Influence of acid etching and universal adhesives on the bond strength to dentin

Abstract The purpose of this study was to evaluate the influence of the application mode of three universal adhesive systems on interfacial physical properties of indirect composite restorations adhesively cemented to dentin cavities. Seventy-eight bovine lower incisors were selected and a slice of dentin (thickness: 2 mm) between the buccal surface and pulp chamber was obtained for each tooth. Conical cavities were made on this surface. The internal walls of the cavities were then coated with a hydrophilic gel, filled with composite resin and photopolymerized. The dentin/cone sets were divided into 6 groups (n=10) according to type of universal adhesive (TETRI: Tetric N Bond, FUT: Futura Bond U, SBU: Single Bond Universal) and acid etching on dentin (A: with acid etching; WA: without acid etching). The acid etching and the adhesive systems were applied to the surface of the dentin. All composite resin cones were sandblasted (Al2O3, 20 s) and silanized. After surface treatment, the cones were cemented (RelyX Ultimate) into the dentin cavity and photopolymerized. After thermocycling (10,000 cycles), samples were submitted to marginal adaptation analysis (using caries detector dye), push-out test (0.5 mm/min), and failure mode analysis. Additional samples were prepared for nanoleakage analysis (SEM). The data (MPa) were analyzed by two-way ANOVA and Tukey's post-test (5%). The groups in which the dentin was acid etched showed significantly lower bond strength values in the push-out test (p<0.01). Dentin acid etching significantly reduced the bond strength between universal adhesive systems and dentin in indirect restorative procedures.

Resumo O objetivo deste estudo foi avaliar a influência do modo de aplicação de três sistemas adesivos universais nas propriedades físicas interfaciais de restaurações indiretas de compósito adesivamente cimentadas a cavidades dentinária. Setenta e oito incisivos inferiores bovinos foram selecionados e uma fatia de dentina (espessura: 2 mm) entre a face vestibular e a câmara pulpar foi obtida para cada dente. Cavidades cônicas foram feitas nesta superfície. As paredes internas das cavidades foram então revestidas com um gel hidrofílico, preenchidas com resina composta, e fotopolimerizados. Os conjuntos dentina/cone foram divididos em 6 grupos (n=10) de acordo com o tipo de adesivo universal (TETRI: Tetric N Bond, FUT: Futura Bond U, SBU: Single Bond Universal) e ácido na dentina (A: com condicionamento ácido; WA: sem condicionamento ácido). O condicionamento ácido e os sistemas adesivos foram aplicados na superfície da dentina. Todos os cones de resina composta foram jateados (Al2O3, 20 s) e silanizados. Após o tratamento superficial, os cones foram cimentados (RelyX Ultimate) na cavidade dentinária e fotopolimerizados. Após a termociclagem (10.000 ciclos), as amostras foram submetidas a análise de adaptação marginal (usando corante detector de carie), teste push-out (0,5 mm/min) e análise do modo de falha. Amostras adicionais foram preparadas para análise de nanoinfiltração (MEV). Os dados (MPa) foram analisados por ANOVA dois fatores e pós-teste de Tukey (5%). Os grupos em que a dentina foi condicionada por ácido apresentaram valores significativamente menores de resistência de união no teste push-out (p<0,01). O condicionamento ácido da dentina reduziu significativamente a resistência de união entre sistemas adesivos universais e dentina em procedimentos restauradores indiretos.

Effect of different surface treatments and multimode adhesive application on the Weibull characteristics, wettability, surface topography and adhesion to CAD/CAM lithium disilicate ceramic

