RESUMO
OBJETIVO: avaliar a resistência ao cisalhamento dos compósitos Transbond XT e Concise Ortodôntico utilizando o potencializador de adesão Ortho Primer. MÉTODOS: a amostra consistiu de 90 incisivos bovinos divididos em seis grupos (n=15). Todos os dentes receberam profilaxia com pedra-pomes e condicionamento do esmalte com ácido fosfórico. No Grupo I, utilizou-se Transbond XT de maneira convencional. O Grupo II foi semelhante ao I, porém, aplicou-se o Ortho Primer ao invés do XT Primer. No Grupo III, após condicionamento, o esmalte foi contaminado com saliva, aplicou-se o Ortho Primer e colagem com Transbond XT. No Grupo IV, utilizou-se o Concise Ortodôntico de maneira convencional. O Grupo V foi semelhante ao IV, porém, utilizou-se o Ortho Primer ao invés da resina fluida. No Grupo VI, após condicionamento, o esmalte foi contaminado com saliva, aplicou-se o Ortho Primer e colagem com Concise. Os corpos de prova foram armazenados em água destilada em estufa a 37ºC por 24h e submetidos ao ensaio de resistência ao cisalhamento. Os dados foram submetidos à ANOVA e ao teste de Tukey (5 por cento). RESULTADOS: a resistência da colagem no Grupo IV foi estatisticamente superior à dos Grupos II, III e VI (p<0,05). Entre os Grupos I, IV e V; e entre os Grupos I, II, III e VI não foram encontradas diferenças estatísticas significativas (p>0,05). O Transbond XT e o Concise utilizados convencionalmente obtiveram os maiores valores adesivos. O Ortho Primer em esmalte seco atuou efetivamente como agente de união dos compósitos avaliados. Em esmalte contaminado, a colagem com Concise obteve baixa resistência adesiva.
OBJECTIVE: To evaluate the shear strength of two composites (Transbond XT and Concise) using an adhesion booster (Ortho Primer).METHODS: The sample consisted of 90 bovine incisors divided into six groups (n=15). All teeth were subjected to prophylaxis with pumice and enamel etching with phosphoric acid. Transbond XT was used conventionally in Group I. Group II was handled similarly to Group I, except that Ortho Primer was applied instead of XT Primer. After etching, the enamel in Group III was contaminated with saliva, Ortho Primer was then applied and bonding performed using Transbond XT. In Group IV, Concise was used conventionally. Group V was handled similarly to Group IV, except that Ortho Primer was applied instead of the fluid resin. After etching, the enamel in Group VI was contaminated with saliva, Ortho Primer was then applied and bonding performed using Concise. The specimens were stored in distilled water at 37 ºC for 24 hours and subjected to shear strength testing. Data were analyzed with ANOVA and Tukey's test (5%).RESULTS: Bond strength in Group IV was statistically higher than in Groups II, III and VI (p<0.05). No statistically significant differences were found among Groups I, IV and V, and between I, II, III and VI (p>0.05). When used conventionally, both Transbond XT and Concise yielded the highest bond strength values. When applied to dry enamel, Ortho Primer acted effectively as a bonding agent for the composites under evaluation. When applied to contaminated enamel, Concise yielded low bond strength.