Effect of delayed light-curing on solubility, color stability, and opacity of Fuji II LC glass ionomer cement: original article / Efeito da fotopolimerização tardia na solubilidade, estabilidade de cor e opacidade do cimento de ionômero de vidro Fuji II LC: artigo original

Objective: Resin-modified glass ionomer (RMGI) cements are among the commonly used restorative materials in low stress-bearing areas and also for temporary restorations. The competition between acid-base reactions and light polymerization reactions in delayed curing of RMGIs can affect their physical and mechanical properties, as well as their degree of conversion. Since solubility, color stability, and opacity are among the main physical properties affecting the durability and clinical service of RMGI restorations, this study aimed to assess the effect of delayed curing on solubility, color stability, and opacity of Fuji II LC RMGI. Material and Methods: This in vitro, experimental study evaluated 80 Fuji II LC RMGI specimens (10 specimens per each in 4 groups) in terms of solubility, color stability, and opacity at 6 months later. Specimens were cured immediately or were cured with 1, 5 and 10 min delay. Results: Maximum solubility and minimum change in opacity and color stability at 6 months were noted in the group with delayed curing by 10 min. A significant difference was noted in the solubility of specimens cured after 10 min and 1 min. Significant differences were also noted in the opacity and color stability of specimens cured after 10 min and all other groups (P < 0.05). Conclusion: Delayed curing by 1 min decreased the solubility of RMGI specimens compared with immediate curing or curing after 5 min. Although this difference did not reach statistical significance. Color stability and changes in opacity are mainly influenced by the acid-base reactions rather than polymerization reactions.(AU)

Objetivo: Cimentos de ionômero de vidro modificado por resina (CIVMR) estão entre os materiais restauradores mais comumente utilizados em áreas de baixa tensão e também para restaurações temporárias. A competição entre reações ácido-base e reações provenientes da fotopolimerização tardia dos CIVRMs podem afetar suas propriedades físicas e mecânicas, bem como seu grau de conversão. Uma vez que a solubilidade, estabilidade de cor e opacidade estão entre as principais propriedades físicas que afetam a durabilidade e o tempo de serviço clinico de restaurações de CIVMR, este estudo teve como objetivo avaliar o efeito da fotopolimerizaçao tardia na solubilidade, estabilidade de cor e opacidade do CIVMR Fuji II LC. Material e Métodos: Este estudo experimental in vitro avaliou 80 espécimes de CIVMR Fuji II LC (4 grupos com 10 espécimes cada) em termos de solubilidade, estabilidade de cor e opacidade apos 6 meses. As amostras foram fotopolimerizadas imediatamente ou com 1, 5 e 10 min de atraso. Resultados: Máxima solubilidade e mínima alteração na opacidade e estabilidade da cor em 6 meses foram observadas no grupo com fotopolimerização tardia em 10 min. Uma diferença significativa foi observada na solubilidade das amostras fotopolimerizadas após 10 min e 1 min. Diferenças significativas também foram observadas na opacidade e estabilidade de cor das amostras fotopolimerizadas após 10 min e em todos os outros grupos (P <0,05). Conclusão: A fotopolimerizaçao tardia em 1 min diminuiu a solubilidade das amostras CIVMR em comparação com a fotopolimerizaçao imediata ou após 5 min. Embora essa diferença não tenha alcançado significância estatística. A estabilidade da cor e as mudanças na opacidade são influenciadas principalmente por reações ácido-base, em vez de reações causadas pela polimerização(AU)

Hygroscopic expansion of bulk fill composites: A three-month report / Expansão higroscópica de compósitos "bulk fill": um relato de três meses

Polymer networks are considered to be largely affected by water and chemical absorption from environment. Objective: The aim of this study was to evaluate the hygroscopic expansion of bulk-fill composite. Material and Methods: Fifteen disks (5 in each group) with different thickness(4mm/2mm) of Tetric N-Ceram Bulk Fill composite(TB) and Tetric N-Ceram composite(TN) were made according to the manufacturer's instruction and stored in deionized water. The length of each specimen was recorded using a digital micrometer at baseline and at the end of 24 h, 1, 2, 4, 12 weeks intervals. Repeated measure ANOVA and Tukey HSD were used to determine the effect of variables. At 12 weeks, the mean hygroscopic expansion after water immersion ranged between 0. 33±0.09mm for TN to 0.41±0.07mm for TB with 2mm thickness. Repeated measure ANOVA revealed a significant increase in hygroscopic expansion over time (P <0.05). Results: The results indicated that at 24hours and 2weeks there was a significant difference among TN and TB with 4mm thickness (p=0.007 and p=0.023, respectively). The other differences were not significant. Hygroscopic expansion affected by the type of composite and the passing of time. Conclusion: The results showed that the time taken to reach stabilization in hygroscopic expansion was shorter for TN in comparison with TB. For 2mm thickness equilibrium was attained earlier. (AU)

Considera-se que as redes de ligações intrínsecas de polímeros são amplamente afetadas pela absorção de água e produtos químicos do meio ambiente. Objetivo: O objetivo deste estudo foi avaliar a expansão higroscópica do compósito bulk-fill. Material e Métodos: Quinze discos (5 em cada grupo) com diferentes espessuras (4mm / 2mm) de compósito Tetric N-Ceram Bulk Fill (TB) e Tetric N-Ceram (TN) foram confeccionados de acordo com as instruções do fabricante e armazenados em água deionizada. O comprimento de cada espécime foi registrado usando um micrômetro digital no início e no final de 24 h, 1, 2, 4, 12 semanas de intervalo. O teste de medidas repetidas ANOVA e Tukey foram usados para determinar o efeito das variáveis. Às 12 semanas, a expansão higroscópica média após imersão em água variou entre 0,33 ± 0,09mm para NT a 0,41 ± 0,07mm para TB com 2mm de espessura. ANOVA revelou um aumento significativo na expansão higroscópica ao longo do tempo (P <0,05). Resultados: Os resultados indicaram que às 24h e 2 semanas houve diferença significativa entre TN e TB com 4mm de espessura (p=0,007 e p=0,023, respectivamente). As outras diferenças não foram significativas. A expansão higroscópica foi afetada pelo tipo de compósito e pelo tempo. Conclusão: Os resultados mostraram que o tempo necessário para alcançar a estabilização na expansão higroscópica foi menor para TN em comparação com TB. Para 2 mm de espessura o equilíbrio foi atingido mais cedo. (AU)