Abstract This paper aims to evaluate the effect of different surface treatments on surface topography, wettability, and shear bond strength of resin cement to glass ceramic. Methodology: For SBS test, 32 blocks (7x7x2 mm) of lithium disilicate were obtained and randomly divided into eight groups (four blocks per group) according to each surface treatment (HF 20 s, 60 s, 120 s + silanization/S or Scotch Bond Universal/ SBU) and the Monobond Etch & Prime - MEP application followed or not by SBU. On each treated surface ceramic block, up to four dual-curing resin cement cylinders were prepared and light-cured for 40s (N=120/n=15). The specimens were thermocycled (10,000 cycles, 5-55°C, 30 s) and the SBS test (50KgF, 0.5 mm/min) was performed. Furthermore, failure analysis, wettability, AFM, and SEM were carried out. SBS data (MPa) were analyzed using Student's t-test, two-way ANOVA, Tukey's test (5%) and Weibull's analysis. Results: For HF experimental groups, two-way ANOVA presented the factors "etching time" and "bonding agent" as significant (p<0.05). After silane application, the HF groups presented similar bond strength. SBU application compromised the SBS, except for 120s etching time (HF120sS: 23.39ᵃ±6.48 MPa; HF120sSBU: 18.76ᵃ±8.81MPa). For MEP groups, SBU application did not significantly affect the results (p=0.41). The MEP group presented the highest Weibull modulus (4.08A) and they were statistically different exclusively from the HF20sSBU (0.58B). Conclusion: The HF 20s, 60s, 120 s followed by silane, promoted similar resin-bond strength to ceramic and the SBU application after HF or MEP did not increase the SBS.

Desempenho clínico de coroas monolíticas posteriores de cerâmica infiltrada por polímero: ensaio clínico controlado e randomizado duplo cego / Clinical performance of posterior monolithic polymer-infiltrated ceramic crowns: double-blind randomized controlled clinical trial

Objetivo: avaliar por meio de um ensaio clínico controlado, randomizado e duplo-cego, o desempenho clínico de coroas monolíticas unitárias posteriores confeccionadas em cerâmica infiltrada por polímero, bem como o impacto da reabilitação na satisfação estética e qualidade de vida dos pacientes. Materiais e Métodos: Um total de 20 pacientes que receberam 36 coroas foram incluídos neste estudo. Todos os pacientes assinaram o termo de consentimento livre e esclarecido (TCLE). Os dentes sob reabilitação foram alocados por meio de um sorteio simples entre os grupos: Grupo Controle: (LD- dissilicato de lítio) e grupo Experimental (PIC -Vita Enamic/Vita Zahnfabrik). Registros fotográficos, radiográficos e informações clínicas foram coletados antes, durante e após a reabilitação. As coroas foram avaliadas quanto à taxa de sobrevida clínica (Critérios de USPSH modificados), satisfação estética (escala visual analógica- EVA), qualidade de vida (Oral Impacts on Daily Performances -OIDP), e tipo de falhas (biológicas e técnicas). A coleta de dados foi realizada por um único examinador calibrado e cego para o tipo de material, nos tempos de seguimento T0 (antes do início do tratamento), T1 (1 mês), T2 (6 meses) e T3 (12 meses). O OIDP e os critérios de USPHS foram analisados descritivamente. A satisfação estética foi analisada com MannWhitney/Teste de Friedman/ pós-testes de Wilcoxon. A análise de sobrevivência foi feita usando Kaplan-Meier seguido do teste de log-rank. O nível de significância foi estabelecido em (5%). Resultados: 36 coroas foram colocadas em 20 pacientes com uma média de idade de 47.17 anos (±13,91), sendo 22 (56,4%) coroas do grupo controle (LD) e 14 (35,9%) para o grupo experimental (PIC). A análise de Kaplan-Meier revelou uma taxa de sobrevida de 83,5% para PIC e de 86,2% para LD sem diferenças significativas entre eles (P>0.05). Quatro falhas foram registradas, 2 em cada grupo, sendo dois descolamentos, uma de PIC após 1 mês e uma de LD após 6meses. Houve também uma fratura do dente (LD) e mobilidade grau III (PIC) após 12 meses de acompanhamento. Não houve diferença significativa na satisfação estética, entre o grupo controle e grupo experimental (Mann-Whitney - P>0.05). A satisfação estética foi significativamente maior após 1(T1), 6(T2) e 12(T3) meses quando comparado ao baseline (T0) (Teste de Friedman - P<0.05). A reabilitação com coroas unitárias impactou positivamente na qualidade de vida dos pacientes. Conclusão: Este estudo demonstra que coroas monolíticas unitárias de PIC apresentaram desempenho clínico, estético e um impacto positivo na qualidade de vida dos pacientes após 12 meses, similar ao LD (AU).

