três técnicas (Grupo 1 - Convencional (C): 500 mW / cm2 / 40 s; Grupo 2 - Soft-Start (SS): 250 mW / cm2 / 20 s + 500 mW / cm2 / 20 s + 500 mW / cm2 / 10 s e Grupo 3 - LED: 250 mW / cm2 / 40 s). Após a fotoativação, as superfícies longitudinais dos materiais foram polidas e marcadas com uma escala milimetrada com 4 mm de comprimento. A profundidade de polimerização foi avaliada através do número de dureza Knoop (NDK), com cinco indentações a cada milímetro. Os dados originais foram submetidos à Análise de Variância de três fatores e teste de Fisher para comparações entre médias (a = 0,01). RESULTADOS: Todos os materiais apresentaram diminuição do NDK do primeiro para o terceiro milímetro (p < 0,01). Os resultados obtidos com os Grupos Convencional e Soft-Start foram similares e superiores ao Grupo LED (p < 0,01). CONCLUSÃO: Este desempenho pode ser relacionado às diferenças nas densidades de energia obtidas com os métodos de fotoativação utilizados