Comparison of microleakage of an alkasite restorative material, a composite resin and a resin-modified glass ionomer

Aim: To compare the microleakage of Cention N, a subgroup of composite resins with a resin-modified glass ionomer (RMGI) and a composite resin. Methods: Class V cavities were prepared on the buccal and lingual surfaces of 46 extracted human molars. The teeth were randomly assigned to four groups. Group A: Tetric N-Bond etch-and-rinse adhesive and Tetric N-Ceram nanohybrid composite resin, group B: Cention N without adhesive, group C: Cention N with adhesive, and group D: Fuji II LC RMGI. The teeth were thermocycled between 5°-55°C (×10,000). The teeth were coated with two layers of nail vanish except for 1 mm around the restoration margins, and immersed in 2% methylene blue (37°C, 24 h) before buccolingual sectioning to evaluate dye penetration under a stereomicroscope (×20). The data were analyzed by the Kruskal-Wallis and Wilcoxon tests (α=0.05). Results: Type of material and restoration margin had significant effects on the microleakage (p<0.05). Dentin margins showed a higher leakage score in all groups. Cention N and RMGI groups showed significant differences at the enamel margin (p=0.025, p=0.011), and for the latter group the scores were higher. No significant difference was found at the dentin margins between the materials except between Cention N with adhesive and RMGI (p=0.031). Conclusion: Microleakage was evident in all three restorative materials. Cention N groups showed similar microleakage scores to the composite resin and displayed lower microleakage scores compared with RMGI

Degree of conversion and water sorption of self-adhesive and conventional flowable composites: an in vitro study

Aim: Self-adhesive flowable composite resins have been recently introduced to the market. Degree of conversion (DC) and water sorption (WS) are two important parameters affecting the properties of restorative materials. This study aimed to assess the DC and WS of a self-adhesive flowable composite resin in comparison with two conventional flowable composite resins. Methods: Vertise Flow (VF) self-adhesive and Tetric-N Flow (TF) and Grandio Flow (GF) conventional flowable composites were evaluated in this in vitro, experimental study. The DC (n=3) was determined by attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR). The WS (n=7) was measured after 7 days of immersion in artificial saliva accordingto ISO 4049specifications. Data were analyzed by one-way ANOVA and a post-hoc test (p<0.05). Results: VF showed the highest DC percentage (84.3%) followed by GF (72.79%) and TF (68.7%). The latter two had no significant difference (p=0.8). WS was the highest in VF (55.2 µg/mm3), and the two conventional flowable composites had a significant difference in WS (19.5 µg/mm3 in TF and 11 µg/mm3 in GF; p<0.001). Conclusions: Flowable composite resins had significant differences in DC and WS, and VF demonstrated the highest DC and WS