Objective: To evaluate, through a controlled, randomized and double-blind clinical trial, the clinical performance of posterior single monolithic crowns made ceramic infiltrated polymer, as well as the impact of rehabilitation on patients' aesthetic satisfaction and quality of life. Materials and Methods: A total of 20 patients who received 36 crowns were included in this study. All patients signed an informed consent form. The teeth under rehabilitation were allocated using a simple draw between the groups: Control Group: (LD- lithium disilicate) and Experimental group (PIC -Vita Enamic). Photographic, radiographic, and clinical information records were collected before, during, and after rehabilitation. The crowns were assessed for clinical survival rate (modified USPSH criteria), aesthetic satisfaction (visual analog scale - VAS), quality of life (Oral Impacts on Daily Performances - OIDP), and type of failures (biological and technical). Data collection was performed by a single examiner calibrated and blinded to the type of material, at the follow-up times T0 (before the start of treatment), T1 (1 month), T2 (6 months), and T3 (12 months). The OIDP and USPHS criteria were analyzed descriptively. Aesthetic satisfaction was analyzed with the Man-Whitney/Friedman test/Wilcoxon post-tests. Survival analysis was performed using Kaplan-Meier followed by the log-rank test. The level of significance was set at (5%). Results: 36 crowns were placed on 20 patients (17 women and 3 men) with a mean age of 47.17 years (± 13.91), with 22 (56.4%) crowns from the control group (LD) and 14 (35.9%) for the group experimental (PIC). The Kaplan-Meier analysis revealed a survival rate of 83.5% for PIC and 86.2% for LD with no significant differences between them (P>0.05). Four failures were recorded, 2 in each group, two detachments after 1(PIC) and 6 months (LD), a tooth fracture (LD), and grade III mobility after (PIC) 12 months of follow-up. There was no significant difference in aesthetic satisfaction between the control group and the experimental group (Mann-Whitney, P>0.05). Aesthetic satisfaction was significantly higher after 1 (T1), 6 (T2), and 12 (T3) months when compared to baseline (T0) (Friedman test - P <0.05). Rehabilitation with single crowns had a positive impact on patients' quality of life. Conclusion: This study demonstrates that single monolithic crowns of PIC presented a good clinical, aesthetic performance and a positive impact on patients' quality of life after 12 months, similarly to PIC (AU).

Hydrofluoric acid concentration, time and use of phosphoric acid on the bond strength of feldspathic ceramics

Abstract The objective of this study was to evaluate the influence of hydrofluoric acid (HF) concentration, etching time, and application of phosphoric acid (PA) followed by neutralization with sodium bicarbonate on the bond strength between a feldspar ceramic and resin cement. Thus, 80 blocks (10 x 12 x 2 mm) of glass ceramic (VM - Vita Mark II - Vita Zahnfabrik) were made and randomly assigned to eight groups (n = 10) according to the factors: HF concentration (5 and 10%), etching time (60 and 120 s), and use of phosphoric acid (PA) (with and without). According to the experimental group, 37% PA (Condac, FGM) was applied after HF etching for 60s. Afterwards, samples were immersed in sodium bicarbonate for 1 min then in an ultrasonic bath in distilled water (5 min) for cleaning. After surface bonding treatment, cylinders (Ø = 2 mm; h = 2 mm) of dual resin cement (AllCem / FGM) were made in the center of each block. The samples were then stored in water (37ºC) for 90 days and submitted to the shear bond test (50 KgF, 1 mm/min). Failure analysis was performed by stereomicroscope and scanning electron microscopy. Data (MPa) were analyzed with 3-way ANOVA and Tukey's test. Only the factor "HF concentration" was significant (p = 0.02). Most failures were of cohesive in ceramic (40%) and mixed types (42.5%). The 10% HF resulted in higher shear bond strength value than the 5% HF. Surface cleaning with phosphoric acid followed by sodium bicarbonate and HF time (60 or 120 seconds) did not influence the resin bond strength to feldspar ceramic.

Effect of hydrofluoric acid concentration and etching time on resin-bond strength to different glass ceramics

