RESUMO
ABSTRACT Purpose: To evaluate inflammatory response in critical bone injuries after implantation of the biomaterial composed of hydroxyapatite (HA)/poly (lactic-coglycolic acid) (PLGA)/BLEED. Methods: Forty-eight male Wistar rats (280 ± 20 grams) were divided into two groups: control group (CG), in which the animals do not receive any type of treatment; and biomaterial group (BG), in which the animals received the HA/PLGA/BLEED scaffold. Critical bone injury was induced in the medial region of the skull calotte with the aid of a trephine drill 8 mm in diameter. The biomaterial was implanted in the form of 1.5-mm thick scaffolds. Serum and calotte were collected at one, three and seven days. Results: Biomaterial had a significant effect on the morphological structure of the bone, accelerating osteoblast activation within three days, without causing exacerbated systemic inflammation. In addition, quantitative real-time polymerase chain reaction (qRT-PCR) analysis showed that BG induced upregulation of osteogenic genes such as runt-related transcription factor 2, and stimulated genes of inflammatory pathways such as tumor necrosis factor-α, on the first day without overexpressing genes related to bone matrix degradation, such as tissue inhibitor of metalloproteinases-1 and matrix metalloproteinase-9. Conclusions: The HA/PLGA/BLEED® association can be used as a bone graft to aid bone repair, as it is capable of modulating expression of important genes at this stage of the repair process.
RESUMO
ABSTRACT Purpose To evaluate and compare two types of different scaffolds in critical bone defects in rats. Methods Seventy male Wistar rats (280 ± 20 grams) divided into three groups: control group (CG), untreated animals; biomaterial group 1 (BG1), animals that received the scaffold implanted hydroxyapatite (HA)/poly(lactic-co-glycolic) acid (PLGA); and biomaterial group 2 (BG2), animals that received the scaffolds HA/PLGA/Bleed. The critical bone defect was induced in the medial region of the skull calotte with the aid of an 8-mm-diameter trephine drill. The biomaterial was implanted in the form of 1.5 mm thick scaffolds, and samples were collected after 15, 30 and 60 days. Non-parametric Mann-Whitney test was used, with the significance level of 5% (p ≤ 0.05). Results Histology revealed morphological and structural differences of the neoformed tissue between the experimental groups. Collagen-1 (Col-1) findings are consistent with the histological ones, in which BG2 presented the highest amount of fibers in its tissue matrix in all evaluated periods. In contrast, the results of receptor activator of nuclear factor kappa-Β ligand (Rank-L) immunoexpression were higher in BG2 in the periods of 30 and 60 days, indicating an increase of the degradation of the biomaterial and the remodeling activity of the bone. Conclusions The properties of the HA/PLGA/Bleed scaffold were superior when compared to the scaffold composed only by HA/PLGA.