Abstract: The objective of this study was to evaluate the effect of the hydrofluoridric acid (HF) concentration and time of acid conditioning on bond strength of three glass ceramics to a resin cement. Thus, fifty blocks (10 mm x 5 mm x 2 mm) of each ceramic (LDCAD: IPS e.max CAD; LCAD: IPS Empress CAD and LDHP: IPS e.max Press) were made and embedded in acrylic resin. The surfaces were polished with sandpaper (#600, 800, 1000, and 1200 grits) and blocks were randomly divided into 15 groups (n = 10) according to the following factors: Concentration of HF (10% and 5%), conditioning time (20 s and 60 s) and ceramic (LDCAD, LDHP, and L). After conditioning, silane (Prosil / FGM) was applied and after 2 min, cylinders (Ø = 2 mm; h = 2 mm) of dual resin cement (AllCem / FGM) were made in the center of each block using a Teflon strip as matrix and light cured for 40 s (1,200 mW/cm2). Then, the samples were thermocycled (10,000 cycles, 5/55°C, 30s) and submitted to the shear bond test (50 KgF, 0.5 mm/min). The data (MPa) were analyzed with 3-way ANOVA and Tukey's test (5%). Failure analysis was performed using a stereomicroscope (20x) and a scanning electron microscope (SEM). ANOVA revealed that the "concentration" factor (p = 0.01) and the interaction "acid concentration X ceramic" (p = 0.009) had a significant effect, however, the "ceramic" (p = 0.897) and "conditioning time" (p = 0.260) factors did not influence the results. The LDHP10%60s (10.98 MPa)aA* group presented significantly higher bond strength than LDHP10%20s (6.57 MPa)bA, LCAD5%20s (6,90 ±3,5)aB and LDHP5%60s (5.66 ± 2,9MPa)aA* groups (Tukey). Failure analysis revealed that 100% of specimens had mixed failure. In conclusion, etching with 5% HF for 20 seconds is recommended for lithium disilicate and leucite-reinforced CAD/CAM ceramics. However, for pressed lithium disilicate ceramic, 10% HF for 60 s showed significantly higher bond strength to resin cement.

Can the application of multi-mode adhesive be a substitute to silicatized/silanized y-tzp ceramics?

Abstract This study evaluated the effectiveness of a multi-mode adhesive (SBU-Scotch Bond Universal/3M) as a substitute for silica coating and silane application on the bonding of zirconia ceramics to resin cement. One-hundred and twenty sintered zirconia ceramic blocks (5 x 5 x 5 mm) were obtained, finished by grounding with silicon carbide paper (#600, #800, #1000 and #1200) and randomly divided into 12 groups (n=10) in accordance with the factors "surface treatment" (ScSi - silicatization + silanization; ScSBU - silicatization + SBU; SBU - SBU without photoactivation and SBUp - SBU photoactivated) and "ceramic" (Lava / 3M ESPE, Ceramill Zirconia / Amann Girrbach and Zirkonzahn / Zirkonzahn). Dual resin cement cylinders (RelyX Ultimate/3M ESPE) were subsequently produced in the center of each block using a silicon matrix (Ø=2 mm, h=5 mm) and photoactivated for 40 s (1200 mW/cm2). The samples were stored for 30 days in distilled water (37ºC) and submitted to shear bond strength test (1 mm/min, 100 KgF). Data (MPa) were analyzed under ANOVA (2 levels) and Tukey test (5%). Complementary analyzes were also performed. ANOVA revealed that only the factor "surface treatment" was significant (p=0.0001). The ScSi treatment (14.28A) promoted statistically higher bond strength values than the other ScSBU (9.03B), SBU (8.47B) and SBUp (7.82B), which were similar to each other (Tukey). Failure analysis revealed that 100% of the failures were mixed. The silica coating followed by the silanization promoted higher bond strength values of resin cement and ceramic, regardless of the zirconia ceramic or SBU.

Resumo Este estudo avaliou a efetividade de um adesivo "multi-mode" (Single Bond Universal/3M) como um substituto para a silicatização e aplicação do silano na resistência de união das cerâmicas de zircônia e um cimento resinoso. Para isso, 120 blocos cerâmicos sinterizados de zircônia nas dimensões de (5 x 5 x 5 mm) foram obtidos, lixados com lixas de granulação decrescente (#600, #800, #1000 e #1200) e divididos aleatoriamente em 12 grupos (n = 10), de acordo com os fatores "tratamento de superfície" (ScSi - silicatização + silanização; ScSBU - silicatização + Single Bond; SBU - SBU sem fotoativação e SBUp - SBU com fotoativação) e "cerâmica" (Lava/3M ESPE, Ceramill Zircônia/ Amann Girrbach e Zirkonzahn/Zirkonzahn). Posteriormente, cilindros de cimento resinoso dual (RelyX Ultimate/3M ESPE) foram confeccionados no centro de cada bloco com auxílio de uma matriz de silicone (Ø=2 mm; h=5 mm) e fotopolimerizados por 40 s (1200 mW/ cm²). Em seguida, as amostras foram armazenadas durante trinta dias em água destilada (37 °C) e submetidas ao ensaio de resistência de união ao cisalhamento (1 mm/min, 100 kgF). Os dados (MPa) foram analisados sob ANOVA (2 fatores) e teste de Tukey (5%). Análises complementares também foram realizadas. ANOVA revelou que apenas o fator "tratamento de superfície" foi significativo (p=0,0001). O tratamento ScSi (14.28A) promoveu valores de adesão estatisticamente superiores aos demais ScSBU (9.03B), SBU (8.47B) e SBUp (7.82B), os quais foram semelhantes entre si (Tukey). A Análise de falhas revelou que 100% da falhas que ocorreram foram mistas. A silicatização seguida da silanização promoveu a melhor resistência de união entre cimento resinoso e a cerâmica, independentemente do tipo da cerâmica ou do SBU.

Influence of testing parameters on the load-bearing capacity of prosthetic materials used for fixed dental prosthesis: A systematic review / Influência de parâmetros de testes na capacidade de suporte de carga de materiais protéticos utilizados para prótese dentária fixa: uma revisão sistemática

Objective: The aim of this study was to systematically review the literature to assess static fracture strength tests applied for fixed dental prostheses (FDPs) and analyze the impact of periodontal ligament (PDL) simulation on the fracture strength. Material and Methods: Original scientific papers published in MEDLINE (PubMed) database between 01/01/1981 and 10/06/2018 were included in this systematic review. The following MeSH terms, search terms, and their combinations were used:"Dentistry", "Fracture Strength", "Fracture Resistance", "Fixed Dental Prosthesis", "Fixed Partial Denture", "Mechanical Loading". Two reviewers performed screening and analyzed the data. Only the in vitro studies that reported on load-bearing capacity of only FDP materials where mean or median values reported in Newnton (N) were included. Results: The selection process resulted in the 57 studies. In total, 36 articles were identified related to allceramics, 10 were fiber reinforced composite resin (FRC), 8 of composite resin (C) and 5 of metalceramic. As for clinical indications, 3 and 4-unit FDPs were more commonly studied (n=32; with PDL=21, without PDL=11), followed by single crowns (n=13; with PDL=3, without PDL=10), and inlay-retained and cantilever FDPs (n=12; with PDL=8, without PDL=4). Conclusion: An inclination for decreased static fracture strength could be observed with the simulation of PDL but due to insufficient data this could not be generalized for all materials used for FDPs (AU)

Objetivo: O objetivo deste estudo foi revisar sistematicamente a literatura para avaliar os testes de força de fratura estática aplicados para próteses dentárias fixas (FDPs) e analisar o impacto da simulação do ligamento periodontal (PDL) na resistência à fratura. Material e Métodos: Artigos científicos originais publicados na base de dados MEDLINE (PubMed) entre 01/01/1981 e 10/06/2018 foram incluídos nesta revisão sistemática. Foram utilizados os seguintes termos MeSH, termos de pesquisa e suas combinações: "Dentistry", "Fracture Strength", "Fracture Resistance", "Fixed Dental Prosthesis", "Fixed Partial Denture", "Mechanical Loading". Dois revisores realizaram a triagem e analisaram os dados. Apenas os estudos in vitro que reportaram a capacidade de suporte de carga de FDP, com os valores das médias ou medianas relatados em Newton (N) foram incluídos. Resultados: O processo de seleção resultou em 57 estudos. No total, 36 artigos foram identificados relacionados à restaurações totalmente cerâmicas, 10 em resina composta reforçada com fibra (FRC), 8 em resina composta (C) e 5 em metalocerâmica. Quanto às indicações clínicas, os PDF de 3 e 4 unidades foram mais comumente estudados (n = 32; com PDL = 21, sem PDL = 11), seguidos de coroas isoladas (n = 13; com PDL = 3, sem PDL = 10) e FDPs retidas por inlays e com cantilever (n = 12; com PDL = 8, sem PDL = 4). Conclusão: Uma inclinação para a diminuição da resistência à fratura estática pôde ser observada com a simulação do PDL, mas devido a dados insuficientes, isso não pôde ser generalizado para todos os materiais utilizados para as FDPs (AU)